CN114478900A - 一种具有抗开裂效果的js防水乳液及其制备方法 - Google Patents
一种具有抗开裂效果的js防水乳液及其制备方法 Download PDFInfo
- Publication number
- CN114478900A CN114478900A CN202210234396.0A CN202210234396A CN114478900A CN 114478900 A CN114478900 A CN 114478900A CN 202210234396 A CN202210234396 A CN 202210234396A CN 114478900 A CN114478900 A CN 114478900A
- Authority
- CN
- China
- Prior art keywords
- parts
- initiator
- acrylate
- emulsion
- sodium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及乳液技术领域，尤其涉及一种具有抗开裂效果的JS防水乳液及其制备方法。本发明所述的具有抗开裂效果的JS防水乳液原料组成为：去离子水500‑600份、乳化剂10‑100份、丙烯酸烷基酯类单体400‑800份、苯乙烯100‑200份、烷基羧酸5‑50份、丙烯酰胺类单体20‑100份、丙烯酸羟基酯类单体单体20‑100份、交联单体10‑50份、水溶性引发剂2‑5份、氧化还原引发剂1‑8份、pH调节剂10‑50份、后添加剂10‑50份、螯合助剂10‑50份。本发明在阴阳角、厚涂应用场景中具有较优异的抗开裂性能，适用于聚合物防水涂料，性能满足国标的要求。
Description
技术领域
本发明涉及乳液技术领域，尤其涉及一种具有抗开裂效果的JS防水乳液及其制备方法。
背景技术
聚合物水泥防水涂料是被广泛使用于建筑物厕浴间、阳台、地下室等区域的柔性防水涂料。由于使用环境中存在阴阳角、链接缝隙、管道等节点部位较多；使得涂膜涂刷厚度、干燥速度的差异而产生不同程度的应力差异，导致涂膜出现开裂情况的发生从而影响防水性能。
因此，如何提供一种具有抗开裂效果的JS防水乳液及其制备方法，使防水乳液能够满足不同使用场景要求，同时保证其具有抗开裂效果是本领域亟待解决的难题。
发明内容
有鉴于此，本发明提供了一种具有抗开裂效果的JS防水乳液及其制备方法，本发明公开的具有抗开裂效果的JS防水乳液能够满足不同使用场景要求，具有优异的抗开裂效果。
为了达到上述目的，本发明采用如下技术方案：
一种具有抗开裂效果的JS防水乳液，包括如下质量份数的原料：乳化剂10-100份、丙烯酸烷基酯类单体400-800份、苯乙烯100-200份、烷基羧酸5-50份、丙烯酰胺类单体20-100份、丙烯酸羟基酯类单体20-100份、交联单体10-50份、水溶性引发剂2-5份、氧化还原引发剂1-8份、pH调节剂10-50份、后添加剂10-50份、螯合助剂10-50份、水500-600份。
优选的，所述乳化剂包括阴离子乳化剂和非离子乳化剂；阴离子乳化剂和非离子乳化剂的质量比为1-4:1；
所述阴离子乳化剂为脂肪醇聚氧乙烯醚磺酸钠、十二烷基硫酸钠、十二烷基磺酸钠、烯丙基脂肪醇聚氧乙烯醚硫酸铵、脂肪醇聚氧乙烯醚磺基琥珀酸半酯二钠盐中的一种或几种；所述非离子乳化剂为烷基酚聚氧乙烯醚，脂肪醇聚氧乙烯醚。
优选的，所述丙烯酸烷基酯类单体为丙烯酸丁酯、丙烯酸-2-乙基己酯、甲基丙烯酸甲酯、丙烯酸乙酯、丙烯酸丙酯、丙烯酸十二烷基酯、丙烯酸十六烷基酯和丙烯酸十八烷基酯中的一种或几种。
优选的，所述烷基羧酸为丙烯酸、甲基丙烯酸、马来酸、马来酸酐、富马酸和富马酸酐中的一种或几种。
优选的，所述丙烯酰胺类单体为丙烯酰胺、甲基丙烯酰胺和N-羟甲基丙烯酰胺中的一种或几种。
优选的，所述丙烯酸羟基酯类单体为丙烯酸-2-羟乙酯、丙烯酸-2羟丙酯和甲基丙烯酸-2-羟乙酯中的一种或几种。
优选的，所述交联单体为甲基丙烯酸缩水甘油酯、乙二醇二甲基丙烯酸酯和三羟甲基丙烷三甲基丙烯酸酯中的一种或几种。
优选的，所述水溶性引发剂为过硫酸钠、过硫酸钾和过硫酸铵中的一种或几种；
所述pH调节剂为氢氧化钠、氢氧化钾、氨水、碳酸钠和碳酸氢钠的一种或几种；
所述氧化还原引发剂为叔丁基过氧化氢-亚硫酸氢钠、叔丁基过氧化氢-亚硫酸钠、叔丁基过氧化氢-亚硫酸氢钠、叔丁基过氧化氢-甲醛合次硫酸氢钠、叔丁基过氧化氢-焦亚硫酸钠和过氧化苯甲酰-焦磷酸亚铁中的一种。
优选的，所述后添加剂为异噻唑啉酮衍生物、苯并米唑酯类、道维希尔-75、1，2-苯并异噻唑啉-3-酮中的一种或几种；
所述的螯合助剂为EDTA、焦磷酸钠、EDTA二钠和腐殖酸钠一种或几种。
本发明的另一目的是提供一种具有抗开裂效果的JS防水乳液的制备方法，包括以下步骤：
1)乳化液的制备：将第一部分水与第一部分乳化剂混合，然后加入丙烯酸烷基酯类单体、苯乙烯、烷基羧酸、丙烯酰胺类单体、丙烯酸羟基酯类单体、交联单体，得到乳化液。
2)反应釜底料准备：取第二部分水加热，然后加入剩余部分的乳化剂，得到反应釜底料；
3)引发剂溶液的制备：将水溶性引发剂分两部分，分别配置成水溶液，记为引发剂A溶液和引发剂B溶液；将氧化还原引发剂配置成水溶液。
4)将1％-5％的乳化液加热升温至80-90℃，加入引发剂A溶液，反应15-30min，引发剂B和乳化液同时滴加，滴加完成之后反应1-1.5h，降温至70-75℃，然后用氧化还原引发剂水溶液进行后处理，降温至50℃，加入pH调节剂、剩余的水、后添加剂和螯合助剂，过滤，得到一种具有抗开裂效果的JS防水乳液。
经由上述的技术方案可知，与现有技术相比，本发明具有如下有益效果：
本发明通过合适的软硬单体搭配、合适的长链单体搭配、合适的亲疏水单体搭配，同时加入含C12-C18的特殊功能单体和交联单体形成高强度的互穿网络结构。本发明公开的乳液用于JS防水涂料中，表面出了优异的拉伸强度及延伸率，较快的干燥速度，涂膜具有良好的的抗开裂效果。
具体实施方式
一种具有抗开裂效果的JS防水乳液，包括如下质量份数的原料：乳化剂10-100份、丙烯酸烷基酯类单体400-800份、苯乙烯100-200份、烷基羧酸5-50份、丙烯酰胺类单体20-100份、丙烯酸羟基酯类单体20-100份、交联单体10-50份、水溶性引发剂2-5份、氧化还原引发剂1-8份、pH调节剂10-50份、后添加剂10-50份、螯合助剂10-50份、水500-600份；优选为乳化剂30-80份、丙烯酸烷基酯类单体500-700份、苯乙烯120-170份、烷基羧酸15-35份、丙烯酰胺类单体40-80份、丙烯酸羟基酯类单体40-80份、交联单体20-40份、水溶性引发剂3-5份、氧化还原引发剂3-7份、pH调节剂20-40份、后添加剂20-40份、螯合助剂20-40份、水520-570份；进一步优选为乳化剂50份、丙烯酸烷基酯类单体600份、苯乙烯150份、烷基羧酸25份、丙烯酰胺类单体60份、丙烯酸羟基酯类单体60份、交联单体30份、水溶性引发剂4份、氧化还原引发剂5份、pH调节剂30份、后添加剂35份、螯合助剂30份、水560份。
在本发明中，所述乳化剂包括阴离子乳化剂和非离子乳化剂；阴离子乳化剂和非离子乳化剂的质量比为1-4:1，优选为3:1。
在本发明中，所述阴离子乳化剂为脂肪醇聚氧乙烯醚磺酸钠、十二烷基硫酸钠、十二烷基磺酸钠、烯丙基脂肪醇聚氧乙烯醚硫酸铵、脂肪醇聚氧乙烯醚磺基琥珀酸半酯二钠盐中的一种或几种；所述非离子乳化剂为烷基酚聚氧乙烯醚，脂肪醇聚氧乙烯醚。
在本发明中，所述丙烯酸烷基酯类单体为丙烯酸丁酯、丙烯酸-2-乙基己酯、甲基丙烯酸甲酯、丙烯酸乙酯、丙烯酸丙酯、丙烯酸十二烷基酯、丙烯酸十六烷基酯和丙烯酸十八烷基酯中的一种或几种。
在本发明中，所述烷基羧酸为丙烯酸、甲基丙烯酸、马来酸、马来酸酐、富马酸和富马酸酐中的一种或几种。
在本发明中，所述丙烯酰胺类单体为丙烯酰胺、甲基丙烯酰胺和N-羟甲基丙烯酰胺中的一种或几种。
在本发明中，所述丙烯酸羟基酯类单体为丙烯酸-2-羟乙酯、丙烯酸-2羟丙酯和甲基丙烯酸-2-羟乙酯中的一种或几种。
在本发明中，所述交联单体为甲基丙烯酸缩水甘油酯、乙二醇二甲基丙烯酸酯和三羟甲基丙烷三甲基丙烯酸酯中的一种或几种。
在本发明中，所述水溶性引发剂为过硫酸钠、过硫酸钾和过硫酸铵中的一种或几种。
在本发明中，所述pH调节剂为氢氧化钠、氢氧化钾、氨水、碳酸钠和碳酸氢钠的一种或几种。
在本发明中，所述氧化还原引发剂为叔丁基过氧化氢-亚硫酸氢钠、叔丁基过氧化氢-亚硫酸钠、叔丁基过氧化氢-亚硫酸氢钠、叔丁基过氧化氢-甲醛合次硫酸氢钠、叔丁基过氧化氢-焦亚硫酸钠和过氧化苯甲酰-焦磷酸亚铁中的一种。
在本发明中，所述后添加剂为异噻唑啉酮衍生物、苯并米唑酯类、道维希尔-75、1，2-苯并异噻唑啉-3-酮中的一种或几种。
在本发明中，所述的螯合助剂为EDTA、焦磷酸钠、EDTA二钠和腐殖酸钠一种或几种。
本发明的另一目的是提供一种具有抗开裂效果的JS防水乳液的制备方法，包括以下步骤：
1)乳化液的制备：将第一部分水与第一部分乳化剂混合，然后加入丙烯酸烷基酯类单体、苯乙烯、烷基羧酸、丙烯酰胺类单体、丙烯酸羟基酯类单体、交联单体，得到乳化液。
2)反应釜底料准备：取第二部分水加热，然后加入剩余部分的乳化剂，得到反应釜底料；
3)引发剂溶液的制备：将水溶性引发剂分两部分，分别配置成水溶液，记为引发剂A溶液和引发剂B溶液；将氧化还原引发剂配置成水溶液。
4)将1％-5％的乳化液加热升温至80-90℃，加入引发剂A溶液，反应15-30min，引发剂B和乳化液同时滴加，滴加速度为2.3-5.8份/min，滴加完成之后反应1-1.5h，降温至70-75℃，然后用氧化还原引发剂水溶液进行后处理，降温至50℃，加入pH调节剂、剩余的水、后添加剂和螯合助剂，过滤，得到一种具有抗开裂效果的JS防水乳液。
在本发明中，第一部分水与第二部分水的质量比为3～5：2～3，优选为4:3；pH调节剂、剩余的水与pH调节剂混合后pH调节剂溶液的质量分数为4～7％，优选为5％。
在本发明中，第一部分乳化剂与剩余部分乳化剂的质量比为90～97:3～10，优选为95:5。
在本发明中，所述步骤1)中加入第一部分乳化剂后混合时间为15～30min，优选为25min；将各类单体加入后混合时间为15～30min，优选为25min。
在本发明中，所述步骤2)中加热温度为80～90℃，优选为85℃。
在本发明中，所述引发剂A溶液和引发剂B溶液中引发剂的质量比为3-7：3-7，优选为5:5；所述引发剂A溶液的质量浓度为4-8％，所述引发剂B溶液的质量浓度为8-13％。
在本发明中，所述氧化还原引发剂水溶液的质量浓度为2-4％，优选为3％。
下面将对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例1
具有抗开裂效果的JS防水乳液由以下重量份的原料组成：去离子水550份；乳化剂30份，其中阴离子乳化剂与非离子乳化剂重量份数比为1.5:1阴离子乳化剂为烯丙基脂肪醇聚氧乙烯醚硫酸钠，非离子乳化剂为脂肪醇聚氧乙烯醚；丙烯酸丁酯150份，丙烯酸十二烷基酯30份，丙烯酸-2-乙基己酯420份；苯乙烯160份；丙烯酸10份；甲基丙烯酰胺45份；丙烯酸羟乙酯25份；甲基丙烯酸缩水甘油酯30份；过硫酸钠4份；叔丁基过氧化氢-亚硫酸钠3份；氢氧化钠15份；异噻唑啉酮衍生物25份；焦磷酸钠35份。
制备步骤如下：
乳化液的制备：乳化缸中加入95％乳化剂、去离子水(第一部分与第二部分总和的4/7)，分散15分钟后，加入丙烯酸丁酯、丙烯酸十二烷基酯、丙烯酸-2-乙基己酯、苯乙烯、丙烯酸、丙烯酰胺类单体、丙烯酸羟乙酯和甲基丙烯酸缩水甘油酯，搅拌15分钟后，即得乳化液。
反应釜底液的制备：往反应釜中加入去离子水(第一部分与第二部分总和的3/7)，加热至85℃，加入5％的乳化剂，得到反应釜底液。
引发剂溶液的制备：水溶性引发剂等分为两部分：引发剂A和引发剂B，分别用去离子水溶解成质量浓度为5％和10％的引发剂A溶液和引发剂B溶液，备用；氧化还原引发剂均配置为质量浓度为3％的去离子水溶液。
将反应釜内温度升高至85℃，加入3.5％的乳化液，引发剂A，反应15分钟后，滴加剩余的乳化液和引发剂B，滴加速度为2.3-5.8份/min，完成后将釜内温度提高至87℃，保温60分钟，降温至75℃，然后用氧化还原引发剂水溶液进行后处理，时间控制在45分钟，后处理完后降温至50℃，加入pH调节剂和剩余的水(相当于质量浓度为8％)，加入后体系pH为7.5，再加入异噻唑啉酮衍生物，焦磷酸钠，过滤出料，得到具有抗开裂效果的JS防水乳液。
实施例2
具有抗开裂效果的JS防水乳液由以下重量份的原料组成：去离子水600份；乳化剂100份，其中阴离子乳化剂与非离子乳化剂重量份数比为1:1阴离子乳化剂为烯丙基脂肪醇聚氧乙烯醚硫酸钠，非离子乳化剂为脂肪醇聚氧乙烯醚；丙烯酸乙酯300份，丙烯酸十二烷基酯80份，丙烯酸-2-乙基己酯420份；苯乙烯200份；甲基丙烯酸50份；N-羟甲基丙烯酰胺100份；丙烯酸羟乙酯100份；甲基丙烯酸缩水甘油酯50份；过硫酸钾5份；叔丁基过氧化氢-焦亚硫酸钠8份；氢氧化钠50份；异噻唑啉酮衍生物50份；焦磷酸钠50份。
制备步骤如下：
乳化液的制备：乳化缸中加入90％乳化剂、去离子水(第一部分与第二部分总和的5/7)，分散30分钟后，加入丙烯酸丁酯、丙烯酸十二烷基酯、丙烯酸-2-乙基己酯、苯乙烯、丙烯酸、丙烯酰胺类单体、丙烯酸羟乙酯和甲基丙烯酸缩水甘油酯，搅拌30分钟后，即得乳化液。
反应釜底液的制备：往反应釜中加入去离子水(第一部分与第二部分总和的2/7)，加热至90℃，加入10％的乳化剂，得到反应釜底液。
引发剂溶液的制备：水溶性引发剂分两部分：引发剂A和引发剂B，分别用去离子水溶解成质量浓度为4％和8％的引发剂A溶液和引发剂B溶液，备用；氧化还原引发剂均配置为质量浓度为2％的去离子水溶液。
将反应釜内温度升高至80℃，加入5％的乳化液，引发剂A，反应25分钟后，滴加剩余的乳化液和引发剂B，滴加速度为2.3-5.8份/min，完成后将釜内温度提高至85℃，保温80分钟，降温至70℃，然后用氧化还原引发剂水溶液进行后处理，时间控制在60分钟，后处理完后降温至50℃，加入pH调节剂和剩余的水(相当于质量浓度为5％)，加入后体系pH为7.2，再加入异噻唑啉酮衍生物，焦磷酸钠，过滤出料，得到具有抗开裂效果的JS防水乳液。
实施例3
具有抗开裂效果的JS防水乳液由以下重量份的原料组成：去离子水500份；乳化剂10份，其中阴离子乳化剂与非离子乳化剂重量份数比为4:1阴离子乳化剂为烯丙基脂肪醇聚氧乙烯醚硫酸钠，非离子乳化剂为脂肪醇聚氧乙烯醚；丙烯酸丁酯400份；苯乙烯100份；丙烯酸5份；丙烯酰胺类单体20份；丙烯酸羟乙酯20份；甲基丙烯酸缩水甘油酯10份；过硫酸钠2份；叔丁基过氧化氢-亚硫酸钠1份；氢氧化钠10份；异噻唑啉酮衍生物10份；焦磷酸钠10份。
制备步骤如下：
乳化液的制备：乳化缸中加入97％乳化剂、去离子水(第一部分与第二部分总和的3/5)，分散25分钟后，加入丙烯酸丁酯、丙烯酸十二烷基酯、丙烯酸-2-乙基己酯、苯乙烯、丙烯酸、丙烯酰胺类单体、丙烯酸羟乙酯和甲基丙烯酸缩水甘油酯，搅拌25分钟后，即得乳化液。
反应釜底液的制备：往反应釜中加入去离子水((第一部分与第二部分总和的2/5))，加热至80℃，加入3％的乳化剂，得到反应釜底液。
引发剂溶液的制备：水溶性引发剂分两部分：引发剂A和引发剂B，分别用去离子水溶解成质量浓度为8％和13％的引发剂A溶液和引发剂B溶液，备用；氧化还原引发剂均配置为质量浓度为4％的去离子水溶液。
将反应釜内温度升高至90℃，加入1％的乳化液，引发剂A，反应30分钟后，滴加剩余的乳化液和引发剂B，滴加速度为2.3-5.8份/min，完成后将釜内温度调节至87℃，保温90分钟，降温至75℃，然后用氧化还原引发剂水溶液进行后处理，时间控制在45分钟，后处理完后降温至50℃，加入pH调节剂和剩余的水(相当于质量浓度为10％)，pH为7.8，再加入异噻唑啉酮衍生物，焦磷酸钠，过滤出料，得到具有抗开裂效果的JS防水乳液。
实施例1
分别采用实施例1-3中的具有抗开裂效果的JS防水乳液进一步制备水泥基聚合物防水涂料，其制备方法如下：
| 物料名称 | 用量 |
| 具有抗开裂效果的JS防水乳液 | 90-95份 |
| 水 | 3-4份 |
| 消泡剂、增稠剂 | 1份 |
| 水泥 | 60-80份 |
| 砂子 | 40-60份 |
| 重钙 | 40-60份 |
按表格的涂料配方中液料和粉料质量范围称量好后，用分散机在400-800r/min转速下将液料和粉料搅拌3-5min后取下，即可得到制备水泥基聚合物防水涂料。
按照国家标准GB/T 23445-2009《聚合物水泥防水涂料》中的检测方法检测其性能。
表1各实施例和对比例得到各项性能测试结果
按照裂缝的宽度和外观表现，降分裂分为5个等级：1级--涂膜无变化；2级--涂膜有颜色变化但无裂纹；3级--裂纹宽度在0.5mm以下；4级--裂纹宽度在0.5mm-1.0mm；5级--裂纹宽度在1mm以上。
由表1可以看出，本发明具有抗开裂效果的JS防水乳液，应用于JS涂料具有较高的拉伸强度和延伸率，具有较快的涂膜干燥速度且抗开裂效果性能较优。
本说明书中各个实施例采用递进的方式描述，每个实施例重点说明的都是与其他实施例的不同之处，各个实施例之间相同相似部分互相参见即可。
对所公开的实施例的上述说明，使本领域专业技术人员能够实现或使用本发明。对这些实施例的多种修改对本领域的专业技术人员来说将是显而易见的，本文中所定义的一般原理可以在不脱离本发明的精神或范围的情况下，在其它实施例中实现。因此，本发明将不会被限制于本文所示的这些实施例，而是要符合与本文所公开的原理和新颖特点相一致的最宽的范围。
Claims (10)
1.一种具有抗开裂效果的JS防水乳液，其特征在于，包括如下质量份数的原料：乳化剂10-100份、丙烯酸烷基酯类单体400-800份、苯乙烯100-200份、烷基羧酸5-50份、丙烯酰胺类单体20-100份、丙烯酸羟基酯类单体20-100份、交联单体10-50份、水溶性引发剂2-5份、氧化还原引发剂1-8份、pH调节剂10-50份、后添加剂10-50份、螯合助剂10-50份、水500-600份。
2.根据权利要求1所述的一种具有抗开裂效果的JS防水乳液，其特征在于，所述乳化剂包括阴离子乳化剂和非离子乳化剂；阴离子乳化剂和非离子乳化剂的质量比为1-4:1；
所述阴离子乳化剂为脂肪醇聚氧乙烯醚磺酸钠、十二烷基硫酸钠、十二烷基磺酸钠、烯丙基脂肪醇聚氧乙烯醚硫酸铵、脂肪醇聚氧乙烯醚磺基琥珀酸半酯二钠盐中的一种或几种；所述非离子乳化剂为烷基酚聚氧乙烯醚，脂肪醇聚氧乙烯醚。
3.根据权利要求1所述的一种具有抗开裂效果的JS防水乳液，其特征在于，所述丙烯酸烷基酯类单体为丙烯酸丁酯、丙烯酸-2-乙基己酯、甲基丙烯酸甲酯、丙烯酸乙酯、丙烯酸丙酯、丙烯酸十二烷基酯、丙烯酸十六烷基酯和丙烯酸十八烷基酯中的一种或几种。
4.根据权利要求1所述的一种具有抗开裂效果的JS防水乳液，其特征在于，所述烷基羧酸为丙烯酸、甲基丙烯酸、马来酸、马来酸酐、富马酸和富马酸酐中的一种或几种。
5.根据权利要求1所述的一种具有抗开裂效果的JS防水乳液，其特征在于，所述丙烯酰胺类单体为丙烯酰胺、甲基丙烯酰胺和N-羟甲基丙烯酰胺中的一种或几种。
6.根据权利要求1所述的一种具有抗开裂效果的JS防水乳液，其特征在于，所述丙烯酸羟基酯类单体为丙烯酸-2-羟乙酯、丙烯酸-2羟丙酯和甲基丙烯酸-2-羟乙酯中的一种或几种。
7.根据权利要求1所述的一种具有抗开裂效果的JS防水乳液，其特征在于，所述交联单体为甲基丙烯酸缩水甘油酯、乙二醇二甲基丙烯酸酯和三羟甲基丙烷三甲基丙烯酸酯中的一种或几种。
8.根据权利要求1所述的一种具有抗开裂效果的JS防水乳液，其特征在于，所述水溶性引发剂为过硫酸钠、过硫酸钾和过硫酸铵中的一种或几种；
所述pH调节剂为氢氧化钠、氢氧化钾、氨水、碳酸钠和碳酸氢钠的一种或几种；
所述氧化还原引发剂为叔丁基过氧化氢-亚硫酸氢钠、叔丁基过氧化氢-亚硫酸钠、叔丁基过氧化氢-亚硫酸氢钠、叔丁基过氧化氢-甲醛合次硫酸氢钠、叔丁基过氧化氢-焦亚硫酸钠和过氧化苯甲酰-焦磷酸亚铁中的一种。
9.根据权利要求1所述的一种具有抗开裂效果的JS防水乳液，其特征在于，所述后添加剂为异噻唑啉酮衍生物、苯并米唑酯类、道维希尔-75、1，2-苯并异噻唑啉-3-酮中的一种或几种；
所述的螯合助剂为EDTA、焦磷酸钠、EDTA二钠和腐殖酸钠一种或几种。
10.根据权利要求1-9任一项所述的一种具有抗开裂效果的JS防水乳液的制备方法，其特征在于，包括以下步骤：
1)乳化液的制备：将第一部分水与第一部分乳化剂混合，然后加入丙烯酸烷基酯类单体、苯乙烯、烷基羧酸、丙烯酰胺类单体、丙烯酸羟基酯类单体、交联单体，得到乳化液。
2)反应釜底料准备：取第二部分水加热，然后加入剩余部分的乳化剂，得到反应釜底料；
3)引发剂溶液的制备：将水溶性引发剂分两部分，分别配置成水溶液，记为引发剂A溶液和引发剂B溶液；将氧化还原引发剂配置成水溶液。
4)将1％-5％的乳化液加热升温至80-90℃，加入引发剂A溶液，反应15-30min，引发剂B和乳化液同时滴加，滴加完成之后反应1-1.5h，降温至70-75℃，然后用氧化还原引发剂水溶液进行后处理，降温至50℃，加入pH调节剂、剩余的水、后添加剂和螯合助剂，过滤，得到一种具有抗开裂效果的JS防水乳液。