CN114224874A - 理疗贴及其制备方法 - Google Patents
理疗贴及其制备方法 Download PDFInfo
- Publication number
- CN114224874A CN114224874A CN202111546207.5A CN202111546207A CN114224874A CN 114224874 A CN114224874 A CN 114224874A CN 202111546207 A CN202111546207 A CN 202111546207A CN 114224874 A CN114224874 A CN 114224874A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- physical therapy
- patch
- far infrared
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种理疗贴及其制备方法，涉及医疗技术领域。本发明提供的理疗贴主要由基材、固定带和治疗药物组成，该理疗贴本身不具粘性，采用固定带捆绑的方式进行固定，避免过敏反应的发生，减小对皮肤的伤害；基材上涂覆有特定配比的治疗药物，其中不粘树脂用于负载其他组分，不具粘性，药效释放速率快；远红外陶瓷粉、磁粉和托玛琳粉按照特定的配比使用能够充分发挥三者间的协同促进作用，有利于理疗贴中热能、磁能及多种人体所需的微量元素的有效发挥。本发明的理疗贴使用舒适，不易过敏，药效快且持久，可重复使用，具有疏通经络、消肿止痛、温经散寒的作用，能够提高人体抗病能力，易于被人群接受。
Description
技术领域
本发明涉及医疗技术领域，尤其是涉及一种理疗贴及其制备方法。
背景技术
随着现代社会的快节奏生活，多数工作人群在繁忙的工作环境和社会压力下，缺乏有效的锻炼、久坐不动，造成的肩颈疾病、关节疾病，严重影响人们的生活健康。在此情况下，多数患者会寻求一些中医手段来缓解疼痛，例如贴敷膏药、理疗贴等，膏药虽然针对特定的病痛具有短暂的治疗，但是膏药外敷容易引起皮肤过敏，皮肤刺激大，不是长期选择，并且由于其粘贴和剥离的形式，对患者皮肤也存在一定的损伤。
理疗贴是通过热敷局部机体组织进而产生热量，通过热量渗透到局部身体，进而起到活血化瘀、散瘀止痛的功效，临床上适用于外感风寒或者感受寒邪等导致的咳嗽、咳喘以及上呼吸道感染等疾病；也可应用于乘凉、饮冷或者吹空调等导致脐部着凉引起腹痛、腹胀等症状偏属于寒邪者；还可以用于感受寒邪或者风湿等引起的全身疼痛，包括肩周炎、颈肩疼痛等症状。然而，现在技术中的理疗贴具有粘性，药效达不到充分有效发挥，恒温时间短，需要经常的更换。并且理疗贴同样是采用粘贴和剥离的形式进行治疗，容易引起皮肤过敏，对患者皮肤存在一定的损伤。
有鉴于此，特提出本发明。
发明内容
本发明的第一目的在于提供一种理疗贴，该理疗贴不具粘性，以固定带的方式进行固定，恒温时间长，药效释放快，可重复使用，以解决现有治疗产品易过敏、无法多次使用的技术问题，能够解决上述问题中的至少一种。
本发明的第二目的在于提供上述理疗贴的制备方法，该方法简单方便，成本低，容易操作。
第一方面，本发明提供了一种理疗贴，主要由基材、固定带和治疗药物组成，所述固定带用于基材的固定；所述治疗药物涂布于基材上；
所述治疗药物包括按质量份数计的如下组分：不粘树脂50-70份、远红外陶瓷粉10-20份、磁粉10-20份、托玛琳粉10-20份和渗透剂0.5-5份。
作为进一步技术方案，所述治疗药物包括按质量份数计的如下组分：不粘树脂55-65份、远红外陶瓷粉12-18份、磁粉12-18份、托玛琳粉12-18份和渗透剂1-5份。
作为进一步技术方案，所述治疗药物包括按质量份数计的如下组分：不粘树脂58-62份、远红外陶瓷粉13-17份、磁粉13-17份、托玛琳粉13-17份和渗透剂1-4份。
作为进一步技术方案，所述不粘树脂包括热熔压敏胶；
优选地，所述不粘树脂的粘度值在100mPa·s以内。
作为进一步技术方案，所述基材包括无纺布。
作为进一步技术方案，所述固定带包括绷带。
作为进一步技术方案，所述基材上治疗药物的涂布量为700-900g/m2，优选为750-850g/m2。
第二方面，本发明提供了一种理疗贴的制备方法，包括如下步骤：
将远红外陶瓷粉、磁粉、托玛琳粉和渗透剂加水调制成糊状，然后与加热至熔化的不粘树脂混合得到治疗药剂，再将治疗药剂涂布于基材上，连接固定带后制备得到所述理疗贴。
作为进一步技术方案，所述不粘树脂加热至融化的温度为140-170℃。
作为进一步技术方案，将所述治疗药剂的温度降低至140℃以下进行涂布。
与现有技术相比，本发明具有如下有益效果：
本发明提供的理疗贴主要由基材、固定带和治疗药物组成，该理疗贴本身不具粘性，采用固定带捆绑的方式进行固定，避免过敏反应的发生，减小对皮肤的伤害；基材上涂覆有特定配比的治疗药物，其中不粘树脂用于负载其他组分，不具粘性，药效释放速率快；远红外陶瓷粉能够辐射出红外光，可以引起人体细胞的原子和分子的共振，促进皮下深层温度上升，并使微血管扩张，加速血液循环，促进组织更新；磁粉产生的磁场能够调节体内生物磁场，舒张血管，加速血流，达到消肿止痛的作用；托玛琳粉具有压电效应和热电效应，能够释放负离子，促进细胞新陈代谢，加速人体机能恢复，本发明将远红外陶瓷粉、磁粉和托玛琳粉按照特定的配比使用能够充分发挥三者间的协同促进作用，有利于理疗贴中热能、磁能及多种人体所需的微量元素的有效发挥。本发明的理疗贴使用舒适，不易过敏，药效快且持久，可重复使用，具有疏通经络、消肿止痛、温经散寒的作用，能够提高人体抗病能力，易于被人群接受。
附图说明
为了更清楚地说明本发明具体实施方式或现有技术中的技术方案，下面将对具体实施方式或现有技术描述中所需要使用的附图作简单地介绍，显而易见地，下面描述中的附图是本发明的一些实施方式，对于本领域普通技术人员来讲，在不付出创造性劳动的前提下，还可以根据这些附图获得其他的附图。
图1为本发明实施例1提供的理疗贴。
具体实施方式
下面将结合实施方式和实施例对本发明的实施方案进行详细描述，但是本领域技术人员将会理解，下列实施方式和实施例仅用于说明本发明，而不应视为限制本发明的范围。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。未注明具体条件者，按照常规条件或制造商建议的条件进行。所用试剂或仪器未注明生产厂商者，均为可以通过市售购买获得的常规产品。
第一方面，本发明提供了一种理疗贴，主要由基材、固定带和治疗药物组成，所述固定带用于基材的固定；所述治疗药物涂布于基材上；
所述治疗药物包括按质量份数计的如下组分：不粘树脂50-70份、远红外陶瓷粉10-20份、磁粉10-20份、托玛琳粉10-20份和渗透剂0.5-5份。
其中，不粘树脂用于负载其他组分，不粘树脂的粘度值在100mPa·s以内，药效释放速率快，本发明中不粘树脂的质量份数例如可以为，但不限于50份、52份、54份、56份、58份、60份、62份、64份、66份、68份或70份。
远红外陶瓷粉能够发出远红外线，远红外线作用于人体能够迅速地被人体皮肤组织吸收，从而引起组成人体细胞的原子和分子的共振，形成热效应，促使皮肤和皮下组织的温度上升，并使重金属粒子、食品中的有毒物质、引起疲劳和老化的乳酸、游离脂肪酸、皮下脂肪、导致高血压的钠离子、以及导致疼痛的尿酸等等妨碍新陈代谢的障碍全部清除，重新使组织复活。另外，皮肤腺活化后，积存在毛细血管孔中的外来残余物，就能够不必经过肾脏，而直接从皮肤和汗水一起排出体外，可避免增加肾脏负担。所以远红外线对于血液循环和微循环障碍引起的多种疾病均具有改善和防治作用。本发明中远红外陶瓷粉的质量份数例如可以为，但不限于10份、12份、14份、16份、18份或20份。
磁粉具有磁场，作用于人体能够影响人体电流分布、荷电微粒的运动、膜系统的通透性等，使组织细胞的生理、生化过程改变，产生镇痛、消肿、促进血液循环等作用。本发明中磁粉的质量份数例如可以为，但不限于10份、12份、14份、16份、18份或20份。
托玛琳可以促进人体的新陈代谢，调节中枢神经系统的功能；可以促进血液循环，对于微循环障碍的患者具有很好的治疗作用；可以调节人体的酸碱平衡，具有净化血液和清除人体内的自由基的功能；以及可以增强人体的抗病能力。本发明中托玛琳粉的质量份数例如可以为，但不限于10份、12份、14份、16份、18份或20份。
本发明中渗透剂包括氮铜、二甲基亚砜、薄荷等，渗透剂的质量份数例如可以为，但不限于0.5份、1份、1.5份、2份、2.5份、3份、3.5份、4份、4.5份或5份。
本发明的理疗贴结合了当代中医理论及先进科技医学，集光学、热学、治疗技能于一体，是一种非粘贴式透皮吸收产品，通过增压感知肌肤热能后，释放出远红外光线，引起人体细胞的原子和分子的共振，进而活化人体细胞，疾速透皮，能够更有效地释放产品中的热能、磁能及多种人体所需微量元素，从而将产品中的矿物质及微量元素快速功效于患处，阻断制痛介质合成，达到疏通经络、消肿止痛、温经散寒的作用，避免了内服药物的毒副作用，克制了一般透皮产品吸收艰难、易过敏的难题，本发明提供的理疗贴本身不具有粘度，可重复使用，有助于节省治疗费用，易被人群接受。
在一些优选的实施方式中，所述治疗药物包括按质量份数计的如下组分：不粘树脂55-65份、远红外陶瓷粉12-18份、磁粉12-18份、托玛琳粉12-18份和渗透剂1-5份。
在一些优选的实施方式中，所述治疗药物包括按质量份数计的如下组分：不粘树脂58-62份、远红外陶瓷粉13-17份、磁粉13-17份、托玛琳粉13-17份和渗透剂1-4份。
通过对治疗药物中各个组分的进一步优化和调整，充分发挥各个组分间的配合作用，提高理疗贴中热能、磁能及多种人体所需的微量元素的有效发挥。
在一些优选的实施方式中，所述不粘树脂包括热熔压敏胶，本发明对于不粘树脂的种类不做具体限制，以非粘贴式的方式使用热熔压敏胶不易过敏，优选采用不粘的热熔压敏胶。
优选地，所述不粘树脂的粘度值在100mPa·s以内。
在一些优选的实施方式中，所述基材包括但不限于无纺布，或者本领域技术人员所熟知的其他能够用于承载药物的基材。
在一些优选的实施方式中，所述固定带包括但不限于绷带，或者本领域技术人员所熟知的其他能够用于固定基材的固定带。
在一些优选的实施方式中，所述基材上治疗药物的涂布量为700-900g/m2，例如可以为，但不限于700g/m2、740g/m2、780g/m2、820g/m2、860g/m2或900g/m2，优选为750-850g/m2。
通过对治疗药物涂布量的进一步优化和调整，充分发挥药物的药效，避免浪费。
第二方面，本发明提供了一种理疗贴的制备方法，包括如下步骤：
将远红外陶瓷粉、磁粉、托玛琳粉和渗透剂加水调制成糊状，然后与加热至熔化的不粘树脂混合得到治疗药剂，再将治疗药剂涂布于基材上，连接固定带后制备得到所述理疗贴。
直接添加远红外陶瓷粉、磁粉、托玛琳粉和渗透剂不易于与树脂充分混溶，加水后粉末与树脂易于充分混溶。
本发明的制备方法简单方便，成本低，容易操作。
在一些优选的实施方式中，所述不粘树脂加热至融化的温度为140-170℃，例如可以为，但不限于140℃、150℃、160℃或170℃。将不粘树脂充分融化，有利于其与治疗药物的充分混合。
在一些优选的实施方式中，将所述治疗药剂的温度降低至140℃以下进行涂布。
下面通过具体的实施例和对比例进一步说明本发明，但是，应当理解为，这些实施例仅仅是用于更详细地说明之用，而不应理解为用于以任何形式限制本发明。
实施例1
一种理疗贴，如图1所示，由涂布有治疗药物的基材和绷带组成，绷带与基材相连，用于基材的固定，治疗药物为：不粘树脂70份、远红外陶瓷粉10份、磁粉20份、托玛琳粉10份和渗透剂5份。
其中，不粘树脂为热熔压敏胶，粘度值＜100mpa·s。
制备方法如下：
1.将不粘树脂加入带自动控温搅拌釜中开始升温(温度的设置140--170)℃，直至树脂全部熔化。
2.在树脂熔化期间将定量的远红外陶瓷粉、磁粉、托玛琳粉和渗透剂放入容器中用水调成糊状备用。
3.当树脂全部熔融后将上述糊状物缓慢加入树脂中并不断搅拌，搅拌频率(10-25)赫兹。
4.当全部添加完毕后观察搅拌釜直至搅拌均匀。
5.开始涂布，将搅拌釜的温度降至140℃以下并将搅拌釜搅拌开关置于放料位置开始放料涂布，涂布厚度控制在700-900g/m2。
6.涂布完成后根据所需规格冲切、包装。
实施例2
一种理疗贴，与实施例1的区别在于治疗药物为：不粘树脂50份、远红外陶瓷粉20份、磁粉10份、托玛琳粉20份和渗透剂0.5份。
实施例3
一种理疗贴，与实施例1的区别在于治疗药物为：不粘树脂60份、远红外陶瓷粉15份、磁粉15份、托玛琳粉15份和渗透剂3份。
对比例1
一种理疗贴，与实施例3的区别在于采用粘性树脂，制备得到的理疗贴的粘合力为3.56±0.41N/cm。
其中，粘性树脂为热熔压敏胶，粘度值为2500～5000mpa·s。
对比例2
一种理疗贴，与实施例3的区别在于采用粘性树脂，制备得到的理疗贴的粘合力为3.44±0.67N/cm。
其中，粘性树脂为热熔压敏胶，粘度值为100～2500mpa·s。
对比例3
一种理疗贴，与实施例3的区别在于采用粘性树脂，制备得到的理疗贴的粘合力为2.89±0.42N/cm。
其中，粘性树脂为热熔压敏胶，粘度值为＞5000mpa·s。
对比例4
一种理疗贴，与实施例3的区别在于治疗药物为：不粘树脂60份、托玛琳粉45份和渗透剂3份。
对比例5
一种理疗贴，与实施例3的区别在于治疗药物为：不粘树脂60份、远红外陶瓷粉45份和渗透剂3份。
对比例6
一种理疗贴，与实施例3的区别在于治疗药物为：不粘树脂60份、磁粉45份和渗透剂3份。
对比例7
一种理疗贴，与实施例3的区别在于治疗药物为：不粘树脂60份、远红外陶瓷粉22份、托玛琳粉23份和渗透剂3份。
对比例8
一种理疗贴，与实施例3的区别在于治疗药物为：不粘树脂60份、磁粉22份、托玛琳粉23份和渗透剂3份。
对比例9
一种理疗贴，与实施例3的区别在于治疗药物为：不粘树脂60份、远红外陶瓷粉22份、磁粉23份和渗透剂3份。
对比例10
一种理疗贴，与实施例3的区别在于治疗药物为：不粘树脂60份、远红外陶瓷粉16份、磁粉16份和托玛琳粉16份。
对比例11
一种理疗贴，与实施例3的区别在于，将不粘树脂替换为粘性树脂，粘性树脂为热熔压敏胶，粘度值为＞5000mpa·s。
试验例1粘合力测试
以实施例3和对比例1-3的理疗贴作为供试品，将供试品的树脂层与洁净的不锈钢板粘结，然后用压辊(2000±50)g在供试品上以300mm/min的速度回滚一次，已确定粘结处无气泡存在。供试品粘贴后，在室温下放置20-40min后进行剥离试验，以水平(600±20)mm/min的速度进行剥离，剥离过程中记录剥离试验机上的读数，结果如表1所示。
试验例2释放速率测试
以实施例3和对比例1-3的理疗贴作为供试品，实验使用TK-12型透皮扩散试验机进行试验，单室扩散池的扩散面积为2.8cm2，接受体积为6.8ml，磁力搅拌速度为300r/min，(37±1)℃恒温水浴，接受液为60％的乙醇溶液，开启上述仪器，将供试品放入接受池上，分别取出1、2、3、4释放介质4ml，用分光光度法测试介质的浓度并计算释放速率。
表1理疗贴中有效成分的释放速率
| 粘度值mpa·s | 粘合力N.cm<sup>-1</sup> | 释放速率μg.cm<sup>-2</sup>.g<sup>-1/2</sup> | |
| 实施例1 | ＜100 | 0.00018 | 353.76±5 |
| 对比例1 | 2500～5000 | 3.44±0.67 | 135.98±7.00 |
| 对比例2 | 100～2500 | 2.89±0.42 | 219.56±1.72 |
| 对比例3 | ＞5000 | 3.56±0.41 | 78.91±6.39 |
从表1的结果中可看出，理疗贴的粘合力越小，有效物质的释放速率越快，而本发明提供的理疗贴为不粘型理疗贴，有助于有效物质的释放。
试验例3
选取年龄在35-55岁的志愿者30人，随机分成2组，每组15人，分别使用实施例3和对比例11提供的理疗贴，分别记录每名志愿者使用过程中的反应，实验结果如表2所示。
表2实施例3和对比例11提供的理疗贴的使用结果
由表2可看出：
本发明提供的理疗贴10分钟后3人有感觉30分钟后15人全部有感觉55分钟后热加强持续120分钟后达到舒适。
对比例11提供的理疗贴20分钟后3人有感觉60分钟后只有9人热加强，480分钟后只有6人感觉舒适，420分钟后2人没感觉，1人20分钟后有凉感一直持续到480分钟，其中2人整个480分钟没感觉。
由此看出本发明提供的理疗贴的释放速度快，包裹小，能达到预期效果。
试验例4
选取年龄在35-55岁的志愿者70人，随机分成7组，每组10人，分别使用实施例3和对比例4-9提供的理疗贴，分别记录每名志愿者使用过程中的反应，实验结果如表2所示。
表3实施例3和对比例4-9提供的理疗贴的使用结果
试验例5
选取年龄在35-55岁的志愿者20人，随机分成2组，每组10人，分别使用实施例3和对比例10提供的理疗贴，分别记录每名志愿者使用过程中的反应，实验结果如表4所示。
表4实施例3和对比例10提供的理疗贴的使用结果
从上述结果中可以看出，将远红外陶瓷粉、磁粉和托玛琳粉按照特定的配比使用能够充分发挥三者间的协同促进作用，有利于理疗贴中热能、磁能及多种人体所需的微量元素的有效发挥。相较于单个组分或者仅两种组分的效果更好。
最后应说明的是：以上各实施例仅用以说明本发明的技术方案，而非对其限制；尽管参照前述各实施例对本发明进行了详细的说明，本领域的普通技术人员应当理解：其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分或者全部技术特征进行等同替换；而这些修改或者替换，并不使相应技术方案的本质脱离本发明各实施例技术方案的范围。
Claims (10)
1.一种理疗贴，其特征在于，主要由基材、固定带和治疗药物组成，所述固定带用于基材的固定；所述治疗药物涂布于基材上；
所述治疗药物包括按质量份数计的如下组分：不粘树脂50-70份、远红外陶瓷粉10-20份、磁粉10-20份、托玛琳粉10-20份和渗透剂0.5-5份。
2.根据权利要求1所述的理疗贴，其特征在于，所述治疗药物包括按质量份数计的如下组分：不粘树脂55-65份、远红外陶瓷粉12-18份、磁粉12-18份、托玛琳粉12-18份和渗透剂1-5份。
3.根据权利要求2所述的理疗贴，其特征在于，所述治疗药物包括按质量份数计的如下组分：不粘树脂58-62份、远红外陶瓷粉13-17份、磁粉13-17份、托玛琳粉13-17份和渗透剂1-4份。
4.根据权利要求1所述的理疗贴，其特征在于，所述不粘树脂包括热熔压敏胶；
优选地，所述不粘树脂的粘度值在100mPa·s以内。
5.根据权利要求1所述的理疗贴，其特征在于，所述基材包括无纺布。
6.根据权利要求1所述的理疗贴，其特征在于，所述固定带包括绷带。
7.根据权利要求1所述的理疗贴，其特征在于，所述基材上治疗药物的涂布量为700-900g/m2，优选为750-850g/m2。
8.根据权利要求1-7任一项所述的理疗贴的制备方法，其特征在于，包括如下步骤：
将远红外陶瓷粉、磁粉、托玛琳粉和渗透剂加水调制成糊状，然后与加热至熔化的不粘树脂混合得到治疗药剂，再将治疗药剂涂布于基材上，连接固定带后制备得到所述理疗贴。
9.根据权利要求8所述的理疗贴的制备方法，其特征在于，所述不粘树脂加热至融化的温度为140-170℃。
10.根据权利要求8所述的理疗贴的制备方法，其特征在于，将所述治疗药剂的温度降低至140℃以下进行涂布。