CN114921225B - 一种常温施工卷材节点高固超韧密封膏及其制备方法 - Google Patents
一种常温施工卷材节点高固超韧密封膏及其制备方法 Download PDFInfo
- Publication number
- CN114921225B CN114921225B CN202210608572.2A CN202210608572A CN114921225B CN 114921225 B CN114921225 B CN 114921225B CN 202210608572 A CN202210608572 A CN 202210608572A CN 114921225 B CN114921225 B CN 114921225B
- Authority
- CN
- China
- Prior art keywords
- asphalt
- parts
- sealing paste
- coiled material
- wax
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明属于建筑材料技术领域，公开了一种常温施工卷材节点高固超韧密封膏及其制备方法。该密封膏包括沥青、石油树脂、纤维、蜡、填料和油酸。本发明的密封膏杜绝了以往需要高温施工的情况，避免了施工的危险性，同时本发明密封膏施工后具有高温不流淌，低温不开裂，防水能力强等一系列的优点。
Description
技术领域
本发明属于建筑材料技术领域，更具体地，涉及一种常温施工卷材节点高固超韧密封膏及其制备方法。
背景技术
目前卷材施工主要分为热熔法和自粘法两种。在施工过程中，卷材搭接边及搭接部位很容易因为施工或卷材自身的问题，造成搭接部位或卷材节点无法实现满粘，继而造成窜水。或者，在卷材施工结束后，随着时间推移，搭接部位或卷材节点会慢慢分离，最终失去防水效果。因此对搭接部位或卷材节点做进一步处理，使整个防水系统实现预期的防水目标是亟待解决的问题。
目前上述问题都是通过使用热熔料修补或使用卷材对搭接部位或节点二次处理解决，但上述方法耗工耗时，同时需要高温加热，并不环保。
因此，亟待开发出一种绿色环保并可以常温施工的卷材节点密封膏。
发明内容
本发明的目的是针对现有技术的不足，提出一种常温施工卷材节点高固超韧密封膏及其制备方法。本发明的密封膏杜绝了以往需要高温施工的情况，避免了施工的危险性，同时本发明密封膏施工后具有高温不流淌，低温不开裂，防水能力强等一系列的优点。
为了实现上述目的，本发明第一方面提供了一种常温施工卷材节点高固超韧密封膏，该密封膏包括沥青、石油树脂、纤维、蜡、填料和油酸。
申请人发现现有的对卷材节点的处理方式为使用热熔料修补，施工前需将热熔料加热，热熔料加热会有大量烟气产生。而本发明的密封膏为常温施工产品，无任何烟气。而且，本发明中，油酸的引入，打开了本来各种原材料中塑性的本身属性，较小的外力即可破坏自身的稳定性，可以使整个产品在常温下具有良好的施工性。同时挥发分较少，完全满足排放标准。同时原材料中的纤维的交联作用，使产品常温下不具备流动性，随着温度升高，蜡在表面析出固化成膜，进一步束缚产品流动，耐高温性能逐步提升，直至稳定固化，形成稳定的密闭体系。
申请人发现以往的密封膏产品多属于低固含的水性产品，施工结束后体积收缩严重，造成粘结性能较低。而本发明选用各种不易挥发的原材料，施工后，随着固化的发生，产生的挥发性物质很少，基本保持施工时的状态，在固化过程中，石油树脂等高分子材料保持很好的结构性均一性，使整个体系保证良好的稳定性，施工结束后体积收缩微小，凝固后整体性能稳定。
申请人发现传统的密封膏所选的原材料基本为绝对的塑性体材料，低温易于脆裂，施工结束后经历一个冻结期产品基本失去自身性能，失去了密封效果。而本发明中石油树脂及纤维都表现出良好的低温性能，纤维同时束缚油酸分离，使整个产品在低温下具有良好的低温性能，不易开裂，进而不会导致整个体系丧失防水性能。
根据本发明，优选地，该密封膏包括以重量份计的以下组分：沥青30-50份、石油树脂1-8份、纤维1-8份、蜡1-8份、填料30-50份和油酸10-25份；进一步优选地，该密封膏包括以重量份计的以下组分：沥青35-40份、石油树脂2-4份、纤维2-4份、蜡2-4份、填料35-45份和油酸12-20份。
根据本发明，优选地，该密封膏的固含量为95-98％。
根据本发明，优选地，所述沥青包括以重量份计的以下组分：石油沥青30-40份和建筑沥青2-10份。
根据本发明，优选地，所述石油沥青为70#石油沥青、90#石油沥青和110#石油沥青中的至少一种。
根据本发明，优选地，所述建筑沥青为10#建筑沥青、溶剂脱沥青和岩沥青中的至少一种。
根据本发明，优选地，所述石油树脂为C5石油树脂和/或C9石油树脂。
根据本发明，优选地，所述纤维为玻璃纤维、木质素纤维和聚酯纤维中的至少一种。
根据本发明，优选地，所述油酸为肉豆蔻油酸、棕榈油酸、反式油酸、蓖麻油酸、亚油酸和芥酸中的至少一种。
根据本发明，优选地，所述蜡为大豆蜡、石蜡和聚乙烯蜡中的至少一种。
根据本发明，优选地，所述填料为重钙、矿粉和轻钙中的至少一种。
本发明第二方面提供了所述的常温施工卷材节点高固超韧密封膏的制备方法，该制备方法包括如下步骤：
S1：在第一温度下，将所述沥青、石油树脂和蜡依次混合搅拌均匀，得到混合物；
S2：在第二温度下，将所述混合物、填料、油酸和纤维依次混合搅拌均匀，得到所述常温施工卷材节点高固超韧密封膏。
根据本发明，优选地，所述第一温度为130-150℃。
根据本发明，优选地，所述第二温度为70-90℃。
根据本发明，优选地，在所述步骤S1中，将所述石油沥青和建筑沥青混合均匀，得到沥青混合物，再将所述沥青混合物与所述石油树脂和蜡依次混合搅拌均匀，得到混合物。
本发明的技术方案的有益效果如下：
(1)本发明的密封膏具有优异的高低温稳定性，解决了卷材节点不可常温施工的难题，产品在自身强度、柔韧性、粘结性能、耐高温、耐低温性能得到提升。
(2)本发明的密封膏在施工中只需常温抹平即可，无需加热，解决了涂盖料加温的难题。
(3)本发明在闭水方面，解决了节点易窜水的问题，闭水效果良好。
(4)本发明在高、低温性能中，由于有纤维及石油树脂成分，纤维能很好的束缚油分，保证良好的低温性能，高温方面也因为有耐高温材料如建筑沥青的保证，确保保温性能良好。
(5)本发明由于原料中不含高挥发物质，更环保，更安全，不论是对施工人员及环境都是有利的，体现出良好的社会效益。
(6)本发明在施工方面，因为是常温施工，大量的降低了人力、物力，体现出较好的经济效益。
本发明的其它特征和优点将在随后具体实施方式部分予以详细说明。
具体实施方式
下面将更详细地描述本发明的优选实施方式。虽然以下描述了本发明的优选实施方式，然而应该理解，可以以各种形式实现本发明而不应被这里阐述的实施方式所限制。相反，提供这些实施方式是为了使本发明更加透彻和完整，并且能够将本发明的范围完整地传达给本领域的技术人员。
实施例1
本实施例提供一种常温施工卷材节点高固超韧密封膏，该密封膏包括以重量份计的以下组分：70#石油沥青36份、10#建筑沥青3份、C5石油树脂2份、聚酯纤维2份、石蜡2份、400目重钙40份和反式油酸15份。
上述密封膏的制备方法包括如下步骤：
S1：在140℃下，先将所述石油沥青和建筑沥青混合均匀(搅拌速度800rpm，搅拌10min)，得到沥青混合物，再将2份石油树脂加入继续搅拌10min，最后将蜡加入继续搅拌30min，得到混合物；
S2：在90℃下，将所述混合物与填料混合搅拌10min，维持温度90℃；再将油酸加入继续搅拌10min，维持温度80℃；最后将纤维加入继续搅拌10min，得到所述常温施工卷材节点高固超韧密封膏。
实施例2
本实施例提供一种常温施工卷材节点高固超韧密封膏，该密封膏包括以重量份计的以下组分：90#石油沥青35份、10#建筑沥青5份、C5石油树脂3份、聚酯纤维2份、聚乙烯蜡2份、200目重钙40份和油酸15份。
实施例3
本实施例提供一种常温施工卷材节点高固超韧密封膏，本实施例与实施例1的区别仅在于：70#石油沥青39份、10#建筑沥青0份，其他组分含量不变。
实施例4
本实施例提供一种常温施工卷材节点高固超韧密封膏，本实施例与实施例1的区别仅在于：90#石油沥青39份、10#建筑沥青0份，其他组分含量不变。
实施例5
本实施例提供一种常温施工卷材节点高固超韧密封膏，本实施例与实施例2的区别仅在于：110#石油沥青39份、10#建筑沥青0份，其他组分含量不变。
对比例1
本对比例提供一种密封膏，本对比例与实施例1的区别仅在于：C5石油树脂0份，其他组分含量不变。
对比例2
本对比例提供一种密封膏，本对比例与实施例1的区别仅在于：石蜡0份，其他组分含量不变。
对比例3
本对比例提供一种密封膏，本对比例与实施例1的区别仅在于：纤维0份，其他组分含量不变。
测试例
本测试例对实施例1-5和对比例1-3的密封膏按照JC/T2428-2017、JC/T408-2005中规定方法进行测试，测试结果如表1所示。
表1
由表1可知，实施例1、2在耐热性和低温柔性上都可以满足防水要求，表干和实干时间相差很小，实施例2表干时间较实施例1稍长，考虑为油分(90#石油沥青油分大于70#石油沥青油分)含量较多的原因，但总体都可以满足防水要求；实施例3、4、5由于缺少10#建筑沥青，耐热性性能下降明显；对比例2由于缺少蜡，表干时间变长，同时耐热性性能小幅下降；对比例3由于缺少纤维，耐热性性能大幅下降，并且整个体系缺少内部交联，使闭水性能也大幅下降。
以上已经描述了本发明的各实施例，上述说明是示例性的，并非穷尽性的，并且也不限于所披露的各实施例。在不偏离所说明的各实施例的范围和精神的情况下，对于本技术领域的普通技术人员来说许多修改和变更都是显而易见的。
Claims (10)
1.一种常温施工卷材节点高固超韧密封膏，其特征在于，该密封膏包括沥青、石油树脂、纤维、蜡、填料和油酸；
所述纤维为聚酯纤维；
所述油酸为肉豆蔻油酸、棕榈油酸、反式油酸、蓖麻油酸、亚油酸和芥酸中的至少一种；
所述沥青包括以下组分：石油沥青和建筑沥青；
所述石油沥青为70#石油沥青、90#石油沥青和110#石油沥青中的至少一种；
所述建筑沥青为10#建筑沥青、溶剂脱沥青和岩沥青中的至少一种。
2.根据权利要求1所述的常温施工卷材节点高固超韧密封膏，其中，该密封膏包括以重量份计的以下组分：沥青30-50份、石油树脂1-8份、纤维1-8份、蜡1-8份、填料30-50份和油酸10-25份。
3.根据权利要求2所述的常温施工卷材节点高固超韧密封膏，其中，该密封膏包括以重量份计的以下组分：沥青35-40份、石油树脂2-4份、纤维2-4份、蜡2-4份、填料35-45份和油酸12-20份。
4.根据权利要求1所述的常温施工卷材节点高固超韧密封膏，其中，该密封膏的固含量为95-98%。
5.根据权利要求1-4中任意一项所述的常温施工卷材节点高固超韧密封膏，其中，
所述沥青包括以重量份计的以下组分：石油沥青30-40份和建筑沥青2-10份。
6.根据权利要求1-4中任意一项所述的常温施工卷材节点高固超韧密封膏，其中，所述石油树脂为C5石油树脂和/或C9石油树脂。
7.根据权利要求1-4中任意一项所述的常温施工卷材节点高固超韧密封膏，其中，所述蜡为大豆蜡、石蜡和聚乙烯蜡中的至少一种。
8.根据权利要求1-4中任意一项所述的常温施工卷材节点高固超韧密封膏，其中，所述填料为重钙、矿粉和轻钙中的至少一种。
9.根据权利要求1-8中任意一项所述的常温施工卷材节点高固超韧密封膏的制备方法，其特征在于，该制备方法包括如下步骤：
S1：在第一温度下，将所述沥青、石油树脂和蜡依次混合搅拌均匀，得到混合物；
S2：在第二温度下，将所述混合物、填料、油酸和纤维依次混合搅拌均匀，得到所述常温施工卷材节点高固超韧密封膏。
10.根据权利要求9所述的常温施工卷材节点高固超韧密封膏的制备方法，其中，
所述第一温度为130-150℃；
所述第二温度为70-90℃；
在所述步骤S1中，将所述石油沥青和建筑沥青混合均匀，得到沥青混合物，再将所述沥青混合物与所述石油树脂和蜡依次混合搅拌均匀，得到混合物。