CN114351317B - 一种服装上的仿旧贴及其生产方法 - Google Patents
一种服装上的仿旧贴及其生产方法 Download PDFInfo
- Publication number
- CN114351317B CN114351317B CN202210065638.8A CN202210065638A CN114351317B CN 114351317 B CN114351317 B CN 114351317B CN 202210065638 A CN202210065638 A CN 202210065638A CN 114351317 B CN114351317 B CN 114351317B
- Authority
- CN
- China
- Prior art keywords
- yarns
- warp
- weft
- finishing
- fdy40d
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明提供一种服装上的仿旧贴及其生产方法，属于纺织服装技术领域。它是由下层经纬纱线和上层经纬纱线经染色后进行经纬双层组织色织交织，下层经纬纱线为FDY40D皮芯型低熔点涤纶复合长丝或能高收缩达百分之三十的FDY40D涤纶牵伸长丝，染成肤色，经纬双层组织织造，下层须为细致紧密的，可以为平纹、斜纹、缎纹组织，而上层必须为二上一下或三上一下的斜纹组织，并且具有各种织疵的跳经纱、跳纬纱或破洞。本发明的仿旧贴不需要将牛仔面料进行人为损伤仿旧破洞处理，在做成的牛仔服装上根据人们喜好，直接将服装上的仿旧贴在适当的地方用熨斗粘合上即可，省时省力，尽显个性化。
Description
技术领域
本发明涉及服装上的装饰帖，特别涉及一种服装上的仿旧贴及其生产方法，属于纺织服装技术领域。
背景技术
由于牛仔布及牛仔服装粗犷豪放，穿着随意，不拘一格，深受广大劳动人民的喜爱，从诞生至今一直流行不衰。牛仔产品也层出不穷，不论是轻磅的、中磅的、重磅的，还是全棉、交织混纺，化纤，或者靛蓝、什色、套色，或者漂洗、彩条双色或肉色、印花、有特殊功能的，以及平纹、斜纹、破斜、凸条、彩格、提花等等。还有流行仿旧的石磨整理，水洗整理，雪花整理，浓漂整理，套色整理，人为损伤整理，以及生物酶整理等等。市场上不论早晚总见有人身着牛仔服、牛仔裤，而且还多见有用织疵、破洞进行装饰，更显粗犷豪放，随意而得体。随着社会的城市化，人们追求着最自然的牛仔化，而且愈演愈烈，但是那种十分流行的织疵、破洞，其实穿起来并不顺利，而且洗涤起来也不方便。人们希望既有仿旧破洞风格，又要穿脱顺利、洗涤方便的牛仔服装。
发明内容
本发明的目的是提供一种服装上的仿旧贴及其生产方法，就目前仿旧牛仔服装的破洞、织疵给人们带来的不便而给予改进，本发明服装上的仿旧贴不需要将牛仔面料进行人为损伤仿旧破洞处理，在做成的牛仔服装上根据人们喜好，直接将服装上的仿旧贴在适当的地方用熨斗粘合上即可，省时省力，尽显个性化。
本发明解决其技术问题所采用的技术方案是：
一种服装上的仿旧贴，是经纬纱线染色后经经纬双层组织色织交织而成。
所述的经纬纱线染色后经经纬双层组织色织交织，是由下层经纬纱线和上层经纬纱线经染色后进行经纬双层组织色织交织。
进一步的，所述的下层经纬纱线有二个方案，第一种方案为FDY40D皮芯型低熔点涤纶复合长丝，是以低熔点改性聚酯L-PET为皮层及普通涤纶PET为芯层经特殊复合纺丝加工而成的，染成肤色。第二种为能高收缩达百分之三十的FDY40D涤纶牵伸长丝，也染成肤色。
进一步的，所述的上层经纬纱线，可以是全棉纱线，可以是化纤纱线，也可以是混纺纱线，也可以为粗支纱线、中支纱线、细支纱线，染色可以为靛蓝色，可以为什色，也可以为套色，也可以根据牛仔服装的颜色和客户喜好染色。
再进一步的，所述的经纬双层组织织造，下层须为细致紧密的，可以为平纹、斜纹、缎纹组织，而上层必须为二上一下或三上一下的斜纹组织，并且具有各种织疵的跳经纱、跳纬纱或破洞的，例如百脚、无经纱破洞或无纬纱破洞等等，而织疵、破洞的大小也可以任意设置，千变万化。
一种服装上的仿旧贴的生产方法，包括以下步骤：
步骤（1）：原料的选择，
下层经纬纱线，第一种方案选择FDY40D皮芯型低熔点熔点185℃±5℃的涤纶复合长丝，并将其在160℃以下染成肤色。第二种方案选择能高收缩达百分之三十的FDY40D涤纶牵伸长丝，在220℃以下也染成肤色。
上层经纬纱线，可以是全棉纱线，可以是化纤纱线，也可以是混纺纱线，可以为粗支纱线、中支纱线、细支纱线，并将其染色，可以为靛蓝色，可以为什色，也可以为套色，也可以根据牛仔服装的颜色和个人喜好染色。
步骤（2）：整经穿综插筘，
将下层经纱按织造工艺整经，整在一个织轴上，
将上层经纱按织造工艺整经，整在一个织轴上，
依照织造工艺将下层经纱、上层经纱按顺序排列，分别将下层经纱穿在素色多臂机综丝上，将上层经纱穿在大提花机花综综丝上并依次插筘。
步骤（3）：提综打纬织造，
下层经纱由素色多臂机进行平纹、斜纹或缎纹的织造，要求整平，且有皮肤表皮细腻的视觉观感，
上层经纱由花综提花机进行二上一下或三上一下的基布斜纹织造，且必须镶嵌有各种织疵，例如跳经纱、跳纬纱，或破洞，例如百脚、无经纱破洞或无纬纱破洞等等，而织疵破洞的大小，都可以由电脑按客户需求随意控制。
步骤（4）：后整理，
后整理包括整纬、预缩和烘干，
当下层经纬纱线用第一方案即用一种FDY40D皮芯型低熔点涤纶复合长丝，后整理必须都在160℃以下的情况下进行即可，
当下层经纬纱线用第二方案选择能高收缩达百分之三十的FDY40D涤纶牵伸长丝的，后整理可以在220℃以不的情况下进行，同时第二方案在后整理最后，还需要在该下层布的与上层布连结织造的反面进行涂胶浆整理，该胶浆一面牢固的粘在下层布上，而另一面冷却后无粘性，但可以在300℃±5℃情况下再次产生粘合作用。
步骤（5）：检验入库。
步骤（6）：使用，
消费者按自己的肤色或者喜好挑选仿旧贴下层布的颜色，根据自己的喜好挑选上层布的织疵的大小和形状，然后将服装上的仿旧贴的下层放在牛仔服装需要粘贴的地方，
如果是用第一方案织造的服装上的仿旧贴，用190℃的电熨斗熨烫5分钟即可。
如果是用第二方案织造的服装上的仿旧贴，用300℃的电熨斗熨烫5分钟即可。
本发明和现有技术相比，具有以下优点和效果：
本发明一种可以仿旧的服装上的仿旧贴，由于是双层组织，具有上下层，不论下层为40D的皮芯型低熔点涤纶丝经纬交织或高收缩达百分之三十的FDY40D涤纶牵伸长丝经纬交织而成的，放置于消费者喜欢的地方进行熨烫，即可牢牢粘附在消费者的牛仔服装上，清洁环保，方便灵活，完全可按照消费者的喜好进行挑选和熨烫。而且耐洗 耐摩，剥离强度也完全符合标准。
而上层却是有各种各样大小不一的织疵和破洞可供各年龄层次各社会阶层的人们根据喜爱选择。
本发明一种服装上的仿旧贴是熨烫在完整的服装面料上的，消费者穿脱服装仍然比较方便，不会因破洞而使人们穿着时伸进缩出出现差错。
本发明一种服装上的仿旧贴，所有织疵、破洞只是假象，牛仔面料还是完整的，不影响保暖，不必担心会有关节发冷的现象发生。
本发明一种服装上的仿旧贴，其下层颜色，可以做到和消费者的皮肤一样，其上层织疵和破洞看上去很自然，因此完全可以以假乱真。而且，由于第一方案下层直接采用了低熔点涤纶丝织造，用于粘贴到服装上方便快捷牢固而且环保，由于第二方案下层还采用了高收缩达百分之三十的FDY40D涤纶牵伸长丝经纬交织，经后整理后，上层的织疵和破洞会因下层收缩而弓起来，立体感更明显，无经纱破洞的纬纱或无纬纱破洞的经纱也会弓起而产生一种飘逸感，更显牛仔风貌。而且下层基布所涂胶漿再次与服装面料粘合也方便快捷牢固而且环保。
对于牛仔面料生产厂家，在生产服装上的仿旧贴时完全可以和牛仔面料采购同批号的上层经纬上层纱线和进行同一批染色后整理，其制成的牛仔服装更为协调。
附图说明
图1为本发明一种服装上的仿旧贴的其中一种式样的正视图。
图2为本发明一种服装上的仿旧贴的其中一种式样的侧视图。
具体实施方式一
下面结合附图并通过实施例对本发明作进一步的详细说明，以下实施例是对本发明的解释而本发明并不局限于以下实施例。
如图1和图2所示，上层织物A和下层织物B形成了一种服装上的仿旧贴的仿旧效果，而且能实现粘贴。
实施例1
步骤（1）：原料的选择，
下层经纬纱线，选择FDY40D皮芯型低熔点熔点185℃±5℃涤纶复合长丝，并将其染成肤色。
上层经纬纱线，可以是全棉纱线，可以是化纤纱线，也可以是混纺纱线，可以为粗支纱线、中支纱线、细支纱线，并将其染色，可以为靛蓝色，可以为什色，也可以为套色，也可以根据牛仔服装的颜色和个人喜好染色。现选择经纱为21s棉纱染腚蓝色,纬纱为16s本白涤纶短纤纱。
步骤（2）：整经穿综插筘，
将下层FDY40D皮芯型低熔点熔点185℃±5℃涤纶复合长丝经纱按织造工艺整经，整在一个织轴上，
将上层21s腚蓝棉纱经纱按织造工艺整经，整在一个织轴上，
依照织造工艺将下层经纱、上层经纱按顺序排列，分别在素色多臂机综丝上和花机提花机综丝上依次穿综插筘。
步骤（3）：提综打纬织造，
下层FDY40D皮芯型低熔点熔点185℃±5℃涤纶复合长丝经纱由素色多臂机和FDY40D皮芯型低熔点熔点185℃±5℃涤纶复合长丝纬纱进行平纹、斜纹或缎纹的织造，整平，且有皮肤表皮细腻的视觉观感，
上层21s棉纱腚蓝经纱由花综提花机和为16s本白涤纶短纤纱进行二上一下的基布左斜斜纹织造，并且还镶嵌有织疵，无经纱破洞和无纬纱破洞，而织疵破洞的大小，都可以由电脑上根据客户需求随意控制。
步骤（4）：后整理，
后整理包括整纬、预缩和烘干，后整理在160℃以下的情况下进行。
步骤（5）：检验入库，
步骤（6）：使用，
消费者按自己的肤色或者喜好挑选仿旧贴下层布的颜色，根据自己的喜好挑选上层布的织疵的大小和形状，然后将服装上的仿旧贴的下层放在牛仔服装需要粘贴的地方，用190℃的电熨斗熨烫5分钟即可。
实施例2
步骤（1）：原料的选择，
下层经纬纱线，选择能高收缩达百分之三十的FDY40D涤纶牵伸长丝，也染成肤色。
上层经纬纱线，可以是全棉纱线，可以是化纤纱线，也可以是混纺纱线，可以为粗支纱线、中支纱线、细支纱线，并将其染色，可以为靛蓝色，可以为什色，也可以为套色，也可以根据牛仔服装的颜色和个人喜好染色。现选择经纱为32/2s棉纱染腚蓝色,纬纱为12s本白涤纶短纤纱。
步骤（2）：整经穿综插筘，
将下层高收缩达百分之三十的FDY40D涤纶牵伸长丝经纱按织造工艺整经，整在一个织轴上，
将上层32/2s棉纱腚蓝经纱按织造工艺整经，整在一个织轴上，
依照织造工艺将下层经纱、上层经纱按顺序排列，分别将下层高收缩达百分之三十的FDY40D涤纶牵伸长丝经纱穿在素色多臂机综丝上，将上层32/2s棉纱腚蓝经纱穿在提花机综丝上并依次穿综插筘。
步骤（3）：提综打纬织造，
下层高收缩达百分之三十的FDY40D涤纶牵伸长丝经纱和高收缩达百分之三十的FDY40D涤纶牵伸长丝纬纱由素色多臂机进行平纹、斜纹或缎纹的织造，要求整平，且有皮肤表皮细腻的视觉观感，
上层32/2s棉纱 腚蓝经纱和12s本白涤纶短纤纬纱由提花机花综进行三上一下的基布右斜斜纹织造，且还镶嵌有各种织疵，如百脚、无经纱破洞或无纬纱破洞等等，而织疵破洞的大小，都可以由电脑根据客户需求随意控制。
步骤（4）：后整理，
后整理包括整纬、预缩和烘干,后整理可以在220℃以下的情况下进行，在后整理最后，还需要在该下层布的与上层布连结织造的反面进行涂胶浆整理，该胶浆一面牢固的粘在下层布上，而另一面冷却后无粘性，但可以在300℃±5℃情况下再次产生粘合作用。
步骤（5）：检验入库，
步骤（6）：使用，
消费者按自己的肤色或者喜好挑选仿旧贴下层布的颜色，根据自己的喜好挑选上层布的织疵的大小和形状，然后将服装上的仿旧贴的下层放在牛仔服装需要粘贴的地方，用300℃的电熨斗熨烫5分钟即可
由于下层采用了高收缩达百分之三十的FDY40D涤纶牵伸长丝经纬交织，经后整理后，上层的织疵和破洞会因下层高收缩而弓起来，立体感更明显，无经纱破洞的纬纱或无纬纱破洞的经纱也会因下层高收缩弓起而产生一种飘逸感，更显牛仔风貌。
本说明书中所描述的以上内容仅仅是对本发明所作的举例说明。本发明所属技术领域的技术人员可以对所描述的具体实施例做各种各样的修改或补充或采用类似的方式替代，只要不偏离本发明说明书的内容或者超越本权利要求书所定义的范围，均应属于本发明的保护范围。
Claims (1)
1.一种服装上的仿旧贴的生产方法，其特征在于：包括以下步骤：
步骤（1）：原料的选择，
下层经纬纱线，选择FDY40D皮芯型低熔点熔点185℃±5℃的涤纶复合长丝或能高收缩达百分之三十的FDY40D涤纶牵伸长丝，染成肤色，
上层经纬纱线，是全棉纱线，或化纤纱线，或混纺纱线，或粗支纱线，或中支纱线，或细支纱线，并将其染色，染色为靛蓝色，或什色，或套色，或根据牛仔服装的颜色和个人喜好染色；
步骤（2）：整经穿综插筘，
将下层经纱按织造工艺整经，整在一个织轴上，
将上层经纱按织造工艺整经，整在一个织轴上，
依照织造工艺将下层经纱、上层经纱按顺序排列，分别将下层经纱穿在素色多臂机综丝上，将上层经纱穿在大提花机花综综丝上，并依次插筘；
步骤（3）：提综打纬织造，
下层经纱由素色多臂机进行平纹、斜纹或缎纹的织造，要求整平，且有皮肤表皮细腻的视觉观感，
上层经纱由花综提花机进行二上一下或三上一下的基布斜纹织造，且必须镶嵌有各种织疵的跳经纱、跳纬纱或破洞；
步骤（4）：后整理，
后整理包括整纬、预缩和烘干，
下层经纬纱线为FDY40D皮芯型低熔点熔点185℃±5℃的涤纶复合长丝时，后整理必须都在160℃以下的情况下进行，
下层经纬纱线为能高收缩达百分之三十的FDY40D涤纶牵伸长丝时，后整理在220℃以下的情况下进行，在后整理最后，还需要在下层布的与上层布连结织造的反面进行涂胶浆整理，该胶浆一面牢固的粘在下层布上，而另一面冷却后无粘性，但能够在300℃±5℃情况下再次产生粘合作用；
步骤（5）：检验入库，
步骤（6）：使用，
消费者按自己的肤色或者喜好挑选服装上的仿旧贴下层布的颜色，根据自己的喜好挑选上层布的织疵的大小和形状，然后将服装上的仿旧贴的下层放在牛仔服装需要粘贴的地方，所有织疵、破洞只是假象，牛仔面料还是完整的，
下层经纬纱线为FDY40D皮芯型低熔点熔点185℃±5℃的涤纶复合长丝时，用190℃的电熨斗熨烫5分钟即可，
下层经纬纱线为能高收缩达百分之三十的FDY40D涤纶牵伸长丝时，用300℃的电熨斗熨烫5分钟即可。