CN114921135A - 一种用于软质pvc的可水洗临时装饰涂料及其制备方法和应用 - Google Patents
一种用于软质pvc的可水洗临时装饰涂料及其制备方法和应用 Download PDFInfo
- Publication number
- CN114921135A CN114921135A CN202210702763.5A CN202210702763A CN114921135A CN 114921135 A CN114921135 A CN 114921135A CN 202210702763 A CN202210702763 A CN 202210702763A CN 114921135 A CN114921135 A CN 114921135A
- Authority
- CN
- China
- Prior art keywords
- resin
- parts
- water
- washable
- soft pvc
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种用于软质PVC的可水洗临时装饰涂料及其制备方法和应用，属于涂料技术领域。本发明以聚乙烯醇PVA树脂作为主体树脂，提高涂料漆膜的柔韧性；以聚醚改性丙烯酸树脂作为改性树脂，提高涂料在软质PVC上的附着力并改善PVA树脂的水溶解性，同时利用少量丙烯酸改性聚氨酯PUA树脂作为第二种改性树脂，硬度低，能够提高与软质PVC的结合力，抵抗素材发生形变导致的开裂。本发明同时在涂料中加入羧酸型丙基甜菜两性表面活性剂，具有增稠和改善水洗残留双重功效，从而加快漆膜水洗时的溶解速度。因此，本发明提供的涂料具有优异的柔韧性，不易开裂，且水洗效果好。
Description
技术领域
本发明涉及涂料技术领域，尤其涉及一种用于软质PVC的可水洗临时装饰涂料及其制备方法和应用。
背景技术
目前，在中国乃至全球兴起一股盲盒热，实现盲盒有多种方法，基本的有盲性的包装，拆盒后知晓内容，也有更特殊的玩法，例如喷涂临时一个涂层，该涂层甚至带有临时装饰性，该涂层可用自来水冲洗，浸泡后完成溶解和脱落，呈现出真实的物品内容。目前，硬质盲盒涂料在市面上已经成熟运用，硬质盲盒涂料是在丙烯酸树脂主链中引入大量的亲水羧基，丙烯酸树脂主链的Tg约在30度，保持了涂层的一定硬度和抗包装粘连性，该种涂料比较容易实现。但是软质素材盲盒还未广泛使用，主要问题为软质素材盲盒在运输过程中碰撞导致软质素材自身发生形变，使得原有硬质盲盒涂料喷在软质素材上容易发生应力差异形变而开裂，或老化后出现开裂现象和粘连，且水洗效果不好。因此，现有硬质盲盒涂料不适用于软质盲盒，但软质素材盲盒也有很大的市场需求量。
发明内容
本发明的目的在于提供一种用于软质PVC的可水洗临时装饰涂料及其制备方法和应用，所述可水洗临时装饰涂料柔韧性优异，用于软质PVC不开裂，水洗效果好。
为了实现上述发明目的，本发明提供以下技术方案：
本发明提供了一种用于软质PVC的可水洗临时装饰涂料，以质量份数计，包括聚乙烯醇PVA树脂20～60份，聚醚改性丙烯酸树脂10～30份，丙烯酸改性聚氨酯PUA树脂3～8份，聚醚改性硅氧烷消泡剂0.1～0.3份，聚醚改性硅氧烷润湿剂0.1～0.3份，含锚固基团分散剂0.2～0.5份，玻璃微粉2.0～5.0份，硅藻土3.0～6.0份，AMP-95多功能助剂0.5～1.5份，聚酰胺蜡流变控制助剂2.0～3.0份，羧酸型丙基甜菜两性表面活性剂2.0～15.0份，乙醇1.0～3.0份，丙二醇甲醚1.0～3.0份，水0～20份，聚氨酯流变助剂0～0.5份，气相二氧化硅0～1.0份，水性专用铝银浆0～15.0份，无树脂水性色浆0～60.0份。
优选的，所述聚乙烯醇PVA树脂为POVAL 3-80。
优选的，所述聚醚改性丙烯酸树脂为改性树脂1Polyox WSRN10-Dow；所述丙烯酸改性聚氨酯PUA树脂为PUA-5870。
优选的，所述聚醚改性硅氧烷消泡剂为Tego 810；所述聚醚改性硅氧烷润湿剂为Tego 270。
优选的，所述含锚固基团分散剂为BYK 190；所述气相二氧化硅为VP RS 92；所述聚氨酯流变助剂为RM-8W。
优选的，所述聚酰胺蜡流变控制助剂为DisparlonAQ633；所述羧酸型丙基甜菜两性表面活性剂为CAB-35椰油酰胺基甜菜碱。
本发明提供了上述技术方案所述可水洗临时装饰涂料的制备方法，包括以下步骤：
将聚乙烯醇PVA树脂、聚醚改性丙烯酸树脂、丙烯酸改性聚氨酯PUA树脂、部分水、乙醇、丙二醇甲醚、含锚固基团分散剂、聚醚改性硅氧烷润湿剂、聚醚改性硅氧烷消泡剂、硅藻土、玻璃微粉、气相二氧化硅和AMP-95多功能助剂混合，进行分散，得到第一混合物料；
将所述第一混合物料、聚氨酯流变助剂、聚酰胺蜡流变控制助剂和部分羧酸型丙基甜菜两性表面活性剂混合，得到第二混合物料；
向所述第二混合物料中加入无树脂水性色浆和/或水性专用铝银浆调至所需颜色，加入剩余羧酸型丙基甜菜两性表面活性剂，采用剩余水调整至所需粘度，得到用于软质PVC的可水洗临时装饰涂料。
优选的，所述第一混合物料的细度＜35μm。
优选的，所述用于软质PVC的可水洗临时装饰涂料在25℃的粘度为90～120KU。
本发明提供了上述技术方案所述用于软质PVC的可水洗临时装饰涂料或上述技术方案所述制备方法制备得到的用于软质PVC的可水洗临时装饰涂料在软质盲盒中的应用。
本发明提供了一种用于软质PVC的可水洗临时装饰涂料，以质量份数计，包括聚乙烯醇PVA树脂20～60份，聚醚改性丙烯酸树脂10～30份，丙烯酸改性聚氨酯PUA树脂3～8份，聚醚改性硅氧烷消泡剂0.1～0.3份，聚醚改性硅氧烷润湿剂0.1～0.3份，含锚固基团分散剂0.2～0.5份，玻璃微粉2.0～5.0份，硅藻土3.0～6.0份，AMP-95多功能助剂0.5～1.5份，聚酰胺蜡流变控制助剂2.0～3.0份，羧酸型丙基甜菜两性表面活性剂2.0～15.0份，乙醇1.0～3.0份，丙二醇甲醚1.0～3.0份，水0～20份，聚氨酯流变助剂0～0.5份，气相二氧化硅0～1.0份，水性专用铝银浆0～15.0份，无树脂水性色浆0～60.0份。本发明以聚乙烯醇PVA树脂作为主体树脂，提高涂料的PVA柔韧性；以聚醚改性丙烯酸树脂作为改性树脂，提高涂料在软质PVC上的附着力并改善PVA树脂的水溶解性，同时利用少量丙烯酸改性聚氨酯PUA树脂作为第二种改性树脂，硬度低，能够提高与软质PVC的结合力，抵抗素材发生形变导致的开裂。而且，所用主体树脂和改性树脂不仅能够保留丙烯酸原有的大量羧基保持水溶解性，还引入了亲水型醚链和亲水性乙烯醇链，此两种链段均具有较好的柔性，但相对羧基丙烯酸的水溶解性较慢，本发明同时在涂料中加入羧酸型丙基甜菜两性表面活性剂，具有增稠和改善水洗残留双重功效，从而加快漆膜水冲洗时的溶解速度。因此，本发明提供的涂料具有优异的柔韧性，不易开裂，且水洗效果好。实施例的结果表面，本发明提供的涂料在软质PVC极限变形的情况下不管运输碰撞，还是高温烘烤均不会出现开裂现象；同时水洗效果好，不残留。
本发明所用羧酸型丙基甜菜两性表面活性剂既能保证产品良好的稳定性和批次之间的粘度稳定性，也适当增加水洗溶解速度，减少了残留问题。
本发明添加功能性环保填料(玻璃微粉和硅藻土)，使得涂料具有多孔呼吸功能，也能快速吸水溶解，提高水洗速度，同时提高未水洗前漆膜的干爽性。
具体实施方式
本发明提供了一种用于软质PVC的可水洗临时装饰涂料，以质量份数计，包括聚乙烯醇PVA树脂20～60份，聚醚改性丙烯酸树脂10～30份，丙烯酸改性聚氨酯PUA树脂3～8份，聚醚改性硅氧烷消泡剂0.1～0.3份，聚醚改性硅氧烷润湿剂0.1～0.3份，含锚固基团分散剂0.2～0.5份，玻璃微粉2.0～5.0份，硅藻土3.0～6.0份，AMP-95多功能助剂0.5～1.5份，聚酰胺蜡流变控制助剂2.0～3.0份，羧酸型丙基甜菜两性表面活性剂2.0～15.0份，乙醇1.0～3.0份，丙二醇甲醚1.0～3.0份，水0～20份，聚氨酯流变助剂0～0.5份，气相二氧化硅0～1.0份，水性专用铝银浆0～15.0份，无树脂水性色浆0～60.0份。
在本发明中，若无特殊说明，所需制备原料均为本领域技术人员熟知的市售商品。
以质量份数计，本发明提供的用于软质PVC的可水洗临时装饰涂料包括聚乙烯醇PVA树脂20～60份，优选为30～50份，更优选为40份。所述聚乙烯醇PVA树脂优选为POVAL 3-80。本发明中聚乙烯醇PVA树脂作为主体树脂。
以所述聚乙烯醇PVA树脂的质量份数为基准，本发明提供的用于软质PVC的可水洗临时装饰涂料包括聚醚改性丙烯酸树脂10～30份，更优选为20份。所述聚醚改性丙烯酸树脂优选为改性树脂1Polyox WSR N10-Dow。本发明中聚醚改性丙烯酸树脂作为主体树脂的改性树脂1。
以所述聚乙烯醇PVA树脂的质量份数为基准，本发明提供的用于软质PVC的可水洗临时装饰涂料包括丙烯酸改性聚氨酯PUA树脂3～8份，更优选为5份。所述丙烯酸改性聚氨酯PUA树脂优选为PUA-5870。本发明利用丙烯酸改性聚氨酯PUA树脂作为主体树脂的改性树脂2。
改性树脂1的柔韧性比主体树脂好，可以180度折弯不开裂，不掉漆，其中改性树脂1水洗性更好，改性树脂2对PVC附着力更好。本发明通过两种改性树脂对主体树脂在PVC附着力、柔韧性进行综合性改善。改性树脂1为聚醚链段，为线性结构，柔性性好，同时聚醚亲水，可以快速溶解于常温水中，但是聚醚树脂本身偏软偏粘，本发明将改性树脂1与PVA及填料相结合改善涂料的干爽性。
以所述聚乙烯醇PVA树脂的质量份数为基准，本发明提供的用于软质PVC的可水洗临时装饰涂料包括聚醚改性硅氧烷消泡剂0.1～0.3份，更优选为0.2份。所述聚醚改性硅氧烷消泡剂优选为Tego 810。本发明利用聚醚改性硅氧烷消泡剂抑制和消除生产过程中产生的泡沫。
以所述聚乙烯醇PVA树脂的质量份数为基准，本发明提供的用于软质PVC的可水洗临时装饰涂料包括聚醚改性硅氧烷润湿剂0.1～0.3份，更优选为0.2～0.3份。所述聚醚改性硅氧烷润湿剂优选为Tego 270。本发明利用聚醚改性硅氧烷润湿剂降低表面张力，快速润湿底材。
以所述聚乙烯醇PVA树脂的质量份数为基准，本发明提供的用于软质PVC的可水洗临时装饰涂料包括含锚固基团分散剂0.2～0.5份，更优选为0.3～0.4份。所述含锚固基团分散剂优选为BYK 190。本发明利用含锚固基团分散剂分散填料，提高生产效率。
以所述聚乙烯醇PVA树脂的质量份数为基准，本发明提供的用于软质PVC的可水洗临时装饰涂料包括玻璃微粉2.0～5.0份，优选为3～4份。所述玻璃微粉的粒径优选为3000目。本发明中玻璃微粉作为功能性填料。
以所述聚乙烯醇PVA树脂的质量份数为基准，本发明提供的用于软质PVC的可水洗临时装饰涂料包括硅藻土3.0～6.0份，优选为4～5份。所述硅藻土优选为硅藻土300号。本发明中硅藻土作为功能性填料。
以所述聚乙烯醇PVA树脂的质量份数为基准，本发明提供的用于软质PVC的可水洗临时装饰涂料包括AMP-95多功能助剂0.5～1.5份，优选为0.6～1.2份，更优选为0.8～1.0份。所述AMP-95多功能助剂优选为GC-96N，本发明利用AMP-95多功能助剂(市售)调节pH值。
以所述聚乙烯醇PVA树脂的质量份数为基准，本发明提供的用于软质PVC的可水洗临时装饰涂料包括聚酰胺蜡流变控制助剂2.0～3.0份，优选为2～2.5份，所述聚酰胺蜡流变控制助剂优选为Disparlon AQ633；本发明利用聚酰胺蜡流变控制助剂发挥防沉、防流挂作用。
以所述聚乙烯醇PVA树脂的质量份数为基准，本发明提供的用于软质PVC的可水洗临时装饰涂料包括羧酸型丙基甜菜两性表面活性剂2.0～15.0份，优选为5.0～10.0份，更优选为6.0～8.0份。所述羧酸型丙基甜菜两性表面活性剂优选为CAB-35椰油酰胺基甜菜碱。本发明利用羧酸型丙基甜菜两性表面活性剂发挥增稠作用，同时增加水洗性。
以所述聚乙烯醇PVA树脂的质量份数为基准，本发明提供的用于软质PVC的可水洗临时装饰涂料包括乙醇1.0～3.0份，更优选为2.0份。本发明利用乙醇改善溶解性。
以所述聚乙烯醇PVA树脂的质量份数为基准，本发明提供的用于软质PVC的可水洗临时装饰涂料包括丙二醇甲醚1.0～3.0份，优选为1.5～2.0份。本发明利用丙二醇甲醚提高成膜性。
以所述聚乙烯醇PVA树脂的质量份数为基准，本发明提供的用于软质PVC的可水洗临时装饰涂料包括水0～20份，优选为7.0～17.2份，更优选为7.3～14.9份。本发明利用水调整涂料的粘度。
以所述聚乙烯醇PVA树脂的质量份数为基准，本发明提供的用于软质PVC的可水洗临时装饰涂料包括聚氨酯流变助剂0～0.5份，优选为0.2～0.3份；所述聚氨酯流变助剂优选为RM-8W。本发明利用聚氨酯流变助剂改善产品流体状态和施工性。
以所述聚乙烯醇PVA树脂的质量份数为基准，本发明提供的用于软质PVC的可水洗临时装饰涂料包括气相二氧化硅0～1.0份，优选为0.3～0.5份；所述气相二氧化硅优选为VP RS 92。本发明利用气相二氧化硅协同防沉。
以所述聚乙烯醇PVA树脂的质量份数为基准，本发明提供的用于软质PVC的可水洗临时装饰涂料包括水性专用铝银浆0～15.0份，所述水性专用铝银浆的粒径优选为8～12微米，本发明利用水性专用铝银浆作为效果颜料浆。
以所述聚乙烯醇PVA树脂的质量份数为基准，本发明提供的用于软质PVC的可水洗临时装饰涂料包括无树脂水性色浆0～60.0份。本发明利用无树脂水性色浆作为实色调色浆。
本发明提供了上述技术方案所述可水洗临时装饰涂料的制备方法，包括以下步骤：
将聚乙烯醇PVA树脂、聚醚改性丙烯酸树脂、丙烯酸改性聚氨酯PUA树脂、部分水、乙醇、丙二醇甲醚、含锚固基团分散剂、聚醚改性硅氧烷润湿剂、聚醚改性硅氧烷消泡剂、硅藻土、玻璃微粉、气相二氧化硅和AMP-95多功能助剂混合，进行分散，得到第一混合物料；
将所述第一混合物料、聚氨酯流变助剂、聚酰胺蜡流变控制助剂和部分羧酸型丙基甜菜两性表面活性剂混合，得到第二混合物料；
向所述第二混合物料中加入无树脂水性色浆和/或水性专用铝银浆调至所需颜色，加入剩余羧酸型丙基甜菜两性表面活性剂，采用剩余水调整至所需粘度，得到用于软质PVC的可水洗临时装饰涂料。
本发明将聚乙烯醇PVA树脂、聚醚改性丙烯酸树脂、丙烯酸改性聚氨酯PUA树脂、部分水、乙醇、丙二醇甲醚、含锚固基团分散剂、聚醚改性硅氧烷润湿剂、聚醚改性硅氧烷消泡剂、硅藻土、玻璃微粉、气相二氧化硅和AMP-95多功能助剂混合，进行分散，得到第一混合物料。本发明对所述混合的过程没有特殊的限定，按照本领域熟知的过程将物料混合均匀即可。在本发明中，所述第一混合物料的细度优选＜35μm；本发明对所述分散的具体过程没有特殊的限定，按照本领域熟知的过程得到上述细度要求的混合物料即可。
得到第一混合物料后，本发明将所述第一混合物料、聚氨酯流变助剂、聚酰胺蜡流变控制助剂和部分羧酸型丙基甜菜两性表面活性剂混合，得到第二混合物料。本发明对制备所述第二混合物料的混合过程没有特殊的限定，按照本领域熟知的过程将物料混合均匀即可。
得到第二混合物料后，本发明向所述第二混合物料中加入无树脂水性色浆和/或水性专用铝银浆调至所需颜色，加入剩余羧酸型丙基甜菜两性表面活性剂，采用剩余水调整至所需粘度，得到用于软质PVC的可水洗临时装饰涂料。
本发明对所述无树脂水性色浆和/或水性专用铝银浆调至所需颜色的具体过程没有特殊的限定，按照本领域熟知的过程调整至所需颜色即可。
本发明对所述部分羧酸型丙基甜菜两性表面活性剂和剩余羧酸型丙基甜菜两性表面活性剂的配比没有特殊的限定，根据涂料的实际稠度需求进行调整即可。在本发明中，所述用于软质PVC的可水洗临时装饰涂料在25℃的粘度优选为90～120KU，更优选为98～110KU，进一步优选为102～105KU。
本发明对所述部分水和剩余水的配比没有特殊的限定，根据实际粘度需求进行调整即可。
本发明提供了上述技术方案所述用于软质PVC的可水洗临时装饰涂料或上述技术方案所述制备方法制备得到的用于软质PVC的可水洗临时装饰涂料在软质盲盒中的应用。本发明对所述应用的方法没有特殊的限定，按照本领域熟知的喷涂或印刷于软质PVC素材上即可。
下面将结合本发明中的实施例，对本发明中的技术方案进行清楚、完整地描述。显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例1～6
实施例所用原料来源为：聚乙烯醇PVA树脂POVAL 3-80；聚醚改性丙烯酸树脂Polyox WSRN10-Dow；丙烯酸改性聚氨酯PUA树脂PUA-5870；聚醚改性硅氧烷消泡剂Tego810迪高；聚醚改性硅氧烷润湿剂Tego 270迪高；含锚固基团分散剂BYK190，BYK；玻璃微粉3000目广东源磊粉体有限公司；硅藻土300号灵寿县盛飞矿产品加工厂；气相二氧化硅VPRS 92德固赛；AM-95多功能助剂GC-96N江苏广成化工有限公司；聚酰胺蜡流变控制助剂DisparlonAQ633；聚氨酯流变助剂RM-8W陶氏化学；羧酸型丙基甜菜两性表面活性剂cab-35，广州天赐实业有限公司；水性专用铝银浆粒径8～12微米，江苏瑞克精细化工有限公司；无树脂水性色浆(红、黄、蓝、绿、黑等)苏州世名科技股份有限公司；
实施例1～6按照表1配料：
表1实施例1～6的涂料的配料
制备方法：
将聚乙烯醇PVA树脂、聚醚改性丙烯酸树脂、丙烯酸改性聚氨酯PUA树脂、部分水、乙醇、丙二醇甲醚、含锚固基团分散剂、聚醚改性硅氧烷润湿剂、聚醚改性硅氧烷消泡剂、硅藻土、玻璃微粉、气相二氧化硅和AMP-95多功能助剂混合，进行分散至细度＜35μm，得到第一混合物料；
将所述第一混合物料、聚氨酯流变助剂、聚酰胺蜡流变控制助剂和部分羧酸型丙基甜菜两性表面活性剂混合，得到第二混合物料；
向所述第二混合物料中加入无树脂水性色浆和/或水性专用铝银浆调至所需颜色，加入剩余羧酸型丙基甜菜两性表面活性剂，采用剩余水调整至所需粘度，得到用于软质PVC的可水洗临时装饰涂料。
对比例1
配料见表2
表2对比例1的涂料的配料
制备方法：
将聚醚改性丙烯酸树脂、部分水、乙醇、丙二醇甲醚、含锚固基团分散剂、聚醚改性硅氧烷润湿剂、聚醚改性硅氧烷消泡剂、滑石粉和AMP-95多功能助剂混合，进行分散至细度＜35μm，得到混合物料；
向所述混合物料中加入无树脂水性色浆和/或水性专用铝银浆调至所需颜色，采用剩余水调整至所需粘度，得到用于软质PVC的可水洗临时装饰涂料。
性能测试
1)依据GB/T 1723-1993记载的方法测试实施例1～6制备的涂料的粘度；将实施例1～6制备的涂料分别喷涂于PVC素材上，在70℃干燥30min后，测试所得PVC素材的柔韧性，具体依据PVC素材在常温下极限变形能力情况下进行折弯测试，所得结果见表3；
2)将实施例1～6制备的涂料分别喷涂于PVC素材上，在70℃干燥30min后，用30℃温水进行水洗，所得结果见表3。
表3实施例1～6制备的涂料的性能指标
柔韧性：A表示180度折弯，无开裂，脱落现象；B表示90度折弯不开裂，不脱落。
由表2可知，本发明提供的涂料具有优异的柔韧性，弯折不开裂，且1分钟内可冲洗，浸泡干净，在PVC素材上没有残留。
2)在PVC素材上分别喷涂对比例1的涂料和实施例3制备的涂料，在温度70℃干燥30min后：
1.进行90°弯曲测试，观察漆膜破损情况，所得结果见表4；
2.置于PE包装袋后进行55℃/10d老化测试，观察漆膜破损情况，所得结果见表4；
3.在相同温度20℃、25℃和30℃分别进行水洗，观察水洗时间以及残留情况，所得结果见表4。
表4实施例3和对比例1的涂料性能对比结果
由表3可知，与对比例1中现有涂料相比，本发明的涂料弯折后不开裂，说明柔韧性优异；在55℃老化10d，漆膜不脱落，且25℃以上水温1min内可洗净，无残留。
以上所述仅是本发明的优选实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明原理的前提下，还可以做出若干改进和润饰，这些改进和润饰也应视为本发明的保护范围。
Claims (10)
1.一种用于软质PVC的可水洗临时装饰涂料，以质量份数计，包括聚乙烯醇PVA树脂20～60份，聚醚改性丙烯酸树脂10～30份，丙烯酸改性聚氨酯PUA树脂3～8份，聚醚改性硅氧烷消泡剂0.1～0.3份，聚醚改性硅氧烷润湿剂0.1～0.3份，含锚固基团分散剂0.2～0.5份，玻璃微粉2.0～5.0份，硅藻土3.0～6.0份，AMP-95多功能助剂0.5～1.5份，聚酰胺蜡流变控制助剂2.0～3.0份，羧酸型丙基甜菜两性表面活性剂2.0～15.0份，乙醇1.0～3.0份，丙二醇甲醚1.0～3.0份，水0～20份，聚氨酯流变助剂0～0.5份，气相二氧化硅0～1.0份，水性专用铝银浆0～15.0份，无树脂水性色浆0～60.0份。
2.根据权利要求1所述的可水洗临时装饰涂料，其特征在于，所述聚乙烯醇PVA树脂为POVAL 3-80。
3.根据权利要求1所述的可水洗临时装饰涂料，其特征在于，所述聚醚改性丙烯酸树脂为改性树脂1Polyox WSR N10-Dow；所述丙烯酸改性聚氨酯PUA树脂为PUA-5870。
4.根据权利要求1所述的可水洗临时装饰涂料，其特征在于，所述聚醚改性硅氧烷消泡剂为Tego 810；所述聚醚改性硅氧烷润湿剂为Tego 270。
5.根据权利要求1所述的可水洗临时装饰涂料，其特征在于，所述含锚固基团分散剂为BYK 190；所述气相二氧化硅为VP RS 92；所述聚氨酯流变助剂为RM-8W。
6.根据权利要求1所述的可水洗临时装饰涂料，其特征在于，所述聚酰胺蜡流变控制助剂为Disparlon AQ633；所述羧酸型丙基甜菜两性表面活性剂为CAB-35椰油酰胺基甜菜碱。
7.权利要求1～6任一项所述可水洗临时装饰涂料的制备方法，包括以下步骤：
将聚乙烯醇PVA树脂、聚醚改性丙烯酸树脂、丙烯酸改性聚氨酯PUA树脂、部分水、乙醇、丙二醇甲醚、含锚固基团分散剂、聚醚改性硅氧烷润湿剂、聚醚改性硅氧烷消泡剂、硅藻土、玻璃微粉、气相二氧化硅和AMP-95多功能助剂混合，进行分散，得到第一混合物料；
将所述第一混合物料、聚氨酯流变助剂、聚酰胺蜡流变控制助剂和部分羧酸型丙基甜菜两性表面活性剂混合，得到第二混合物料；
向所述第二混合物料中加入无树脂水性色浆和/或水性专用铝银浆调至所需颜色，加入剩余羧酸型丙基甜菜两性表面活性剂，采用剩余水调整至所需粘度，得到用于软质PVC的可水洗临时装饰涂料。
8.根据权利要求7所述的制备方法，其特征在于，所述第一混合物料的细度＜35μm。
9.根据权利要求7所述的制备方法，其特征在于，所述用于软质PVC的可水洗临时装饰涂料在25℃的粘度为90～120KU。
10.权利要求1～6任一项所述用于软质PVC的可水洗临时装饰涂料或权利要求7～9任一项所述制备方法制备得到的用于软质PVC的可水洗临时装饰涂料在软质盲盒中的应用。