CN114410165A - Difficult-to-fall colored decorative paint - Google Patents
Difficult-to-fall colored decorative paint Download PDFInfo
- Publication number
- CN114410165A CN114410165A CN202210240201.3A CN202210240201A CN114410165A CN 114410165 A CN114410165 A CN 114410165A CN 202210240201 A CN202210240201 A CN 202210240201A CN 114410165 A CN114410165 A CN 114410165A
- Authority
- CN
- China
- Prior art keywords
- paint
- primer
- parts
- decorative paint
- brushing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a color decorative paint difficult to fall off, and relates to the field of architectural paints. The difficult-to-fall colored decorative paint comprises a primer, a decorative paint and a protective paint, and the spraying step comprises the following steps: performing surface treatment on the wall surface to be sprayed, smearing putty, leveling the putty, waiting for drying, and preparing a primer and a brushing tool; after the putty is dried, the primer is brushed on the wall surface by using a brushing tool, the brushing thickness is 2-3.5mm, and when 30-50min is up to the primer is completely dried, the decorative paint is prepared at the same time, so that the ground color decorative paint and the color decorative paint are formed. According to the invention, by means of compounding the primer, the decorative paint and the protective paint, the primer is utilized to improve the alkali-resistant and waterproof capabilities of the inner layer and the adhesiveness of the inner layer, and simultaneously, a compact high-transparency paint film is formed through the polyester crosslinking reaction of the protective paint, so that the acid-base resistance and the scrubbing resistance of the outer paint surface are improved under the condition of ensuring the color of the decorative paint, the service life of the paint surface is effectively prolonged, and the practicability of the paint is enhanced.
Description
Technical Field
The invention relates to the technical field of architectural paints, in particular to a color decorative paint difficult to fall off.
Background
The decorative paint is a kind of chemical mixture paint capable of covering the surface of object firmly and serving as protection, decoration, sign and other special purposes. The book of coating technology which is relatively authoritative in the Chinese coating world is defined as follows: the paint is a material which can be coated on the surface of an object by different construction processes to form a continuous solid film with firm adhesion and certain strength. The film thus formed is generally called a coating film, also called a paint film or a coating. The paint is composed of film forming matter, filler (pigment and filler), solvent and assistant. The components can be slightly changed according to the performance requirements, for example, the varnish has no pigment and filler, the powder coating can have no solvent, the paint belongs to an organic chemical high polymer material, and the formed coating film belongs to a high polymer compound type. According to the modern popular classification of chemical products, the coating belongs to fine chemical products. Modern coatings are gradually becoming a multifunctional engineering material, an important industry in the chemical industry. At present, the exterior wall of domestic buildings and the indoor wall and floor decoration paint are mostly prepared from acrylic emulsion paint, and the color of the acrylic emulsion paint is prepared by adding chemical dye. Art paints are the main landscape in decorative design: the courtyard, the vestibule, the TV wall, the corridor post, the bar counter, furred ceiling can produce extremely elegant effect, and its moderate price accords with the demand of each stratum decoration and fitment completely again: hotels, clubs, dance halls, night clubs, resorts, and luxury villas, apartments, and houses may be used for interior wall decoration. More and more consumers choose to decorate the wall surface with the art paint, and the key reason is that people gradually abandon the fussy mood of hard filling and over-expression of wealth of the five-color decorative material, and change the mood to the funny natural and simple style, the rural wind and light low-carbon art paint advocates the development concept of green, environmental protection and art, and natural wheat straws and raw bamboo fibers are introduced into the paint for manufacturing by utilizing plant materials for painting. Therefore, the method has to reflect distinctive individual characteristics and show unique artistic style and charm while conforming to the characteristics of the times.
Although the existing color decorative paint meets the requirements of people on decoration, when in actual use, the paint surface is easily influenced by the environment, the conditions of paint surface fading, falling off and the like are caused, the aesthetic property of a building is seriously influenced, and a certain improvement space is provided.
Disclosure of Invention
Technical problem to be solved
Aiming at the defects of the prior art, the invention provides a color decorative paint difficult to fall off, and solves the problem that the paint surface is easily influenced by the environment when the existing color decorative paint is actually used, so that the conditions of paint surface fading, falling and the like are caused, and the building attractiveness is seriously influenced.
(II) technical scheme
In order to achieve the purpose, the invention is realized by the following technical scheme: the color decorative paint difficult to fall off comprises a primer, a decorative paint and a protective paint, and the spraying steps are as follows:
s1, performing surface treatment on a wall surface to be sprayed, smearing putty, leveling the putty, waiting for drying, and preparing a primer and a brushing tool;
s2, after the putty is dried, brushing the primer on the wall surface by using a brushing tool, wherein the brushing thickness is 2-3.5mm, waiting for 30-50min until the primer is completely dried, and simultaneously blending the decorative paint to form base color decorative paint and color decorative paint;
s3, when the primer is completely dried, secondarily brushing the residual primer on the wall surface again, wherein the brushing thickness is 1-1.5mm, and waiting for 10-20min until the paint surface of the primer is in a semi-dry state;
s4, when the primer surface is in a semi-dry state, spraying the base color decorative paint on the primer surface by using spraying equipment, and when the primer surface is dried completely, brushing and painting the colored decorative paint by using brushing equipment or spraying equipment or directly spraying patterns by using model paper;
s5, after the pattern is completely sprayed, removing the model paper to wait for the paint to be dried or directly waiting for the paint to be dried;
and S6, after the paint surface is dried, completely brushing the protective paint on the paint surface by using brushing equipment, and waiting for the paint surface to be dried.
Preferably, the primer comprises 5-8 parts of titanium dioxide, 12-15 parts of calcined aluminum silicate, 28-32 parts of acrylic emulsion, 0.5-0.9 part of wetting dispersant, 0.2-0.3 part of defoaming agent, 0.3-0.5 part of antiseptic mildew inhibitor, 3-6 parts of ethylene glycol, 0.3-0.5 part of propylene glycol benzoic acid, 0.2-0.3 part of thickening agent, 0.5-2 parts of nano silicon dioxide, 1-3 parts of glass fiber, 2-4 parts of methyltrichlorosilane, 2-5 parts of zinc stearate and the balance of deionized water.
Preferably, the decorative paint comprises the following materials in percentage by weight: 3-5 parts of pigment powder, 15-20 parts of water-based unsaturated polyester emulsion, 30-35 parts of water-based acrylic resin emulsion, 3-5 parts of polyacrylate, 0.5-1.2 parts of dispersing agent, 3-6 parts of defoaming agent and the balance of deionized water.
Preferably, the material ratio of the protective paint is 25-30 of polyurethane, 25-35 of acrylic resin, 15-25 of hydroxyl acrylic resin, 1.4-3.6 of functional auxiliary agent, 4-6 of film-forming auxiliary agent, 0.2-0.5 of pH regulator, and the balance of deionized water.
Preferably, the pigment powder of the decorative paint is packaged separately, and is mixed and configured on site to form the ground color decorative paint and the multiple color decorative paints according to the on-site requirements.
(III) advantageous effects
The invention provides a color decorative paint difficult to fall off. The method has the following beneficial effects:
1. according to the invention, by means of compounding the primer, the decorative paint and the protective paint, the primer is utilized to improve the alkali-resistant and waterproof capabilities of the inner layer and the adhesiveness of the inner layer, and simultaneously, a compact high-transparency paint film is formed through the polyester crosslinking reaction of the protective paint, so that the acid-base resistance and the scrubbing resistance of the outer paint surface are improved under the condition of ensuring the color of the decorative paint, the service life of the paint surface is effectively prolonged, and the practicability of the paint is enhanced.
2. The color and the dosage of the decorative paint can be modulated on site through the pigment powder which is independently packaged, the ground color decorative paint and various color decorative paints are formed, the material utilization rate is improved, the color diversity is expanded, the complex patterns can be conveniently drawn, and the practicability of the invention is enhanced.
Detailed Description
The technical solutions in the embodiments of the present invention will be clearly and completely described below, and it is obvious that the described embodiments are only a part of the embodiments of the present invention, and not all embodiments. All other embodiments, which can be derived by a person skilled in the art from the embodiments given herein without making any creative effort, shall fall within the protection scope of the present invention.
The first embodiment is as follows:
the embodiment of the invention provides a difficult-to-fall colored decorative paint, which comprises a primer, a decorative paint and a protective paint, and the spraying steps are as follows:
s1, performing surface treatment on a wall surface to be sprayed, smearing putty, leveling the putty, waiting for drying, and preparing a primer and a brushing tool;
s2, after the putty is dried, brushing the primer on the wall surface by using a brushing tool, wherein the brushing thickness is 3.5mm, waiting for 50min until the primer is completely dried, and simultaneously blending the decorative paint to form a ground color decorative paint and a color decorative paint;
s3, when the primer is completely dried, secondarily brushing the residual primer on the wall surface again, wherein the brushing thickness is 1.5mm, and waiting for 20min until the paint surface of the primer is in a semi-dry state;
s4, when the primer surface is in a semi-dry state, spraying the base color decorative paint on the primer surface by using spraying equipment, and when the primer surface is dried completely, brushing and drawing by using color decorative paint by using brushing equipment;
s5, directly waiting for drying of the paint surface after the pattern is brushed and drawn;
and S6, after the paint surface is dried, completely brushing the protective paint on the paint surface by using brushing equipment, and waiting for the paint surface to be dried.
The primer comprises 8 parts of titanium dioxide, 12 parts of calcined aluminum silicate, 32 parts of acrylic emulsion, 0.5 part of wetting dispersant, 0.3 part of defoaming agent, 0.3 part of anti-corrosion mildew inhibitor, 6 parts of ethylene glycol, 0.3 part of propylene glycol benzoic acid, 0.3 part of thickening agent, 2 parts of nano silicon dioxide, 1 part of glass fiber, 4 parts of methyl trichlorosilane and 2 parts of zinc stearate, the rest components are deionized water, and the decorative paint comprises the following materials in parts by weight: 5 parts of pigment powder, 20 parts of water-based unsaturated polyester emulsion, 35 parts of water-based acrylic resin emulsion, 3 parts of polyacrylate, 0.5 part of dispersing agent and 3 parts of defoaming agent, wherein the rest components are deionized water, the pigment powder of the decorative paint is independently packaged and is subjected to on-site mixing configuration to form base color decorative paint and various colored decorative paints according to on-site requirements, the protective paint comprises 30 parts of polyurethane, 25 parts of acrylic resin, 25 parts of hydroxyl acrylic resin, 1.4 parts of functional auxiliary agent, 4 parts of film-forming auxiliary agent and 0.5 part of pH regulator, and the rest components are deionized water.
According to the invention, by compounding the primer, the decorative paint and the protective paint, the primer is utilized to improve the alkali-resistant and waterproof capabilities of the inner layer and the adhesiveness of the inner layer, and simultaneously, a compact high-transparency paint film is formed through the polyester crosslinking reaction of the protective paint, so that the acid-base resistance and the scrubbing resistance of the outer paint surface are improved under the condition of ensuring the color of the decorative paint, the service life of the paint surface is effectively prolonged, and the practicability of the paint is enhanced
Example two:
the difference between the present embodiment and the first embodiment is: the color decorative paint difficult to fall off comprises a primer, a decorative paint and a protective paint, and the spraying steps are as follows:
s1, performing surface treatment on a wall surface to be sprayed, smearing putty, leveling the putty, waiting for drying, and preparing a primer and a brushing tool;
s2, after the putty is dried, brushing the primer on the wall surface by using a brushing tool, wherein the brushing thickness is 2mm, waiting for 30min until the primer is completely dried, and simultaneously blending the decorative paint to form a ground color decorative paint and a color decorative paint;
s3, when the primer is completely dried, secondarily brushing the residual primer on the wall surface again, wherein the brushing thickness is 1mm, and waiting for 10min until the primer surface is in a semi-dry state;
s4, when the priming paint surface is in a semi-dry state, spraying the base color decorative paint on the priming paint surface by using spraying equipment, and when the priming paint surface is dried completely, directly spraying patterns by using colored decorative paint by using the spraying equipment and the model paper;
s5, after the pattern is sprayed, removing the model paper to wait for the drying of the paint surface, wherein the forming efficiency of the paint surface is higher and the paint surface is suitable for large-range long-range decoration;
and S6, after the paint surface is dried, completely brushing the protective paint on the paint surface by using brushing equipment, and waiting for the paint surface to be dried.
The primer comprises 5-8 parts of titanium dioxide, 15 parts of calcined aluminum silicate, 32 parts of acrylic emulsion, 0.9 part of wetting dispersant, 0.3 part of defoaming agent, 0.5 part of anti-corrosion mildew inhibitor, 3-6 parts of ethylene glycol, 0.3 part of propylene glycol benzoic acid, 0.3 part of thickening agent, 2 parts of nano-silica, 3 parts of glass fiber, 2 parts of methyltrichlorosilane and 5 parts of zinc stearate, the rest components are deionized water, 5 parts of pigment powder, 15 parts of water-based unsaturated polyester emulsion, 30 parts of water-based acrylic resin emulsion, 3 parts of polyacrylate, 0.5-1.2 parts of dispersant, 6 parts of defoaming agent, the rest components are deionized water, the pigment powder of the decorative paint is independently packaged, and the primer is prepared by mixing on site according to the on-site requirement to form base color decorative paint and various color decorative paints, and the protective paint comprises 30 parts of polyurethane, 25 parts of acrylic resin and 25 parts of hydroxy acrylic resin, 3.6 functional auxiliary agents, 6 film forming auxiliary agents and 0.5 pH regulator, and the balance of deionized water.
The color and the dosage of the decorative paint can be modulated on site through the pigment powder which is independently packaged, the ground color decorative paint and various color decorative paints are formed, the material utilization rate is improved, the color diversity is expanded, the complex patterns can be conveniently drawn, and the practicability of the invention is enhanced.
Although embodiments of the present invention have been shown and described, it will be appreciated by those skilled in the art that changes, modifications, substitutions and alterations can be made in these embodiments without departing from the principles and spirit of the invention, the scope of which is defined in the appended claims and their equivalents.
Claims (5)
1. The color decorative paint difficult to fall off comprises a primer, a decorative paint and a protective paint, and the spraying steps are as follows:
s1, performing surface treatment on a wall surface to be sprayed, smearing putty, leveling the putty, waiting for drying, and preparing a primer and a brushing tool;
s2, after the putty is dried, brushing the primer on the wall surface by using a brushing tool, wherein the brushing thickness is 2-3.5mm, waiting for 30-50min until the primer is completely dried, and simultaneously blending the decorative paint to form base color decorative paint and color decorative paint;
s3, when the primer is completely dried, secondarily brushing the residual primer on the wall surface again, wherein the brushing thickness is 1-1.5mm, and waiting for 10-20min until the paint surface of the primer is in a semi-dry state;
s4, when the primer surface is in a semi-dry state, spraying the base color decorative paint on the primer surface by using spraying equipment, and when the primer surface is dried completely, brushing and painting the colored decorative paint by using brushing equipment or spraying equipment or directly spraying patterns by using model paper;
s5, after the pattern is completely sprayed, removing the model paper to wait for the paint to be dried or directly waiting for the paint to be dried;
and S6, after the paint surface is dried, completely brushing the protective paint on the paint surface by using brushing equipment, and waiting for the paint surface to be dried.
2. The difficult-to-peel colored decorative paint according to claim 1, wherein: the primer comprises, by weight, 5-8 parts of titanium dioxide, 12-15 parts of calcined aluminum silicate, 28-32 parts of acrylic emulsion, 0.5-0.9 part of wetting dispersant, 0.2-0.3 part of defoaming agent, 0.3-0.5 part of antiseptic mildew preventive, 3-6 parts of ethylene glycol, 0.3-0.5 part of propylene glycol benzoic acid, 0.2-0.3 part of thickener, 0.5-2 parts of nano-silica, 1-3 parts of glass fiber, 2-4 parts of methyltrichlorosilane and 2-5 parts of zinc stearate, and the balance of deionized water.
3. The difficult-to-peel colored decorative paint according to claim 1, wherein: the decorative paint comprises the following materials in percentage by weight: 3-5 parts of pigment powder, 15-20 parts of water-based unsaturated polyester emulsion, 30-35 parts of water-based acrylic resin emulsion, 3-5 parts of polyacrylate, 0.5-1.2 parts of dispersing agent, 3-6 parts of defoaming agent and the balance of deionized water.
4. The difficult-to-peel colored decorative paint according to claim 1, wherein: the material proportion of the protective paint is that polyurethane 25-30, acrylic resin 25-35, hydroxyl acrylic resin 15-25, functional auxiliary agent 1.4-3.6, film forming auxiliary agent 4-6, pH regulator 0.2-0.5, and the rest component is deionized water.
5. The difficult-to-peel colored decorative paint according to claim 3, wherein: the pigment powder of the decorative paint is packaged separately, and is mixed and configured on site according to the on-site requirements to form the ground color decorative paint and various colored decorative paints.