CN110317504A - A kind of coat system and its construction method of high dirt resistance imitation wood line sandrock effect - Google Patents
A kind of coat system and its construction method of high dirt resistance imitation wood line sandrock effect Download PDFInfo
- Publication number
- CN110317504A CN110317504A CN201910429047.2A CN201910429047A CN110317504A CN 110317504 A CN110317504 A CN 110317504A CN 201910429047 A CN201910429047 A CN 201910429047A CN 110317504 A CN110317504 A CN 110317504A
- Authority
- CN
- China
- Prior art keywords
- parts
- effect
- dirt resistance
- dope layer
- high dirt
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of coat systems of high dirt resistance imitation wood line sandrock effect, including the sandstone aggregate dope layer set gradually from the inside to the outside, wood grain effect dope layer and high dirt resistance finishing varnish layer, sandstone aggregate dope layer includes the raw material of following mass fraction: 103~135 parts of deionized water, 1.6~2.0 parts of ethylhydroxyethylcellulose, 0.1~0.2 part of wetting dispersing agent, 0.4~0.6 part of pH adjusting agent, 0.6~0.8 part of defoaming agent, 4~6 parts of propylene glycol, 110~130 parts of pure-acrylic emulsion, 5.5~6.5 parts of coalescing agent, 1.3~1.5 parts of preservative, alkali soluble rises 0.5~0.9 part of thickener, 700~750 parts of natural colour sand.Coat system emulator of the invention is high and has the texture of natural wood grain sandstone, it is able to satisfy standard " GB/T 9779-2015 Multi wall architectural coatings " "-III type of inside/outside wall is compound " index request, with reliable quality, it can be widely applied to villa, high-grade office building, holiday village etc. and pursue personalized, differentiation building decoration style building, also can be used for room background wall decoration.
Description
Technical field
The invention belongs to building coating field, in particular to the coat system of a kind of high dirt resistance imitation wood line sandrock effect and
Its construction method.
Background technique
Natural sandstone is a kind of sedimentary rock.It is effect solution of the rock before millions upon millions of years due to weathering and erosion and flowing water erosion
Body becomes sand formation cuttings, rear again through geological movement, is squeezed the geology physics such as cementing and absorption minerals, calcification by diastrophe and makees
With stratified sedimentation forms, and compactness is very high from level to level for formation, the lithotome of decorative pattern variation multiplicity.
Natural sandstone not only health environment-friendly but also had been rich in dicoration, increasingly by the favor of architectural decoration.Natural sandstone
Plain weave sandstone, wood grain sandrock, random line sandstone can be divided by surface texture.Wood grain sandrock surface has thickness different, light and dark
Straight line texture, just like wood grain, decorated style, which is recovered one's original simplicity, not to be lost luxurious atmosphere not only, get close to nature but also brings plain warmth, standby
It is pursued.
But natural sandstone forms that the period is very long, and exploitation, processing, freight are expensive, decoration cost is high, from it is great and by
It is that graininess, porosity are larger in its surface, freeze-thaw damage easily occurs after rainy season in winter, there are security risks.Therefore, one kind can
The coat system in the high dirt resistance imitation wood line sandrock effect of building wall decoration is applied, can necessarily solve disadvantages mentioned above
Farthest meet architectural decoration to the decoration demand of wood grain sandrock simultaneously.
Summary of the invention
In view of the above-mentioned problems, the purpose of the present invention is to provide a kind of coat systems of high dirt resistance imitation wood line sandrock effect
And its construction method, coating simulated effect can not only reach 85% or more of natural wood grain sandstone, and have natural wood grain sand
The thick and heavy luxurious sandstone texture of rock also has excellent strength character, outdoor durable and stain resistance；Coat system it is each
Coating is complete aqueous based systems, environmentally protective, environmental-friendly.
To achieve the goals above, The technical solution adopted by the invention is as follows:
A kind of coat system of high dirt resistance imitation wood line sandrock effect, the sandstone aggregate including setting gradually from the inside to the outside apply
The bed of material, wood grain effect dope layer and high dirt resistance finishing varnish layer, the sandstone aggregate dope layer includes following mass fraction
Raw material: 103~135 parts of deionized water, 1.6~2.0 parts of ethylhydroxyethylcellulose, 0.1~0.2 part of wetting dispersing agent, pH
0.4~0.6 part of regulator, 0.6~0.8 part of defoaming agent, 4~6 parts of propylene glycol, 110~130 parts of pure-acrylic emulsion, coalescing agent 5.5
~6.5 parts, 1.3~1.5 parts of preservative, alkali soluble rises 0.5~0.9 part of thickener, 700~750 parts of natural colour sand.
Further, the wood grain effect dope layer includes following components: protection sol solution, toning base-material and isolation are anti-
Supernatant paint, mass ratio are as follows: protection sol solution: toning base-material: it is isolated anti-settling varnish=150~180 part: 300~360 parts: 460
~550 parts.
Wherein, the protection sol solution includes the raw material of following mass fraction: 920~940 parts of deionized water, protective glue
60~80 parts of powder.
Wherein, the toning base-material includes the raw material of following mass fraction: 480~530 parts of deionized water, ethyl hydroxyl second
9~10 parts of base cellulose, 4~5 parts of wetting dispersing agent, 1~1.5 part of PH regulator, 3~4 parts of defoaming agent, inorganic color stuffing 100
~150, it 8~12 parts of propylene glycol, 250~270 parts of silicone acrylic emulsion, 15~16.2 parts of coalescing agent, 1.5~2.0 parts of preservative, protects
50~60 parts of sol solution of shield.
Wherein, the anti-settling varnish of isolation includes the raw material of following mass fraction: 405~455 parts of deionized water, anti-corrosion
2.7~3.5 parts of agent, 450~540 parts of silicone acrylic emulsion, 27~32.5 parts of coalescing agent, 18~21.7 parts of propylene glycol, defoaming agent 3.5
~4 parts, 1~1.5 part of PH regulator, isolation 4~6 parts of anti-settling agent, 4.5~5.4 parts of alkali swollen thickener.
Further, the high dirt resistance finishing varnish layer includes the raw material of following mass fraction: deionized water 410~
450 parts, 8~10 parts of alkali swollen thickener, 1.0~1.5 parts of preservative, 230~250 parts of pure-acrylic emulsion, inorganic hybridization lotion 230
~250 parts, 56~61 parts of coalescing agent, 8~10 parts of propylene glycol, 0.5~1.0 part of defoaming agent, 2.5~3.0 parts of PH regulator, base
0.5~1.0 part of material wetting agent.
The invention also discloses the construction method of the coat system of above-mentioned high dirt resistance imitation wood line sandrock effect, including it is as follows
Step:
S1, spraying sandstone aggregate dope layer.
S2, after sandstone aggregate dry paint layer >=8h, spray wood grain effect dope layer.
S3, before the non-surface drying of wood grain effect dope layer, it is quick along fixed direction on the surface of wood grain effect dope layer
Brush out wood grain effect.
S4, after wood grain effect dry paint layer >=for 24 hours, in the surface roller coating high dirt resistance cover of wood grain effect dope layer
Varnish.
Further, in step S1, sandstone aggregate dope layer is sprayed using lacquer spray gun special.
Further, in step S2, using inner pressed spray gun spraying wood grain effect dope layer.
Further, quick along fixed direction on the surface of wood grain effect dope layer using scrub-brush in step S2
Brush out wood grain effect.
The invention has the following beneficial effects: 1, it can realistically show unique, thick and heavy, the luxurious texture of sandstone, and its
Self weight is far below natural wood grain sandstone, is used for external wall of high-rise building facing, building can be made to have more personalized, differentiation
Decorated style；2, it is successively constructed acquisition by sandstone aggregate coating, wood grain effect coating, high dirt resistance finishing varnish, applies series of strata
Each layer of the coating of uniting is complete aqueous based systems, environmentally protective, environmental-friendly.3, high dirt resistance finishing varnish long-lasting protection in
Surface layer has dust-proof dirt-resistant, antibacterial and mouldproof, weather-proof guarantor's light and other effects, can be improved imitation wood line sandrock effect coat system
Bulk life time；4, sandstone aggregate coating uses spraying process, brushes size by the discharging speed and air pressure that adjust spray gun, can obtain
The apparent effect of sandstone of any concave-convex degree is obtained, decorated style there are more selections, more enriches；5, used in present invention construction
Tool be that the tool of acquisition is commonly used and facilitated in architectural decoration, the construction technology of each coating is also work commonly used in the trade
Skill limits construction of the invention by tool and technique, can be realized with most common spraying process and roll coating process, operation
Simply, easy for construction.
Detailed description of the invention
Fig. 1 is the structural schematic diagram of the coat system of high dirt resistance imitation wood line sandrock effect in the present invention.
Primary clustering symbol description: 1, through the processed wall of alkali-resistant sealing primer；2, sandstone aggregate dope layer；3, wood grain
Effect dope layer；4, high dirt resistance finishing varnish layer.
Specific embodiment
With reference to the accompanying drawings and detailed description, the present invention will be further described.
As shown in Figure 1, a kind of coat system of high dirt resistance imitation wood line sandrock effect, including what is set gradually from the inside to the outside
Sandstone aggregate dope layer 2, wood grain effect dope layer 3, high dirt resistance finishing varnish layer 4.
Embodiment one
A kind of coat system of high dirt resistance imitation wood line sandrock effect, is made of the material in following table:
In embodiment one, the construction method of the coat system of high dirt resistance imitation wood line sandrock effect:
The first step sprays sandstone with lacquer spray gun special on having already passed through the processed wall 1 of alkali-resistant sealing primer
Aggregate dope layer 2.
Second step, after 2 drying >=8h of sandstone aggregate dope layer, with inner pressed spray gun spraying wood grain effect dope layer 3.
Third step quickly brushes out wood along fixed direction with large size scrub-brush before the non-surface drying of wood grain effect dope layer 3
Line effect.
4th step, after wood grain effect dry paint layer >=for 24 hours, with undercoat roller roller coating high dirt resistance finishing varnish layer 4:
It answers careful roller coating and is unable to holiday, uniform gloss should be formed after surface drying, be completely dried time >=48h/25 DEG C, be completely dried
Before, it should not drench with rain；If construction environment temperature is lower than 25 DEG C, the time being completely dried should be appropriately extended.
Embodiment one can get the decorative effect of yellow class wood grain sandrock: plain, warm.
Embodiment two
A kind of coat system of high dirt resistance imitation wood line sandrock effect, is made of the material in following table:
In embodiment two, the construction method of the coat system of high dirt resistance imitation wood line sandrock effect:
The first step sprays sandstone with lacquer spray gun special on having already passed through the processed wall 1 of alkali-resistant sealing primer
Aggregate dope layer 2.
Second step, after 2 drying >=8h of sandstone aggregate dope layer, with inner pressed spray gun spraying wood grain effect dope layer 3.
Third step quickly brushes out wood along fixed direction with large size scrub-brush before the non-surface drying of wood grain effect dope layer 3
Line effect.
4th step, after wood grain effect dry paint layer >=for 24 hours, with undercoat roller roller coating high dirt resistance finishing varnish layer 4:
It answers careful roller coating and is unable to holiday, uniform gloss should be formed after surface drying, be completely dried time >=48h/25 DEG C, be completely dried
Before, it should not drench with rain；If construction environment temperature is lower than 25 DEG C, the time being completely dried should be appropriately extended.
Embodiment two can get the decorative effect of grey system wood grain sandrock: simple, natural.
Above-mentioned two embodiments are detected according to standard " GB/T 9779-2015 Multi wall architectural coatings ", can get in following table
Performance indicator:
As seen from the above table, a kind of coat system of high dirt resistance imitation wood line sandrock effect of the present invention not only has high emulation
Decorative effect, the performance requirement of coating is also able to satisfy standard requirements, especially suitable for high-grade hotel, club, villa, spends a holiday
The building decoration in village, museum and municipal works, has a vast market foreground.
Although specifically showing and describing the present invention in conjunction with preferred embodiment, those skilled in the art should be bright
It is white, it is not departing from the spirit and scope of the present invention defined by the appended claims, in the form and details to this hair
It is bright to make a variety of changes, it is protection scope of the present invention.
Claims (10)
1. a kind of coat system of high dirt resistance imitation wood line sandrock effect, it is characterised in that: including what is set gradually from the inside to the outside
Sandstone aggregate dope layer, wood grain effect dope layer and high dirt resistance finishing varnish layer, the sandstone aggregate dope layer include with
The raw material of lower mass fraction: 103~135 parts of deionized water, 1.6~2.0 parts of ethylhydroxyethylcellulose, wetting dispersing agent 0.1
~0.2 part, 0.4~0.6 part of pH adjusting agent, 0.6~0.8 part of defoaming agent, 4~6 parts of propylene glycol, 110~130 parts of pure-acrylic emulsion,
5.5~6.5 parts of coalescing agent, 1.3~1.5 parts of preservative, alkali soluble rises 0.5~0.9 part of thickener, natural colour sand 700~750
Part.
2. a kind of coat system of high dirt resistance imitation wood line sandrock effect as described in claim 1, it is characterised in that: described
Wood grain effect dope layer includes following components: protection sol solution, toning base-material and the anti-settling varnish of isolation, mass ratio are as follows: protection
Sol solution: toning base-material: it is isolated anti-settling varnish=150~180 part: 300~360 parts: 460~550 parts.
3. a kind of coat system of high dirt resistance imitation wood line sandrock effect as claimed in claim 2, it is characterised in that: described
Protection sol solution includes the raw material of following mass fraction: 920~940 parts of deionized water, protecting 60~80 parts of rubber powder.
4. a kind of coat system of high dirt resistance imitation wood line sandrock effect as claimed in claim 2, it is characterised in that: described
Toning base-material includes the raw material of following mass fraction: 480~530 parts of deionized water, 9~10 parts of ethylhydroxyethylcellulose, and profit
4~5 parts of hygroscopic water powder, 1~1.5 part of PH regulator, 3~4 parts of defoaming agent, inorganic color stuffing 100~150, propylene glycol 8~12
Part, 250~270 parts of silicone acrylic emulsion, 15~16.2 parts of coalescing agent, 1.5~2.0 parts of preservative, protect 50~60 parts of sol solution.
5. a kind of coat system of high dirt resistance imitation wood line sandrock effect as claimed in claim 2, it is characterised in that: described
The raw material that anti-settling varnish includes following mass fraction: 405~455 parts of deionized water, 2.7~3.5 parts of preservative, the third cream of silicon is isolated
450~540 parts of liquid, 27~32.5 parts of coalescing agent, 18~21.7 parts of propylene glycol, 3.5~4 parts of defoaming agent, PH regulator 1~
1.5 parts, isolation 4~6 parts of anti-settling agent, 4.5~5.4 parts of alkali swollen thickener.
6. a kind of coat system of high dirt resistance imitation wood line sandrock effect as described in claim 1, it is characterised in that: described
High dirt resistance finishing varnish layer includes the raw material of following mass fraction: 410~450 parts of deionized water, alkali swollen thickener 8~10
Part, 1.0~1.5 parts of preservative, 230~250 parts of pure-acrylic emulsion, 230~250 parts of inorganic hybridization lotion, coalescing agent 56~61
Part, 8~10 parts of propylene glycol, 0.5~1.0 part of defoaming agent, 2.5~3.0 parts of PH regulator, 0.5~1.0 part of substrate wetting agents.
7. such as a kind of construction party of the coat system of high dirt resistance imitation wood line sandrock effect of any of claims 1-6
Method, which comprises the steps of:
S1, spraying sandstone aggregate dope layer；
S2, after sandstone aggregate dry paint layer >=8h, spray wood grain effect dope layer；
S3, before the non-surface drying of wood grain effect dope layer, quickly brushed out on the surface of wood grain effect dope layer along fixed direction
Wood grain effect；
S4, after wood grain effect dry paint layer >=for 24 hours, it is clear in the surface roller coating high dirt resistance cover of wood grain effect dope layer
Paint.
8. a kind of construction method of the coat system of high dirt resistance imitation wood line sandrock effect as claimed in claim 7, feature
It is: in step S1, sandstone aggregate dope layer is sprayed using lacquer spray gun special.
9. a kind of construction method of the coat system of high dirt resistance imitation wood line sandrock effect as claimed in claim 7, feature
It is: in step S2, using inner pressed spray gun spraying wood grain effect dope layer.
10. a kind of construction method of the coat system of high dirt resistance imitation wood line sandrock effect as claimed in claim 7, feature
It is: in step S2, wood grain effect is quickly brushed out along fixed direction on the surface of wood grain effect dope layer using scrub-brush.