Abstract

The present invention relates to a production process for decorative glass. Glass is used as a base plate, a protective film is pasted on the surface of the base plate, and a pattern is drawn on the protective film. The pattern is newly traced and engraved according to the line of the pattern. The protective film is taken off, and the base plate is ground into a black surface by carborundum. After the black surface is washed and dried, a liquid state protective film is coated on the black surface needing to be engraved, and an irregular pattern is drawn on the liquid state protective film. Firstly, the irregular pattern is dried under 60 to 90 DEG C, and the irregular pattern is engraved by high pressure carborundum; then, the base plate is placed into water to be soaked for 1 to 2 hours, the liquid state of the liquid state protective film which is dried is newly recovered; thirdly, the liquid state protective film is cleaned by a cleaning agent, and is dried under 40 to 60 DEG C, and glass luster increasing paint is sprayed on the engraved pattern. The present invention has the key point that the ornaments of artificial diamond, natural gemstone, artificial crystal, natural crystal, etc. can be glued in proper positions of the base plate by photographic glue through the irradiation of an ultraviolet light source according to requirements. The present invention can be widely applied to the elegant unique decoration of houses, scriptoriums, restaurants, etc.

Description

A kind of production technology of ambetti

(1) technical field

The invention belongs to the glassware field.

(2) technical background

U.S.A is one of human target of pursuing.Along with the raising of expanding economy and national life level, people are just stronger to the pursuit of U.S..No matter be ordinary residence, garden district, villa, or office room, market, restaurant are all carrying out the graceful unique or finishing that breaks fresh ground, to increase its aesthetic feeling.In various decorations, lack bound glass, the ambetti goods with aesthetic feeling will be for increasing many colors in the whole Decoration Design.But present ambetti goods are single flat glass pattern, lack stereovision, third dimension, color sense and beautiful feeling.

(3) summary of the invention

The invention provides a kind of production technology of ambetti, the glassware that this production technology is produced has artistic effect lucuriant in design, that third dimension is strong.

The technical scheme that adopts

A kind of ambetti comprises substrate, and substrate is a glass, the multiple pattern with aesthetic feeling of processing and fabricating on the substrate, and the intrinsic a plurality of ornaments of glue.

Above-mentioned ornament can be natural gemstone, rhinestone, synthetic cut stone, synthetic quartz, mineral crystal etc.

A kind of production technology of ambetti comprises:

1, size cutting on demand on glass plate, as substrate, and with its periphery polishing, cleaning glass powder is dried the moisture content of glass surface again the glass that cuts down.

2, stick diaphragm at glass surface, on diaphragm, draw out pattern.

3, retouch quarter again by the lines of pattern with icking tool.

4, needs are polished into black facial diaphragm and take off, with the polishing of high pressure diamond dust, again with behind the cleaning fluid cleaning dust, the moisture content of oven dry glass surface, bake out temperature is 40-60 ℃.

5, needing to coat liquid protective film on the black surface glass of depiction, draw out irregular abstract design with specific purpose tool on liquid protective film, with the liquid protective film oven dry, bake out temperature is 60-90 ℃ again.

6, the pattern on the liquid protective film of having dried with high pressure diamond dust engraving.

7, glass is placed in the water soaked 1-2 hour, make the liquid protective film of having dried return to liquid state again, clean the liquid protective film that remains on the glass surface with cleaning fluid again, dry the moisture content of glass surface then, bake out temperature is 40-60 ℃.

8, the spraying glass lacquer that adds lustre on the pattern of engraving after the drying, cleans and repairs the unnecessary lacquer that adds lustre to of glass surface.

9, pasting protective film on demand, retouch quarter after, the diaphragm of needs colouring place is taken off, with the color that the air brushing of the special-purpose colored lacquer of glass goes out to need, remove diaphragm then, finishing pattern.

10, as required, depict the profile pattern, again look coating is added in the glass special use and be coated in the pattern of being described, and more than 12 hours, after look coating is added in oven dry, clear up finishing pattern in oven dry under 40-60 ℃ the temperature with the upright line glue of glass.

11, on request, can be with ornament sensitization glue such as rhinestone, natural gemstone, synthetic quartz metals, by the ultraviolet light source irradiation, glue is solid on glass surface.

12, last, the diaphragm of not taking off on the substrate is all removed the cleaning finishing pattern.

Outward appearance convex-concave of the present invention rises and falls, have very strong stereovision, third dimension, color sense, intersperse ornament and color sprayings such as natural gemstone, rhinestone again, has luxurious beautiful, artistic effect that third dimension is extremely strong, simultaneously also can with the compound double glazing body that becomes of safety glass, reach insulation, function such as heat insulation, explosion-proof.

(4) description of drawings

Fig. 1 is the floor map of an embodiment of the present invention.

(5) specific embodiment

A kind of ambetti comprises substrate 1, and substrate 1 is a glass, and two triangle patterns 2 and 3, three circular patterns 4 and 5 and

large square patterns

6 and 9 little square patterns 7 are arranged on it.Wherein, triangle pattern 2 is positioned at the topmost of substrate 1, there is bright frame 8 at its edge, two circular patterns 4 and 5 are positioned at the below of triangle pattern 2, and circular pattern 5 is positioned at circular pattern 4, the intrinsic synthetic cut stone of circular pattern 5 gluings, triangle pattern 3 is positioned at two circular patterns 4 and 5 belows, the intrinsic rhinestone of its gluing: large

square pattern

6 and 9 little square patterns 7 vertically evenly are spaced below triangle pattern 3, and bright frame 10 is arranged around 9 little square patterns 7, the periphery of substrate 1 has frame 11, there is bright frame 12 frame 11 inside edges, the different synthetic quartz of glue respectively intrinsic one is arranged in the bright frame 12 between 13,9 little square patterns 7 of plate face.

A kind of production technology of ambetti comprises following process:

1, glass of cutting is as substrate 1 on glass plate, and the periphery of polishing substrate 1 cleans the moisture content that substrate 1 surface is dried in the back.Bake out temperature is 50 ℃.

2, stick diaphragm on substrate 1 surface, on diaphragm, draw out pattern.

3, retouch quarter again by the lines of pattern with icking tool.

4, taking off with the diaphragm of

pattern

2,3,4,5,6,7 and frame 11 and corresponding section, plate face 13 position on the substrate 1, the glass surface that exposes is sprayed into black face with high pressure diamond dust.

5, with behind the washing agent cleaning dust, the moisture content of oven dry glass surface, bake out temperature is 50 ℃.

6, coat liquid protective film on the substrate 1 with on the surface of

pattern

2,4,5,6,7, corresponding section, position, and on liquid protective film, drawing out irregular pattern.Liquid protective film is dried, bake out temperature is 80 ℃ again.

7, the pattern on the liquid protective film of having dried with high pressure diamond dust engraving.

8, substrate 1 is placed in the water soaked 2 hours, make the liquid protective film of having dried return to liquid state again.

9, remain in substrate 1 lip-deep liquid protective film with the washing agent cleaning, and dry its surperficial moisture content, bake out temperature is 50 ℃.

10, on the substrate 1 with the surface of corresponding section,

pattern

2,4,5,6,7 position on spraying glass special use adding lustre to lacquer, the oven dry lacquer that adds lustre to then, bake out temperature is 50 ℃, and the unnecessary lacquer that adds lustre to of cleaning refacing.

11, on the glass surface of substrate 1, paste layer protecting film again, plate face 13 is retouched quarter after, take diaphragm off, the colour lacquer of using for glass with blue look from top to bottom, shallow by being deep to, air brushing becomes the color of transition, removes diaphragm, finishing pattern then.

12, depict three limits of triangle pattern 3 with upright line glue, again glass is added look coating with light green color and be coated in the triangle, oven dry is 10 hours under 50 ℃ of temperature, after look coating is added in oven dry, and the cleaning finishing pattern.

13, by photoresists and ultraviolet light source irradiation cementation an ornament 9 is being arranged respectively on triangle pattern 3 and the circular pattern 5 and between 9 little square patterns 7, wherein, the ornament 9 of cementation is a rhinestone in the triangle pattern 3, the ornament 9 of cementations is a synthetic cut stone in the circular pattern 5, and the ornament of cementation is the synthetic quartz of different shape between 9 little square patterns 7.

14, take the diaphragm at

bright frame

8,10 and 12 places off, cleaning and finishing pattern.

16, safety glass and the figuratum substrate 1 usefulness hollow adhesive tape with a same size is combined into double glazing.

Claims

1, a kind of production technology of ambetti is characterized in that this production technology comprises:

A, glass of cutting is as substrate (1) on glass plate, and the periphery of polishing substrate (1) cleans the moisture content on back oven dry substrate (1) surface, and bake out temperature is 40-60 ℃;

B, stick diaphragm, on diaphragm, draw out pattern, and retouch quarter again by the lines of pattern on substrate (1) surface;

C, the diaphragm that needs are polished into the facial position of crow are taken off, with the diamond dust polishing, clean dust with washing agent again after, the moisture content of oven dry glass surface;

D, needing to coat liquid protective film on the black surface glass of depiction, and on liquid protective film, draw out irregular abstract design, then with liquid protective film oven dry, bake out temperature 60-90 ℃, carve pattern on the liquid protective film of having dried with high pressure diamond dust again;

E, substrate (1) is placed in the water soaked 1-2 hour, make the liquid protective film of having dried return to liquid state again, clean the liquid protective film that remains on the glass surface with cleaning agent again, dry the moisture content of glass surface then, bake out temperature is 40-60 ℃;

F, on the pattern of engraving the spraying glass lacquer that adds lustre to;

G, need, on substrate, paste layer protecting film again by design, retouch quarter after, the diaphragm of needs colouring place is taken off, with the air brushing of the special-purpose colored lacquer of glass go out need color, remove diaphragm then, finishing pattern;

H, depict the external form pattern, again the look coating of using for glass that adds is coated in the pattern of being described with the upright line glue of glass, in oven dry under 40-60 ℃ the temperature more than 12 hours, after look coating is added in oven dry, the cleaning finishing pattern;

I, according to designing requirement, with ornament sensitization glue, shine by ultraviolet light source, glue is solid on substrate;

J, last all removes the diaphragm of not taking off on the substrate (1), the cleaning finishing pattern.

2, the production technology of a kind of ambetti according to claim 1 is characterized in that described ornament is rhinestone, natural gemstone, synthetic quartz, mineral crystal, natural shellfish.