CN113861445A - 一种环保阻燃密胺水性乳液及其制备方法 - Google Patents
一种环保阻燃密胺水性乳液及其制备方法 Download PDFInfo
- Publication number
- CN113861445A CN113861445A CN202111098864.8A CN202111098864A CN113861445A CN 113861445 A CN113861445 A CN 113861445A CN 202111098864 A CN202111098864 A CN 202111098864A CN 113861445 A CN113861445 A CN 113861445A
- Authority
- CN
- China
- Prior art keywords
- flame
- parts
- retardant
- portions
- stirring
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种环保阻燃密胺水性乳液及其制备方法，包括分别取中适量的尿素、密胺、聚乙烯醇、纯静水、丙烯酸丁酯、去离子水、甲基丙烯酸甲酯、阻燃填料、溴化苯乙烯、活性剂、催化剂放入反应釜中，随后调节反应釜内部的温度，对其通过搅拌叶片进行旋转搅拌；在搅拌过程中的溶液，向内加入阻燃填料，继续搅拌均匀：取搅拌后的溶液，向内依次加入活性剂和催化剂，再次通过搅拌叶片高速搅拌20～40min：放置特定的容器进行储存，真空室内温度保存。该种环保阻燃密胺水性乳液及其制备方法，设计简单新颖，具有良好的阻燃效率。
Description
技术领域
本发明涉及水性乳液技术领域，具体为一种环保阻燃密胺水性乳液及其制备方法。
背景技术
三聚氰胺（Melamine），俗称密胺、蛋白精，分子式为C3H6N6，IUPAC命名为“1,3,5-三嗪-2,4,6-三胺”，是一种三嗪类含氮杂环有机化合物，被用作化工原料，三聚氰胺以尿素为原料，生产1吨三聚氰胺约需3吨尿素。中国是世界上最大的尿素生产国，尿素产量大且价格低廉，即使在国家实行高关税抑制尿素出口的背景下，每年尿素出口量仍达（300～700）万吨，丰富的尿素资源使得中国三聚氰胺生产具有得天独厚的优势。中国三聚氰胺产能扩张严重，致使中国三聚氰胺企业竞争激烈，行业产品价格上涨乏力，现有的一般水性乳液阻燃效率较差，同时制做过程中，费时费力。因此我们对此做出改进，提出一种环保阻燃密胺水性乳液及其制备方法。
发明内容
为了解决上述技术问题，本发明提供了如下的技术方案：
本发明一种环保阻燃密胺水性乳液，包括以下组分的原料制得：尿素15.0份～40.0份、密胺30.0份～60.0份、聚乙烯醇8.0份～20.0份、纯静水9.0份～28.0份、丙烯酸丁酯12.0份～32.0份、去离子水15.0份～35.0份、甲基丙烯酸甲酯5.0份～8.0份、阻燃填料19.0份～75.0份、溴化苯乙烯30.0份～60.0份、活性剂4.0份～12.0份、催化剂2.0份～8.0份。
作为本发明的一种优选技术方案，所述阻燃填料采用红磷、二溴苯乙烯和聚苯乙烯的一种或者几种。
作为本发明的一种优选技术方案，所述活性剂为二甲基环己胺、三聚氰胺聚磷酸盐和丙烯酸异辛酯的混合物。
作为本发明的一种优选技术方案，所述活性剂为甲苯二异氰酸酯和烯丙基磺酸钠的一种或者几种。
一种环保阻燃密胺水性乳液的制备方法，包括以下几个步骤：
步骤一：按照一定的质量分数和比例准备若干份尿素15.0份～40.0份、密胺30.0份～60.0份、聚乙烯醇8.0份～20.0份、纯静水9.0份～28.0份、丙烯酸丁酯12.0份～32.0份、去离子水15.0份～35.0份、甲基丙烯酸甲酯5.0份～8.0份、阻燃填料19.0份～75.0份、溴化苯乙烯30.0份～60.0份、活性剂4.0份～12.0份和催化剂2.0份～8.0份；
步骤二：分别取步骤一中适量的尿素、密胺、聚乙烯醇、纯静水、丙烯酸丁酯、去离子水、甲基丙烯酸甲酯、阻燃填料、溴化苯乙烯、活性剂、催化剂放入反应釜中，随后调节反应釜内部的温度，对其通过搅拌叶片进行旋转搅拌；
步骤三：在步骤二搅拌过程中的溶液，向内加入阻燃填料，继续搅拌均匀；
步骤四：取步骤三搅拌后的溶液，向内依次加入活性剂和催化剂，再次通过搅拌叶片高速搅拌20～40min；
步骤五：放置特定的容器进行储存，真空室内温度保存。
作为本发明的一种优选技术方案，所述步骤二中反应釜内的温度控制在40-60℃，同时搅拌30～40min。
作为本发明的一种优选技术方案，所述步骤四中加入催化剂后搅拌35min时，向内加入偶联剂。
作为本发明的一种优选技术方案，所述步骤五中真空保存之前需进行真空干燥处理，真空干燥的温度为30-50℃，干燥的时间为1h。
本发明的有益效果是：分别取中适量的尿素、密胺、聚乙烯醇、纯静水、丙烯酸丁酯、去离子水、甲基丙烯酸甲酯、阻燃填料、溴化苯乙烯、活性剂、催化剂放入反应釜中，随后调节反应釜内部的温度，对其通过搅拌叶片进行旋转搅拌；提高了耐火极限，在搅拌过程中的溶液，向内加入阻燃填料，继续搅拌均匀：取搅拌后的溶液，向内依次加入活性剂和催化剂，再次通过搅拌叶片高速搅拌20～40min：放置特定的容器进行储存，真空室内温度保存，该方法设计简单新颖，具有良好的阻燃效率。
附图说明
附图用来提供对本发明的进一步理解，并且构成说明书的一部分，与本发明的实施例一起用于解释本发明，并不构成对本发明的限制。在附图中：
图1是本发明一种环保阻燃密胺水性乳液及其制备方法的方法步骤图。
具体实施方式
以下结合附图对本发明的优选实施例进行说明，应当理解，此处所描述的优选实施例仅用于说明和解释本发明，并不用于限定本发明。
实施例：如图1所示，本发明一种环保阻燃密胺水性乳液，包括以下组分的原料制得：尿素15.0份～40.0份、密胺30.0份～60.0份、聚乙烯醇8.0份～20.0份、纯静水9.0份～28.0份、丙烯酸丁酯12.0份～32.0份、去离子水15.0份～35.0份、甲基丙烯酸甲酯5.0份～8.0份、阻燃填料19.0份～75.0份、溴化苯乙烯30.0份～60.0份、活性剂4.0份～12.0份、催化剂2.0份～8.0份。
其中，阻燃填料采用红磷、二溴苯乙烯和聚苯乙烯的一种或者几种。
其中，活性剂为二甲基环己胺、三聚氰胺聚磷酸盐和丙烯酸异辛酯的混合物。
其中，活性剂为甲苯二异氰酸酯和烯丙基磺酸钠的一种或者几种。
一种环保阻燃密胺水性乳液的制备方法，包括以下几个步骤：
步骤一：按照一定的质量分数和比例准备若干份尿素15.0份～40.0份、密胺30.0份～60.0份、聚乙烯醇8.0份～20.0份、纯静水9.0份～28.0份、丙烯酸丁酯12.0份～32.0份、去离子水15.0份～35.0份、甲基丙烯酸甲酯5.0份～8.0份、阻燃填料19.0份～75.0份、溴化苯乙烯30.0份～60.0份、活性剂4.0份～12.0份和催化剂2.0份～8.0份；
步骤二：分别取步骤一中适量的尿素、密胺、聚乙烯醇、纯静水、丙烯酸丁酯、去离子水、甲基丙烯酸甲酯、阻燃填料、溴化苯乙烯、活性剂、催化剂放入反应釜中，随后调节反应釜内部的温度，对其通过搅拌叶片进行旋转搅拌；
步骤三：在步骤二搅拌过程中的溶液，向内加入阻燃填料，继续搅拌均匀；
步骤四：取步骤三搅拌后的溶液，向内依次加入活性剂和催化剂，再次通过搅拌叶片高速搅拌20～40min；
步骤五：放置特定的容器进行储存，真空室内温度保存。
其中，步骤二中反应釜内的温度控制在40-60℃，同时搅拌30～40min。
其中，步骤四中加入催化剂后搅拌35min时，向内加入偶联剂。
其中，步骤五中真空保存之前需进行真空干燥处理，真空干燥的温度为30-50℃，干燥的时间为1h。
工作原理：使用时，按照一定的质量分数和比例准备若干份尿素15.0份～40.0份、密胺30.0份～60.0份、聚乙烯醇8.0份～20.0份、纯静水9.0份～28.0份、丙烯酸丁酯12.0份～32.0份、去离子水15.0份～35.0份、甲基丙烯酸甲酯5.0份～8.0份、阻燃填料19.0份～75.0份、溴化苯乙烯30.0份～60.0份、活性剂4.0份～12.0份和催化剂2.0份～8.0份；步骤二：分别取步骤一中适量的尿素、密胺、聚乙烯醇、纯静水、丙烯酸丁酯、去离子水、甲基丙烯酸甲酯、阻燃填料、溴化苯乙烯、活性剂、催化剂放入反应釜中，随后调节反应釜内部的温度，对其通过搅拌叶片进行旋转搅拌；反应釜内的温度控制在40-60℃，同时搅拌30～40min；步骤三：在步骤二搅拌过程中的溶液，向内加入阻燃填料，继续搅拌均匀；向内加入阻燃填料，继续搅拌均匀；步骤四：取步骤三搅拌后的溶液，向内依次加入活性剂和催化剂，再次通过搅拌叶片高速搅拌20～40min；再向内依次加入活性剂和催化剂，再次通过搅拌叶片高速搅拌20～40min；步骤五：放置特定的容器进行储存，真空室内温度保存。
最后应说明的是：在本发明的描述中，需要说明的是，术语“竖直”、“上”、“下”、“水平”等指示的方位或位置关系为基于附图所示的方位或位置关系，仅是为了便于描述本发明和简化描述，而不是指示或暗示所指的装置或元件必须具有特定的方位、以特定的方位构造和操作，因此不能理解为对本发明的限制。
在本发明的描述中，还需要说明的是，除非另有明确的规定和限定，术语“设置”、“安装”、“相连”、“连接”应做广义理解，例如，可以是固定连接，也可以是可拆卸连接，或一体地连接；可以是机械连接，也可以是电连接；可以是直接相连，也可以通过中间媒介间接相连，可以是两个元件内部的连通。对于本领域的普通技术人员而言，可以根据具体情况理解上述术语在本发明中的具体含义。
以上所述仅为本发明的优选实施例而已，并不用于限制本发明，尽管参照前述实施例对本发明进行了详细的说明，对于本领域的技术人员来说，其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换。凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (8)
1.一种环保阻燃密胺水性乳液，其特征在于，包括以下组分的原料制得：尿素15.0份～40.0份、密胺30.0份～60.0份、聚乙烯醇8.0份～20.0份、纯静水9.0份～28.0份、丙烯酸丁酯12.0份～32.0份、去离子水15.0份～35.0份、甲基丙烯酸甲酯5.0份～8.0份、阻燃填料19.0份～75.0份、溴化苯乙烯30.0份～60.0份、活性剂4.0份～12.0份、催化剂2.0份～8.0份。
2.根据权利要求1所述的一种环保阻燃密胺水性乳液，其特征在于，所述阻燃填料采用红磷、二溴苯乙烯和聚苯乙烯的一种或者几种。
3.根据权利要求1所述的一种环保阻燃密胺水性乳液及其制备方法，其特征在于，所述活性剂为二甲基环己胺、三聚氰胺聚磷酸盐和丙烯酸异辛酯的混合物。
4.根据权利要求1所述的一种环保阻燃密胺水性乳液及其制备方法，其特征在于，所述活性剂为甲苯二异氰酸酯和烯丙基磺酸钠的一种或者几种。
5.一种环保阻燃密胺水性乳液的制备方法，其特征在于，包括以下几个步骤：
步骤一：按照一定的质量分数和比例准备若干份尿素15.0份～40.0份、密胺30.0份～60.0份、聚乙烯醇8.0份～20.0份、纯静水9.0份～28.0份、丙烯酸丁酯12.0份～32.0份、去离子水15.0份～35.0份、甲基丙烯酸甲酯5.0份～8.0份、阻燃填料19.0份～75.0份、溴化苯乙烯30.0份～60.0份、活性剂4.0份～12.0份和催化剂2.0份～8.0份；
步骤二：分别取步骤一中适量的尿素、密胺、聚乙烯醇、纯静水、丙烯酸丁酯、去离子水、甲基丙烯酸甲酯、阻燃填料、溴化苯乙烯、活性剂、催化剂放入反应釜中，随后调节反应釜内部的温度，对其通过搅拌叶片进行旋转搅拌；
步骤三：在步骤二搅拌过程中的溶液，向内加入阻燃填料，继续搅拌均匀；
步骤四：取步骤三搅拌后的溶液，向内依次加入活性剂和催化剂，再次通过搅拌叶片高速搅拌20～40min；
步骤五：放置特定的容器进行储存，真空室内温度保存。
6.根据权利要求5所述的一种环保阻燃密胺水性乳液的制备方法，其特征在于，所述步骤二中反应釜内的温度控制在40-60℃，同时搅拌30～40min。
7.根据权利要求5所述的一种环保阻燃密胺水性乳液的制备方法，其特征在于，所述步骤四中加入催化剂后搅拌35min时，向内加入偶联剂。
8.根据权利要求5所述的一种环保阻燃密胺水性乳液的制备方法，其特征在于，所述步骤五中真空保存之前需进行真空干燥处理，真空干燥的温度为30-50℃，干燥的时间为1h。