CN114521667A - Solid-loaded fragrant herbal incense bullet matrix with high smoking quality and preparation method thereof

Info

Publication number: CN114521667A
Application number: CN202011317858.2A
Authority: CN
Inventors: 柳文凤; 黎礼丽; 黄静文; 支瑞韵; 彭兴宇; 肖选虎
Original assignee: Yunnan Yunshuo Technology Co ltd
Current assignee: Yunnan Yunshuo Technology Co ltd
Priority date: 2020-11-23
Filing date: 2020-11-23
Publication date: 2022-05-24

Abstract

The invention discloses a solid fragrant herbal medicine-carrying fragrant bullet substrate with high suction quality and a preparation method thereof, wherein the substrate comprises the following components: the core material module comprises liquorice and special plant fiber particles, and is prepared by simple mixing after microwave expansion; the spice module comprises a solvent, a natural targeted extraction aroma component, a natural plant latent aroma flavoring agent and a sweetener. The preparation method comprises the following steps of mixing the perfume module prepared by the method according to the base material liquid ratio of 1: 0.1 to 1: 20, adding the mixture into the core material prepared by the method, uniformly mixing, and adding 1-30 parts of additive and 1-30 parts of wrapping agent. The heating non-combustible natural grass incense prepared by the invention has targeted characteristic aroma (the characteristic aroma is prominent), strong physiological satisfaction, large smoke quantity and good smoking feeling.

Description

Solid-loaded fragrant herbal incense bullet matrix with high smoking quality and preparation method thereof

Technical Field

The invention relates to the technical field of processing of heating non-combustible smoking products, in particular to a solid fragrant herbal pellet substrate with high smoking quality and a preparation method thereof.

Background

Unlike traditional cigarette, the low temperature cigarette designed based on the idea of "heating without burning" can heat the smoking section to a degree just enough to emit flavor without burning. When ordinary cigarettes are smoked, a plurality of harmful substances are generated at the high temperature of 350-600 ℃, and the harmful substances are reduced when low-temperature non-combustible products are mostly below 300 ℃. At present, the smoking section of the cigarette which is not combusted by heating mainly adopts a flavoring process to load aroma components, additives and the like on carrier particles, so that the smoking experience can be improved, and the product has strong aroma and comfortable taste.

Plant fiber is a sclerenchyma tissue widely distributed in seed plants. The special fiber can obviously improve the flavor of the low-temperature heating non-combustible product, and the product has additional characteristic style on the basis of having thick flavor, thereby being different from other products.

In recent years, domestic tobacco enterprises also carry out a great deal of research on the aspects of heating reconstituted tobacco and heat sources of non-burning cigarettes, and a series of research results of heating the non-burning cigarette reconstituted tobacco in different modes, different heating types, different heating heat sources and the like are formed. However, the substrate materials mainly use the existing tobacco materials or add feed liquid in the reconstituted tobacco processing process, the product is applied to heating non-combustion cigarette products, the defects of small smoke quantity, low physiological satisfaction, obvious smoke attenuation and the like occur, and the smoking quality of the product is influenced.

Disclosure of Invention

The invention aims to provide a solid fragrance-carrying herbal incense substrate with high smoking quality and a preparation method thereof, which can restore the natural property of the special plant fiber taste, increase the richness of the smoking taste of particles, enhance the characteristic fragrance of the particle taste in a targeted manner, and improve the fragrance quality and the smoke amount of smoke.

A solid fragrance-carrying herbal incense bullet substrate with high smoking quality and a preparation method thereof comprise the following steps: .

(1) A core material module: crushing liquorice into particles with the particle size range of 6-40 meshes, and then performing microwave expansion treatment with the treatment power of 400-3000 w. The special plant fiber particles are dried to 0 to 20 percent of water content and crushed to 20 to 200 meshes, and then are fully mixed with the liquorice particles according to 0 to 100 parts to prepare the core material.

(2) A fragrance module: the natural target-extracted aroma components comprise, but are not limited to, 10-90 parts of one or any combination of more of tobacco extract, fruit extract, flower extract, herbal extract, medicine extract and the like; the natural plant latent fragrant aroma-emitting agent comprises one or any combination of 0-5 parts of glycoside compounds, 0-5 parts of sugar ester compounds, 0-5 parts of Amadori compounds, 0-5 parts of terpene compounds, 0-5 parts of lipoid compounds and the like; the sweetener includes, but is not limited to, one or any combination of 0.00001-1 part of mogroside, 0.00001-1 part of stevioside, 0.1-40 parts of liquorice and the like. The solvent is 5-90 parts of mixture of glycerol, propylene glycol, 1, 3-butanediol and the like. The above materials are mixed and stirred uniformly according to a certain proportion to prepare the spice module.

(3) Additive: the additive is prepared by combining one or more of flower and fruit refined extract reconstruction particles such as 0-50 parts of mulberry refined extract reconstruction particles, 0-50 parts of rose refined extract reconstruction particles, 0-50 parts of blueberry refined extract reconstruction particles and the like in any proportion and then combining the flower and fruit refined extract reconstruction particles with 1-99 parts of inorganic filler particles.

(4) Wrapping agent: including but not limited to one or any combination of solid powder essence, anticaking agent ammonium ferric citrate, rose solid powder and the like.

(5) Mixing the prepared core material and the spice module according to the proportion of 1: 0.5-1: 5, flatly paving the mixture in a baking tray, setting the temperature to be 45-280 ℃, baking for 15 minutes to 4 hours until the water content is reduced to 0-20%, taking out the mixture, cooling to 35 ℃, adding 1-30 parts of additive and 1-30 parts of wrapping agent, and uniformly mixing to obtain the finished product.

The invention has the beneficial effects that:

the solid aroma-carrying herbal incense with high smoking quality prepared by the invention has targeted characteristic aroma, strong physiological satisfaction, large smoking amount and good smoking feeling. The natural characteristic of the special plant fiber taste is restored, the richness of the granule smoking taste is increased, the characteristic aroma of the granule taste is enhanced in a targeted mode, the aroma quality and the smoke quantity of the smoke are improved, and the like.

Drawings

Fig. 1 is a preparation flow of the solid aroma-carrying herbal incense matrix with high smoking quality and the preparation method thereof provided by the invention.

Detailed Description

The following further describes the embodiments of the present invention. It should be noted that the description of the embodiments is provided to help understanding of the present invention, but the present invention is not limited thereto. In addition, the technical features involved in the embodiments of the present invention described below may be combined with each other as long as they do not conflict with each other.

Example 1:

100 parts of licorice particles serving as a core material, 10 parts of a solvent, 80 parts of a natural target aroma main body, 9 parts of a natural plant latent aroma agent and 1 part of a sweetener are uniformly mixed to serve as a spice, the spice is loaded on the core material according to a ratio of 1:2, the mulberry powder particles and the inorganic filler particles are uniformly mixed and added after being dried, and finally, 5 parts of antagonists are uniformly mixed and added to prepare the solid aroma-carrying herbal aroma bullet matrix with high suction quality.

Example 2:

80 parts of liquorice particles, 20 parts of freeze-dried pineapple particles, uniformly stirring the mixture to serve as a base material, 30 parts of a solvent, 65 parts of a natural target aroma main body, 4 parts of a natural plant latent aroma, 1 part of a sweetener, uniformly mixing the mixture to serve as an aroma, loading the aroma on a core material according to a ratio of 1:1, uniformly mixing and adding 5 parts of blueberry powder particles and 5 parts of inorganic filler particles after drying, and finally uniformly mixing and adding 10 parts of an antagonist to prepare the solid aroma-carrying herbal aroma bullet matrix with high suction quality.

Example 3:

80 parts of liquorice particles, 20 parts of highland barley stalk particles, uniformly stirring the mixture to serve as a base material, 30 parts of a solvent, 70 parts of a natural target aroma main body, 8 parts of a natural plant latent aroma causing agent and 1 part of a sweetener, uniformly mixing the materials to serve as an aroma, loading the aroma on a core material according to a ratio of 1:1, uniformly mixing and adding 5 parts of rose fine extract powder particles and 5 parts of inorganic filler particles after drying, and finally uniformly mixing and adding 10 parts of an antagonist to prepare the solid aroma-loaded herbal incense matrix with high suction quality.

Example 4:

90 parts of licorice particles, 10 parts of rye straw particles are uniformly stirred to serve as a base material, 30 parts of a solvent, 65 parts of a natural target aroma main body, 8 parts of a natural plant latent aroma causing agent and 1 part of a sweetener are uniformly mixed to serve as an aroma, the aroma is loaded on a core material according to a ratio of 1:1.5, after being baked and dried, 5 parts of blueberry powder particles and 5 parts of inorganic filler particles are uniformly mixed and added, and finally, 5 parts of antagonist is uniformly mixed and added to prepare the solid aroma-carrying herbal aroma bullet matrix with high suction quality.

Claims

1. A high smoking quality solid fragrance-bearing herbal fragrance bullet substrate comprising: the core material module is prepared by simply mixing after microwave expansion; the flavor module comprises 5-90 parts of a mixture of solvents such as glycerol, propylene glycol and 1, 3-butanediol, 10-90 parts of natural target extraction aroma components such as tobacco extract and other plant extracts, 1-60 parts of natural plant latent aroma agents such as terpene compounds and glycolipid compounds, and 0-50 parts of sweeteners such as mogroside and sucralose.

2. A preparation method of a solid fragrant herbal medicine-loaded base material with high smoking quality comprises the steps of mixing and spreading a core material prepared by the method in claim 1 and a spice module in claim 1 in a ratio of 1: 0.5-1: 5 in a baking pan, setting the temperature to be 45-280 ℃, baking for 15 minutes to 4 hours until the water content is reduced to 0% -20%, taking out the core material and the spice module, cooling to 35 ℃, adding 1-30 parts of an additive and 1-30 parts of a wrapping agent, and uniformly mixing to obtain the solid fragrant herbal medicine-loaded base material.

3. The core module of a high-suction quality solid herbal incense matrix according to claim 1, wherein the diameter of the licorice particles in the core module of a high-suction quality solid herbal incense matrix is in the range of 6-40 mesh, and the power of the microwave expansion treatment is 400w-3000 w.

4. The core material module of a high-suction-quality solid herbal-loaded fragrance matrix according to claim 1, wherein the characteristic plant fiber particles in the core material module of a high-suction-quality solid herbal-loaded fragrance matrix according to claim 1 include, but are not limited to, black wheat straw particles, highland barley straw particles, freeze-dried fruit particles such as pineapple particles, and the like.

5. The core material module of the high-suction-quality solid herbal incense matrix-loaded according to claim 1, wherein the characteristic plant fiber particles in the core material module of the high-suction-quality solid herbal incense matrix-loaded according to claim 1 are dried to 0% -20% of moisture and crushed to 20-200 meshes, and then are fully mixed with the licorice particles by 0-100 parts to form the core material.

6. The method of claim 1, wherein the natural target-extracted flavor components of the flavor module of the high-smoking-quality solid herbal-loaded incense base include, but are not limited to, one or any combination of tobacco extract, fruit extract, flower extract, herb extract, and herb extract.

7. The method of claim 1, wherein the natural plant pro-fragrance in the flavor module of the high-smoking-quality solid herbal incense substrate comprises one or more of, but not limited to, 0-5 parts of glycosides, 0-5 parts of sugar esters, 0-5 parts of Amadori, 0-5 parts of terpenes, and 0-5 parts of lipids.

8. The method of making a high-smoking quality solid supported herbal fragrance matrix according to claim 1, wherein the sweetener in the flavor module of the high-smoking quality solid supported herbal fragrance matrix according to claim 1 comprises one or any combination of, but not limited to, 0.00001-1 parts mogroside, 0.00001-1 parts stevioside, 0.1-40 parts licorice root, etc.

9. The preparation method of the solid aroma-carrying herbal fragrance matrix with high smoking quality as claimed in claim 1, wherein the additives in the solid aroma-carrying herbal fragrance matrix with high smoking quality as claimed in claim 1 include, but are not limited to, one or more of flower and fruit type refined extract reconstruction particles such as 0-50 parts of mulberry refined extract reconstruction particles, 0-50 parts of rose refined extract reconstruction particles, 0-50 parts of blueberry refined extract reconstruction particles and the like, which are combined in any proportion, and then combined with 1-99 parts of inorganic filler particles to prepare the additives.

10. The method for preparing the solid herbal incense matrix with high smoking quality as claimed in claim 1, wherein the wrapping agent of the solid herbal incense matrix with high smoking quality as claimed in claim 1 includes but is not limited to one or any combination of solid powder essence, anti-caking agent ferric ammonium citrate, rose solid powder, etc.