CN115044423A - 一种浓缩铁粉去除剂及其制备方法 - Google Patents
一种浓缩铁粉去除剂及其制备方法 Download PDFInfo
- Publication number
- CN115044423A CN115044423A CN202210572027.2A CN202210572027A CN115044423A CN 115044423 A CN115044423 A CN 115044423A CN 202210572027 A CN202210572027 A CN 202210572027A CN 115044423 A CN115044423 A CN 115044423A
- Authority
- CN
- China
- Prior art keywords
- sodium hydroxide
- iron powder
- aes
- ethyl alcohol
- absolute ethyl
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种浓缩铁粉去除剂及其制备方法，本发明采用巯基乙酸、氢氧化钠、CQAL200、AES、APG0810、柠檬酸钠、无水乙醇、去离子水、82009A紫罗兰香精作为原料，其中，巯基乙酸与氢氧化钠配合，以在与铁粉混合反应后显示明显，有效快速去除汽车表面的氧化层，CQAL200、AES、APG0810共同配合，以提高清洗去污能力，柠檬酸钠作为螯合剂，制备后的去除剂无腐蚀、低毒、发泡量稳定，82009A紫罗兰香精的加入使该去除剂散发香味，无刺激性气味。
Description
技术领域
本发明涉及化工技术领域，尤其是涉及一种浓缩铁粉去除剂及其制备方法。
背景技术
铁粉去除剂，也叫氧化层清洗剂，是除掉汽车漆面上氧化层的最佳药剂，铁粉去除剂专门针对漆面氧化层的特性而研究的配方，能够彻底去除漆面及轮毂上的金属氧化物，特别适合白色车翻新时使用，配合魔术粘土使用，不需抛光即可达到抛光的效果。深色车使用具有同样效果；现有的去除剂清洗效果差，清洗时间长，且需要较多用量，因此需要研发一种清洗效果佳、低毒无毒、无腐蚀的铁粉去除剂。
发明内容
针对现有技术的不足，本发明的目的在于提供一种清洗效果佳、无腐蚀低毒的浓缩铁粉去除剂及其制备方法。
为实现上述目的，本发明提供的方案为：一种浓缩铁粉去除剂，包括以下质量百分比：巯基乙酸18-21％；氢氧化钠6-8％；CQAL200 1-3％；AES 0.5-1.5％；APG0810 0.1-1％；柠檬酸钠0.1-0.5％；无水乙醇4-6％；去离子水60-70％；82009A紫罗兰香精0.1-0.2％。
本发明的有益效果为：整体清洗效果佳，有效去除氧化层，该去除剂通过采用巯基乙酸、氢氧化钠、CQAL200、AES、APG0810、柠檬酸钠、无水乙醇、去离子水、82009A紫罗兰香精作为原料，其中，巯基乙酸与氢氧化钠配合，以在与铁粉混合反应后显示明显，有效快速去除汽车表面的氧化层，CQAL200、AES、APG0810共同配合，以提高清洗去污能力，柠檬酸钠作为螯合剂，制备后的去除剂无腐蚀、低毒、发泡量稳定，82009A紫罗兰香精的加入使该去除剂散发香味，无刺激性气味。
进一步地，所述巯基乙酸18％；氢氧化钠7％；CQAL200 2％；AES 1.5％；APG08101％；柠檬酸钠0.3％；无水乙醇5％；去离子水65％；82009A紫罗兰香精0.2％。
本发明还包括浓缩铁粉去除剂的制备方法，包括以下步骤：
S1.按质量百分比称量巯基乙酸、氢氧化钠、CQAL200、AES、APG0810、柠檬酸钠、无水乙醇、去离子水、82009A紫罗兰香精，向去离子水逐渐加入氢氧化钠，搅拌至完全溶解；
S2.向步骤S1的混合溶液加入巯基乙酸并搅拌，直至中和反应完全，然后测PH值，若PH值为6.5-7.5，则进行步骤S3；若PH值不为6.5-7.5，则相对应添加巯基乙酸或氢氧化钠，直至将PH值调为6.5-7.5，再进行步骤S3；
S3.将步骤S2中和后的混合溶液静置，直至溶液温度下降至50℃以下，然后加入柠檬酸钠混合搅拌，直至搅拌均匀透明；
S4.向步骤S3中搅拌后的溶液依次加入CQAL200、AES、APG0810、无水乙醇、82009A紫罗兰香精混合搅拌，直至搅拌均匀透明；
S5.将步骤S4搅拌后的溶液倒入塑料瓶或玻璃瓶内，然后封装。本发明首先将氢氧化钠溶于水，然后加入巯基乙酸进行中和反应，由于氢氧化钠溶于水以及中和反应会发热，在降温后，依次将剩余的原料加入搅拌均匀，利用复配作用，使制得的去除剂清洗性能强，发泡量稳定，有效去除汽车表面的氧化层，且无腐蚀，低毒、无刺激性气味。
进一步地，所述步骤S1、S2、S3、S4中均采用配料锅进行原料的混合搅拌。
进一步地，所述步骤S1、S2、S3、S4中均采用均质器进行原料的混合搅拌。
进一步地，所述均质器中，搅拌速度为200-300r/min。
附图说明
图1为本发明的整体结构俯视图。
具体实施方式
下面结合具体实施例对本发明作进一步说明：
实施例一：
参见附图1所示，一种浓缩铁粉去除剂及其制备方法，包括以下质量百分比：巯基乙酸18％；氢氧化钠6％；CQAL200 1％；AES 0.5％；APG0810 0.1％；柠檬酸钠0.2％；无水乙醇4％；去离子水70％；82009A紫罗兰香精0.2％。
本实施例还包括浓缩铁粉去除剂的制备方法，包括以下步骤：
S1.按质量百分比称量巯基乙酸、氢氧化钠、CQAL200、AES、APG0810、柠檬酸钠、无水乙醇、去离子水、82009A紫罗兰香精，向去离子水逐渐加入氢氧化钠，搅拌至完全溶解。
S2.向步骤S1的混合溶液加入巯基乙酸并搅拌，直至中和反应完全，然后测PH值，若PH值为6.5-7.5，则进行步骤S3；若PH值不为6.5-7.5，则相对应添加巯基乙酸或氢氧化钠，直至将PH值调为6.5-7.5，再进行步骤S3。
S3.将步骤S2中和后的混合溶液静置，直至溶液温度下降至50℃以下，然后加入柠檬酸钠混合搅拌，直至搅拌均匀透明。
S4.向步骤S3中搅拌后的溶液依次加入CQAL200、AES、APG0810、无水乙醇、82009A紫罗兰香精混合搅拌，直至搅拌均匀透明。
S5.将步骤S4搅拌后的溶液倒入塑料瓶或玻璃瓶内，然后封装。
在本实施例中，步骤S1、S2、S3、S4中均采用配料锅或均质器进行原料的混合搅拌；其中，当采用均质器中，搅拌速度为200r/min。
在本实施例中，首先将氢氧化钠溶于水，然后加入巯基乙酸进行中和反应，以增强整体清洗效果，由于前者氢氧化钠溶于水以及中和反应会发热，因此，需要静置一段时间降温后，再加入依次柠檬酸钠、CQAL200、AES、APG0810、无水乙醇、82009A紫罗兰香精，以制得本实施例的铁粉去除剂，其中，CQAL200、AES、APG0810可提高清洗去污能力，起泡性好，巯基乙酸与氢氧化钠配合，在与铁粉混合反应后显色明显，有效去除汽车表面的氧化层，提高整体清洗能力，且散发香味，无任何刺激性气味。
实施例二：
参见附图1所示，一种浓缩铁粉去除剂及其制备方法，包括以下质量百分比：巯基乙酸21％；氢氧化钠8％；CQAL200 3％；AES 1％；APG0810 0.4％；柠檬酸钠0.5％；无水乙醇6％；去离子水60％；82009A紫罗兰香精0.1％。
本实施例还包括浓缩铁粉去除剂的制备方法，包括以下步骤：
S1.按质量百分比称量巯基乙酸、氢氧化钠、CQAL200、AES、APG0810、柠檬酸钠、无水乙醇、去离子水、82009A紫罗兰香精，向去离子水逐渐加入氢氧化钠，搅拌至完全溶解。
S2.向步骤S1的混合溶液加入巯基乙酸并搅拌，直至中和反应完全，然后测PH值，若PH值为6.5-7.5，则进行步骤S3；若PH值不为6.5-7.5，则相对应添加巯基乙酸或氢氧化钠，直至将PH值调为6.5-7.5，再进行步骤S3。
S3.将步骤S2中和后的混合溶液静置，直至溶液温度下降至50℃以下，然后加入柠檬酸钠混合搅拌，直至搅拌均匀透明。
S4.向步骤S3中搅拌后的溶液依次加入CQAL200、AES、APG0810、无水乙醇、82009A紫罗兰香精混合搅拌，直至搅拌均匀透明。
S5.将步骤S4搅拌后的溶液倒入塑料瓶或玻璃瓶内，然后封装。
在本实施例中，步骤S1、S2、S3、S4中均采用配料锅或均质器进行原料的混合搅拌；其中，当采用均质器中，搅拌速度为300r/min。
在本实施例中，首先将氢氧化钠溶于水，然后加入巯基乙酸进行中和反应，以增强整体清洗效果，由于前者氢氧化钠溶于水以及中和反应会发热，因此，需要静置一段时间降温后，再加入依次柠檬酸钠、CQAL200、AES、APG0810、无水乙醇、82009A紫罗兰香精，以制得本实施例的铁粉去除剂，其中，CQAL200、AES、APG0810可提高清洗去污能力，起泡性好，巯基乙酸与氢氧化钠配合，在与铁粉混合反应后显色明显，有效去除汽车表面的氧化层，提高整体清洗能力，且散发香味，无任何刺激性气味。
实施例三：
参见附图1所示，一种浓缩铁粉去除剂及其制备方法，包括以下质量百分比：巯基乙酸18％；氢氧化钠7％；CQAL200 2％；AES 1.5％；APG0810 1％；柠檬酸钠0.3％；无水乙醇5％；去离子水65％；82009A紫罗兰香精0.2％。
本实施例还包括浓缩铁粉去除剂的制备方法，包括以下步骤：
S1.按质量百分比称量巯基乙酸、氢氧化钠、CQAL200、AES、APG0810、柠檬酸钠、无水乙醇、去离子水、82009A紫罗兰香精，向去离子水逐渐加入氢氧化钠，搅拌至完全溶解。
S2.向步骤S1的混合溶液加入巯基乙酸并搅拌，直至中和反应完全，然后测PH值，若PH值为6.5-7.5，则进行步骤S3；若PH值不为6.5-7.5，则相对应添加巯基乙酸或氢氧化钠，直至将PH值调为6.5-7.5，再进行步骤S3。
S3.将步骤S2中和后的混合溶液静置，直至溶液温度下降至50℃以下，然后加入柠檬酸钠混合搅拌，直至搅拌均匀透明。
S4.向步骤S3中搅拌后的溶液依次加入CQAL200、AES、APG0810、无水乙醇、82009A紫罗兰香精混合搅拌，直至搅拌均匀透明。
S5.将步骤S4搅拌后的溶液倒入塑料瓶或玻璃瓶内，然后封装。
在本实施例中，步骤S1、S2、S3、S4中均采用配料锅或均质器进行原料的混合搅拌；其中，当采用均质器中，搅拌速度为250r/min。
在本实施例中，首先将氢氧化钠溶于水，然后加入巯基乙酸进行中和反应，以增强整体清洗效果，由于前者氢氧化钠溶于水以及中和反应会发热，因此，需要静置一段时间降温后，再加入依次柠檬酸钠、CQAL200、AES、APG0810、无水乙醇、82009A紫罗兰香精，以制得本实施例的铁粉去除剂，其中，CQAL200、AES、APG0810可提高清洗去污能力，起泡性好，巯基乙酸与氢氧化钠配合，在与铁粉混合反应后显色明显，有效去除汽车表面的氧化层，提高整体清洗能力，且散发香味，无任何刺激性气味。
从上述实验指标可得，实施例一、实施例二、实施例三的气味性、腐蚀性、密度基本一致，而在清洗效果、清洗时间、净洗力中，实施例一与实施例二相近，实施例三为最佳，综上所述，实施例三为最佳实施例。
以上所述之实施例仅为本发明的较佳实施例，并非对本发明做任何形式上的限制。任何熟悉本领域的技术人员，在不脱离本发明技术方案范围情况下，都可利用上述揭示的技术内容对本发明技术方案作出更多可能的变动和润饰，或修改为等同变化的等效实施例。故凡未脱离本发明技术方案的内容，依据本发明之思路所作的等同等效变化，均应涵盖于本发明的保护范围内。
Claims (6)
1.一种浓缩铁粉去除剂，其特征在于：包括以下质量百分比：巯基乙酸18-21％；氢氧化钠6-8％；CQAL200 1-3％；AES 0.5-1.5％；APG0810 0.1-1％；柠檬酸钠0.1-0.5％；无水乙醇4-6％；去离子水60-70％；82009A紫罗兰香精0.1-0.2％。
2.根据权利要求1所述的一种浓缩铁粉去除剂，其特征在于：所述巯基乙酸18％；氢氧化钠7％；CQAL200 2％；AES 1.5％；APG0810 1％；柠檬酸钠0.3％；无水乙醇5％；去离子水65％；82009A紫罗兰香精0.2％。
3.一种如权利要求1所述的浓缩铁粉去除剂的制备方法，其特征在于：包括以下步骤：
S1.按质量百分比称量巯基乙酸、氢氧化钠、CQAL200、AES、APG0810、柠檬酸钠、无水乙醇、去离子水、82009A紫罗兰香精，向去离子水逐渐加入氢氧化钠，搅拌至完全溶解；
S2.向步骤S1的混合溶液加入巯基乙酸并搅拌，直至中和反应完全，然后测PH值，若PH值为6.5-7.5，则进行步骤S3；若PH值不为6.5-7.5，则相对应添加巯基乙酸或氢氧化钠，直至将PH值调为6.5-7.5，再进行步骤S3；
S3.将步骤S2中和后的混合溶液静置，直至溶液温度下降至50℃以下，然后加入柠檬酸钠混合搅拌，直至搅拌均匀透明；
S4.向步骤S3中搅拌后的溶液依次加入CQAL200、AES、APG0810、无水乙醇、82009A紫罗兰香精混合搅拌，直至搅拌均匀透明；
S5.将步骤S4搅拌后的溶液倒入塑料瓶或玻璃瓶内，然后封装。
4.根据权利要求3所述的一种浓缩铁粉去除剂的制备方法，其特征在于：所述步骤S1、S2、S3、S4中均采用配料锅进行原料的混合搅拌。
5.根据权利要求3所述的一种浓缩铁粉去除剂的制备方法，其特征在于：所述步骤S1、S2、S3、S4中均采用均质器进行原料的混合搅拌。
6.根据权利要求5所述的一种浓缩铁粉去除剂的制备方法，其特征在于：所述均质器中，搅拌速度为200-300r/min。