CN114809491A - Quick-drying type assembly type building interior wall latex paint and interior wall paint spraying construction method thereof - Google Patents

Quick-drying type assembly type building interior wall latex paint and interior wall paint spraying construction method thereof Download PDF

Info

Publication number
CN114809491A
CN114809491A CN202210323895.7A CN202210323895A CN114809491A CN 114809491 A CN114809491 A CN 114809491A CN 202210323895 A CN202210323895 A CN 202210323895A CN 114809491 A CN114809491 A CN 114809491A
Authority
CN
China
Prior art keywords
interior wall
putty
drying
quick
wall surface
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN202210323895.7A
Other languages
Chinese (zh)
Inventor
肖蓉华
张凤琼
陈立斌
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangdong Meike Design Engineering Co ltd
Original Assignee
Guangdong Meike Design Engineering Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guangdong Meike Design Engineering Co ltd filed Critical Guangdong Meike Design Engineering Co ltd
Priority to CN202210323895.7A priority Critical patent/CN114809491A/en
Publication of CN114809491A publication Critical patent/CN114809491A/en
Pending legal-status Critical Current

Abstract

The invention discloses a quick-drying type assembly building interior wall latex paint and an interior wall paint spraying construction method thereof, belonging to the field of interior decoration, the quick-drying type assembly building interior wall latex paint and the interior wall paint spraying construction method thereof comprise a base layer treatment, firstly peeling, loosening and bulging or other sundries on a wall surface and other base layers are removed and leveled, dust, dirt, splash, mortar flow marks or sundries remained on the surface of the base layer are removed and cleaned, putty is repaired, pits, gaps or other parts on the wall surface and other base layers are leveled by plaster, after drying, the protruded parts are leveled by No. 1 abrasive paper, and floating dust, dirt, splash or sundries are cleaned, the number of times of putty scraping can be determined by the flatness of the base layer or the wall surface, the putty scraping is at least three times, the mixing ratio of the putty is a weight ratio, the putty scraping is divided into two types, the quick-drying type assembly building interior wall latex paint can be realized, the construction time of interior wall latex paint can be effectively reduced, the conditions of bottom penetration, obvious racking joint, obvious brushing lines, uneven color separation lines and the like occur.

Description

Quick-drying type assembly type building interior wall latex paint and interior wall paint spraying construction method thereof
Technical Field
The invention relates to the field of interior decoration, in particular to quick-drying type fabricated building interior wall latex paint and an interior wall paint spraying construction method thereof.
Background
Interior finishing includes room design, finishing, furniture arrangement and various small decoration points. The decoration construction in the building is emphasized, and the long-term continuous decoration is included during the decoration design construction period and after the building is placed.
Wherein, at this in-process of fitment, involve the wall whitewash, furred ceiling, ceramic tile and the laying of wall brick etc. and when the wall whitewashes, an indispensable process is just the whitewash of interior wall emulsion paint, and the construction method of present interior wall emulsion paint often produces the bottom of penetrating, connects obviously, brush line obvious, the different scheduling problem of colour separation line.
Disclosure of Invention
1. Technical problem to be solved
Aiming at the problems in the prior art, the invention aims to provide the quick-drying type assembly building interior wall latex paint and the interior wall paint spraying construction method thereof, which can be realized and effectively reduce the occurrence of the conditions of bottom penetration, obvious joint, obvious brushing, uneven color separation lines and the like during the interior wall latex paint construction.
2. Technical scheme
In order to solve the above problems, the present invention adopts the following technical solutions.
The quick-drying type assembly type building interior wall latex paint and the interior wall paint spraying construction method thereof comprise the following steps:
s1: treating a base layer, namely removing and leveling the skinning, loosening and bulging or other impurities on the wall surface and other base layers, and removing and cleaning dust, dirt, splash, mortar flow marks or impurities remained on the surface of the base layer;
s2: repairing putty, namely leveling pits, gaps or other positions of the wall surface and other base layers which are collided with by using plaster, grinding the protruded positions by using No. 1 abrasive paper after drying, and cleaning floating dust, dirt, splashed foam or sundries;
s3: the putty coating is carried out for at least three times, and the mixing ratio of the putty to the putty is a weight ratio which is divided into two types;
s4: applying an emulsion thin coat comprising applying a first emulsion thin coat-applying a second emulsion thin coat-applying a third emulsion thin coat.
Further, in the S3, the weight ratio of the putty suitable for being used indoors is as follows: polyvinyl acetate emulsion: talc powder or whiting powder: 2% carboxymethyl cellulose solution ═ 1: 5: 3.5.
further, the weight ratio of the other putty suitable for the outer wall, the kitchen, the toilet and the bathroom in the S3 is as follows: polyvinyl acetate emulsion: cement: water 1: 5: 1.
further, the method of puttying in S3 comprises:
a1: firstly, using a rubber scraper to transversely and fully scrape, using a scraper to follow the scraper, leaving no joint, paying attention to clean and falling when scraping the last head of the scraper, grinding with No. 1 abrasive paper after drying, grinding and polishing floating putty and spots, and cleaning the wall surface;
a2: the second time of vertical full scraping by using a rubber scraper, the used materials and the method are the same as those of the first time of putty, and after drying, the putty is ground by using No. 1 abrasive paper and cleaned;
a3: and thirdly, repairing putty by using a rubber scraper, fully scraping the putty by using a steel sheet scraper, leveling and polishing a base layer such as a semi-wall surface and the like, drying, and then, polishing by using fine sand paper, wherein the putty is not leaked to be ground or worn.
Further, the method of applying the first-pass emulsion thin coating in S4 includes: the coating sequence is that the top plate is firstly brushed and then the wall surface is brushed, the wall surface is firstly cleaned after the top plate is brushed and then the wall surface is brushed, then the dust on the wall surface is cleaned by cloth, the emulsion thin coating is brushed by a row pen, when a new row pen is used, the movable row pen is carefully cleaned, the emulsion thin coating is uniformly stirred before being used, a proper amount of water is added for diluting, the first time coating is prevented from being coated, putty is re-compensated after drying, the putty to be compensated is dried and sanded by abrasive paper, and the cleaning is carried out.
Further, the method for applying the second emulsion thin coating in S4 includes: the operation needs the same first time, the paint is fully stirred before use, when the emulsion thin paint is not thick, no water or little water is added to prevent bottom exposure, after the paint film is dried, small pimples and brush hair on the wall surface are ground by fine abrasive paper, and the paint is cleaned after being ground to be smooth.
Further, the method of applying the third emulsion thin coating in S4 includes: the operation requires the same emulsion thin coating as the second time, and the emulsion paint film is dried quickly, so the operation needs to be continuously and quickly carried out, the coating is gradually carried out from one end to the other end in the coating process, the upper and lower brushing are mutually connected, the latter row of pens is close to the former row of pens, and the joint is prevented from being processed after drying.
3. Advantageous effects
Compared with the prior art, the invention has the advantages that:
(1) this scheme carries out basic unit's processing earlier, gets rid of debris, later mends pit recess, gap etc. through putty, and the putty ratio of rethread puttying and two kinds of different uses, and at last through the thin coating of application emulsion of three times again, when effectively reducing interior wall emulsion paint construction, the condition such as penetrating end, joint clearly, brush the line obviously, the colour separation line is uneven takes place.
Detailed Description
The technical scheme in the embodiment of the invention is clearly and completely described below; it is obvious that the described embodiments are only a part of the embodiments of the present invention, and not all embodiments, and all other embodiments obtained by those skilled in the art without any inventive work are within the scope of the present invention.
Example 1:
the quick-drying type assembly type building interior wall latex paint and the interior wall paint spraying construction method thereof comprise the following steps:
s1: the method comprises the following steps of (1) base layer treatment, namely, removing and chiseling the peeling, loosening and bulging or other impurities on the wall surface and other base layers, and removing and cleaning dust, dirt, splash, mortar flow marks or impurities remained on the surface of the base layer to avoid the influence of the residual impurities on the flatness of the surface of the base layer;
s2: repairing putty, namely leveling pits, gaps or other positions of the wall surface and other base layers which are collided with by using plaster, grinding the protruded positions by using No. 1 abrasive paper after drying, and cleaning floating dust, dirt, splashed foam or sundries;
s3: the putty coating is carried out for at least three times, and the mixing ratio of the putty to the putty is a weight ratio which is divided into two types;
s4: applying an emulsion thin coat comprising applying a first emulsion thin coat-applying a second emulsion thin coat-applying a third emulsion thin coat.
Preferably, one of the S3 putties suitable for indoor use is as follows by weight: polyvinyl acetate emulsion: talc powder or whiting powder: 2% carboxymethyl cellulose solution ═ 1: 5: 3.5.
preferably, the weight ratio of the other putty suitable for the outer wall, the kitchen, the toilet and the bathroom in the S3 is as follows: polyvinyl acetate emulsion: cement: water 1: 5: 1.
preferably, the method of puttying in S3 comprises the steps of:
a1: firstly, using a rubber scraper to transversely and fully scrape, using a scraper to follow the scraper, leaving no joint, paying attention to clean and falling when scraping the last head of the scraper, grinding with No. 1 abrasive paper after drying, grinding and polishing floating putty and spots, and cleaning the wall surface;
a2: the second time of vertical full scraping by using a rubber scraper, the used materials and the method are the same as those of the first time of putty, and after drying, the putty is ground by using No. 1 abrasive paper and cleaned;
a3: and thirdly, repairing putty by using a rubber scraper, fully scraping the putty by using a steel sheet scraper, leveling and polishing a base layer such as a semi-wall surface and the like, drying, and then, polishing by using fine sand paper, wherein the putty is not leaked to be ground or worn.
Preferably, the first-pass emulsion thin coating applied in S4 is applied by: the coating sequence is that the top plate is firstly brushed and then the wall surface is brushed, the wall surface is firstly cleaned after the top plate is brushed and then the wall surface is brushed, the wall surface dust is cleaned by cloth, the emulsion thin coating is generally brushed by a row of pens, when a new row of pens is used, the movable row of pens is cleaned, the emulsion thin coating is uniformly stirred before being used, water is properly added for dilution, and the phenomenon that the coating cannot be applied all the time is avoided. Drying, adding putty, grinding, and cleaning.
Preferably, the second emulsion thin coat application in S4 is performed by: the operation needs the same operation, the emulsion is fully stirred before use, if the emulsion is thin, water is not added or is added as little as possible if the emulsion is not thick, so that the bottom is not exposed, after a paint film is dried, small pimples and brush hair on the wall surface are ground by fine abrasive paper, and the paint film is cleaned after being ground to be smooth.
Preferably, the third emulsion thin coat application in S4 is performed by: the operation requires the same second emulsion thin coating. Because the latex paint film is dried quickly, the operation should be continuously and quickly carried out, when brushing, the paint is gradually brushed from one end to the other end, the upper and lower brushes are mutually connected, the latter row of pens is close to the former row of pens, and the joint is prevented from being treated after drying.
When in use: at first carry out basic unit's processing, peel, not hard up and swell or other debris are clear away and are dug the chisel out on wall and other basic units, and clean up wall and other basic units, later repair pit recess, gap etc. through putty, guarantee the level and smooth of wall, then through scraping putty cooperation two kinds of putty proportions of different uses many times again, make the wall further level, at last through the thin coating of application emulsion of three times again, when effectively reducing interior wall emulsion paint construction, the condition emergence such as transparent bottom, connect the combed obviously, the line of brushing is obvious, the colour separation line is uneven.
The foregoing is only a preferred embodiment of the present invention; the scope of the invention is not limited thereto. Any person skilled in the art should also be able to cover the technical scope of the present invention by the equivalent or modified embodiments and the modified concepts of the present invention.

Claims (7)

1. The quick-drying type assembly type building interior wall latex paint and the interior wall paint spraying construction method thereof are characterized by comprising the following steps:
s1: treating a base layer, namely removing and leveling the skinning, loosening and bulging or other impurities on the wall surface and other base layers, and removing and cleaning dust, dirt, splash, mortar flow marks or impurities remained on the surface of the base layer;
s2: repairing putty, namely leveling pits, gaps or other positions of the wall surface and other base layers which are collided with by using plaster, grinding the protruded positions by using No. 1 abrasive paper after drying, and cleaning floating dust, dirt, splashed foam or sundries;
s3: the putty coating is carried out for at least three times, and the mixing ratio of the putty to the putty is a weight ratio which is divided into two types;
s4: applying an emulsion thin coat comprising applying a first emulsion thin coat-applying a second emulsion thin coat-applying a third emulsion thin coat.
2. The quick-drying type assembly type building interior wall latex paint and the interior wall painting construction method thereof according to claim 1, are characterized in that: one of the S3 putty suitable for indoor use comprises the following components in percentage by weight: polyvinyl acetate emulsion: talc powder or whiting powder: 2% carboxymethyl cellulose solution ═ 1: 5: 3.5.
3. the quick-drying type assembly type building interior wall latex paint and the interior wall painting construction method thereof according to claim 1, are characterized in that: the weight ratio of the other putty suitable for the outer wall, the kitchen, the toilet and the bathroom in the S3 is as follows: polyvinyl acetate emulsion: cement: water 1: 5: 1.
4. the quick-drying type assembly type building interior wall latex paint and the interior wall painting construction method thereof according to claim 1, are characterized in that: the putty-applying method in S3 comprises the following steps:
a1: firstly, using a rubber scraper to transversely and fully scrape, using a scraper to follow the scraper, leaving no joint, grinding with No. 1 abrasive paper after drying, flattening and polishing floating putty and stains, and cleaning the wall surface;
a2: the second time of vertical full scraping by using a rubber scraper, the used materials and the method are the same as those of the first time of putty, and after drying, the putty is ground by using No. 1 abrasive paper and cleaned;
a3: and thirdly, using a rubber scraper to repair putty, using a steel sheet scraper to fully scrape the putty, using a semi-wall surface and other base layers to scrape and polish, and using fine sand paper to grind and polish after drying.
5. The quick-drying type assembly type building interior wall latex paint and the interior wall painting construction method thereof according to claim 1, are characterized in that: the method for applying the first-pass emulsion thin coating in the step S4 comprises the following steps: the coating sequence is that the top plate is brushed and then the wall surface is brushed, the wall surface is cleaned firstly after the top plate is brushed and then the wall surface is cleaned firstly, then the wall surface dust is wiped by cloth, the emulsion thin coating is brushed by a brush pen, the emulsion thin coating is evenly stirred before use, a proper amount of water is added for dilution, putty is re-supplemented after drying, the putty to be re-supplemented is dried, sanded and cleaned.
6. The quick-drying type assembly type building interior wall latex paint and the interior wall painting construction method thereof according to claim 1, are characterized in that: the method for applying the second emulsion thin coating in the S4 comprises the following steps: the operation needs to be carried out for the first time, the emulsion thin coating is fully stirred before use, no water or less water is added when the emulsion thin coating is not thick, after a paint film is dried, fine abrasive paper is used for polishing away small pimples and brush hair on the wall surface, and the paint is cleaned after being polished to be smooth.
7. The quick-drying type assembly type building interior wall latex paint and the interior wall painting construction method thereof according to claim 1, are characterized in that: the method for applying the third emulsion thin coating in the S4 comprises the following steps: the operation requires the same second emulsion thin coating, the operation is continuous and rapid, the coating is started from one end and gradually coated to the other end, the upper end and the lower end of the coating are sequentially brushed and mutually connected, and the next row of pens is immediately connected with the previous row of pens.
CN202210323895.7A 2022-03-29 2022-03-29 Quick-drying type assembly type building interior wall latex paint and interior wall paint spraying construction method thereof Pending CN114809491A (en)