CN113896978A - 一种eva收纳篮及其制备方法 - Google Patents
一种eva收纳篮及其制备方法 Download PDFInfo
- Publication number
- CN113896978A CN113896978A CN202111280034.7A CN202111280034A CN113896978A CN 113896978 A CN113896978 A CN 113896978A CN 202111280034 A CN202111280034 A CN 202111280034A CN 113896978 A CN113896978 A CN 113896978A
- Authority
- CN
- China
- Prior art keywords
- storage basket
- base film
- eva
- basket
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本申请涉及日常生活用品领域,具体公开了一种EVA收纳篮及其制备方法。一种EVA收纳篮,包括收纳篮体以及收纳篮底,所述收纳篮体以及所述收纳篮底皆由基膜制得,所述基膜由以下重量百分比的原料制备:EVA 65%‑75%;POE 5%‑12%;MVLDPE7%‑16%;LDPE 6%‑12%。制备方法为:制备基膜,然后将基膜制备成EVA收纳篮;制备基膜具体包括以下步骤:先将EVA、POE、MVLDPE和LDPE混合均匀得到混合物,混合物进行密炼、开炼、造粒,得到半成品;对半成品进行共混熔融、挤出,流延,冷却定型,得到基膜。本申请的一种EVA收纳篮提高收纳篮的质量和使用体验的优点。
Description
技术领域
本申请涉及日常生活用品的技术领域,更具体地说,它涉及一种EVA收纳篮及其制备方法。
背景技术
收纳篮作为日常生活用品中常用的生活工具,一般用于承载生活物品。随着消费水平的提高,在日常生活中对收纳篮的需求愈加多样化,市面上收纳篮的种类也随之增多,收纳篮多应用于卧室、客厅以及浴室等多种生活场景中。
收纳篮一般采用网布制成,网布类收纳篮制作简单,但是由于网布质地较柔软,支撑力不足,且耐久性较差,长时间使用后容易出现垮塌的问题,影响使用体验。
发明内容
为了提高收纳篮的质量和使用体验,本申请提供一种EVA收纳篮及其制备方法。
第一方面,本申请提供的一种EVA收纳篮,采用如下的技术方案:
一种EVA收纳篮,包括收纳篮体以及收纳篮底,所述收纳篮体以及所述收纳篮底皆由基膜制得,所述基膜由以下重量百分比的原料制备:
EVA 65%-75%;
POE 5%-12%;
MVLDPE7%-16%;
LDPE 6%-12%;
其它助剂0%-10%。
通过采用上述技术方案,EVA为乙烯-醋酸乙酯共聚物,POE为聚烯烃热塑性弹性体,MVLDPE为茂金属低密度聚乙烯,LDPE为低密度聚乙烯,以EVA作为主要基体来制备基膜,基膜的质地较网布硬,使收纳篮的支撑力提高,并且POE、MVLDPE和LDPE各自均具有一定的韧性和抗弯能力,通过合适的比例使POE、MVLDPE和LDPE协同对EVA基体起加强作用,在不增加基膜厚度的同时提高了基膜的强度,从而提高收纳篮耐折弯能力,其中MVLDPE可以促使各原料熔融后混合更加均匀,促使基膜的韧性好,使得收纳篮可经受多次拉伸,从而有效延长收纳篮的使用寿命,从而提高收纳篮的质量和使用体验。
优选的,所述其它助剂包括爽滑剂,所述爽滑剂为油酸酰胺和芥酸酰胺的一种或两种组合物,所述爽滑剂在基膜的原料中所占重量百分比为0.05%-0.12%。
通过采用上述技术方案,加入爽滑剂,使得基膜的质地更加柔软,油酸酰胺和芥酸酰胺均可以提高基膜的表面光洁度,从而提高收纳篮使用时的舒适度。
优选的,所述其它助剂包括碳酸钙,所述碳酸钙在基膜的原料中所占重量百分比为6%-10%。
通过采用上述技术方案,碳酸钙起到填充效果,补强基膜的内部结构,可以提高基膜的结构稳定性,提高基膜的韧性。
优选的,所述其它助剂包括爽滑剂和碳酸钙,所述爽滑剂在基膜的原料中所占重量百分比为0.1%-0.11%,所述碳酸钙在基膜的原料中所占重量百分比为7.25%-7.35%,所述爽滑剂为油酸酰胺和芥酸酰胺的组合物,所述油酸酰胺与芥酸酰胺的质量比为1:(0.4~0.6)。
通过采用上述技术方案,该组合和比例下配合的爽滑剂与碳酸钙,碳酸钙表面与EVA、MVLDPE的摩擦阻力大大降低,从而降低碳酸钙结块的情况,提高碳酸钙的分散性,从而提高了韧性的同时,对耐撕裂性能有良好的补充。
优选的,所述其它助剂包括聚二甲基硅氧烷,所述聚二甲基硅氧烷在基膜的原料中所占重量百分比为0.75%-0.90%。
通过采用上述技术方案,聚二甲基硅氧烷可以起到消泡剂的作用,通过吸收空气中的水分含量,有效抑制生产过程中材料中气泡的产生,配合爽滑剂和碳酸钙使用,提高基膜的抗冲击性能,使基膜成型质量更好。
优选的,所述其它助剂包括防霉剂,所述防霉剂为异维生素C钠和吡硫锌中的一种或两种的组合物,所述防霉剂在基膜的原料中所占重量百分比为2%-5%。
通过采用上述技术方案,提高收纳篮的防霉抗菌功能,使存放于收纳篮的物品不易受霉菌干扰。
优选的,所述其它助剂包括聚磷酸铵,所述聚磷酸铵在基膜的原料中所占重量百分比为5%-9%。
通过采用上述技术方案,提高收纳篮的阻燃效果,使得收纳篮在高温下不易变形,性能稳定。
优选的,所述收纳篮体与所述收纳篮底之间通过缝纫带相连接,所述收纳篮体上设置有提带。
通过采用上述技术方案,缝纫带的设置使得收纳篮体和收纳篮底可以分开生产,然后再进行连接,提高生产效率,提带可以便于使用者携带收纳篮。
第二方面,本申请提供一种EVA收纳篮的制备方法,包括以下步骤:
制备基膜,然后将基膜制备成收纳篮体和收纳篮底,固定连接收纳篮体和收纳篮底,制得EVA收纳篮;
制备基膜具体包括以下步骤:
步骤1a,按质量配比称取EVA、POE、MVLDPE和LDPE;
步骤2a,先将EVA、POE、MVLDPE和LDPE混合均匀得到混合物,混合物进行密炼,密炼结束后再进行开炼、造粒,再经振动散热后得到半成品;
步骤3a,对半成品进行共混熔融、挤出,流延,冷却定型,得到基膜。
通过采用上述技术方案,制备出具有良好的强度和韧性的基膜,使得收纳篮具有较高的支撑力,同时便于拉伸折叠,提高收纳篮的实用性。
优选的,制备基膜完成到制得EVA收纳篮之间包括以下步骤:
将基膜层叠压制为收纳篮底;
将基膜绕成圆柱状后通过缝纫带固定为收纳篮体;
将收纳篮体的一侧通过缝纫带与收纳篮底进行固定连接,将提带粘接于所述收纳篮体的外侧壁,制得EVA收纳篮。
通过采用上述技术方案,制备效率高,收纳篮体以及收纳篮底之间连接紧密,收纳篮整体稳固性高。
综上所述,本申请具有以下有益效果:
1、本申请采用EVA、POE、MVLDPE和LDPE四种材料作为主体材料,EVA为乙烯-醋酸乙酯共聚物,POE为聚烯烃热塑性弹性体,MVLDPE为茂金属低密度聚乙烯,LDPE为低密度聚乙烯,以EVA作为主要基体来制备基膜,基膜的质地较网布硬,使收纳篮的支撑力提高,并且POE、MVLDPE和LDPE各自均具有一定的韧性和抗弯能力,通过合适的比例使POE、MVLDPE和LDPE协同对EVA基体起加强作用,在不增加基膜厚度的同时提高了基膜的强度,从而提高收纳篮耐折弯能力,其中MVLDPE可以促使各原料熔融后混合更加均匀,促使基膜的韧性好,使得收纳篮可经受多次拉伸,从而有效延长收纳篮的使用寿命,从而提高收纳篮的质量和使用体验;
2、本申请加入油酸酰胺和芥酸酰胺以使基膜的质地更加柔软,提高收纳篮的使用舒适度,并且本申请还加入碳酸钙作为填料,补强基膜,同时还提高了基膜的耐撕裂能力,提高收纳篮的耐用性。
附图说明
图1是本申请提供的收纳篮的整体结构示意图;
图2是本申请提供的收纳篮的整体结构示意图。
附图标记说明:1、收纳篮体;2、收纳篮底;3、缝纫带;4、提带。
具体实施方式
以下结合附图1-2、制备例、实施例以及对比例对本申请作进一步详细说明。
EVA选购自杜邦公司,型号460;
POE选购自陶氏化学公司,型号8150;
MVLDPE选购自陶氏化学公司,型号5220G;
LDPE选购自中国石化集团茂名石油化工有限公司,型号1850A;
聚二甲基硅氧烷选购自,上海箭宇化工(苏州)有限公司,型号JY-810;
聚磷酸铵选购自山东开普勒生物科技有限公司,聚合度2000。
实施例1
一种基膜,由以下原料制备而成:
6.5kgEVA、1.2kgPOE、1.15kgMVLDPE、1.15kgLDPE。
一种基膜的制备方法,包括以下步骤:
步骤1a,称取EVA、POE、MVLDPE、LDPE;
步骤2a,将EVA、POE、MVLDPE、LDPE混合均匀得到混合物,使用密炼机进行密炼,密炼温度为130℃,密炼时间为20min,密炼结束后再进行开炼、造粒,再经振动散热后得到半成品;
步骤3a,将半成品投入双螺杆挤出机,共混熔融、挤出,转速为40r/min,五区温度依次分别为150℃、160℃、170℃、180℃、180℃,挤出后流延,流延温度为140℃,冷却定型,得到基膜。
一种EVA收纳篮的制备方法,如图1和图2所示,包括以下步骤:
步骤1b,将基膜层叠压制为收纳篮底2;
步骤2b,将基膜绕成圆柱状,将基膜相近的两侧边通过缝纫带3固定,制得收纳篮体1;
步骤3b,将收纳篮体1的一端边缘通过缝纫带3与收纳篮底2的边缘进行固定,将两个提带4分别粘接于收纳篮体1的外侧壁相对两侧,制得EVA收纳篮。
实施例2~实施例17
实施例2至实施例17与实施例1的区别在于基膜的原料不同,具体情况如表1和表2所示。
表1单位(kg)
表2单位(kg)
对比例
对比例1~对比例5
对比例1至对比例5与实施例5的区别在于基膜的原料不同,如表3所示,其中,对比例1至对比例5均不加入油酸酰胺、芥酸酰胺、碳酸钙、聚二甲基硅氧烷、异维生素C钠、吡硫锌和聚磷酸铵。
表3单位(kg)
EVA | POE | MVLDPE | LDPE | |
对比例1 | 6.00 | 0.80 | 2.20 | 1.00 |
对比例2 | 8.10 | 0.80 | 0.10 | 1.00 |
对比例3 | 7.90 | 0.10 | 1.00 | 1.00 |
对比例4 | 8.00 | 0.80 | 1.00 | 0.20 |
对比例5 | 6.40 | 1.60 | 1.00 | 1.00 |
性能检测试验
根据GB/T 1040.3-2006《塑料拉伸性能的测定第3部分:薄塑和薄片的试验条件》,测定不同的实施例以及对比例的制备的基膜的拉伸强度,测试数据如表4所示。
根据GB/T 9341-2008《塑料弯曲性能的测定》,测定不同的实施例以及对比例的制备的基膜的弯曲模量,测试数据如表4所示。
根据GB/T 16578.1-2008《塑料薄膜和薄片耐撕裂性能的测定》,测定不同的实施例以及对比例的制备的基膜的撕裂强度,测试数据如表4所示。
根据GB/T 1843-2008《塑料悬臂梁冲击强度的测定测试》,测定不同实施例以及对比例制备的基膜的缺口冲击强度,测试数据如表4所示。
根据GB/T 24128-2018《塑料塑料防霉剂的防霉效果评估》测试不同实施例以及对比例制备的基膜的防霉效果,测试结果如表4所示。
根据UL94,测试不同实施例以及对比例制备的基膜的阻燃效果,测试结果如表4所示。
表4
根据表4可以看出,结合实施例5与对比例1-5,本申请所制备的基膜具有良好的拉伸强度、弯曲模量、撕裂强度和耐冲击性能,因此由基膜制得的收纳篮的强度和韧性佳,结构结实,耐弯折,且抵抗外力的能力好,使得收纳篮的耐用性高,可以提高收纳篮的使用体验;并且说明EVA、POE、MVLDPE和LDPE四者是在限定范围内相互协同作用的,从而起到提高基膜性能的效果。
结合实施例5与实施例1-4,通过在限定范围内调整EVA、POE、MVLDPE和LDPE四者的占比关系,可以使基膜获得更加均衡的拉伸强度、弯曲模量、撕裂强度和耐冲击性能。
结合实施例5与实施例6-11,只加入爽滑剂油酸酰胺和芥酸酰胺对基膜的拉伸强度、弯曲模量、撕裂强度和耐冲击性能并没有较大影响,只加入碳酸钙可以对拉伸强度和冲击强度有一定的提高,而控制油酸酰胺和芥酸酰胺的总占比以及两者之间的配比,且控制碳酸钙的总占比,可以额外获得提高撕裂强度的效果,从而进一步提高基膜抵抗外力的能力,提高收纳篮的耐用性,同时保持基膜良好的弯曲模量,提高抗弯折能力。
结合实施例11与实施例12-13,配合聚二甲基硅氧烷的加入,基膜的冲击强度进一步增强,从而提高收纳篮的韧性。
结合实施例5与实施例14-15,加入异维生素C钠和吡硫锌作为防霉剂,可以抑制霉菌在基膜的生长,从而提高收纳篮的防霉抗菌性能。
结合实施例5与实施例16-17,加入聚磷酸铵作为阻燃剂,使得基膜的阻燃效果更好。
本具体实施例仅仅是对本申请的解释,其并不是对本申请的限制,本领域技术人员在阅读完本说明书后可以根据需要对本实施例做出没有创造性贡献的修改,但只要在本申请的权利要求范围内都受到专利法的保护。
Claims (10)
1.一种EVA收纳篮,其特征在于:包括收纳篮体(1)以及收纳篮底(2),所述收纳篮体(1)以及所述收纳篮底(2)皆由基膜制得,所述基膜由以下重量百分比的原料制备:
EVA 65%-75%;
POE 5%-12%;
MVLDPE7%-16%;
LDPE 6%-12%;
其它助剂 0%-10%。
2.根据权利要求1所述的一种EVA收纳篮,其特征在于:所述其它助剂包括爽滑剂,所述爽滑剂为油酸酰胺和芥酸酰胺的一种或两种组合物,所述爽滑剂在基膜的原料中所占重量百分比为0.05%-0.12%。
3.根据权利要求2所述的一种EVA收纳篮,其特征在于:所述其它助剂包括碳酸钙,所述碳酸钙在基膜的原料中所占重量百分比为6%-10%。
4.根据权利要求2所述的一种EVA收纳篮,其特征在于:所述其它助剂包括爽滑剂和碳酸钙,所述爽滑剂在基膜的原料中所占重量百分比为0.1%-0.11%,所述碳酸钙在基膜的原料中所占重量百分比为7.25%-7.35%,所述爽滑剂为油酸酰胺和芥酸酰胺的组合物,所述油酸酰胺与芥酸酰胺的质量比为1:(0.4~0.6)。
5.根据权利要求1所述的一种EVA收纳篮,其特征在于:所述其它助剂包括聚二甲基硅氧烷,所述聚二甲基硅氧烷在基膜的原料中所占重量百分比为0.75%-0.90%。
6.根据权利要求1所述的一种EVA收纳篮,其特征在于:所述其它助剂包括防霉剂,所述防霉剂为异维生素C钠和吡硫锌中的一种或两种的组合物,所述防霉剂在基膜的原料中所占重量百分比为2%-5%。
7.根据权利要求1所述的一种EVA收纳篮,其特征在于:所述其它助剂包括聚磷酸铵,所述聚磷酸铵在基膜的原料中所占重量百分比为5%-9%。
8.根据权利要求1所述的一种EVA收纳篮,其特征在于:所述收纳篮体(1)与所述收纳篮底(2)之间通过缝纫带(3)相连接,所述收纳篮体(1)上设置有提带(4)。
9.权利要求1-8所述的一种EVA收纳篮的制备方法,其特征在于:包括以下步骤:
制备基膜,然后将基膜制备成收纳篮体和收纳篮底,固定连接收纳篮体和收纳篮底,制得EVA收纳篮;
制备基膜具体包括以下步骤:
步骤1a,按质量配比称取EVA、POE、MVLDPE和LDPE;
步骤2a,先将EVA、POE、MVLDPE和LDPE混合均匀得到混合物,混合物进行密炼,密炼结束后再进行开炼、造粒,再经振动散热后得到半成品;
步骤3a,对半成品进行共混熔融、挤出,流延,冷却定型,得到基膜。
10.根据权利要求9所述的一种EVA收纳篮的制备方法,其特征在于:制备基膜完成到制得EVA收纳篮之间包括以下步骤:
将基膜层叠压制为收纳篮底(2);
将基膜绕成圆柱状后通过缝纫带(3)固定为收纳篮体(1);
将收纳篮体(1)的一侧通过缝纫带(3)与收纳篮底(2)进行固定连接,将提带(4)粘接于所述收纳篮体(1)的外侧壁,制得EVA收纳篮。