CN114086680B - 一种墙面隔音防火建筑材料及墙面设计结构 - Google Patents
一种墙面隔音防火建筑材料及墙面设计结构 Download PDFInfo
- Publication number
- CN114086680B CN114086680B CN202111445996.3A CN202111445996A CN114086680B CN 114086680 B CN114086680 B CN 114086680B CN 202111445996 A CN202111445996 A CN 202111445996A CN 114086680 B CN114086680 B CN 114086680B
- Authority
- CN
- China
- Prior art keywords
- sound
- wall
- groove
- building material
- fireproof
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种墙面隔音防火建筑材料及墙面设计结构,具体涉及建筑材料技术领域,本发明通过采用连接槽、连接框、密封软垫、挤压板、接触块、挤压球、支撑块、吸音槽、防护垫和隔板,连接更为稳定的同时保证连接处紧密,同时多个支撑块之间形成连续的波浪状结构,实现对噪音的多角度反射,在噪音被反射进入吸音槽内部后,更进一步实现对噪音的反射吸收,且隔板与吸音结构之间为分隔状态,在对声音起到吸收的同时增加声音在隔板和吸音结构间的反射程度,使本装置整体的组装过程顺利紧密的同时保证整体的防火和隔音性能更为理想,且本隔音防火建筑材料的墙面可以实现装配式安装,材料可以重复利用,可以避免材料的浪费,达到节省资源的目的。
Description
技术领域
本发明涉及建筑材料技术领域,更具体地说,本发明涉及一种墙面隔音防火建筑材料及墙面设计结构。
背景技术
国民整体生活水平的不断提升,其社会面临的诸多安全风险也逐渐显现,尤其是近年来较为高发的高层火灾事故。这种事故的出现一方面影响着人们的人身和财产安全,另一方面也直接体现出我国目前在这方面的相关机制的不成熟和不完善,因此对于该方面的深入研究是新型社会发展的必要因素和根据。所以要想最大化避免火灾事故带给人类的影响和损失,首先要从以下三点进行改进:第一,我国相关消防部门要起到带头作用,在完善消防机制和措施的同时,要加强对于火灾点的巡视和检查工作,尤其是高层建筑;第二,坚决抵制造成消防事故的因素的出现和发展,一旦发现,立即处理;第三,要定期通过举办或者组织相关消防安全的知识讲座或者培训来提升全民的消防预防意识和处理能力,以免使得在出现火灾情况时造成更大的伤亡。
建筑材料可分为结构材料、装饰材料和某些专用材料,结构材料包括木材、竹材、石材、水泥、混凝土、金属、砖瓦、陶瓷、玻璃、工程塑料、复合材料等,装饰材料包括各种涂料、油漆、镀层、贴面、各色瓷砖、具有特殊效果的玻璃等,专用材料指用于防水、防潮、防腐、防火、阻燃、隔音、隔热、保温、密封等,建筑材料需要具备较高的机械强度、如抗折强度和抗压强度,若其抗折强度也抗压强度较低,建筑材料的安全性能无法得到保障,除了机械强度外,建筑材料也需要具备较高的保温防火性能,防止发生火宅时建筑材料发生燃烧的现象,随着城市化的大力推进,住房问题关乎人民生活根本,良好、安全的居住环境越来越被人们渴求,只有居住安全、放心,人们才能更好的生活并工作;不仅如此,室内办公环境的好坏直接影响民众的工作效率;所以,寻求安全、安心的室内建筑成为人们的普遍诉求。对于建筑行业来说,建筑用材是一个至关重要的因素,只有用材性能好,安全,建筑才能被人们放心的使用。
建筑隔声是为改善建筑物室内声环境,隔离噪声等干扰而采取的措施,包括空气声隔声和结构隔声两个方面。所谓空气声,是指经空气传播或透过建筑构件传至室内的声音;如人们的谈笑声、收音机声、交通噪声等。所谓结构声,是指机电设备、地面或地下车辆以及打桩、楼板上的走动等所造成的振动,经地面或建筑构件传至室内而辐射出的声音。在建筑物内空气声和结构声是可以互相转化的。因为空气声的振动能够迫使构件产生振动成为结构声,而结构声辐射出声音时,也就成为空气声。减少空气声的传递要从减少或阻止空气的振动入手,而减少结构声的传递则必须采取隔振或阻尼的办法。
建筑材料是在建筑工程中所应用的各种材料。建筑材料种类繁多,大致分为:(1)无机材料,它包括金属材料(包括黑色金属材料和有色金属材料)和非金属材料(如天然石材、烧土制品、水泥、混凝土及硅酸盐制品等)。(2)有机材料,它包括植物质材料、合成高分子材料(包括塑料、涂料、粘胶剂)和沥青材料。(3)复合材料,它包括沥青混凝土、聚合物混凝土等,一般由无机非金属材料与有机材料复合而成。
近年来,为保护耕地、保护环境、节约能源,国家已经出台相关政策,将逐步禁止使用传统粘土烧结墙材;而在矿山领域,排放的矿山废渣量已达50~60亿t并且每年以3~4亿t的速度增长,这些固体废弃物的处理处置已成为许多矿山企业的沉重包袱,一旦处理处置不当,不仅会导致工程灾害加剧、资源浪费、环境污染,同时会给社会、经济、环境造成严重的危害;铁尾矿的堆存量最多,占全部尾矿堆存总量的近1/3。所以利用铁尾矿开发研究一种新型轻质建材,对于推动我国墙体材料的革新和尾矿的综合利用具有积极意义。
现有大量建筑采用可燃甚至是易燃的有机保温材料如聚苯板、挤塑板和聚氨酯等,其最大的缺陷是防火安全性差,易老化、易燃烧。
这些低耐火等级和耐火极限的产品推向市场后,为建筑火灾事故埋下先天性安全隐患,造成了巨大的生命财产损失。同时这些建筑节能的实现是以大量消耗能源和资源为代价的。现有外墙保温系统产品主要由高分子材料和水泥等组成,其中聚苯板和聚氨酯等有机保温材料,在生产过程还需要消耗大量的石化能源。因此,利用选矿尾矿制备建筑外墙防火陶瓷保温材料,把城市建筑节能发展和保护生态环境与选矿尾矿资源化综合利用有机结合起来,具有广阔发展前景。
在经济迅猛发展的社会背景下,建筑行业随之实现了快速的发展,各种高层、超高层建筑得以出现,虽然在一定程度上节省了居住用地,但同时也增加了消防安全防护的难度。建筑项目施工过程中涉及到众多材料的应用,而防火材料是必备材料之一,也是建设单位比较关注的一种应用材料。文中对各种建筑防火材料的应用进行了分别分析,经由分析可知防火材料对建筑领域具有重要应用价值,是确保建筑物符合消防安全等级的重要保障。
高分子防火材料是近几年建筑领域较长应用到的一种防火材料,其中较为常见的包括石膏、新型化工合成阻燃剂、金属板与符合金属板材料等。第一,石膏材料。石膏是当前建筑领域最常用的建筑材料,其特点在于水化速度快、凝结速度快等。石膏建筑材料的防火性能较好,但是比较容易受到渗水影响,从而降低防水性能。第二,新型化工合成阻燃剂。此种材料的特点是阻燃性能好、无毒、无味、无色透明等,对普通才给给予ZRY阻燃处理,有效的提升了阻燃效果,遇到火之后不会燃烧,能够抑制火焰的蔓延,避免火灾发生。第三,金属板与符合金属板材料。金属复合板也被称之为夹心板,表面两层为金属板,具有保温功能,其特点在于高刚度、低强度。
新型高分子轻质防火是近几年出现在市场上的一种建筑防火材料,较具有代表性的包括石棉与矿渣棉玻璃棉、硅酸铝纤维等。第一,石棉与矿渣棉。岩棉是天然岩石经过高温熔融制成的,由于其具有导热系数低与不燃等投点,可作为防火构件应用,同时也能够作为防火的隔热板材。第二,玻璃棉。玻璃棉是在岩棉后出现的全新隔热性能较好、容重轻的隔热保温材料。玻璃棉在建筑工程中应用具有着较好的隔热、隔冷、保温等优势。第三,硅酸铝纤维。硅酸铝纤维也被称之为陶瓷棉,是较为特殊的全新轻质耐火材料,能够作为防火门的芯材、吊顶板材等应用,从而达到隔火隔热效果。
混凝土板材与砌块加气均属于轻质高分子材料,其中混凝土是国内主要施工应用材料,应用较为广泛。加气化混凝土所指向的是在混凝土的基础上,融合存在钙元素的物质,与硅酸在发气剂的作用下支撑砌块或条状板材,其能够达到与混凝土同样的防火效果。混凝土板材与砌块加气等轻质化高分子材料能够作为称重结构的施工材料,应用此类型建筑材料到施工过程中,有助于强化建筑结构,且提升防火安全性。
如中国专利(申请号为:CN107700699B)公开了一种建筑墙板连接结构及其连接方法,包括墙板连接母头和墙板连接公头,墙板连接母头包括母头前侧连接板、母头后侧连接板和母头连接板,母头前侧连接板和母头后侧连接板平行设置连接在母头连接板两端构成工字型架板,工字型架板一侧为第一墙板连接口,工字型架板另一侧为连接件对接口,母头连接板上设有多层偏心轮轴装置,每层与母头前侧连接板和母头后侧连接板对应分别设有一套偏心轮轴装置,使用墙板通过插设在第二墙板连接口内实现与墙板连接公头一体连接;使用墙板通过插设在第一墙板连接口内实现与墙板连接母头一体连接,转动偏心轮轴装置使插头上的公头插板与连接件对接口上的母头前侧连接板和母头后侧连接板压紧牢固连接。
但是现有的装饰墙板自身在组装时相邻两结构之间组装存在明显的缝隙,甚至难以保证整体的稳定性,因此存在明显的结构上的隔音和防火性能缺点,同时隔音性能多是简单采用隔音板进行隔断声音传播,导致整体的隔音性能不够理想,因此需要一种墙面隔音防火建筑材料及墙面设计结构来解决上述问题。
发明内容
为了克服现有技术的上述缺陷,本发明提供了一种墙面隔音防火建筑材料及墙面设计结构,本发明所要解决的技术问题是:建筑表面会使用装饰墙板进行装饰,以提升美观性能或增加防护隔音性能,但是现有的装饰墙板自身在组装时相邻两结构之间组装存在明显的缝隙,甚至难以保证整体的稳定性,因此存在明显的结构上的隔音和防火性能缺点,同时隔音性能多是简单采用隔音板进行隔断声音传播,导致整体的隔音性能不够理想的问题。
为实现上述目的,本发明提供如下技术方案:一种墙面隔音防火建筑材料的墙面设计结构,包括组合框,所述组合框的背面开设有连接槽,所述连接槽内壁的左右两侧面均开设有密封槽,所述组合框的正面与连接框的背面固定连接,所述连接框内壁的左右两侧面均开设有凹槽,所述凹槽内壁设置有若干第一导向套,所述第一导向套内壁与第一移动杆的外表面滑动连接,相对两个所述第一移动杆的相对面分别与两个挤压球的相背面固定连接,两个所述挤压球的相对面分别与斜块的左右两侧面搭接。
所述斜块的正面与第二移动杆背面的一端固定连接,所述第二移动杆正面的一端与接触块的背面固定连接,所述第一移动杆的另一端与挤压板的外表面固定连接,所述挤压板的外表面与密封软垫的外表面搭接,所述密封软垫的外表面与凹槽内壁固定连接,所述组合框内壁与隔音防火组件的外表面固定连接。
作为本发明的进一步方案:所述第二移动杆的外表面与第二导向套内壁滑动连接,所述第二导向套与连接框内壁固定连接。
作为本发明的进一步方案:所述接触块设置为半球状,所述接触块的直径大于第二移动杆的直径。
作为本发明的进一步方案:所述密封软垫的尺寸小于凹槽的尺寸,所述接触块与第二导向套之间的距离大于斜块倾斜面的长度。
作为本发明的进一步方案:所述密封软垫的高度与密封槽的高度相同,所述密封槽设置为V形。
作为本发明的进一步方案:所述密封软垫的位置与密封槽的位置相对应,所述挤压板的形状设置为V形。
作为本发明的进一步方案:所述连接框的尺寸与连接槽的尺寸相对应,所述组合框采用泡沫铝制成。
作为本发明的进一步方案:所述隔音防火组件包括两个防护垫,两个所述防护垫的相对面均设置有吸音结构,两个所述吸音结构的相对面设置有同一隔板,所述吸音结构靠近防护垫的一面设置有若干支撑块,所述吸音结构靠近防护垫的一面开设有若干吸音槽。
作为本发明的进一步方案:所述吸音结构靠近隔板的一面设置有若干横支撑梁,所述吸音结构靠近隔板的一面设置有若干纵支撑梁。
作为本发明的进一步方案:所述防护垫、吸音结构、支撑块和隔板均采用隔音防火建筑材料制成。
一种墙面隔音防火建筑材料,所述隔音防火建筑材料包括以下重量组分:铁尾矿45-55份、氢氧化镁粉10-13份、阻燃剂11-13份、发泡剂1-1.5份、氧化铝8-12份、氧化硅8-12份和聚苯乙烯泡沫15-21份。
一种墙面隔音防火建筑材料,包括以下重量组分:铁尾矿48-52份、氢氧化镁粉11-12份、阻燃剂11-12份、发泡剂1-1.3份、氧化铝9-11份、氧化硅9-11份和聚苯乙烯泡沫16-20份。
一种墙面隔音防火建筑材料,包括以下重量组分:铁尾矿50份、氢氧化镁粉11份、阻燃剂11份、发泡剂1.2份、氧化铝10份、氧化硅10份和聚苯乙烯泡沫18份。
一种墙面隔音防火建筑材料的制备方法,包括以下步骤:
S1、首先称取配方量的上述组分,采用冲洗的方式对铁尾矿进行表面清洗,在铁尾矿完成干燥后,对铁尾矿进行均化处理,并将铁尾矿放入粉碎设备中,将其粉碎至7.45μm,发泡剂粒度为0.045mm,并将铁尾矿原料、氢氧化镁粉、氧化铝、氧化硅和聚苯乙烯泡沫加入搅拌器中,搅拌时间保持在45min-55min,搅拌速度保持在1000r/min;
S2、向S1中物料混合结束的搅拌器中加入阻燃剂和发泡剂,搅拌16min-20min,搅拌时温度保持在28-33℃之间,然后加入适量水进行搅拌,得到隔音防火建材基料;
S3、将S2中得到的基料注入成型模型中,并将模具放入加压设备中,然后将压制成型的建筑材料取出,并进行烘干处理,最后得到隔音防火建筑材料,随后将隔音防火建筑材料进行清洗和喷涂处理,将得到的隔音防火建筑材料进行包装。
本发明的另一目的在于提供一种墙面隔音防火建筑材料墙面设计结构的使用方法,包括以下步骤:
当需要对组合框进行组装时,首先将连接框对应连接槽的位置位置,同时推动组合框移动的同时带动连接框靠近连接槽移动,同时接触块带动第二移动杆移动,第二移动杆通过斜块挤压两挤压球移动,同时两挤压球带动第一移动杆和挤压板移动,此时挤压板对密封软垫进行挤压,同时密封软垫受压变形并进入密封槽内,密封软垫进入密封槽并紧密接触,此时完成对相邻两个组合框的连接。
本发明的有益效果在于:
1、本发明通过采用连接槽、连接框、密封软垫、挤压板、接触块、挤压球、斜块、支撑块、吸音槽、防护垫和隔板,连接框进入连接槽内部时,连接槽与接触块接触并进行挤压,此时第二移动杆带动斜块对挤压球进行挤压,此时两挤压球带动挤压板对密封软垫进行挤压,同时密封软垫变形进入密封槽内实现对连接槽与连接框之间连接处的密封,连接更为稳定的同时保证连接处紧密,同时多个支撑块之间形成连续的波浪状结构,实现对噪音的多角度反射,在噪音被反射进入吸音槽内部后,更进一步实现对噪音的反射吸收,增加声波在吸音结构表面的衰减程度,同时采用横支撑梁和纵支撑梁,对吸音结构整体起到支撑加强作用,且隔板与吸音结构之间为分隔状态,在对声音起到吸收的同时增加声音在隔板和吸音结构间的反射程度,使本装置整体的组装过程顺利紧密的同时保证整体的防火和隔音性能更为理想;
2、本发明通过采用氢氧化镁属于无机阻燃剂,阻燃机理是燃烧时释放出结合的水,同时也降低了有机材料的可燃性,成本低廉,增加产品的防火性能,采用铁尾矿作为建筑材料的主料,实现对废料的再次回收利用,节省能源的同时,做到资源的合理充分利用,通过加入聚苯乙烯泡沫,使得产品在具有保温效果的同时隔音性能更好。
附图说明
图1为本发明立体的结构示意图;
图2为本发明连接框立体的剖面结构示意图;
图3为本发明连接框俯视立体的剖面结构示意图;
图4为本发明隔音防火组件立体的内部结构示意图;
图5为本发明吸音结构立体的结构示意图;
图6为本发明吸音结构后视立体的结构示意图;
图中:1、组合框;2、连接槽;3、密封槽;4、连接框;5、凹槽;6、第一导向套;7、第一移动杆;8、挤压球;9、斜块;10、第二移动杆;11、接触块;12、第二导向套;13、密封软垫;14、挤压板;15、隔音防火组件;151、防护垫;152、吸音结构;1521、支撑块;1522、吸音槽;1523、横支撑梁;1524、纵支撑梁;153、隔板。
具体实施方式
下面将结合本发明实施例中的附图,对本发明实施例中的技术方案进行清楚、完整地描述,显然,所描述的实施例仅仅是本发明一部分实施例,而不是全部的实施例。基于本发明中的实施例,本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例,都属于本发明保护的范围。
如图1-6所示,本发明提供了一种墙面隔音防火建筑材料的墙面设计结构,包括组合框1,组合框1的背面开设有连接槽2,通过设置连接槽2,方便连接框4进入连接槽2实现多个组合框1之间的组装,连接槽2内壁的左右两侧面均开设有密封槽3,组合框1的正面与连接框4的背面固定连接,连接框4内壁的左右两侧面均开设有凹槽5,凹槽5内壁设置有若干第一导向套6,通过设置第一导向套6和第二导向套12,第一导向套6可对第一移动杆7的移动过程进行导向和支撑,保证挤压球8与斜块9的稳定顺利移动操作,第二导向套12可对第二移动杆10的移动起到支撑导向作用,保证在接触块11受压时可稳定控制第二移动杆10和斜块9的移动,第一导向套6内壁与第一移动杆7的外表面滑动连接,相对两个第一移动杆7的相对面分别与两个挤压球8的相背面固定连接,通过设置第一移动杆7、挤压球8和斜块9,在斜块9靠近挤压球8移动并推动挤压球8时,利用斜块9的斜面可挤压两挤压球8相互远离移动,实现自动控制两第一移动杆7和挤压板14对密封软垫13的挤压,两个挤压球8的相对面分别与斜块9的左右两侧面搭接。
斜块9的正面与第二移动杆10背面的一端固定连接,第二移动杆10正面的一端与接触块11的背面固定连接,第二移动杆10的外表面与第二导向套12内壁滑动连接,第二导向套12与连接框4内壁固定连接,第一移动杆7的另一端与挤压板14的外表面固定连接,挤压板14的外表面与密封软垫13的外表面搭接,密封软垫13的外表面与凹槽5内壁固定连接,组合框1内壁与隔音防火组件15的外表面固定连接,通过设置挤压板14,挤压板14在移动的同时可对密封软垫13进行挤压,控制密封软垫13变形与密封槽3紧密接触,同时挤压板14的形状与密封槽3形状相同,可对连接框4起到简单限位作用。
隔音防火组件15包括两个防护垫151,两个防护垫151的相对面均设置有吸音结构152,两个吸音结构152的相对面设置有同一隔板153,吸音结构152靠近防护垫151的一面设置有若干支撑块1521,吸音结构152靠近防护垫151的一面开设有若干吸音槽1522,吸音结构152靠近隔板153的一面设置有若干横支撑梁1523,吸音结构152靠近隔板153的一面设置有若干纵支撑梁1524,通过设置吸音槽1522和支撑块1521,吸音槽1522与支撑块1521组合形成连续的波浪状结构,实现对噪音的多次反射,同时噪音进入吸音槽1522后多次沿多种方向进行反射,使噪音的衰减速度更为充分量良好。
接触块11设置为半球状,接触块11的直径大于第二移动杆10的直径,密封软垫13的尺寸小于凹槽5的尺寸,接触块11与第二导向套12之间的距离大于斜块9倾斜面的长度,密封软垫13的高度与密封槽3的高度相同,密封槽3设置为V形。
如图1和图2所示,密封软垫13的位置与密封槽3的位置相对应,挤压板14的形状设置为V形,连接框4的尺寸与连接槽2的尺寸相对应,组合框1采用泡沫铝制成,通过采用泡沫铝,泡沫铝是在纯铝或铝合金中加入添加剂后,经过发泡工艺而成,同时兼有金属和气泡特征,它密度小、高吸收冲击能力强、耐高温、防火性能强、抗腐蚀、隔音降噪、导热率低、电磁屏蔽性高、耐候性强、有过滤能力、易加工、易安装、成形精度高、可进行表面涂装,泡沫铝具有优异的物理性能、化学性能和力学性能以及可回收性。
如图3和图4所示,防护垫151、吸音结构152、支撑块1521和隔板153均采用隔音防火建筑材料制成。
一种墙面隔音防火建筑材料,隔音防火建筑材料包括以下重量组分:铁尾矿45-55份、氢氧化镁粉10-13份、阻燃剂11-13份、发泡剂1-1.5份、氧化铝8-12份、氧化硅8-12份和聚苯乙烯泡沫15-21份。
一种墙面隔音防火建筑材料,包括以下重量组分:铁尾矿48-52份、氢氧化镁粉11-12份、阻燃剂11-12份、发泡剂1-1.3份、氧化铝9-11份、氧化硅9-11份和聚苯乙烯泡沫16-20份。
一种墙面隔音防火建筑材料,包括以下重量组分:铁尾矿50份、氢氧化镁粉11份、阻燃剂11份、发泡剂1.2份、氧化铝10份、氧化硅10份和聚苯乙烯泡沫18份。
一种墙面隔音防火建筑材料的制备方法,包括以下步骤:
S1、首先称取配方量的上述组分,采用冲洗的方式对铁尾矿进行表面清洗,在铁尾矿完成干燥后,对铁尾矿进行均化处理,并将铁尾矿放入粉碎设备中,将其粉碎至7.45μm,发泡剂粒度为0.045mm,并将铁尾矿原料、氢氧化镁粉、氧化铝、氧化硅和聚苯乙烯泡沫加入搅拌器中,搅拌时间保持在45min-55min,搅拌速度保持在1000r/min;
S2、向S1中物料混合结束的搅拌器中加入阻燃剂和发泡剂,搅拌16min-20min,搅拌时温度保持在28-33℃之间,然后加入适量水进行搅拌,得到隔音防火建材基料;
S3、将S2中得到的基料注入成型模型中,并将模具放入加压设备中,然后将压制成型的建筑材料取出,并进行烘干处理,最后得到隔音防火建筑材料,随后将隔音防火建筑材料进行清洗和喷涂处理,将得到的隔音防火建筑材料进行包装。
本发明工作原理:当需要对组合框1进行组装时,首先将连接框4对应连接槽2的位置位置,同时推动组合框1移动的同时带动连接框4靠近连接槽2移动,同时接触块11带动第二移动杆10移动,第二移动杆10通过斜块9挤压两挤压球8移动,同时两挤压球8带动第一移动杆7和挤压板14移动,此时挤压板14对密封软垫13进行挤压,同时密封软垫13受压变形并进入密封槽3内,密封软垫13进入密封槽3并紧密接触,此时完成对相邻两个组合框1的连接。
综上可得,本发明中:
本发明通过采用连接槽2、连接框4、密封软垫13、挤压板14、接触块11、挤压球8、斜块9、支撑块1521、吸音槽1522、防护垫151和隔板153,连接框4进入连接槽2内部时,连接槽2与接触块11接触并进行挤压,此时第二移动杆10带动斜块9对挤压球8进行挤压,此时两挤压球8带动挤压板14对密封软垫13进行挤压,同时密封软垫13变形进入密封槽3内实现对连接槽2与连接框4之间连接处的密封,连接更为稳定的同时保证连接处紧密,同时多个支撑块1521之间形成连续的波浪状结构,实现对噪音的多角度反射,在噪音被反射进入吸音槽1522内部后,更进一步实现对噪音的反射吸收,增加声波在吸音结构152表面的衰减程度,同时采用横支撑梁1523和纵支撑梁1524,对吸音结构152整体起到支撑加强作用,且隔板153与吸音结构152之间为分隔状态,在对声音起到吸收的同时增加声音在隔板153和吸音结构152间的反射程度,使本装置整体的组装过程顺利紧密的同时保证整体的防火和隔音性能更为理想;
本发明通过采用氢氧化镁属于无机阻燃剂,阻燃机理是燃烧时释放出结合的水,同时也降低了有机材料的可燃性,成本低廉,增加产品的防火性能,采用铁尾矿作为建筑材料的主料,实现对废料的再次回收利用,节省能源的同时,做到资源的合理充分利用,通过加入聚苯乙烯泡沫,使得产品在具有保温效果的同时隔音性能更好。
最后应说明的几点是:首先,在本申请的描述中,需要说明的是,除非另有规定和限定,术语“安装”、“相连”、“连接”应做广义理解,可以是机械连接或电连接,也可以是两个元件内部的连通,可以是直接相连,“上”、“下”、“左”、“右”等仅用于表示相对位置关系,当被描述对象的绝对位置改变,则相对位置关系可能发生改变;
其次:本发明公开实施例附图中,只涉及到与本公开实施例涉及到的结构,其他结构可参考通常设计,在不冲突情况下,本发明同一实施例及不同实施例可以相互组合;
最后:以上所述仅为本发明的优选实施例而已,并不用于限制本发明,凡在本发明的精神和原则之内,所作的任何修改、等同替换、改进等,均应包含在本发明的保护范围之内。
Claims (3)
1.一种墙面隔音防火建筑材料的墙面设计结构,包括组合框(1),其特征在于:所述组合框(1)的背面开设有连接槽(2),所述连接槽(2)内壁的左右两侧面均开设有密封槽(3),所述组合框(1)的正面与连接框(4)的背面固定连接,所述连接框(4)内壁的左右两侧面均开设有凹槽(5),所述凹槽(5)内壁设置有若干第一导向套(6),所述第一导向套(6)内壁与第一移动杆(7)的外表面滑动连接,相对两个所述第一移动杆(7)的相对面分别与两个挤压球(8)的相背面固定连接,两个所述挤压球(8)的相对面分别与斜块(9)的左右两侧面搭接;
所述斜块(9)的正面与第二移动杆(10)背面的一端固定连接,所述第二移动杆(10)正面的一端与接触块(11)的背面固定连接,所述第一移动杆(7)的另一端与挤压板(14)的外表面固定连接,所述挤压板(14)的外表面与密封软垫(13)的外表面搭接,所述密封软垫(13)的外表面与凹槽(5)内壁固定连接,所述组合框(1)内壁与隔音防火组件(15)的外表面固定连接;
所述密封软垫(13)的尺寸小于凹槽(5)的尺寸,所述接触块(11)与第二导向套(12)之间的距离大于斜块(9)倾斜面的长度,所述密封软垫(13)的高度与密封槽(3)的高度相同,所述密封槽(3)设置为V形,所述密封软垫(13)的位置与密封槽(3)的位置相对应,所述挤压板(14)的形状设置为V形,所述连接框(4)的尺寸与连接槽(2)的尺寸相对应,所述组合框(1)采用泡沫铝制成;
所述隔音防火组件(15)包括两个防护垫(151),两个所述防护垫(151)的相对面均设置有吸音结构(152),两个所述吸音结构(152)的相对面设置有同一隔板(153),所述吸音结构(152)靠近防护垫(151)的一面设置有若干支撑块(1521),所述吸音结构(152)靠近防护垫(151)的一面开设有若干吸音槽(1522),所述吸音结构(152)靠近隔板(153)的一面设置有若干横支撑梁(1523),所述吸音结构(152)靠近隔板(153)的一面设置有若干纵支撑梁(1524),所述防护垫(151)、吸音结构(152)、支撑块(1521)和隔板(153)均采用隔音防火建筑材料制成。
2.根据权利要求1所述的一种墙面隔音防火建筑材料的墙面设计结构,其特征在于:所述第二移动杆(10)的外表面与第二导向套(12)内壁滑动连接,所述第二导向套(12)与连接框(4)内壁固定连接。
3.根据权利要求1所述的一种墙面隔音防火建筑材料的墙面设计结构,其特征在于:所述接触块(11)设置为半球状,所述接触块(11)的直径大于第二移动杆(10)的直径。