CN115089754A - 一种医用溶胀高倍吸水湿性敷料（膜布） - Google Patents
一种医用溶胀高倍吸水湿性敷料（膜布） Download PDFInfo
- Publication number
- CN115089754A CN115089754A CN202210752938.3A CN202210752938A CN115089754A CN 115089754 A CN115089754 A CN 115089754A CN 202210752938 A CN202210752938 A CN 202210752938A CN 115089754 A CN115089754 A CN 115089754A
- Authority
- CN
- China
- Prior art keywords
- dressing
- parts
- weight
- mixture
- stirrer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种医用溶胀高倍吸水湿性敷料(膜布)，其原料包括如下重量的组分：纯化水80‑95重量份；几丁聚糖10‑70重量份；胶原肽1‑12重量份；表皮生长因子0.01‑1.5重量份；海藻酸盐0‑10重量份；100％纤维素纤维0‑15重量份。该医用溶胀高倍吸水湿性敷料(膜布)，内部增加了100％纤维素纤维，使敷料内部结构中增加了非晶区，形成导水微孔，具有高保湿的特性，且敷料内部形成氢键交联，使敷料具有高溶胀和微弹性，并且该敷料内部含有水凝螯合基团，提高敷料的重金属离子吸附能力。
Description
技术领域
本发明涉及医用敷料相关技术领域，具体为一种医用溶胀高倍吸水湿性敷料(膜布)。
背景技术
随着对创面愈合过程的病理生理的深入研究，人们对创面愈合过程的理解也越来越深刻，从而导致了医用创面敷料的不断改进与发展。今天，新型的创面护理用敷料相对于早期而言，已经发生了革命性的变化，而且多种不同性能的医用敷料可供临床护理人员选用。对于现有的医用医用敷料来说，还是存有很大一部分问题，就比如：
现有的医用敷料在使用时溶胀性和保湿性较低，容易造成二次机械性损伤，使用具有局限性，为此我们提出一种医用溶胀高倍吸水湿性敷料(膜布)，以便解决上述中所提到的问题。
发明内容
本发明的目的在于提供一种医用溶胀高倍吸水湿性敷料(膜布)，以解决上述背景技术中提出的目前的医用敷料在使用时溶胀性和保湿性较低，容易造成二次机械性损伤，使用具有局限性的问题。
为实现上述目的，本发明提供如下技术方案：一种医用溶胀高倍吸水湿性敷料(膜布)，其原料包括如下重量份数的组分：
一种医用溶胀高倍吸水湿性敷料(膜布)，其原料包括如下重量的组分：
纯化水80-95重量份；
几丁聚糖10-70重量份；
胶原肽1-12重量份；
表皮生长因子0.01-1.5重量份；
海藻酸盐0-10重量份；
100％纤维素纤维0-15重量份。
所述医用溶胀高倍吸水湿性敷料(膜布)的制备包括以下步骤：
步骤(一)：取按重量份的纯化水、几丁聚糖和胶原肽在搅拌机中进行充分搅拌，形成混合物A；
步骤(二)：再按重量份的纯化水、表皮生长因子、海藻酸盐和100％纤维素纤维放入到搅拌机中进行搅拌，形成混合物B；
步骤(三)：再将搅拌均匀的混合物1倒入到装有混合物B的搅拌机中一同搅拌，形成固态粉状混合物C；
步骤(四)：将固态粉状混合物C放入到灭菌装置中进行灭菌处理；
步骤(五)：将灭菌处理后的固态粉状混合物C进行密封包装形成产品。
优选的，所述步骤(一)、步骤(二)和步骤(三)中的搅拌机中的搅拌速率为30-40rpm，搅拌的时间为10-15min。
优选的，所述步骤(四)中灭菌装置采用紫外线灭菌法，在灭菌的同时保证搅拌机的正常搅拌，使其灭菌更加均匀。
一种如权利要求1所述的一种医用溶胀高倍吸水湿性敷料(膜布)的使用方法，使用步骤如下：
步骤(六)：从包装好的产品中取出敷料，并敷与使用者的受伤部或其他肌肤位置，使敷料在使用者的脸上或其他肌肤位置形成膜布；
步骤(七)：待5-15分钟后，可挤压膜布，使敷料内部凝胶深入皮肤；
步骤(八)：再从使用者的受伤部或其他肌肤位置将敷料膜布撕下。
与现有技术相比，本发明的有益效果是：该医用溶胀高倍吸水湿性敷料(膜布)，适用各种创口，其内部增加了100％纤维素纤维，使敷料内部结构中增加了非晶区，形成导水微孔，具有高保湿的特性，且敷料内部形成氢键交联，使敷料具有高溶胀和微弹性，并且该敷料内部含有水凝螯合基团，提高敷料的重金属离子吸附能力。
具体实施方式
下面将对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
本发明提供如下技术方案：
实施例1：
一种医用溶胀高倍吸水湿性敷料(膜布)，其原料包括如下重量份数的组分：
纯化水80重量份；
几丁聚糖10重量份；
胶原肽5重量份；
表皮生长因子0.05重量份；
海藻酸盐2重量份；
100％纤维素纤维5重量份。
所述医用溶胀高倍吸水湿性敷料(膜布)的制备包括以下步骤：
步骤(一)：取按重量份的纯化水、几丁聚糖和胶原肽在搅拌机中进行充分搅拌，形成混合物A，其中搅拌机中的搅拌速率为30-40rpm，搅拌的时间为10-15min；
步骤(二)：再按重量份的纯化水、表皮生长因子、海藻酸盐和100％纤维素纤维放入到搅拌机中进行搅拌，形成混合物B，其中搅拌机中的搅拌速率为30-40rpm，搅拌的时间为10-15min；
步骤(三)：再将搅拌均匀的混合物1倒入到装有混合物B的搅拌机中一同搅拌，形成固态粉状混合物C，其中搅拌机中的搅拌速率为30-40rpm，搅拌的时间为10-15min；
步骤(四)：将固态粉状混合物C放入到灭菌装置中进行灭菌处理，灭菌装置采用紫外线灭菌法，在灭菌的同时保证搅拌机的正常搅拌，使其灭菌更加均匀；
步骤(五)：将灭菌处理后的固态粉状混合物C进行密封包装形成产品。
一种医用溶胀高倍吸水湿性敷料(膜布)的使用方法，使用步骤如下：
步骤(六)：从包装好的产品中取出敷料，并敷与使用者的受伤部或其他肌肤位置，使敷料在使用者的脸上或其他肌肤位置形成膜布；
步骤(七)：待5-15分钟后，可挤压膜布，使敷料内部凝胶深入皮肤；
步骤(八)：再从使用者的受伤部或其他肌肤位置将敷料膜布撕下。
实施例2：
一种医用溶胀高倍吸水湿性敷料(膜布)，其原料包括如下重量份数的组分：
纯化水85重量份；
几丁聚糖30重量份；
胶原肽8重量份；
表皮生长因子3重量份；
海藻酸盐6重量份；
100％纤维素纤维7重量份。
所述医用溶胀高倍吸水湿性敷料(膜布)的制备包括以下步骤：
步骤(一)：取按重量份的纯化水、几丁聚糖和胶原肽在搅拌机中进行充分搅拌，形成混合物A，其中搅拌机中的搅拌速率为30-40rpm，搅拌的时间为10-15min；
步骤(二)：再按重量份的纯化水、表皮生长因子、海藻酸盐和100％纤维素纤维放入到搅拌机中进行搅拌，形成混合物B，其中搅拌机中的搅拌速率为30-40rpm，搅拌的时间为10-15min；
步骤(三)：再将搅拌均匀的混合物1倒入到装有混合物B的搅拌机中一同搅拌，形成固态粉状混合物C，其中搅拌机中的搅拌速率为30-40rpm，搅拌的时间为10-15min；
步骤(四)：将固态粉状混合物C放入到灭菌装置中进行灭菌处理，灭菌装置采用紫外线灭菌法，在灭菌的同时保证搅拌机的正常搅拌，使其灭菌更加均匀；
步骤(五)：将灭菌处理后的固态粉状混合物C进行密封包装形成产品。
一种医用溶胀高倍吸水湿性敷料(膜布)的使用方法，使用步骤如下：
步骤(六)：从包装好的产品中取出敷料，并敷与使用者的受伤部或其他肌肤位置，使敷料在使用者的脸上或其他肌肤位置形成膜布；
步骤(七)：待5-15分钟后，可挤压膜布，使敷料内部凝胶深入皮肤；
步骤(八)：再从使用者的受伤部或其他肌肤位置将敷料膜布撕下。
实施例1：
一种医用溶胀高倍吸水湿性敷料(膜布)，其原料包括如下重量份数的组分：
纯化水90重量份；
几丁聚糖60重量份；
胶原肽10重量份；
表皮生长因子6重量份；
海藻酸盐8重量份；
100％纤维素纤维10重量份。
所述医用溶胀高倍吸水湿性敷料(膜布)的制备包括以下步骤：
步骤(一)：取按重量份的纯化水、几丁聚糖和胶原肽在搅拌机中进行充分搅拌，形成混合物A，其中搅拌机中的搅拌速率为30-40rpm，搅拌的时间为10-15min；
步骤(二)：再按重量份的纯化水、表皮生长因子、海藻酸盐和100％纤维素纤维放入到搅拌机中进行搅拌，形成混合物B，其中搅拌机中的搅拌速率为30-40rpm，搅拌的时间为10-15min；
步骤(三)：再将搅拌均匀的混合物1倒入到装有混合物B的搅拌机中一同搅拌，形成固态粉状混合物C，其中搅拌机中的搅拌速率为30-40rpm，搅拌的时间为10-15min；
步骤(四)：将固态粉状混合物C放入到灭菌装置中进行灭菌处理，灭菌装置采用紫外线灭菌法，在灭菌的同时保证搅拌机的正常搅拌，使其灭菌更加均匀；
步骤(五)：将灭菌处理后的固态粉状混合物C进行密封包装形成产品。
一种医用溶胀高倍吸水湿性敷料(膜布)的使用方法，使用步骤如下：
步骤(六)：从包装好的产品中取出敷料，并敷与使用者的受伤部或其他肌肤位置，使敷料在使用者的脸上或其他肌肤位置形成膜布；
步骤(七)：待5-15分钟后，可挤压膜布，使敷料内部凝胶深入皮肤；
步骤(八)：再从使用者的受伤部或其他肌肤位置将敷料膜布撕下。
尽管已经示出和描述了本发明的实施例，对于本领域的普通技术人员而言，可以理解在不脱离本发明的原理和精神的情况下可以对这些实施例进行多种变化、修改、替换和变型，本发明的范围由所附权利要求及其等同物限定。
Claims (4)
1.一种医用溶胀高倍吸水湿性敷料(膜布)，其原料包括如下重量的组分：
纯化水80-95重量份；
几丁聚糖10-70重量份；
胶原肽1-12重量份；
表皮生长因子0.01-1.5重量份；
海藻酸盐0-10重量份；
100％纤维素纤维0-15重量份。
所述医用溶胀高倍吸水湿性敷料(膜布)的制备包括以下步骤：
步骤(一)：取按重量份的纯化水、几丁聚糖和胶原肽在搅拌机中进行充分搅拌，形成混合物A；
步骤(二)：再按重量份的纯化水、表皮生长因子、海藻酸盐和100％纤维素纤维放入到搅拌机中进行搅拌，形成混合物B；
步骤(三)：再将搅拌均匀的混合物1倒入到装有混合物B的搅拌机中一同搅拌，形成固态粉状混合物C；
步骤(四)：将固态粉状混合物C放入到灭菌装置中进行灭菌处理；
步骤(五)：将灭菌处理后的固态粉状混合物C进行密封包装形成产品。
2.根据权利要求1中所述的一种医用溶胀高倍吸水湿性敷料(膜布)，其特征在于：所述步骤(一)、步骤(二)和步骤(三)中的搅拌机中的搅拌速率为30-40rpm，搅拌的时间为10-15min。
3.根据权利要求1所述的一种医用溶胀高倍吸水湿性敷料(膜布)，其特征在于：所述步骤(四)中灭菌装置采用紫外线灭菌法，在灭菌的同时保证搅拌机的正常搅拌，使其灭菌更加均匀。
4.一种如权利要求1所述的一种医用溶胀高倍吸水湿性敷料(膜布)的使用方法，使用步骤如下：
步骤(六)：从包装好的产品中取出敷料，并敷与使用者的受伤部或其他肌肤位置，使敷料在使用者的脸上或其他肌肤位置形成膜布；
步骤(七)：待5-15分钟后，可挤压膜布，使敷料内部凝胶深入皮肤；
步骤(八)：再从使用者的受伤部或其他肌肤位置将敷料膜布撕下。