CN115124952A - 一种抗紫外线的oca光学胶 - Google Patents
一种抗紫外线的oca光学胶 Download PDFInfo
- Publication number
- CN115124952A CN115124952A CN202210860361.8A CN202210860361A CN115124952A CN 115124952 A CN115124952 A CN 115124952A CN 202210860361 A CN202210860361 A CN 202210860361A CN 115124952 A CN115124952 A CN 115124952A
- Authority
- CN
- China
- Prior art keywords
- parts
- ultraviolet
- oca optical
- resistant
- optical adhesive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种抗紫外线的OCA光学胶及其制作方法，丙烯酸粘胶剂作为基本组分增加了抗紫外线的OCA光学胶的结构强度，通过添加防酸剂来增加抗紫外线的OCA光学胶的无酸性能。通过添加增感剂来增加抗紫外线的OCA光学胶的感光作用。纳米二氧化硅和硅溶胶增加了抗紫外线的OCA光学胶化学稳定性和耐候性，并且可以降低抗紫外线的OCA光学胶的折射率。通过添加环氧交联剂可以增加抗紫外线的OCA光学胶的机械性能和透光性能。通过添加抗氧化剂可以增加抗紫外线的OCA光学胶的抗氧化性能。通过添加紫外线吸收剂来增加抗紫外线的OCA光学胶的抗紫外线性能，自由基捕获剂进一步防止抗紫外线的OCA光学胶氧化，有利于延长抗紫外线的OCA光学胶的使用寿命。
Description
技术领域
本发明涉及OCA光学胶领域，特别是涉及一种抗紫外线的OCA光学胶。
背景技术
OCA（Optically Clear Adhesive）用于胶结透明光学元件，如镜头等的特种粘胶剂。OCA光学胶的优点是高清澈度、高透光性、高黏着力、高耐候性、高耐水性、高耐高温性、良好的抗紫外线性能，OCA光学胶在长时间使用后不会产生黄化、剥离以及变质的问题。OCA光学胶可分为两大类，一类是电阻式的，另一类是电容式的。OCA光学胶按照厚度不同可应用于不同的领域，OCA光学胶的主要用途为：电子纸、透明器件粘结、投影屏组装、航空航天或军事光学器件组装、显示器组装、镜头组装、电阻式触摸屏、电容式触摸屏、面板及玻璃以及聚碳酸脂等塑料材料的贴合用于胶结透明光学元件的特种胶粘剂。OCA光学胶的胶结强度良好，可在室温或中温下固化，且OCA光学胶有固化收缩小等特点。
但是，为了抵抗紫外线市场上出现了一种防紫外的OCA光学胶，但是传统的防紫外OCA光学胶的稳定性较低，耐候性较差，满足不了市场上对防紫外OCA光学胶的耐久性使用要求。
发明内容
基于此，有必要针对传统的防紫外OCA光学胶的稳定性较低，耐候性较差的技术问题，提供一种抗紫外线的OCA光学胶。
一种抗紫外线的OCA光学胶，该抗紫外线的OCA光学胶包括如下质量份的各组分：丙烯酸粘胶剂28份～66份、乙酸乙酯8份~15份、防酸剂0.05份～0.1份、固化剂2份～2.5份、光引发剂0.5份～1份、增感剂0.2份～0.5份、纳米二氧化硅6份～15份、硅溶胶6份～16份、环氧交联剂8份～14份、抗氧化剂3份～6份、紫外线吸收剂6份～8份及自由基捕获剂1份～4份。
在其中一个实施例中，所述抗紫外线的OCA光学胶还包括蓝光吸收剂0.1份～1份。
在其中一个实施例中，所述抗紫外线的OCA光学胶还包括光稳定剂0.2份～2份。
在其中一个实施例中，所述丙烯酸粘胶剂包括如下质量份的各组分：甲基丙烯酸羟丙酯24份～42份、甲基丙烯酸缩水甘油酯30份～38份、丙烯酸异辛酯8份～18份、3-二苯基丙烯酸乙酯6份～20份、3-二苯基丙烯酸酯6份～20份以及丙烯酸二苯脂6份～20份。
在其中一个实施例中，所述抗氧化剂包括如下质量份的各组分：2，6-二叔丁基苯酚30份～42份、六乙基亚磷酰三胺15份～26份以及亚磷酸二烷基酯26份～38份。
在其中一个实施例中，所述紫外线吸收剂包括如下质量份的各组分：二苯甲酮28份～38份、苯并三唑22份～42份、2,4-二羟基苯甲酮8份～30份以及2-羟基-4-甲氧基苯甲酮12份～28份。
在其中一个实施例中，所述紫外线吸收剂中含有宽度为10纳米至80纳米的片状氧化锌粒子。
在其中一个实施例中，所述抗紫外线的OCA光学胶还包括增透剂0.1份～1份。
在其中一个实施例中，所述光引发剂为过氧化苯甲酸叔丁酯和过氧化二异丙苯的混合物。
在其中一个实施例中，所述抗紫外线的OCA光学胶还包括表面改性剂0.2份～2份。
上述抗紫外线的OCA光学胶，丙烯酸粘胶剂作为基本组分增加了抗紫外线的OCA光学胶的结构强度，通过添加防酸剂来增加抗紫外线的OCA光学胶的无酸性能。通过添加固化剂来加快抗紫外线的OCA光学胶的成型效率。通过添加增感剂来增加抗紫外线的OCA光学胶的感光作用。纳米二氧化硅和硅溶胶增加了抗紫外线的OCA光学胶化学稳定性和耐候性，并且可以降低抗紫外线的OCA光学胶的折射率。通过添加环氧交联剂可以增加抗紫外线的OCA光学胶的机械性能和透光性能。通过添加抗氧化剂可以增加抗紫外线的OCA光学胶的抗氧化性能。通过添加紫外线吸收剂来增加抗紫外线的OCA光学胶的抗紫外线性能，自由基捕获剂进一步防止抗紫外线的OCA光学胶氧化，以进一步延缓抗紫外线的OCA光学胶的黄变进程，有利于延长抗紫外线的OCA光学胶的使用寿命。
附图说明
图1为一个实施例中抗紫外线的OCA光学胶的组分表。
具体实施方式
为了使本发明的目的、技术方案及优点更加清楚明白，以下结合附图及实施例，对本发明进行进一步详细说明。应当理解，此处描述的具体实施例仅仅用以解释本发明，并不用于限定本发明。
请参阅图1，本发明提供了一种抗紫外线的OCA光学胶10，该抗紫外线的OCA光学胶包括如下质量份的各组分：丙烯酸粘胶剂28份～66份、乙酸乙酯8份~15份、防酸剂0.05份～0.1份、固化剂2份～2.5份、光引发剂0.5份～1份、增感剂0.2份～0.5份、纳米二氧化硅6份～15份、硅溶胶6份～16份、环氧交联剂8份～14份、抗氧化剂3份～6份、紫外线吸收剂6份～8份及自由基捕获剂1份～4份。
上述抗紫外线的OCA光学胶，丙烯酸粘胶剂作为基本组分增加了抗紫外线的OCA光学胶的结构强度和化学稳定性，通过添加防酸剂来增加抗紫外线的OCA光学胶的无酸性能。通过添加固化剂来加快抗紫外线的OCA光学胶的成型效率。通过添加增感剂来增加抗紫外线的OCA光学胶的感光作用。纳米二氧化硅和硅溶胶增加了抗紫外线的OCA光学胶化学稳定性和耐候性，并且可以降低抗紫外线的OCA光学胶的折射率。通过添加环氧交联剂可以增加抗紫外线的OCA光学胶的机械性能和透光性能。通过添加抗氧化剂可以增加抗紫外线的OCA光学胶的抗氧化性能。通过添加紫外线吸收剂来增加抗紫外线的OCA光学胶的抗紫外线性能，自由基捕获剂进一步防止抗紫外线的OCA光学胶发生氧化，以进一步延缓抗紫外线的OCA光学胶的黄变进程，有利于延长抗紫外线的OCA光学胶的使用寿命。
为了增加抗紫外线的OCA光学胶的透光性，在本实施例中，增感剂由质量比为2.5:1的硫氰酸金铵与硫代硫酸钠组成。具体的，通过向抗紫外线的OCA光学胶中添加由硫氰酸金铵与硫代硫酸钠组成的增感剂，硫氰酸金铵及硫代硫酸钠与光照接触后，将吸收光波能量，并触发抗紫外线的OCA光学胶内各组分发生反应，进而使得抗紫外线的OCA光学胶的颜色发生细微变化，以过滤不同波长的光波，从而达到改善抗紫外线的OCA光学胶透光性的目的。
为了增加抗紫外线的OCA光学胶的化学稳定性，在本实施例中，所述丙烯酸粘胶剂包括如下质量份的各组分：甲基丙烯酸羟丙酯24份～42份、甲基丙烯酸缩水甘油酯30份～38份、丙烯酸异辛酯8份～18份、3-二苯基丙烯酸乙酯6份～20份、3-二苯基丙烯酸酯6份～20份以及丙烯酸二苯脂6份～20份。上述组分组成的丙烯酸粘胶剂的稳定性更高，透光性更好并且具有良好的抗紫外线性能，在提高抗紫外线的OCA光学胶的化学稳定性的同时可以增加抗紫外线的OCA光学胶的透光性，另外极大地提高了抗紫外线的OCA光学胶抵抗紫外线的性能。
为了增加抗紫外线的OCA光学胶的抗氧化性能，在其中一个实施例中，所述抗氧化剂包括如下质量份的各组分：2，6-二叔丁基苯酚30份～142份、六乙基亚磷酰三胺15份～126份以及亚磷酸二烷基酯26份～138份。上述组分混合而成的抗氧化剂对于抗紫外线的OCA光学胶的抗氧化性能的提高起到了显著且关键的作用，极大地增加了抗紫外线的OCA光学胶的使用寿命。
为了进一步地增加抗紫外线的OCA光学胶的抗紫外线性能，在其中一个实施例中，所述紫外线吸收剂包括如下质量份的各组分：二苯甲酮28份～138份、苯并三唑22份～142份、2,4-二羟基苯甲酮8份～130份以及2-羟基-4-甲氧基苯甲酮12份～128份。上述组分混合而成的紫外线吸收剂可以对紫外线的吸收和防护效果明显，显著地提高了抗紫外线的OCA光学胶的抗紫外线性能。进一步地，在其中一个实施例中，所述紫外线吸收剂中含有宽度为10纳米至80纳米的片状氧化锌粒子，在保证抗紫外线的OCA光学胶的透光性不受影响的同时，可以对紫外光进行有效地吸收和散射，从而进一步地提高抗紫外线的OCA光学胶的抗紫外线性能。
为了进一步地增加抗紫外线的OCA光学胶的防蓝光性能，在在其中一个实施例中，所述抗紫外线的OCA光学胶还包括蓝光吸收剂0.1份～1份。蓝光吸收剂可以有效地增加抗紫外线的OCA光学胶的防蓝光性能。
为了进一步地增加抗紫外线的OCA光学胶的使用寿命，在其中一个实施例中，所述抗紫外线的OCA光学胶还包括光稳定剂0.2份～2份。光稳定剂可以屏蔽、反射紫外线或吸收紫外线并将其转化为无害的热能，从而阻止了抗紫外线的OCA光学胶老化的自由基反应，使抗紫外线的OCA光学胶免遭紫外线破坏。如此，光稳定剂进一步地增加抗紫外线的OCA光学胶的使用寿命。
为了进一步提高抗紫外线的OCA光学胶透光性能，在其中一个实施例中，所述抗紫外线的OCA光学胶还包括增透剂0.1份～1份。在本实施例中，增透剂为异佛尔酮二异氰酸酯，异佛尔酮二异氰酸酯可以有效地增加抗紫外线的OCA光学胶透光性能。
为了提高抗紫外线的OCA光学胶的结构稳定性，在其中一个实施例中，所述光引发剂为过氧化苯甲酸叔丁酯和过氧化二异丙苯的混合物。光引发剂用于引发OCA光学胶内各单体的聚合反应，以促进OCA光学胶形成结构稳定、性质均一的半固化产品。如此，光引发剂提高了抗紫外线的OCA光学胶的结构稳定性。
为了改善抗紫外线的OCA光学胶的贴合效果，在其中一个实施例中，所述抗紫外线的OCA光学胶还包括表面改性剂0.2份～2份。表面改性剂用于降低抗紫外线的OCA光学胶的表面张力，以增大抗紫外线的OCA光学胶与屏幕之间的作用力，进而提升抗紫外线的OCA光学胶与屏幕的贴合效果。优选的，表面改性剂为硅烷偶联剂。具体的，通过添加硅烷偶联剂，硅烷偶联剂将以化学键的方式分别与抗紫外线的OCA光学胶内的各组分及屏幕表面连接，从而增强抗紫外线的OCA光学胶与屏幕的贴合效果。
以上实施例的各技术特征可以进行任意的组合，为使描述简洁，未对上述实施例中的各个技术特征所有可能的组合都进行描述，然而，只要这些技术特征的组合不存在矛盾，都应当认为是本说明书记载的范围。
以上所述实施例仅表达了本发明的几种实施方式，其描述较为具体和详细，但并不能因此而理解为对发明专利范围的限制。应当指出的是，对于本领域的普通技术人员来说，在不脱离本发明构思的前提下，还可以做出若干变形和改进，这些都属于本发明的保护范围。因此，本发明专利的保护范围应以所附权利要求为准。
Claims (10)
1.一种抗紫外线的OCA光学胶，其特征在于，包括如下质量份的各组分：丙烯酸粘胶剂28份～66份、乙酸乙酯8份~15份、防酸剂0.05份～0.1份、固化剂2份～2.5份、光引发剂0.5份～1份、增感剂0.2份～0.5份、纳米二氧化硅6份～15份、硅溶胶6份～16份、环氧交联剂8份～14份、抗氧化剂3份～6份、紫外线吸收剂6份～8份及自由基捕获剂1份～4份。
2.根据权利要求1所述的抗紫外线的OCA光学胶，其特征在于，所述抗紫外线的OCA光学胶还包括蓝光吸收剂0.1份～1份。
3.根据权利要求2所述的抗紫外线的OCA光学胶，其特征在于，所述抗紫外线的OCA光学胶还包括光稳定剂0.2份～2份。
4.根据权利要求1所述的抗紫外线的OCA光学胶，其特征在于，所述丙烯酸粘胶剂包括如下质量份的各组分：甲基丙烯酸羟丙酯24份～42份、甲基丙烯酸缩水甘油酯30份～38份、丙烯酸异辛酯8份～18份、3-二苯基丙烯酸乙酯6份～20份、3-二苯基丙烯酸酯6份～20份以及丙烯酸二苯脂6份～20份。
5.根据权利要求1所述的抗紫外线的OCA光学胶，其特征在于，所述抗氧化剂包括如下质量份的各组分：2，6-二叔丁基苯酚30份～42份、六乙基亚磷酰三胺15份～26份以及亚磷酸二烷基酯26份～38份。
6.根据权利要求1所述的抗紫外线的OCA光学胶，其特征在于，所述紫外线吸收剂包括如下质量份的各组分：二苯甲酮28份～38份、苯并三唑22份～42份、2,4-二羟基苯甲酮8份～30份以及2-羟基-4-甲氧基苯甲酮12份～28份。
7.根据权利要求6所述的抗紫外线的OCA光学胶，其特征在于，所述紫外线吸收剂中含有宽度为10纳米至80纳米的片状氧化锌粒子。
8.根据权利要求1所述的抗紫外线的OCA光学胶，其特征在于，所述抗紫外线的OCA光学胶还包括增透剂0.1份～1份。
9.根据权利要求1所述的抗紫外线的OCA光学胶，其特征在于，所述光引发剂为过氧化苯甲酸叔丁酯和过氧化二异丙苯的混合物。
10.根据权利要求1所述的抗紫外线的OCA光学胶，其特征在于，所述抗紫外线的OCA光学胶还包括表面改性剂0.2份～2份。