CN114456668A - 一种水性高光面漆及其制备方法 - Google Patents
一种水性高光面漆及其制备方法 Download PDFInfo
- Publication number
- CN114456668A CN114456668A CN202210213069.7A CN202210213069A CN114456668A CN 114456668 A CN114456668 A CN 114456668A CN 202210213069 A CN202210213069 A CN 202210213069A CN 114456668 A CN114456668 A CN 114456668A
- Authority
- CN
- China
- Prior art keywords
- water
- monomer
- unsaturated monomer
- finish paint
- acrylic emulsion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种水性高光面漆及其制备方法，高光面漆由水性阳离子羟基丙烯酸乳液A、水性阳离子羟基丙烯酸乳液B、消泡剂、流平剂、润湿剂、水、光引发剂、增稠剂组成；所述水性阳离子羟基丙烯酸乳液A由疏水性不饱和单体、丙烯酸酯单体、含羟基不饱和单体、含羧基不饱和单体制备而成，所述含羟基不饱和单体的摩尔占比为3‑10％；所述含羟基不饱和单体的摩尔占比为0.1‑2％；所述水性阳离子羟基丙烯酸乳液B由疏水性不饱和单体、丙烯酸酯单体、含羟基不饱和单体、含羧基不饱和单体制备而成，所述含羟基不饱和单体的摩尔占比为0.1‑2％；所述含羟基不饱和单体的摩尔占比为3‑10％。得到的面漆能达到接近镜面的效果，在漆面形成的倒影不会出现弯折。
Description
技术领域
本发明涉及一种水性高光面漆及其制备方法。
背景技术
与传统的溶剂型涂料相比，水性涂料具有价格低、使用安全，节省资源和能源，减少环境污染和公害等优点，因而已成为当前涂料工业发展的主要方向之一。中国专利申请CN201510455083.8《一种丙烯酸乳液涂层》，公开了一种丙烯酸乳液涂层，其特征在于，包括以下组分：甲基丙烯酸甲酯25-35份、丙烯酸丁酯10-17份、甲基丙烯酸3-7份、乙酰乙酸基甲基丙烯酸乙酯4-9份、改性蒙脱土3-6份、乳化剂3-7份、合成剂1-2份，固化剂1-4份，去离子水30-35份。该发明的涂层能够涂于塑料包装外部，具有良好的隔离水汽、气味、空气等效果，有效防止食品等氧化。
中国专利申请CN201510257097.9《纺织品用拒水、拒油、耐晒、抗扭曲弯挠、耐寒、无光皮膜水性涂层胶及制备方法》，公开了织品用拒水、拒油、耐晒、抗扭曲弯挠、耐寒、无光皮膜水性涂层胶，其原料重量配比丙烯酸异辛酯70-80、甲基丙烯酸异冰片酯20-30、甲基丙烯酸缩水甘油酯2-4、甲基丙烯酸三氟乙酯10-15、乙烯基三甲氧基硅烷5-8、丙烯酸羟丙酯1.5-2、脂肪醇聚氧乙烯醚XL90为2-5，十二烷基苯磺酸钠0.5-0.8，过硫酸铵0.3-0.8，去离子水110-176经乳化、引发聚合，再复配增稠剂缔合型聚氨酯流平流变剂3-5，交联剂封端异氰酸酯2-3，消光剂聚甲基脲树脂10-15、消光剂粒径2-7μm的二氧化硅10-15，制成。
水性羟基聚丙烯酸酯虽然污染比传统溶剂型羟基丙烯酸树脂大大降低，但是一般的羟基丙烯酸乳液，制漆后其光泽较低，丰满度不理想，并由于水作溶剂原因，干燥速度较慢，性能满足不了人们需求。因此，开发一种高环保性与性能优越的羟基丙烯酸树脂是一种涂料发展工业一种趋势。
发明内容
本发明的目的是为解决现有技术的不足，提供了一种水性高光面漆，所述高光面漆由水性阳离子羟基丙烯酸乳液A、水性阳离子羟基丙烯酸乳液B、消泡剂、流平剂、润湿剂、水、光引发剂、增稠剂组成；
所述水性阳离子羟基丙烯酸乳液A由疏水性不饱和单体、丙烯酸酯单体、含羟基不饱和单体、含羧基不饱和单体制备而成，所述含羟基不饱和单体的摩尔占比为3-10％；所述含羟基不饱和单体的摩尔占比为0.1-2％；
所述水性阳离子羟基丙烯酸乳液B由疏水性不饱和单体、丙烯酸酯单体、含羟基不饱和单体、含羧基不饱和单体制备而成，所述含羟基不饱和单体的摩尔占比为0.1-2％；所述含羟基不饱和单体的摩尔占比为3-10％。
所述水性阳离子羟基丙烯酸乳液A与所述水性阳离子羟基丙烯酸乳液B的质量比为1：0.7-1.5。
所述疏水性不饱和单体选自苯乙烯单体、对甲基苯乙烯单体、甲基丙烯酸异冰片酯单体中的一种或几种。
所述丙烯酸酯单体选自丙烯酸甲酯单体、甲基丙烯酸甲酯单体、甲基丙烯酸乙酯单体、丙烯酸乙酯单体中的一种或几种。
所述含羟基不饱和单体选自丙烯酸羟乙酯、甲基丙烯酸羟乙酯、丙烯酸羟丙酯中的一种或几种。
所述含羧基不饱和单体选自丙烯酸、甲基丙烯酸、马来酸、富马酸中的一种或几种。
所述消泡剂为有机硅氧烷类消泡剂。
所述流平剂为丙烯酸酯类流平剂或聚硅氧烷类流平剂
所述润湿剂为有机硅聚醚共聚物、非离子表面活性剂、阴离子表面活性剂中的一种或多种。
所述增稠剂为聚醚类增稠剂或聚氨酯类增稠剂。
水性阳离子羟基丙烯酸乳液A、水性阳离子羟基丙烯酸乳液B的制备方法如下：
将溶剂、疏水性不饱和单体加入反应器中并加热至140℃；
滴加第一单体混合物后，继续反应1小时，所述第一单体混合物包括：甲基丙烯酸单体、含羟基不饱和单体及引发剂；
滴加第二单体混合物后，继续反应1小时，所述第二单体混合物包括：甲基丙烯酸单体、含羧基不饱和单体及引发剂；
然后加入中和剂后继续加入水进行分散，得到羟基丙烯酸分散体产品。
由于光固化过程中，水性丙烯酸分散体成膜后，利用体系中存在的少量的羟基和羧基，大大减少了成膜后膜内的水的含量，从而减少了因为干燥不彻底导致的光泽度下降的问题。得到的面漆能达到接近镜面的效果，在漆面形成的倒影不会出现弯折。
参考以下详细说明更易于理解本申请的上述以及其他特征、方面和优点。
附图说明
通过阅读参照以下附图对非限制性实施例所作的详细描述，本发明的其它特征、目的和优点将会变得更明显：
图1为漆面的反射的效果照片。
图2为漆面光泽度的效果照片。
具体实施方式
为使本发明实施例的目的、技术方案和优点更加清楚，下面将结合本发明实施例的附图，对本发明实施例的技术方案进行清楚、完整地描述。显然，所描述的实施例是本发明的一部分实施例，而不是全部的实施例。基于所描述的本发明的实施例，本领域普通技术人员在无需创造性劳动的前提下所获得的所有其它实施例，都属于本发明保护的范围。
除非另作定义，此处使用的技术术语或者科学术语应当为本发明所属领域内具有一般技能的人士所理解的通常意义。本发明专利申请说明书以及权利要求书中使用的“第一”、“第二”以及类似的词语并不表示任何顺序、数量或者重要性，而只是用来区分不同的组成部分。同样，“一个”或者“一”等类似词语也不表示数量限制，而是表示存在至少一个。
实施例1：
水性阳离子羟基丙烯酸乳液A
将20g溶剂、0.5mol对甲基苯乙烯单体加入反应器中并加热至140℃；
滴加第一单体混合物滴加完成时间4小时后，继续反应1小时，第一单体混合物：2mol甲基丙烯酸甲酯、0.3mol甲基丙烯酸羟乙酯及10g DTBP；
滴加第二单体混合物滴加完成时间4小时后，继续反应1小时，第二单体混合物：2mol丙烯酸甲酯、0.04mol丙烯酸及2.5g DTBP；
然后加入中和剂后继续加入500g水，得到羟基丙烯酸分散体产品。
水性阳离子羟基丙烯酸乳液B
将20g溶剂、0.5mol甲基丙烯酸异冰片酯加入反应器中并加热至140℃；
滴加第一单体混合物滴加完成时间4小时后，继续反应1小时，第一单体混合物：2mol甲基丙烯酸甲酯、0.04mol甲基丙烯酸羟乙酯及10g DTBP；
滴加第二单体混合物滴加完成时间4小时后，继续反应1小时，第二单体混合物：2mol丙烯酸甲酯、0.3mol丙烯酸及2.5g DTBP；
然后加入中和剂后继续加入500g水，得到羟基丙烯酸分散体产品。
高光面漆由100重量份的水性阳离子羟基丙烯酸乳液A、100重量份的水性阳离子羟基丙烯酸乳液B、2重量份的消泡剂、2重量份的流平剂、1重量份的润湿剂、50重量份的水、2重量份的光引发剂、5重量份的消泡剂增稠剂组成。将面漆喷涂在木地板表面，带漆面表干后进行UV固化成膜，成膜后的如图1的左图。
而不加入水性阳离子羟基丙烯酸乳液B对比图为图1的右图，可以明显看出，右图漆面倒影存在曲折。
实施例2
水性阳离子羟基丙烯酸乳液A
将20g溶剂、0.5mol甲基丙烯酸异冰片酯加入反应器中并加热至140℃；
滴加第一单体混合物滴加完成时间4小时后，继续反应1小时，第一单体混合物：2mol甲基丙烯酸甲酯、0.2mol甲基丙烯酸羟乙酯及10g DTBP；
滴加第二单体混合物滴加完成时间4小时后，继续反应1小时，第二单体混合物：2mol丙烯酸甲酯、0.05mol丙烯酸及2.5g DTBP；
然后加入中和剂后继续加入500g水，得到羟基丙烯酸分散体产品。
水性阳离子羟基丙烯酸乳液B
将20g溶剂、0.5mol甲基丙烯酸异冰片酯加入反应器中并加热至140℃；
滴加第一单体混合物滴加完成时间4小时后，继续反应1小时，第一单体混合物：2mol甲基丙烯酸甲酯、0.05mol甲基丙烯酸羟乙酯及10g DTBP；
滴加第二单体混合物滴加完成时间4小时后，继续反应1小时，第二单体混合物：2mol丙烯酸甲酯、0.2mol丙烯酸及2.5g DTBP；
然后加入中和剂后继续加入500g水，得到羟基丙烯酸分散体产品。
高光面漆由100重量份的水性阳离子羟基丙烯酸乳液A、100重量份的水性阳离子羟基丙烯酸乳液B、2重量份的消泡剂、2重量份的流平剂、1重量份的润湿剂、50重量份的水、2重量份的光引发剂、5重量份的消泡剂增稠剂组成。将面漆喷涂在木地板表面，带漆面表干后进行UV固化成膜，成膜后的如图2的左图。而不加入水性阳离子羟基丙烯酸乳液B对比图为图2的右图。可以看出，加入了水性阳离子羟基丙烯酸乳液B的漆面光泽度更好。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点,对于本领域技术人员而言，显然本发明不限于上述示范性实施例的细节，而且在不背离本发明的精神或基本特征的情况下，能够以其他的具体形式实现本发明。因此，无论从哪一点来看，均应将实施例看作是示范性的，而且是非限制性的，本发明的范围由所附权利要求而不是上述说明限定，因此旨在将落在权利要求的等同要件的含义和范围内的所有变化囊括在本发明内。不应将权利要求中的任何附图标记视为限制所涉及的权利要求。
此外，应当理解，虽然本说明书按照实施方式加以描述，但并非每个实施方式仅包含一个独立的技术方案，说明书的这中叙述方式仅仅是为清楚起见，本领域技术人员应当将说明书作为一个整体，各实施例中的技术方案也可以经适当组合，形成本领域技术人员可以理解的其他实施方式。
Claims (10)
1.一种水性高光面漆，其特征在于，所述高光面漆由水性阳离子羟基丙烯酸乳液A、水性阳离子羟基丙烯酸乳液B、消泡剂、流平剂、润湿剂、水、光引发剂、增稠剂组成；
所述水性阳离子羟基丙烯酸乳液A由疏水性不饱和单体、丙烯酸酯单体、含羟基不饱和单体、含羧基不饱和单体制备而成，所述含羟基不饱和单体的摩尔占比为3-10％；所述含羟基不饱和单体的摩尔占比为0.1-2％；
所述水性阳离子羟基丙烯酸乳液B由疏水性不饱和单体、丙烯酸酯单体、含羟基不饱和单体、含羧基不饱和单体制备而成，所述含羟基不饱和单体的摩尔占比为0.1-2％；所述含羟基不饱和单体的摩尔占比为3-10％。
2.根据权利要求1所述的一种水性高光面漆，其特征在于，所述水性阳离子羟基丙烯酸乳液A与所述水性阳离子羟基丙烯酸乳液B的质量比为1：0.7-1.5。
3.根据权利要求1所述的一种水性高光面漆，其特征在于，所述疏水性不饱和单体选自苯乙烯单体、对甲基苯乙烯单体、甲基丙烯酸异冰片酯单体中的一种或几种。
4.根据权利要求1所述的一种水性高光面漆，其特征在于，所述丙烯酸酯单体选自丙烯酸甲酯单体、甲基丙烯酸甲酯单体、甲基丙烯酸乙酯单体、丙烯酸乙酯单体中的一种或几种。
5.根据权利要求1所述的一种水性高光面漆，其特征在于，所述含羟基不饱和单体选自丙烯酸羟乙酯、甲基丙烯酸羟乙酯、丙烯酸羟丙酯中的一种或几种。
6.根据权利要求1所述的一种水性高光面漆，其特征在于，所述含羧基不饱和单体选自丙烯酸、甲基丙烯酸、马来酸、富马酸中的一种或几种。
7.根据权利要求1所述的一种水性高光面漆，其特征在于，所述消泡剂为有机硅氧烷类消泡剂。
8.根据权利要求1所述的一种水性高光面漆，其特征在于，所述流平剂为丙烯酸酯类流平剂或聚硅氧烷类流平剂。
9.根据权利要求1所述的一种水性高光面漆，其特征在于，所述润湿剂为有机硅聚醚共聚物、非离子表面活性剂、阴离子表面活性剂中的一种或多种,所述增稠剂为聚醚类增稠剂或聚氨酯类增稠剂。
10.根据权利要求1所述的一种水性高光面漆，其特征在于，水性阳离子羟基丙烯酸乳液A、水性阳离子羟基丙烯酸乳液B的制备方法如下：
将溶剂、疏水性不饱和单体加入反应器中并加热至140℃；
滴加第一单体混合物后，继续反应1小时，所述第一单体混合物包括：甲基丙烯酸单体、含羟基不饱和单体及引发剂；
滴加第二单体混合物后，继续反应1小时，所述第二单体混合物包括：甲基丙烯酸单体、含羧基不饱和单体及引发剂；
然后加入中和剂后继续加入水进行分散，得到羟基丙烯酸分散体产品。