CN114306720A - 一种含有芦荟凝胶的伤口敷料及其制备方法 - Google Patents
一种含有芦荟凝胶的伤口敷料及其制备方法 Download PDFInfo
- Publication number
- CN114306720A CN114306720A CN202210003258.1A CN202210003258A CN114306720A CN 114306720 A CN114306720 A CN 114306720A CN 202210003258 A CN202210003258 A CN 202210003258A CN 114306720 A CN114306720 A CN 114306720A
- Authority
- CN
- China
- Prior art keywords
- molecular weight
- wound dressing
- weight polyisobutylene
- aloe gel
- cyclodextrin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种含有芦荟凝胶的伤口敷料及其制备方法,所述伤口敷料由以下重量百分比原料配制而成:其中高分子量聚异丁烯10‑15%、低分子量聚异丁烯15‑25%、交联羧甲基纤维素钠15‑20%、刺梧桐胶5‑7%、环糊精5‑10%、芦荟凝胶2‑8%、水杨酸1‑3%、粉末香精0.1‑2%、茶油2‑5%、壳聚糖2‑5%。本发明具有良好的吸水性、初粘性、持粘性,当吸收渗液后产品具有很好的完整性,且从皮肤剥离时,不会刺激皮肤,在粘贴过程中,对皮肤有一定的修复功能,同时可以吸收渗液的异味,而且制作工艺简便易行,设备要求简单,便于大批量生产。
Description
技术领域
本发明涉及伤口敷料技术领域,该伤口敷料用于造口、伤口等领域,尤其涉及一种含有芦荟凝胶的伤口敷料及其制备方法。
背景技术
压敏胶是一类具有对压力有敏感性的胶粘剂。主要用于制备压敏胶带。一般压敏胶的剥离力指胶粘带与被粘表面加压粘贴后所表现的剥离力;胶粘剂的内聚力指压敏胶分子之间的作用力;胶粘剂的粘基力指胶粘剂与基材之间的附着力。这样的压敏胶粘剂在使用过程中才不会有脱胶等现象的发生。压敏胶广泛以用于许多领域,比如用作标签,工业胶带,邮票,文具产品的组件,以及医疗产品,如胶带、造口产品、伤口护理产品和透气输送设备等。
芦荟的凝胶中含有环糊精复合物,有消炎,消肿,止痛,止痒及抑制细菌生长的效用,可作天然的治伤药用。目前,在一些造口产品及伤口护理产品使用时,大多都采用常规的医疗用品,治疗效果也有一定的疗效,但是对患者的所使用的伤口敷料对伤口治愈周期较长,吸臭特性和吸水性一般。
发明内容
本发明提供了一种含有芦荟凝胶的伤口敷料及其制备方法,以解决上述技术问题。
为了达到上述目的,本发明的技术方案是这样实现的:所述伤口敷料由以下重量百分比原料配制而成:其中高分子量聚异丁烯10-15%、低分子量聚异丁烯15-25%、交联羧甲基纤维素钠15-20%、刺梧桐胶5-7%、环糊精5-10%、芦荟凝胶2-8%、水杨酸1-3%、粉末香精0.1-2%、茶油2-5%、壳聚糖2-5%。
一种含有芦荟凝胶的伤口敷料的制备方法,包括如下步骤:
步骤一、打开密炼机电源,温度设置为140℃,待设备升温至140℃时,称取高分子量聚异丁烯和低分子量聚异丁烯放于密炼机中,先以温度140±10℃对橡胶进行加热10min,然后以150±10r/min速度边加热边搅拌15-30min,在搅拌过程中必须保持密炼机的为真空状态,直到橡胶变成均匀的熔融状态;
步骤二、称取交联羧甲基纤维素钠、刺梧桐胶、环糊精、水杨酸、壳聚糖及粉末香精,首先在容器中将环糊精和粉末香精混合均匀,然后加入其它粉末状的物料混合均匀,再称取芦荟凝胶、茶油,并在另外的容器中混合均匀;
步骤三、在温度140±10℃、转速为150±10r/min时,将混合好的粉料、液体物料分两次加入到密炼机中,且每次加入后正向搅拌15min、反向搅拌15min,直到变成均匀的胶体状态;
步骤四、将上述胶料倒出,冷却30min后,用硫化机或小型挤出机将其制备成不同厚度,不同规格的敷料样片。
优选的,所述步骤二中粉末状的物料分2次添加,同时分次加入芦荟凝胶、茶油两种液体物料。
与现有技术相比,本发明的有益效果在于:
本发明主要用于伤口敷料和造口底盘方面,原料加入了芦荟凝胶,环糊精成分,单独或与其它吸水性化合物联合使用,特别适合作为造口患者和伤口敷料的屏障粘合剂,可以吸收臭味,其中添加的香料含有香味成分的粘合剂对于掩盖皮肤上尿液和粪便引起的不良气味非常有用,但是香味会刺激皮肤,或者容易引起过敏反应,当香味与环糊精物质复合时,当环糊精变湿时,香味被释放,释放的量由水分进入的速率和量控制,这样潜在的刺激或过敏问题都会被最小化或消除。另外水杨酸,壳聚糖这类活性成分的加入,在产品使用过程中,可以将活性成分传递到皮肤表里,有助于保护皮肤。
该伤口敷料制备的产品具有良好的吸水性、初粘性、持粘性,当吸收渗液后产品具有很好的完整性,且从皮肤剥离时,不会刺激皮肤,在粘贴过程中,对皮肤有一定的修复功能,同时可以吸收渗液的异味,而且制作工艺简便易行,设备要求简单,便于大批量生产。
附图说明
无
具体实施方式
以下将对本发明实施例的技术方案进行清楚、完整的描述,显然,所描述的实施例仅仅是本发明的一部分实施例,而不是全部的实施例。基于本发明中的实施例,本领域普通技术人员在没有做出创造性劳动的前提下所得到的所有其它实施例,都属于本发明所保护的范围。
本发明涉及一种含有芦荟凝胶的伤口敷料,伤口敷料由以下重量百分比原料配制而成:其中高分子量聚异丁烯10-15%、低分子量聚异丁烯15-25%、交联羧甲基纤维素钠15-20%、刺梧桐胶5-7%、环糊精5-10%、芦荟凝胶2-8%、水杨酸1-3%、香料0.1-2%、茶油2-5%、壳聚糖2-5%。
一种含有芦荟凝胶的伤口敷料的制备方法,包括如下步骤:
步骤一、打开密炼机电源,温度设置为140℃,待设备升温至140℃时,称取高分子量聚异丁烯和低分子量聚异丁烯放于密炼机中,先以温度140±10℃对橡胶进行加热10min,然后以150±10r/min速度边加热边搅拌15-30min,在搅拌过程中必须保持密炼机的为真空状态,直到橡胶变成均匀的熔融状态;
步骤二、称取交联羧甲基纤维素钠、刺梧桐胶、环糊精、水杨酸、壳聚糖及粉末香精,首先在容器中将环糊精和粉末香精混合均匀,然后加入其它粉末状的物料混合均匀,再称取芦荟凝胶、茶油,并在另外的容器中混合均匀;
步骤三、在温度140±10℃、转速为150±10r/min时,将混合好的粉料、液体物料分两次加入到密炼机中,且每次加入后正向搅拌15min、反向搅拌15min,直到变成均匀的胶体状态;
步骤四、将上述胶料倒出,冷却30min后,用硫化机或小型挤出机将其制备成不同厚度,不同规格的敷料样片。
同时,在步骤二中粉末状的物料分2次添加,同时分次加入芦荟凝胶、茶油两种液体物料。
本发明伤口敷料能够吸收与体液和/或伤口相关的气味的粘合剂,以及具有改进的将活性成分传递到伤口或皮肤能力的粘合剂。同时,水胶体粘合剂是一种独特的医药用压敏胶粘合剂,具有双重属性,可以作为伤口敷料,也可以直接以用于开放性伤口,可以固定在周围完整的皮肤上,使皮肤保持正常的湿润状态,将对皮肤的刺激和损伤降到最低。
将芦荟凝胶溶解在合适的溶剂中,并分散在压敏胶粘合剂中,以形成两相体系,即以可控的方式释放芦荟中所含的环糊精。
同时,所添加的水杨酸、壳聚糖为活性成分,含有这种活性成分的水胶体可以被制成造口胶片,将活性成分传递到皮肤表里。
含有香精成分的粘合剂对于掩盖皮肤上尿液和粪便引起的不良气味非常有用,但是香味会刺激皮肤,或者容易引起过敏反应,当香味与环糊精物质复合时,当环糊精变湿时,香味被释放,释放的量由水分进入的速率和量控制,这样潜在的刺激或过敏问题都会被最小化或消除。
以上所述,仅是本发明的较佳实施例而已,并非对本发明作任何形式上的限制,任何熟悉本专业的技术人员,在不脱离本发明技术方案范围内,当可利用上述揭示的技术内容作出些许更动或修饰为等同变化的等效实施例,但凡是未脱离本发明技术方案的内容,依据本发明的技术实质对以上实施例所作的任何简单修改、等同变化与修饰,均仍属于本发明技术方案的范围内。
Claims (3)
1.一种含有芦荟凝胶的伤口敷料,其特征在于:所述伤口敷料由以下重量百分比原料配制而成:其中高分子量聚异丁烯10-15%、低分子量聚异丁烯15-25%、交联羧甲基纤维素钠15-20%、刺梧桐胶5-7%、环糊精5-10%、芦荟凝胶2-8%、水杨酸1-3%、粉末香精0.1-2%、茶油2-5%、壳聚糖2-5%。
2.一种含有芦荟凝胶的伤口敷料的制备方法,其特征在于:包括如下步骤:
步骤一、打开密炼机电源,温度设置为140℃,待设备升温至140℃时,称取高分子量聚异丁烯和低分子量聚异丁烯放于密炼机中,先以温度140±10℃对橡胶进行加热10min,然后以150±10r/min速度边加热边搅拌15-30min,在搅拌过程中必须保持密炼机的为真空状态,直到橡胶变成均匀的熔融状态;
步骤二、称取交联羧甲基纤维素钠、刺梧桐胶、环糊精、水杨酸、壳聚糖及粉末香精,首先在容器中将环糊精和粉末香精混合均匀,然后加入其它粉末状的物料混合均匀,再称取芦荟凝胶、茶油,并在另外的容器中混合均匀;
步骤三、在温度140±10℃、转速为150±10r/min时,将混合好的粉料、液体物料分两次加入到密炼机中,且每次加入后正向搅拌15min、反向搅拌15min,直到变成均匀的胶体状态;
步骤四、将上述胶料倒出,冷却30min后,用硫化机或小型挤出机将其制备成不同厚度,不同规格的敷料样片。
3.根据权利要求2所述一种含有芦荟凝胶的伤口敷料的制备方法,其特征在于:所述步骤二中粉末状的物料分2次添加,同时分次加入芦荟凝胶、茶油两种液体物料。