CN114102778A - 木质纤维疏解剂、制备方法及应用方法 - Google Patents
木质纤维疏解剂、制备方法及应用方法 Download PDFInfo
- Publication number
- CN114102778A CN114102778A CN202111257822.4A CN202111257822A CN114102778A CN 114102778 A CN114102778 A CN 114102778A CN 202111257822 A CN202111257822 A CN 202111257822A CN 114102778 A CN114102778 A CN 114102778A
- Authority
- CN
- China
- Prior art keywords
- wood fiber
- potassium
- wood
- calcium oxide
- fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种木质纤维疏解剂、制备方法及应用方法,本发明所指的制取木质纤维的原料,是指自然界含有纤维素的植物,包括各种木材和非木材植物;本发明的组份质量百分比为:氧化钾15%;氢氧化钾15%;碳酸钾15%;硅酸钾4%;氧化钙1%;软水占比为50%;木质纤维松软剂的制备方法包括以下步骤:反应罐中先注入软水,然后将氧化钙加入反应罐中,边加边搅拌;依次将氧化钾、氢氧化钾和碳酸钾分别加入反应好的氧化钙溶液中;将硅酸钾添加至上述溶液中,搅拌均匀后冷却至常温。本发明木质纤维疏解剂的制备方法,制成的木质纤维质地柔软,色泽明亮,可塑性好,方便于后续产业的深加工制造及应用;脱除木素的比例高,便于后续产业的深加工制造及应用。
Description
技术领域
本发明涉及木质纤维技术领域,具体的说,是涉及一种木质纤维疏解剂的制备方法。
背景技术
随着需求多样化和科技的发展,可再生资源正越来越受到人们的重视,用途也愈来愈广泛。木质纤维经化学方法、生物方法配合物理加工再生制成再生纤维,既可用于纺织、家庭、装饰、包装等行业,利用它的保温、柔软、可塑、吸附、填充、环保性;也可以用于混凝土砂浆、石膏制品、木质海绵、沥青道路,保证了生产的稳定性和施工的合易性,增加强度及表面的附着力,防止涂层开裂,提高保水性;还可以作为新型环保的绿植喷播覆盖物,在自干的过程中相互锁定形成网状结构的覆盖面,与土壤表面有效粘结,很好地削减雨水冲刷力,增强水土和肥料流失保护力,同时还可以改善土壤的透气性。
木质纤维的开发正越来越受到人们的重视。生产木质纤维的方法很多,有化学法、生物法、物理法、爆破法等。各种方法都各有利弊,其中化学物理法最多。由于传统的化学物理法用氢氧化钠进行处理,溶出物中含有氢氧化钠造成十分严重的污染。采用氢氧化钠回收设备造价高,投资大,流程长,运行复杂,因此大大限制了中小型木质纤维生产厂家的正常运营。
发明内容
针对上述现有技术中的不足,本发明提供一种生产木质纤维疏解剂的制备方法。用该木质纤维疏解剂制备的木质纤维质地柔软,色泽明亮,可塑性好,方便于后续产业的深加工制造及应用。
本发明制取木质纤维的原料,是指自然界含有纤维素的植物,包括各种木材和非木材(竹子、芦苇、棉、麻、甘蔗、秸秆、草类等)植物。
本发明所采取的技术方案是:
一种木质纤维疏解剂,包括以下质量百分比的组份:
氧化钾 15%;
氢氧化钾 15%;
碳酸钾 15%;
硅酸钾 4%;
氧化钙 1%;
软水占比为 50%。
一种木质纤维松软剂的制备方法,包括以下步骤:
(1)反应罐中先注入软水,然后将氧化钙加入反应罐中,边加边搅拌,使之充分反应;
(2)再依次将氧化钾、氢氧化钾和碳酸钾分别加入反应好的氧化钙溶液中,搅拌均匀;
(3)最后将硅酸钾添加至上述溶液中,搅拌均匀后冷却至常温。
一种木质纤维松软剂的应用方法,包括以下步骤:
(1)洗涤疏解阶段:所用材料为竹片,竹片经水力洗涤机洗涤后进入连续蒸煮器,纤维疏解剂则通过计量泵泵入蒸煮器喷洒于竹片表面,纤维疏解剂质量为竹片质量的8%;通过螺旋叶片的推送作用,带动竹片与疏解剂均匀混合,蒸煮器温度维持在85~90℃,恒温保持45~47min;
(2)挤压磨解阶段:后经螺旋输送机推送进入螺旋挤压机挤压,再经高浓度盘磨磨解后即得所需木质纤维。
一种木质纤维疏解剂,包括以下质量百分比的组份:
氧化钾 15%;
氢氧化钾 20%;
碳酸钾 10%;
硅酸钾 4.5%;
氧化钙 0.5%;
软水占比为 50%。
一种木质纤维松软剂的制备方法,包括以下步骤:
(1)反应罐中先注入软水,然后将氧化钙加入反应罐中,边加边搅拌,使之充分反应;
(2)再依次将氧化钾、氢氧化钾和碳酸钾分别加入反应好的氧化钙溶液中,搅拌均匀;
(3)最后将硅酸钾添加至上述溶液中,搅拌均匀后冷却至常温。
一种木质纤维松软剂的应用方法,包括以下步骤:
(1)洗涤疏解阶段:所用材料为木片,木片经水力洗涤机洗涤后进入连续蒸煮器,纤维疏解剂则通过计量泵泵入蒸煮器喷洒于木片表面,纤维疏解剂质量为木片质量的20%;
通过螺旋叶片的推送作用,带动木片与疏解剂均匀混合,蒸煮器温度维持在95~100℃,恒温保持48~50min;
(2)挤压磨解阶段:后经螺旋输送机推送进入螺旋挤压机挤压,再经高浓度盘磨磨解后即得所需木质纤维。
本发明相对现有技术的有益效果:
本发明木质纤维疏解剂的制备方法,制成的木质纤维质地柔软,色泽明亮,可塑性好,方便于后续产业的深加工制造及应用;脱除木素的比例高,便于后续产业的深加工制造及应用;木质纤维疏解剂处理植物纤维后,溶出物中含有钾、钙元素,方便下一步的废液的处理及深加工。
具体实施方式
以下实施例对本发明进行详细的说明:
一种木质纤维疏解剂,包括以下质量百分比的组份:
氧化钾 15%;
氢氧化钾 15%;
碳酸钾 15%;
硅酸钾 4%;
氧化钙 1%;
软水占比为 50%。
一种木质纤维松软剂的制备方法,包括以下步骤:
(1)反应罐中先注入软水,然后将氧化钙加入反应罐中,边加边搅拌,使之充分反应;
(2)再依次将氧化钾、氢氧化钾和碳酸钾分别加入反应好的氧化钙溶液中,搅拌均匀;
(3)最后将硅酸钾添加至上述溶液中,搅拌均匀后冷却至常温。即得木质纤维疏解剂。
一种木质纤维松软剂的应用方法,包括以下步骤:
(1)洗涤疏解阶段:所用材料为木片,木片经水力洗涤机洗涤后进入连续蒸煮器,纤维疏解剂则通过计量泵泵入蒸煮器喷洒于木片表面,纤维疏解剂质量为木片质量的8%;通过螺旋叶片的推送作用,带动木片与疏解剂均匀混合,蒸煮器温度维持在85~90℃,恒温保持45~47min;
(2)挤压磨解阶段:后经螺旋输送机推送进入螺旋挤压机挤压,再经高浓度盘磨磨解后即得所需木质纤维。
附表1,木片制得的木质纤维的性能特点
浆种 | 成品收取率(%) | 纤维长度(mm) | 游离度(CSF) |
木质纤维 | 90~93 | 2.0~2.5 | 400~700 |
一种木质纤维疏解剂,包括以下质量百分比的组份:
氧化钾 15%;
氢氧化钾 20%;
碳酸钾 10%;
硅酸钾 4.5%;
氧化钙 0.5%;
软水占比为 50%。
一种木质纤维松软剂的制备方法,包括以下步骤:
(1)反应罐中先注入软水,然后将氧化钙加入反应罐中,边加边搅拌,使之充分反应;
(2)再依次将氧化钾、氢氧化钾和碳酸钾分别加入反应好的氧化钙溶液中,搅拌均匀;
(3)最后将硅酸钾添加至上述溶液中,搅拌均匀后冷却至常温。即得木质纤维疏解剂。
一种木质纤维松软剂的应用方法,包括以下步骤:
(1)洗涤疏解阶段:所用材料为竹片,竹片经水力洗涤机洗涤后进入连续蒸煮器,纤维疏解剂则通过计量泵泵入蒸煮器喷洒于竹片表面,纤维疏解剂质量为竹片质量的20%;
通过螺旋叶片的推送作用,带动木片与疏解剂均匀混合,蒸煮器温度维持在95~100℃,恒温保持48~50min;
(2)挤压磨解阶段:后经螺旋输送机推送进入螺旋挤压机挤压,再经高浓度盘磨磨解后即得所需木质纤维。
附表1,竹片制得的木质纤维的性能特点
浆种 | 成品收取率(%) | 纤维长度(mm) | 游离度(CSF) |
木质纤维 | 80~82 | 1.5~2.8 | 200~370 |
本发明木质纤维疏解剂的制备方法,制成的木质纤维质地柔软,色泽明亮,可塑性好,方便于后续产业的深加工制造及应用;脱除木素的比例高,便于后续产业的深加工制造及应用;木质纤维疏解剂处理植物纤维后,溶出物中含有钾、钙元素,方便下一步的废液的处理及深加工。
以上所述,仅是本发明的较佳实施例而已,并非对本发明的结构作任何形式上的限制。凡是依据本发明的技术实质对以上实施例所作的任何简单修改、等同变化与修饰,均属于本发明的技术方案范围内。
Claims (6)
1.一种木质纤维疏解剂,其特征在于,包括以下质量百分比的组份:
氧化钾15%;
氢氧化钾15%;
碳酸钾15%;
硅酸钾4%;
氧化钙1%;
软水占比为50%。
2.一种权利要求1所述木质纤维松软剂的制备方法,其特征在于包括以下步骤:
(1)反应罐中先注入软水,然后将氧化钙加入反应罐中,边加边搅拌,使之充分反应;
(2)再依次将氧化钾、氢氧化钾和碳酸钾分别加入反应好的氧化钙溶液中,搅拌均匀;
(3)最后将硅酸钾添加至上述溶液中,搅拌均匀后冷却至常温。
3.一种权利要求2所述木质纤维松软剂的应用方法,其特征在于包括以下步骤:
(1)洗涤疏解阶段:所用材料为木片,木片经水力洗涤机洗涤后进入连续蒸煮器,纤维疏解剂则通过计量泵泵入蒸煮器喷洒于木片表面,纤维疏解剂质量为木片质量的8%;通过螺旋叶片的推送作用,带动木片与疏解剂均匀混合,蒸煮器温度维持在85~90℃,恒温保持45~47min;
(2)挤压磨解阶段:后经螺旋输送机推送进入螺旋挤压机挤压,再经高浓度盘磨磨解后即得所需木质纤维。
4.一种木质纤维疏解剂,其特征在于,包括以下质量百分比的组份:
氧化钾15%;
氢氧化钾20%;
碳酸钾10%;
硅酸钾4.5%;
氧化钙0.5%;
软水占比为50%。
5.一种权利要求4所述木质纤维松软剂的制备方法,其特征在于包括以下步骤:
(1)反应罐中先注入软水,然后将氧化钙加入反应罐中,边加边搅拌,使之充分反应;
(2)再依次将氧化钾、氢氧化钾和碳酸钾分别加入反应好的氧化钙溶液中,搅拌均匀;
(3)最后将硅酸钾添加至上述溶液中,搅拌均匀后冷却至常温。
6.一种权利要求4所述木质纤维松软剂的应用方法,其特征在于包括以下步骤:
(1)洗涤疏解阶段:所用材料为木片,木片经水力洗涤机洗涤后进入连续蒸煮器,纤维疏解剂则通过计量泵泵入蒸煮器喷洒于竹片表面,纤维疏解剂质量为木片质量的20%;
通过螺旋叶片的推送作用,带动木片与疏解剂均匀混合,蒸煮器温度维持在95~100℃,恒温保持48~50min;
(2)挤压磨解阶段:后经螺旋输送机推送进入螺旋挤压机挤压,再经高浓度盘磨磨解后即得所需木质纤维。