CN115142173A - 一种海岛型纤维弹性面料 - Google Patents

一种海岛型纤维弹性面料 Download PDF

Info

Publication number
CN115142173A
CN115142173A CN202210617965.XA CN202210617965A CN115142173A CN 115142173 A CN115142173 A CN 115142173A CN 202210617965 A CN202210617965 A CN 202210617965A CN 115142173 A CN115142173 A CN 115142173A
Authority
CN
China
Prior art keywords
sea
island
component
fiber
elastic fabric
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN202210617965.XA
Other languages
English (en)
Inventor
季嵩
宋跃武
王水萍
孙晓东
管文泉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nantong Dilen Co ltd
Original Assignee
Nantong Dilen Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nantong Dilen Co ltd filed Critical Nantong Dilen Co ltd
Priority to CN202210617965.XA priority Critical patent/CN115142173A/zh
Publication of CN115142173A publication Critical patent/CN115142173A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种海岛型纤维弹性面料，由经纱和纬纱沉浮交织而成，所述经纱中含有三组分海岛型纤维，或所述纬纱中含有三组分海岛型纤维，或所述经纱和所述纬纱中均含有三组分海岛型纤维，或所述经纱和所述纬纱100％使用三组分海岛型纤维。本发明可使得所制备的海岛型纤维弹性面料具有桃皮绒外观及触感，优越的回弹性，轻巧的伸展性，柔软的手感，自由伸展无约束的时尚面料，能够满足了当下人们追求极高的穿着舒适度。

Description

一种海岛型纤维弹性面料
技术领域
本发明涉及面料技术领域，尤其涉及一种海岛型纤维弹性面料。
背景技术
我国是世界上最大的纺织品服装制备国、出口国和消费国，出口额占全球出口贸易的四分之一以上，随着人们生活水平的不断提高，人们对服装性能的要求不断提高；制作服装的面料的布面光泽度、弹性、手感以及风格等越来越受到人们的关注。
目前，服装正向着方便化发展，以适应快节奏的现代化生活；因为弹性织物的伸缩自如、舒适合体等性能迎合了现代人追求舒适随意、方便快捷的生活方式，所以弹性面料的服装广泛地被消费者所喜爱和穿着。
弹性面料用于主要用于制作成服装，可增加服装的舒适性和贴身性，在现有制备的弹性面料中，往往弹力过于生硬，柔软型和伸展性较差，大大降低了人们穿着的舒适度。
发明内容
为了现有技术存在的上述技术缺陷，本发明提供了一种海岛型纤维弹性面料，可以有效解决背景技术中的问题。
为了解决上述技术问题，本发明提供的技术方案具体如下：
本发明实施例公开了一种海岛型纤维弹性面料，由经纱和纬纱沉浮交织而成，所述经纱中含有三组分海岛型纤维，或所述纬纱中含有三组分海岛型纤维，或所述经纱和所述纬纱中均含有三组分海岛型纤维，或所述经纱和所述纬纱100％使用三组分海岛型纤维；其中所述三组分海岛型纤维在本实施例所述的海岛型纤维弹性面料中的混率为50％～100％。
在上述任一方案中优选的是，所述三组分海岛型纤维包括岛组分和海组分；所述岛组分为双组分，包括A组分和B组分,所述A组分与所述B组分的粘度差在不小于0.4，所述A组分和所述B组分可以是聚对苯二甲酸乙二醇酯、聚对苯二甲酸丙二酯、聚酰胺以及聚丙烯等任意的组合。
在上述任一方案中优选的是，所述海组分为氢氧化钠可溶解的纤维或利用介质水在容器内130摄氏度以下溶解的纤维，至少包括PVA水溶性聚酯。
在上述任一方案中优选的是，所述岛组分与所述海组分的占比为50：50～95：5。
在上述任一方案中优选的是，所述岛组分和所述海组分可以是非再生，也可以是再生；其中再生100％可以是化学法，也可以是物理法，也可以是半化学半物理法。
在上述任一方案中优选的是，所述岛组分和所述海组分纤维的光泽可以是全消光、半消光、有光的任意组合，也可以是改性与非改性的任意组合。
在上述任一方案中优选的是，所述岛组分和所述海组分纤维的断面可以是花生形，圆形，长方形，正方形，扁平形等几何形状，所述岛组分和所述海组分纤维可以是实体，也可以是中空等。
在上述任一方案中优选的是，面料的纱线中可含其他再生或非再生化学纤维、再生或非再生天然纤维。
在上述任一方案中优选的是，所述再生化学纤维包括再生涤纶短纤维、再生涤纶长丝、再生尼龙短纤维、再生尼龙长丝等。
在上述任一方案中优选的是，所述非再生化学纤维包括非再生涤纶短纤维、非再生涤纶长丝、非再生尼龙短纤维、非再生尼龙长丝等。
在上述任一方案中优选的是，所述再生或非再生天然纤维包括羊毛纤维或棉纤维等。
在上述任一方案中优选的是，可以使用含功能性的纤维，所述含功能性的纤维包括抗静电、抗病毒、防污、防虫和阻燃等功能性纤维。
在上述任一方案中优选的是，面料的经密度为50～500根/cm，纬密度为50～500根/cm。
在上述任一方案中优选的是，面料的组织为三原组织、三原变化组织、多层组织等，所述经纱和纬纱按照交织，根据组织的最小单位进行配列，其中，所述配列包括经纬纱线根数的比例及经纬纱线粗细的比例。
在上述任一方案中优选的是，面料的门幅100～300cm；面料的弹性伸长率为5％-50％，弹性回复率大于70％；面料的克重范围为30-500g/㎡；面料的经向和纬向的撕裂强度大于4N。
在上述任一方案中优选的是，面料采用的穿综方法为顺穿法、逆穿法、飞穿法、照图穿法、间断穿法、分区穿法、及相互的组合；其中，所述经纱的穿筘，可以是偶数倍的穿入，也可以奇数倍的穿入。
在上述任一方案中优选的是，面料可以在后加工时设置有纳米防污防抗静电抗病毒、阻燃等加工操作，也可以在后加工时设置印花、压花、压光、涂层、贴膜、吸汗、防泼水、单向导湿等加工操作。
在上述任一方案中优选的是，海岛型纤维弹性面料的制备方法，包括以下步骤：步骤一：将单丝纤度在0.01～0.3dtex之间的三组分海岛型纤维进行机织形成机织坯布；
步骤二：在50℃对坯布进行精练20min后，在50℃下冷堆开纤，然后在130℃进行本练20min，再在170℃下定型；
步骤三：定型后在130℃染色30min，最后在180℃下定型，得到海岛型纤维弹性面料。
在上述任一方案中优选的是，开纤时先进行冷堆，利用药剂进行减量处理，减量率为15％～35％，开纤率大于80％。
在上述任一方案中优选的是，通过公式：减量率％＝(Wo-Wi)/Wo*100，计算减量率；Wo为碱减量前干燥试样质量；Wi为碱减量后干燥试样质量。
在上述任一方案中优选的是，通过公式：
Figure BDA0003674045000000041
计算开纤率。
在上述任一方案中优选的是，通过对氢氧化钠的比例及堆置时间的进行调节，如下表所示，当减量率大于22.7％时，开纤充分，能够充分体现海岛型纤维弹性面料的特点。
与现有技术相比，本发明的有益效果：
本发明提供了一种海岛型纤维弹性面料，该制备方法包括三组分海岛型纤维纱线的制备、胚布、加工到成品，可使得所制备的海岛型纤维弹性面料具有桃皮绒外观及触感，优越的回弹性，轻巧的伸展性，柔软的手感，自由伸展无约束的时尚面料，能够满足了当下人们追求极高的穿着舒适度。
附图说明
附图用于对本发明的进一步理解，与本发明的实施例一起用于解释本发明，并不构成对本发明的限制。
图1为本发明海岛型纤维弹性面料的纤维示意图；
图2为本发明海岛型纤维弹性面料的纤维花生形断面示意图；
图3为本发明海岛型纤维弹性面料的纤维圆形断面示意图；
图4为本发明海岛型纤维弹性面料的纤维中空型断面示意图；
图5为本发明海岛型纤维弹性面料的纤维扁平型断面示意图；
图6为本发明海岛型纤维弹性面料的纤维十字型断面示意图；
图7为本发明海岛型纤维弹性面料的纤维八角中空型断面示意图；
图8为本发明海岛型纤维弹性面料的纤维接合型断面示意图；
图9为本发明海岛型纤维弹性面料的纤维芯鞘型断面示意图；
图10为本发明海岛型纤维弹性面料的纤维多芯鞘型断面示意图；
图11为本发明海岛型纤维弹性面料的纤维多层接合型断面示意图；
图12为本发明海岛型纤维弹性面料的不同开纤状态下纤维示意图。
具体实施方式
为了使本发明的目的、技术方案及优点更加清楚明白，以下结合附图及实施例，对本发明进行进一步详细说明。应当理解，此处所描述的具体实施例仅仅用以解释本发明，并不用于限定本发明。
需要说明的是，当元件被称为“固定于”或“设置于”另一个元件，它可以直接在另一个元件上或者间接在该另一个元件上。当一个元件被称为是“连接于”另一个元件，它可以是直接连接到另一个元件或间接连接至该另一个元件上。
在本发明的描述中，需要理解的是，术语“长度”、“宽度”、“上”、“下”、“前”、“后”、“左”、“右”、“竖直”、“水平”、“顶”、“底”“内”、“外”等指示的方位或位置关系为基于附图所示的方位或位置关系，仅是为了便于描述本发明和简化描述，而不是指示或暗示所指的装置或元件必须具有特定的方位、以特定的方位构造和操作，因此不能理解为对本发明的限制。
此外，术语“第一”、“第二”仅用于描述目的，而不能理解为指示或暗示相对重要性或者隐含指明所指示的技术特征的数量。由此，限定有“第一”、“第二”的特征可以明示或者隐含地包括一个或者更多个该特征。在本发明的描述中，“多个”的含义是两个或两个以上，除非另有明确具体的限定。
为了更好地理解上述技术方案，下面将结合说明书附图及具体实施方式对本发明技术方案进行详细说明。
如图1所示，本发明提供了一种海岛型纤维弹性面料，由经纱和纬纱沉浮交织而成，所述经纱中含有三组分海岛型纤维，或所述纬纱中含有三组分海岛型纤维，或所述经纱和所述纬纱中均含有三组分海岛型纤维，或所述经纱和所述纬纱100％使用三组分海岛型纤维；其中所述三组分海岛型纤维在本实施例所述的海岛型纤维弹性面料中的混率为50％～100％。
在本实施例所述的海岛型纤维弹性面料中，所述三组分海岛型纤维包括岛组分和海组分；所述岛组分为双组分，包括A组分和B组分,所述A组分与所述B组分的粘度差在不小于0.4，所述A组分和所述B组分可以是聚对苯二甲酸乙二醇酯、聚对苯二甲酸丙二酯、聚酰胺以及聚丙烯等任意的组合。
在本实施例所述的海岛型纤维弹性面料中，所述海组分为氢氧化钠可溶解的纤维或利用介质水在容器内130摄氏度以下溶解的纤维，至少包括PVA水溶性聚酯。
在本实施例所述的海岛型纤维弹性面料中，所述岛组分与所述海组分的占比为50：50～95：5。
在本实施例所述的海岛型纤维弹性面料中，所述岛组分和所述海组分可以是非再生，也可以是再生；其中再生100％可以是化学法，也可以是物理法，也可以是半化学半物理法。
在本实施例所述的海岛型纤维弹性面料中，所述岛组分和所述海组分纤维的光泽可以是全消光、半消光、有光的任意组合，也可以是改性与非改性的任意组合。
如图2至图11所示，在本实施例所述的海岛型纤维弹性面料中，所述岛组分和所述海组分纤维的断面可以是花生形，圆形，长方形，正方形，扁平形、十字型、八角中空型、接合型、芯鞘型、多芯鞘型、错层接合型等任意形状，所述岛组分和所述海组分纤维可以是实体，也可以是中空等。
在本实施例所述的海岛型纤维弹性面料中，面料的纱线中可含其他再生或非再生化学纤维、再生或非再生天然纤维。
在本实施例所述的海岛型纤维弹性面料中，所述再生化学纤维包括再生涤纶短纤维、再生涤纶长丝、再生尼龙短纤维、再生尼龙长丝等。
在本实施例所述的海岛型纤维弹性面料中，所述非再生化学纤维包括非再生涤纶短纤维、非再生涤纶长丝、非再生尼龙短纤维、非再生尼龙长丝等。
在本实施例所述的海岛型纤维弹性面料中，所述再生或非再生天然纤维包括羊毛纤维或棉纤维等。
在实际应用中，通过采用不同的纤维能够制得不同材质的面料，进而可通过结合不同材纤维的各个优点，可得到应用于不同需求的面料。
在本实施例所述的海岛型纤维弹性面料中，可以使用含功能性的纤维，所述含功能性的纤维包括抗静电、抗病毒、防污、防虫和阻燃等功能性纤维。
在本实施例所述的海岛型纤维弹性面料中，面料的经密度为50～500根/cm，纬密度为50～500根/cm。
在本实施例所述的海岛型纤维弹性面料中，面料的组织为三原组织、三原变化组织、多层组织等，所述经纱和纬纱按照交织，根据组织的最小单位进行配列，其中，所述配列包括经纬纱线根数的比例及经纬纱线粗细的比例。
在本实施例所述的海岛型纤维弹性面料中，面料的门幅100～300cm；面料的弹性伸长率为5％-50％，弹性回复率大于70％；面料的克重范围为30-500g/㎡；面料的经向和纬向的撕裂强度大于4N。
在本实施例所述的海岛型纤维弹性面料中，面料采用的穿综方法为顺穿法、逆穿法、飞穿法、照图穿法、间断穿法、分区穿法、及相互的组合；其中，所述经纱的穿筘，可以是偶数倍的穿入，也可以奇数倍的穿入。
在本实施例所述的海岛型纤维弹性面料中，面料可以在后加工时设置有纳米防污防抗静电抗病毒、阻燃等加工操作，也可以在后加工时设置印花、压花、压光、涂层、贴膜、吸汗、防泼水、单向导湿等加工操作。
在本实施例所述的海岛型纤维弹性面料中，海岛型纤维弹性面料的制备方法，包括以下步骤：
步骤一：将单丝纤度在0.01～0.3dtex之间的三组分海岛型纤维进行机织形成机织坯布；
步骤二：在50℃对坯布进行精练20min后，在50℃下冷堆开纤，然后在130℃进行本练20min，再在170℃下定型；
步骤三：定型后在130℃染色30min，最后在180℃下定型，得到海岛型纤维弹性面料。
其中，开纤时先进行冷堆，利用药剂进行减量处理，减量率为15％～35％，开纤率大于80％。
进一步的，通过公式：减量率％＝(Wo-Wi)/Wo*100，计算减量率；Wo为碱减量前干燥试样质量；Wi为碱减量后干燥试样质量。
进一步的，通过公式：
Figure BDA0003674045000000101
计算开纤率。
进一步的，如图11所示，通过对氢氧化钠的比例及堆置时间的进行调节，当减量率大于22.7％时，开纤充分，能够充分体现海岛型纤维弹性面料的特点。
与现有技术相比，本发明提供的有益效果是：
本发明提供了一种海岛型纤维弹性面料，该制备方法包括三组分海岛型纤维纱线的制备、胚布、加工到成品，可使得所制备的海岛型纤维弹性面料具有桃皮绒外观及触感，优越的回弹性，轻巧的伸展性，柔软的手感，自由伸展无约束的时尚面料，能够满足了当下人们追求极高的穿着舒适度。
以上仅为本发明的优选实施例而已，并不用于限制本发明，尽管参照前述实施例对本发明进行了详细的说明，对于本领域的技术人员来说，其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换。凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。

Claims (10)

1.一种海岛型纤维弹性面料，其特征在于：所述弹性面料由经纱和纬纱沉浮交织而成，所述经纱中含有三组分海岛型纤维，或所述纬纱中含有三组分海岛型纤维，或所述经纱和所述纬纱中均含有三组分海岛型纤维，或所述经纱和所述纬纱100％使用三组分海岛型纤维。
2.根据权利要求1所述的海岛型纤维弹性面料，其特征在于：所述三组分海岛型纤维在海岛型纤维弹性面料中的混率范围为50％～100％。
3.根据权利要求2所述的海岛型纤维弹性面料，其特征在于：所述三组分海岛型纤维包括岛组分和海组分，所述岛组分包括A组分和B组分,所述A组分与所述B组分的粘度差不小于0.4dl/g，所述A组分和所述B组分为聚对苯二甲酸乙二醇酯、聚对苯二甲酸丙二酯、聚酰胺以及聚丙烯的任意组合。
4.根据权利要求3所述的海岛型纤维弹性面料，其特征在于：所述海组分为氢氧化钠可溶解的纤维或利用介质水在容器内130摄氏度以下溶解的纤维，至少包括PVA水溶性聚酯。
5.根据权利要求4所述的海岛型纤维弹性面料，其特征在于：所述岛组分与所述海组分的占比为50：50～95：5。
6.根据权利要求5所述的海岛型纤维弹性面料，其特征在于：所述岛组分和所述海组分为非再生或再生。
7.根据权利要求6所述的海岛型纤维弹性面料，其特征在于：所述岛组分和所述海组分纤维的光泽为全消光、半消光、有光的任意组合，或改性与非改性的任意组合。
8.根据权利要求7所述的海岛型纤维弹性面料，其特征在于：所述岛组分和所述海组分纤维的断面为几何形状，所述岛组分和所述海组分纤维为实体或中空。
9.根据权利要求8所述的海岛型纤维弹性面料，其特征在于：所述经纱和纬纱中包括再生或非再生化学纤维、再生或非再生天然纤维中的一种或多种。
10.根据权利要求9所述的海岛型纤维弹性面料，其特征在于：所述海岛型纤维弹性面料中，面料的门幅100～300cm；面料的弹性伸长率为5％-50％，弹性回复率大于70％；面料的克重范围为30-500g/㎡；面料的经向和纬向的撕裂强度大于4N。
CN202210617965.XA 2022-06-01 2022-06-01 一种海岛型纤维弹性面料 Pending CN115142173A (zh)