CN114989698A - 一种防脱落涂料 - Google Patents
一种防脱落涂料 Download PDFInfo
- Publication number
- CN114989698A CN114989698A CN202210701666.4A CN202210701666A CN114989698A CN 114989698 A CN114989698 A CN 114989698A CN 202210701666 A CN202210701666 A CN 202210701666A CN 114989698 A CN114989698 A CN 114989698A
- Authority
- CN
- China
- Prior art keywords
- parts
- polyoxyethylene ether
- raw materials
- following raw
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种防脱落涂料，包括：环氧树脂固化剂40‑45份、水性超支化树脂10‑20份、超细轻质碳酸钙粉末10‑15份、改性填料5‑10份、亚麻油酸5‑8份、棚砂粉4‑10份、防腐剂1‑3份、分散剂2‑4份、湿润剂3‑5份、表面活性剂4‑10份、活性稀释剂1‑9份、表面改性剂4‑8份、环氧固化剂2‑10份、水性消泡剂3‑9份、流平剂1‑6份、高岭土4‑12份、腰果酚甲醛缩聚物2‑8份、二乙烯三胺1‑2份、二溴甲烷2.5‑3.8份、四氢呋喃3.5‑7份、壬基酚聚氧乙烯醚3.5‑4.7份、高岭土3‑7份、苯乙基萘酚聚氧乙烯醚1.5‑1.6份、十八烷醇基聚氧乙烯醚2.5‑5份、N‑甲基脂肪酰胺基牛磺酸盐1.5‑2份、山梨醇脂肪醇酸酯1.8‑3份和纯水60‑70份。本发明能够防止脱落。
Description
技术领域
本发明涉及地坪涂料的技术领域，具体为一种防脱落涂料。
背景技术
随着人们生活水平的提升，目前的内墙建筑涂料的发展在原有装饰功能的基础上也不断地向着多功能化、高环境要求的绿色建筑涂料的方向发展。多功能化是指涂料除装饰功能外同时具有节能、调节湿度、除臭、抗菌防霉、净化空气、隔音、屏蔽有害电磁波等等的健康功能。
但是现有的涂料还是存在容易脱落的问题，故此需要改进。
发明内容
本发明的目的在于提供一种防脱落涂料，以解决上述背景技术中提出的涂料容易脱落的问题。
为实现上述目的，本发明提供如下技术方案：一种防脱落涂料，包括按照以下份数配比的原料：环氧树脂固化剂40-45份、水性超支化树脂10-20份、超细轻质碳酸钙粉末10-15份、改性填料5-10份、亚麻油酸5-8份、棚砂粉4-10份、防腐剂1-3份、分散剂2-4份、湿润剂3-5份、表面活性剂4-10份、活性稀释剂1-9份、表面改性剂4-8份、环氧固化剂2-10份、水性消泡剂3-9份、流平剂1-6份、高岭土4-12份、腰果酚甲醛缩聚物2-8份、二乙烯三胺1-2份、二溴甲烷2.5-3.8份、四氢呋喃3.5-7份、壬基酚聚氧乙烯醚3.5-4.7份、高岭土3-7份、苯乙基萘酚聚氧乙烯醚1.5-1.6份、十八烷醇基聚氧乙烯醚2.5-5份、N-甲基脂肪酰胺基牛磺酸盐1.5-2份、山梨醇脂肪醇酸酯1.8-3份和纯水60-70份。
作为优选，所述的防脱落涂料还包括按照以下份数配比的原料：抗划伤剂0.1-0.5份。
作为优选，所述的防脱落涂料还包括按照以下份数配比的原料：铯钨青铜粉3-5份；纳米氧化锡锑4-5份。
作为优选，所述的防脱落涂料还包括按照以下份数配比的原料：阻燃剂12-15份。
作为优选，所述的防脱落涂料还包括按照以下份数配比的原料：方解石粉10-15份。
作为优选，所述的防脱落涂料还包括按照以下份数配比的原料：艾草粉末1-3份。
作为优选，包括按照以下份数配比的原料：环氧树脂固化剂42份、水性超支化树脂12份、超细轻质碳酸钙粉末11份、改性填料6份、亚麻油酸6份、棚砂粉8份、防腐剂2份、分散剂3份、湿润剂4份、表面活性剂7份、活性稀释剂8份、表面改性剂6份、环氧固化剂8份、水性消泡剂6份、流平剂4份、高岭土11份、腰果酚甲醛缩聚物4份、二乙烯三胺1份、二溴甲烷4份、四氢呋喃6份、壬基酚聚氧乙烯醚4份、高岭土5份、苯乙基萘酚聚氧乙烯醚1.5份、十八烷醇基聚氧乙烯醚3份、N-甲基脂肪酰胺基牛磺酸盐1.5份、山梨醇脂肪醇酸酯2份和纯水66份。
作为优选，包括按照以下份数配比的原料：环氧树脂固化剂45份、水性超支化树脂20份、超细轻质碳酸钙粉末12份、改性填料8份、亚麻油酸8份、棚砂粉10份、防腐剂2份、分散剂3份、湿润剂4份、表面活性剂4-10份、活性稀释剂4份、表面改性剂5份、环氧固化剂5份、水性消泡剂4份、流平剂2份、高岭土5份、腰果酚甲醛缩聚物3份、二乙烯三胺1份、二溴甲烷3份、四氢呋喃5份、壬基酚聚氧乙烯醚4份、高岭土5份、苯乙基萘酚聚氧乙烯醚1.5份、十八烷醇基聚氧乙烯醚4份、N-甲基脂肪酰胺基牛磺酸盐1.5份、山梨醇脂肪醇酸酯2份和纯水70份。
与现有技术相比，本发明的有益效果如下：通过使用腰果酚结合二乙烯三胺改性后的腰果酚甲醛缩聚物与环氧树脂共混交联结合而成腰果酚缩甲醛二乙烯三胺聚合物不仅保持了腰果漆优良的物理机械性能和耐化学性能,而且其硬度、耐碱性明显改善，使整体能够提高涂料的耐腐蚀性，同时长时间使用不会防止脱落。
具体实施方式
下面将结合本发明实施例，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例1：
本实施例公开的一种防脱落涂料，包括按照以下份数配比的原料：环氧树脂固化剂40-45份、水性超支化树脂10-20份、超细轻质碳酸钙粉末10-15份、改性填料5-10份、亚麻油酸5-8份、棚砂粉4-10份、防腐剂1-3份、分散剂2-4份、湿润剂3-5份、表面活性剂4-10份、活性稀释剂1-9份、表面改性剂4-8份、环氧固化剂2-10份、水性消泡剂3-9份、流平剂1-6份、高岭土4-12份、腰果酚甲醛缩聚物2-8份、二乙烯三胺1-2份、二溴甲烷2.5-3.8份、四氢呋喃3.5-7份、壬基酚聚氧乙烯醚3.5-4.7份、高岭土3-7份、苯乙基萘酚聚氧乙烯醚1.5-1.6份、十八烷醇基聚氧乙烯醚2.5-5份、N-甲基脂肪酰胺基牛磺酸盐1.5-2份、山梨醇脂肪醇酸酯1.8-3份和纯水60-70份。
在本实施例中所述的防脱落涂料，包括按照以下份数配比的原料：环氧树脂固化剂42份、水性超支化树脂11份、超细轻质碳酸钙粉末12份、改性填料6份、亚麻油酸6份、棚砂粉6份、防腐剂2份、分散剂3份、湿润剂4份、表面活性剂6份、活性稀释剂8份、表面改性剂5份、环氧固化剂4份、水性消泡剂5份、流平剂4份、高岭土6份、腰果酚甲醛缩聚物3份、二乙烯三胺1份、二溴甲烷3份、四氢呋喃5份、壬基酚聚氧乙烯醚4份、高岭土4份、苯乙基萘酚聚氧乙烯醚1.5份、十八烷醇基聚氧乙烯醚3份、N-甲基脂肪酰胺基牛磺酸盐1.6份、山梨醇脂肪醇酸酯2份和纯水65份
作为优选，所述的防脱落涂料还包括按照以下份数配比的原料：抗划伤剂0.1-0.5份。
作为优选，所述的防脱落涂料还包括按照以下份数配比的原料：铯钨青铜粉3-5份；纳米氧化锡锑4-5份。
作为优选，所述的防脱落涂料还包括按照以下份数配比的原料：阻燃剂12-15份。
作为优选，所述的防脱落涂料还包括按照以下份数配比的原料：方解石粉10-15份。
作为优选，所述的防脱落涂料还包括按照以下份数配比的原料：艾草粉末1-3份。
实施例3：
本实施例公开的一种防脱落涂料，包括按照以下份数配比的原料：环氧树脂固化剂45份、水性超支化树脂20份、超细轻质碳酸钙粉末15份、改性填料10份、亚麻油酸8份、棚砂粉10份、防腐剂3份、分散剂4份、湿润剂5份、表面活性剂10份、活性稀释剂9份、表面改性剂8份、环氧固化剂10份、水性消泡剂9份、流平剂6份、高岭土12份、腰果酚甲醛缩聚物8份、二乙烯三胺2份、二溴甲烷3.8份、四氢呋喃7份、壬基酚聚氧乙烯醚4.7份、高岭土7份、苯乙基萘酚聚氧乙烯醚1.6份、十八烷醇基聚氧乙烯醚5份、N-甲基脂肪酰胺基牛磺酸盐2份、山梨醇脂肪醇酸酯3份和纯水70份。
作为优选，所述的防脱落涂料还包括按照以下份数配比的原料：抗划伤剂0.1-0.5份。
作为优选，所述的防脱落涂料还包括按照以下份数配比的原料：铯钨青铜粉3-5份；纳米氧化锡锑4-5份。
作为优选，所述的防脱落涂料还包括按照以下份数配比的原料：阻燃剂12-15份。
作为优选，所述的防脱落涂料还包括按照以下份数配比的原料：方解石粉10-15份。
作为优选，所述的防脱落涂料还包括按照以下份数配比的原料：艾草粉末1-3份。
在本实施例中所述的抗划伤剂0.2份，所述的铯钨青铜粉5份；纳米氧化锡锑4.5份，所述的阻燃剂12份，所述的方解石粉10份，艾草粉末1份。
实施例4：
本实施例公开的一种防脱落涂料，包括按照以下份数配比的原料：环氧树脂固化剂42份、水性超支化树脂12份、超细轻质碳酸钙粉末11份、改性填料6份、亚麻油酸6份、棚砂粉8份、防腐剂2份、分散剂3份、湿润剂4份、表面活性剂7份、活性稀释剂8份、表面改性剂6份、环氧固化剂8份、水性消泡剂6份、流平剂4份、高岭土11份、腰果酚甲醛缩聚物4份、二乙烯三胺1份、二溴甲烷4份、四氢呋喃6份、壬基酚聚氧乙烯醚4份、高岭土5份、苯乙基萘酚聚氧乙烯醚1.5份、十八烷醇基聚氧乙烯醚3份、N-甲基脂肪酰胺基牛磺酸盐1.5份、山梨醇脂肪醇酸酯2份和纯水66份。
作为优选，所述的防脱落涂料还包括按照以下份数配比的原料：抗划伤剂0.1-0.5份。
作为优选，所述的防脱落涂料还包括按照以下份数配比的原料：铯钨青铜粉3-5份；纳米氧化锡锑4-5份。
作为优选，所述的防脱落涂料还包括按照以下份数配比的原料：阻燃剂12-15份。
作为优选，所述的防脱落涂料还包括按照以下份数配比的原料：方解石粉10-15份。
作为优选，所述的防脱落涂料还包括按照以下份数配比的原料：艾草粉末1-3份。
在本实施例中所述的抗划伤剂0.5份，所述的铯钨青铜粉4份；纳米氧化锡锑4份，所述的阻燃剂15份，所述的方解石粉14份。
实施例5：
本实施例公开的一种防脱落涂料，包括按照以下份数配比的原料：环氧树脂固化剂45份、水性超支化树脂20份、超细轻质碳酸钙粉末12份、改性填料8份、亚麻油酸8份、棚砂粉10份、防腐剂2份、分散剂3份、湿润剂4份、表面活性剂4-10份、活性稀释剂4份、表面改性剂5份、环氧固化剂5份、水性消泡剂4份、流平剂2份、高岭土5份、腰果酚甲醛缩聚物3份、二乙烯三胺1份、二溴甲烷3份、四氢呋喃5份、壬基酚聚氧乙烯醚4份、高岭土5份、苯乙基萘酚聚氧乙烯醚1.5份、十八烷醇基聚氧乙烯醚4份、N-甲基脂肪酰胺基牛磺酸盐1.5份、山梨醇脂肪醇酸酯2份和纯水70份。
作为优选，所述的防脱落涂料还包括按照以下份数配比的原料：抗划伤剂0.1-0.5份。
作为优选，所述的防脱落涂料还包括按照以下份数配比的原料：铯钨青铜粉3-5份；纳米氧化锡锑4-5份。
作为优选，所述的防脱落涂料还包括按照以下份数配比的原料：阻燃剂12-15份。
作为优选，所述的防脱落涂料还包括按照以下份数配比的原料：方解石粉10-15份。
作为优选，所述的防脱落涂料还包括按照以下份数配比的原料：艾草粉末1-3份。在本实施例中所述的抗划伤剂0.3份，所述的铯钨青铜粉4份；纳米氧化锡锑5份，所述的阻燃剂14份，所述的方解石粉12份。
下面结合上述实施例进行本发明与现有技术的涂料的测试，测试结果如下表所示，
综上所述，本发明相比现有技术具有高耐腐蚀性、高冲击强度、韧性、而且不易脱落。
对于本领域技术人员而言，显然本发明不限于上述示范性实施例的细节，而且在不背离本发明的精神或基本特征的情况下，能够以其他的具体形式实现本发明。因此，无论从哪一点来看，均应将实施例看作是示范性的，而且是非限制性的，本发明的范围由所附权利要求而不是上述说明限定，因此旨在将落在权利要求的等同要件的含义和范围内的所有变化囊括在本发明内。
Claims (8)
1.一种防脱落涂料，其特征在于：包括按照以下份数配比的原料：环氧树脂固化剂40-45份、水性超支化树脂10-20份、超细轻质碳酸钙粉末10-15份、改性填料5-10份、亚麻油酸5-8份、棚砂粉4-10份、防腐剂1-3份、分散剂2-4份、湿润剂3-5份、表面活性剂4-10份、活性稀释剂1-9份、表面改性剂4-8份、环氧固化剂2-10份、水性消泡剂3-9份、流平剂1-6份、高岭土4-12份、腰果酚甲醛缩聚物2-8份、二乙烯三胺1-2份、二溴甲烷2.5-3.8份、四氢呋喃3.5-7份、壬基酚聚氧乙烯醚3.5-4.7份、高岭土3-7份、苯乙基萘酚聚氧乙烯醚1.5-1.6份、十八烷醇基聚氧乙烯醚2.5-5份、N-甲基脂肪酰胺基牛磺酸盐1.5-2份、山梨醇脂肪醇酸酯1.8-3份和纯水60-70份。
2.根据权利要求1所述的一种防脱落涂料，其特征在于：所述的防脱落涂料还包括按照以下份数配比的原料：抗划伤剂0.1-0.5份。
3.根据权利要求1所述的一种防脱落涂料，其特征在于：所述的防脱落涂料还包括按照以下份数配比的原料：铯钨青铜粉3-5份；纳米氧化锡锑4-5份。
4.根据权利要求1所述的一种防脱落涂料，其特征在于：所述的防脱落涂料还包括按照以下份数配比的原料：阻燃剂12-15份。
5.根据权利要求1所述的一种防脱落涂料，其特征在于：所述的防脱落涂料还包括按照以下份数配比的原料：方解石粉10-15份。
6.根据权利要求1所述的一种防脱落涂料，其特征在于：所述的防脱落涂料还包括按照以下份数配比的原料：艾草粉末1-3份。
7.根据权利要求1所述的一种防脱落涂料，其特征在于：包括按照以下份数配比的原料：环氧树脂固化剂42份、水性超支化树脂12份、超细轻质碳酸钙粉末11份、改性填料6份、亚麻油酸6份、棚砂粉8份、防腐剂2份、分散剂3份、湿润剂4份、表面活性剂7份、活性稀释剂8份、表面改性剂6份、环氧固化剂8份、水性消泡剂6份、流平剂4份、高岭土11份、腰果酚甲醛缩聚物4份、二乙烯三胺1份、二溴甲烷4份、四氢呋喃6份、壬基酚聚氧乙烯醚4份、高岭土5份、苯乙基萘酚聚氧乙烯醚1.5份、十八烷醇基聚氧乙烯醚3份、N-甲基脂肪酰胺基牛磺酸盐1.5份、山梨醇脂肪醇酸酯2份和纯水66份。
8.根据权利要求1所述的一种防脱落涂料，其特征在于：包括按照以下份数配比的原料：环氧树脂固化剂45份、水性超支化树脂20份、超细轻质碳酸钙粉末12份、改性填料8份、亚麻油酸8份、棚砂粉10份、防腐剂2份、分散剂3份、湿润剂4份、表面活性剂4-10份、活性稀释剂4份、表面改性剂5份、环氧固化剂5份、水性消泡剂4份、流平剂2份、高岭土5份、腰果酚甲醛缩聚物3份、二乙烯三胺1份、二溴甲烷3份、四氢呋喃5份、壬基酚聚氧乙烯醚4份、高岭土5份、苯乙基萘酚聚氧乙烯醚1.5份、十八烷醇基聚氧乙烯醚4份、N-甲基脂肪酰胺基牛磺酸盐1.5份、山梨醇脂肪醇酸酯2份和纯水70份。