CN110655835B - 一种零voc水性内墙调色涂料组合物的制备与应用 - Google Patents
一种零voc水性内墙调色涂料组合物的制备与应用 Download PDFInfo
- Publication number
- CN110655835B CN110655835B CN201810688780.1A CN201810688780A CN110655835B CN 110655835 B CN110655835 B CN 110655835B CN 201810688780 A CN201810688780 A CN 201810688780A CN 110655835 B CN110655835 B CN 110655835B
- Authority
- CN
- China
- Prior art keywords
- weight
- parts
- water
- coating composition
- zero
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明提供了一种零VOC水性内墙调色涂料组合物,所述组合物制备配方包括以下重量份数的组分:成膜物质30~50重量份;颜料0~30重量份;填料30~50重量份;水性微细氧化聚乙烯蜡乳化液0.5~1.5重量份;增稠剂0‑2重量份;分散剂0.5‑1.5重量份;润湿剂0.1‑0.5重量份;成膜助剂1.5~2.5重量份;其他助剂0.5~3.0重量份;以及可接受量的水。本发明的涂料组合物形成的涂料具有高环保性能、高效的抗甲醛功能、优异的调色功能,与各种系列色浆相容性好;本发明的涂料组合物形成的漆膜具有较高的硬度、优异的抗湿擦掉粉性能、抗指划发白性能、疏水性和耐污渍性能。
Description
技术领域
本发明涉及水性内墙涂料的调色的技术与应用领域,具体涉及一种高环保性的零VOC水性内墙调色涂料组合物的制备与应用。
背景技术
随着国家和世界的发展,物质生活富裕度日益增高,我们对生活的环境中有害物质对自身的安全损害的关注越来越强。近年来,水性建筑涂料发展日新月异,新技术层出不穷。市场上对水性建筑涂料的功能性的要求也越来越多,在注重涂料环保性能要求的同时,涂层的各种特殊的功能性能都受到了广大的消费者群体的关注。
我们生活的世界是个丰富多彩的空间,这就赋予了需要色彩缤纷的涂层来装饰我们生活的家,休闲娱乐的商场、电影院、饭店,等等。现有的水性深色调色涂料需要添加大量的色浆调色,这样就会导致漆膜涂层的亲水性能较强,所以优异的湿擦掉粉性能一直是水性深色调色漆的挑战目标。
综上所述,本领域迫切的需要研制一种零VOC水性内墙调色涂料,用于建筑墙面,产品需要满足高环保的要求;优异的抗湿擦掉粉性能和抗指划发白性能的要求;以及良好的调色功能,与各种系列色浆相容性好;疏水性,耐污渍性能均较好,且漆膜硬度高;而且具有高效的抗甲醛功能。
发明内容
本发明的目的在于研制一种零VOC水性内墙调色涂料组合物,用于建筑墙面,使其既有优异的抗湿擦掉粉性能和抗指划发白性能的要求,同时产品满足高环保的要求、优异的抗甲醛性能、优异的耐污渍性能。
本发明第一方面提供一种零VOC水性内墙调色涂料组合物,所述零VOC水性内墙调色涂料组合物制备配方包括以下重量份数的组分:
可接受量的水,
其中,所述的水性微细氧化聚乙烯蜡乳化液中,颗粒平均粒径为0.01~0.1μm,
所述零VOC水性内墙调色涂料组合物的颜料体积浓度为30~50%。
在另一优选例中,所述其他助剂包含以下重量份的组分:
在另一优选例中,所述消泡剂选自:有机硅类消泡剂、矿物油类消泡剂或其组合;
所述pH调节剂选自:有机醇胺pH调节剂、无机pH调节剂或其组合。
在另一优选例中,所述消泡剂中,有机硅类消泡剂与矿物油类消泡剂重量比为1~1.5:1~1.5。
在另一优选例中,所述的组合物不含有防冻剂,优选不含乙二醇防冻剂或丙二醇防冻剂。
在另一优选例中,所述增稠剂选自:纤维素醚、聚氨酯类流变调节剂、无机膨润土或其组合;
所述分散剂选自:钠盐、铵盐或其组合;
所述润湿剂为烷基醚型润湿剂:
成膜助剂为成膜助剂为醇酯型成膜助剂。
在另一优选例中,所述的润湿剂选自下组:烷基醚硫酸钠、烷基酚醚二磺酸钠、烷基苯磺酸钠或其组合。
在另一优选例中,所述的成膜助剂为十二碳醇酯型成膜助剂。
在另一优选例中,所述颜料为钛白粉;
所述填料选自下组:硅灰石、硅宝、云母粉、滑石粉、煅烧高岭土、霞石粉、重钙或其组合。
在另一优选例中,所述的颜料为金红石型钛白粉
在另一优选例中,所述成膜物质为丙烯酸共聚物乳液。
在另一优选例中,所述丙烯酸共聚物乳液粒径分布为150~240nm,玻璃化温度Tg为:40~50℃,所述丙烯酸共聚物乳液最低成膜温度MFFT为:40~50℃。
本发明第二方面提供一种如本发明第一方面所示的零VOC水性内墙调色涂料组合物的制备方法,所述的制备方法包括以下步骤:
(1)将水放入分散罐内,转速控制在300~500转/分钟;
(2)依次将分散剂、润湿剂、消泡剂、增稠剂加入到分散罐内,搅拌3±1分钟;
(3)将颜填料加入分散罐内,提高转速至1200~1800转/分钟,高速分散15±3分钟;
(4)高速分散后降转速至600~800转/分钟,加入水,搅拌3±1分钟;
(5)缓慢加入成膜物质,搅拌5±2分钟;
(6)接着加入成膜助剂,搅拌3±1分钟;
(7)再依次加入防霉剂和防腐剂,搅拌3±1分钟;
(8)缓慢加入水性微细氧化聚乙烯蜡乳化液,搅拌3±1分钟;
(9)再加入增稠剂,搅拌3±1分钟,调节流平性;
(10)然后加入pH调节剂,达到需要的pH值(pH为8-10);
(11)最后加入水调节粘度,得到所述零VOC水性内墙调色涂料组合物。
应理解,在本发明范围内中,本发明的上述各技术特征和在下文(如实施例)中具体描述的各技术特征之间都可以互相组合,从而构成新的或优选的技术方案。限于篇幅,在此不再一一累述。
附图说明
图1显示为实施例1色浆相容性图。
图2显示为实施例1和市售竞品的湿擦掉粉对比图。
具体实施方式
下面结合具体实施例,进一步阐述本发明。应理解,这些实施例仅用于说明本发明而不用于限制本发明的范围。下列实施例中未注明具体条件的实验方法,通常按照国家标准测定。若没有相应的国家标准,则按照通用的国际标准、常规条件、或按照制造厂商所建议的条件进行。除非另外说明,否则所有的份数为重量份,所有的百分比为重量百分比,所述的聚合物分子量为数均分子量。
除非另有定义或说明,本文中所使用的所有专业与科学用语与本领域技术熟练人员所熟悉的意义相同。此外任何与所记载内容相似或均等的方法及材料皆可应用于本发明方法中。
一种零VOC水性内墙调色涂料组合物
零VOC水性内墙调色涂料组合物制备配方包括以下重量份数的组分:
可接受量的水,
其中,所述的水性微细氧化聚乙烯蜡乳化液中,颗粒平均粒径为0.01~0.1μm,
所述零VOC水性内墙调色涂料组合物的颜料体积浓度为30~50%。
所述其他助剂包含以下重量份的组分:
在本发明中,所述的消泡剂选自:有机硅类消泡剂、矿物油类消泡剂或其组合;所述pH调节剂选自:有机醇胺pH调节剂、无机pH调节剂或其组合。
所述消泡剂包括:
有机硅类消泡剂 1.0~1.5重量份;以及
矿物油类消泡剂 1.0~1.5重量份。
制备方法
一种零VOC水性内墙调色涂料组合物的制备方法,包括以下步骤:
(1)将水放入分散罐内,转速控制在300~500转/分钟;
(2)依次将分散剂、润湿剂、消泡剂、增稠剂加入到分散罐内,搅拌3±1分钟;
(3)将颜填料加入分散罐内,提高转速至1200~1800转/分钟,高速分散15±3分钟;
(4)高速分散后降转速至600~800转/分钟,加入水,搅拌3±1分钟;
(5)缓慢加入成膜物质,搅拌5±2分钟;
(6)接着加入成膜助剂,搅拌3±1分钟;
(7)再依次加入防霉剂和防腐剂,搅拌3±1分钟;
(8)缓慢加入水性微细氧化聚乙烯蜡乳化液,搅拌3±1分钟;
(9)再加入增稠剂,搅拌3±1分钟,调节流平性;
(10)然后加入pH调节剂,达到需要的pH值(pH为8-10);
(11)最后加入水调节粘度,得到所述零VOC水性内墙调色涂料组合物。
发明优点:
1、具有高效的抗甲醛功能。
2、具有优异的调色功能,与各种系列色浆相容性好。
3、具有优异的抗湿擦掉粉性能和抗指划发白性能。
4、具体疏水性,耐污渍性能较好,以及较高的硬度。
5、该涂料组合物形成的涂料漆膜提高了内墙调色涂料产品的品质。
实施例1
本发明零VOC水性内墙调色涂料组合物的一种实施例,本实施例所述零VOC水性内墙调色涂料组合物配方制备包括以下重量份数的组分:
本实施例所述的一种零VOC水性内墙涂料组合物的制备方法,包括以下步骤:
(1)将水放入分散罐内,转速控制在300~500转/分钟;
(2)然后依次将分散剂、润湿剂、消泡剂、增稠剂加入到分散罐内,搅拌3±1分钟;
(3)将颜填料加入分散罐内,提高转速至1200~1800转/分钟,高速分散15±3分钟;
(4)高速分散后降转速至600~800转/分钟,加入水,搅拌3±1分钟;
(5)缓慢加入成膜物质,搅拌5±2分钟;
(6)接着加入成膜助剂,搅拌3±1分钟;
(7)再依次加入防霉剂和防腐剂,搅拌3±1分钟;
(8)缓慢加入水性微细氧化聚乙烯蜡乳化液,搅拌3±1分钟;
(9)再加入增稠剂,搅拌3±1分钟,调节流平性;
(10)然后加入pH调节剂,达到需要的pH值(pH为8-10);
(11)最后加入水调节粘度,得到所述零VOC水性内墙调色涂料组合物。
实施例2
本发明零VOC水性内墙涂料组合物的一种实施例,本实施例所述零VOC水性内墙调色涂料组合物配方制备包括以下重量份数的组分:
本实施例所述的一种零VOC水性内墙涂料组合物的制备方法,包括以下步骤:
(1)将水放入分散罐内,转速控制在300~500转/分钟;
(2)然后依次将分散剂、润湿剂、消泡剂、增稠剂加入到分散罐内,搅拌3±1分钟;
(3)将颜填料加入分散罐内,提高转速至1200~1800转/分钟,高速分散15±3分钟;
(4)高速分散后降转速至600~800转/分钟,加入水,搅拌3±1分钟;
(5)缓慢加入成膜物质,搅拌5±2分钟;
(6)接着加入成膜助剂,搅拌3±1分钟;
(7)再依次加入防霉剂和防腐剂,搅拌3±1分钟;
(8)缓慢加入水性微细氧化聚乙烯蜡乳化液,搅拌3±1分钟;
(9)再加入增稠剂,搅拌3±1分钟,调节流平性;
(10)然后加入pH调节剂,达到需要的pH值(pH为8-10);
(11)最后加入水调节粘度,得到所述零VOC水性内墙调色涂料组合物。
实施例3
本发明零VOC水性内墙涂料组合物的一种实施例,本实施例所述水性涂料配方制备包括以下重量份数的组分:
本实施例所述的一种零VOC水性内墙涂料组合物的制备方法,包括以下步骤
(1)将水放入分散罐内,转速控制在300~500转/分钟;
(2)然后依次将分散剂、润湿剂、消泡剂、增稠剂加入到分散罐内,搅拌3±1分钟;
(3)将颜填料加入分散罐内,提高转速至1200~1800转/分钟,高速分散15±3分钟;
(4)高速分散后降转速至600~800转/分钟,加入水,搅拌3±1分钟;
(5)缓慢加入成膜物质,搅拌5±2分钟;
(6)接着加入成膜助剂,搅拌3±1分钟;
(7)再依次加入防霉剂和防腐剂,搅拌3±1分钟;
(8)缓慢加入水性微细氧化聚乙烯蜡乳化液,搅拌3±1分钟;
(9)再加入增稠剂,搅拌3±1分钟,调节流平性;
(10)然后加入pH调节剂,达到需要的pH值(pH为8-10);
(11)最后加入水调节粘度,得到所述零VOC水性内墙调色涂料组合物。
实施例4
本发明零VOC水性内墙涂料组合物的一种实施例,本实施例所述水性涂料配方制备包括以下重量份数的组分:
本实施例所述的一种零VOC水性内墙涂料组合物的制备方法,包括以下步骤:
(1)将水放入分散罐内,转速控制在300~500转/分钟;
(2)然后依次将分散剂、润湿剂、消泡剂、增稠剂加入到分散罐内,搅拌3±1分钟;
(3)将颜填料加入分散罐内,提高转速至1200~1800转/分钟,高速分散15±3分钟;
(4)高速分散后降转速至600~800转/分钟,加入水,搅拌3±1分钟;
(5)缓慢加入成膜物质,搅拌5±2分钟;
(6)接着加入成膜助剂,搅拌3±1分钟;
(7)再依次加入防霉剂和防腐剂,搅拌3±1分钟;
(8)缓慢加入水性微细氧化聚乙烯蜡乳化液,搅拌3±1分钟;
(9)再加入增稠剂,搅拌3±1分钟,调节流平性;
(10)然后加入pH调节剂,达到需要的pH值(pH为8-10);
(11)最后加入水调节粘度,得到所述零VOC水性内墙调色涂料组合物。
测试
对本发明产品实施例1~4的制备的涂料漆膜的全性能进行测试:施工性、耐水性、耐碱性、附着力、耐擦洗性、厚膜开裂、冻融稳定性、热储存稳定性、挥发性有机物含量(VOC)等,其中主要性能测试参照GB/T9756-2009内墙涂料国家标准和JG/T 1074-2008等标准,测试性能结果都满足标准要求。
具体地,实施例1的测试结果见表1:
表1性能测试
检验项目名称 | 单位 | 技术要求 | 检验结果 |
容器中状态 | / | 无硬块,搅拌后呈均有状态 | 符合 |
施工性 | / | 刷涂二道无障碍 | 符合 |
耐水性 | / | 48h无异常 | 合格 |
耐碱性 | / | 48h无异常 | 合格 |
耐擦洗性 | 次 | ≥1000 | >10000 |
厚膜开裂 | / | 低温/常温 | 合格 |
热储存稳定性 | / | 55℃热储存两周 | 合格 |
冻融稳定性 | / | 6次循环无异常 | 合格 |
附着力 | 级 | ≤1级 | 0级 |
甲醛净化效率 | % | ≥75 | ≥89.3 |
挥发性有机物含量(VOC) | g/L | ≤2 | 未检出 |
对本发明产品实施例1~4的制备的涂料漆膜的特殊性能进行测试:色浆相容性、湿擦掉粉性能、抗指划发白性能、甲醛净化效率等,测试性能结果都满足发明要求。具体地,实施例1和市售竞品的测试结果如图1和图2所示。
其中,图1显示为实施例1色浆相容性图、图2显示为实施例1和市售竞品的湿擦掉粉对比图。
针对实施例1的产品、市售竞品1以及市售竞品2分别用毛巾去湿擦漆膜一定次数后观察漆膜的掉粉情况,掉粉情况如图2所示,实施例1对应的巾上面颜色最浅,表示实施例1涂层抗湿擦掉粉性能最好
本发明制备的零VOC水性内墙涂料组合物具有广泛的调色性能,与色浆相容性好,满足高环保的要求、优异的抗湿擦掉粉性能和抗指划发白性能的要求,且产品具有优异的抗甲醛功能,符合儿童所需的家装装饰和教育场所装饰,亦可用于儿童教育的DIY涂料用品。
在本发明提及的所有文献都在本申请中引用作为参考,就如同每一篇文献被单独引用作为参考那样。此外应理解,在阅读了本发明的上述讲授内容之后,本领域技术人员可以对本发明作各种改动或修改,这些等价形式同样落于本申请所附权利要求书所限定的范围。
Claims (1)
1.一种零VOC水性内墙调色涂料组合物,其特征在于,所述零VOC水性内墙调色涂料组合物制备配方由以下重量份数的组分组成:
成膜物质:DOW SF-105M乳液 40重量份;
颜料:金红石型钛白粉 0.5重量份;
填料:由硅灰石JA 2123、硅宝、滑石粉、煅烧高岭土和重钙组成共41重量份;
水性蜡乳液:Lubrizol公司的蜡乳液WAX 966 1.0重量份;和
涂料助剂,由以下重量份数的组分组成:润湿剂 0.4重量份;分散剂1.0重量份;pH调节剂VANTEX-T 0.3重量份;醇酯类溶剂 2.0重量份;增稠剂:由聚氨酯类流变调节剂和无机膨润土组成共1.2重量份;有机硅消泡剂 0.60重量份;防霉剂 0.4重量份;防腐剂0.2重量份;和纯水18重量份;
其中,所述分散剂选自:钠盐、铵盐,或其组合;且
所述的润湿剂选自下组:烷基醚硫酸钠、烷基酚醚二磺酸钠、烷基苯磺酸钠,或其组合。