CN113774669A - 一种天然乳胶纤维的制备方法 - Google Patents
一种天然乳胶纤维的制备方法 Download PDFInfo
- Publication number
- CN113774669A CN113774669A CN202111083274.8A CN202111083274A CN113774669A CN 113774669 A CN113774669 A CN 113774669A CN 202111083274 A CN202111083274 A CN 202111083274A CN 113774669 A CN113774669 A CN 113774669A
- Authority
- CN
- China
- Prior art keywords
- natural latex
- fiber
- fibers
- parts
- stock solution
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种天然乳胶纤维的制备方法，一种天然乳胶纤维，包括以下份数，纤维100份，天然乳胶原液2‑8份，亲水200‑300份，抗菌剂0.5‑1.5份。上述天然乳胶纤维的制备方法包括以下步骤：步骤1、将称取各原料备用。步骤2、将天然乳胶原液与抗菌剂混合搅拌均匀。步骤3、将混合原液与水混合搅拌均匀，得到液体。步骤4、将纤维分批放入容器中，同时分批注入混合液体。步骤5、将混合液体与纤维通过蒸汽升温至50‑60度，保温30‑45分钟。步骤6、将纤维取出，脱水、烘干，得到天然乳胶短纤维。本发明的有益效果是外面用乳胶包覆，使纤维在不失保暖的情况下可对人体睡眠安稳、抑制细菌、螨虫滋生。
Description
技术领域
本发明涉及纺织领域，具体的是涉及纤维及其制备方法。
背景技术
天然乳胶制品由于透气性、吸湿性、柔软触觉以及高弹性等特点，受到广大用户的喜爱。天然乳胶是橡胶树汁液，整个生产过程都是“物理工艺”，没有化学工艺参与，从根本上做到无毒无害，可以说它是人类安全，又不污染环境。
人的一辈子当中三分之一的时间是在睡眠上的，而家纺是睡眠时必备的。目前，家纺品种繁多，如被子就有棉花、羽绒、蚕丝、羊毛、涤纶纤维、晴纶纤维、锦纶、莫代尔、莱赛尔、竹纤维、聚乳酸粘胶等，现在技术中还没有涉及到将天然乳胶应用在短纤维上，将短纤维应用于家纺寝室之中。
乳胶由于是天然的原料制成，会散发出独一无二乳香味，这个香味不仅能使人睡眠安稳，还具有抑制螨虫滋生。而且因为材质的关系，它不产生静电，这就大大的减少了灰尘的侵入，对呼吸道疾病的改善很有帮助。
发明内容
针对现有技术中还没有涉及到将天然乳胶应用于短纤维上用于家纺寝室中，普通的纤维没有香味，不能使人睡眠安稳和抑制细菌、螨虫滋生的功能。本发明提供了一种天然乳胶纤维的制备方法，外面用乳胶包覆。使纤维在不失保暖的情况下可对人体睡眠安稳、抑制细菌、螨虫滋生。
优先的，所述一种天然乳胶纤维为乳胶将涤纶中空短纤维包覆。
优选的短纤维为1Dtex-22Dtex的涤纶、晴纶、锦纶、羽绒、蚕丝、羊毛、莫代尔、莱赛尔、棉花、竹纤维、聚乳酸、粘胶的纤维。
优选的一种天然乳胶纤维，包括以下份数，纤维100份，天然乳胶原液2-8份，亲水200-300份，抗菌剂0.5-1.5份。
上述天然乳胶纤维的制备方法包括以下步骤：
步骤1、将称取各原料备用。
步骤2、将天然乳胶原液与抗菌剂混合搅拌均匀。
步骤3、将混合原液与水混合搅拌均匀，得到液体。
步骤4、将纤维分批放入容器中，同时分批注入混合液体。
步骤5、将混合液体与纤维通过蒸汽升温至50-60度，保温30-45分钟。
步骤6、将纤维取出，脱水、烘干，得到天然乳胶短纤维。
具体实施方法
下面将结合本发明实施例，对本发明实施例中的技术方案进行完整的描述。显然，所描述的实施例仅仅是本发明的一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例都属于本发明保护的范围。
实施例一
一种天然乳胶纤维包括涤纶纤维100份，天然乳胶原液5份，亲水250份，抗菌剂1份。
上述天然乳胶纤维的制备方法如下：
步骤1、将称取各原料备用。
步骤2、将天然乳胶原液与抗菌剂混合搅拌均匀。
步骤3、将混合原液与水混合搅拌均匀，得到液体。
步骤4、将纤维分批放入容器中，同时分批注入混合液体。
步骤5、将混合液体与纤维通过蒸汽升温至55度，保温40分钟。
步骤6、将纤维取出，脱水、烘干，得到天然乳胶涤纶短纤维。
实施例二
一种天然乳胶纤维包括晴纶纤维100份，天然乳胶原液2份，亲水200份，抗菌剂0.5份。
上述天然乳胶纤维的制备方法如下：
步骤1、将称取各原料备用。
步骤2、将天然乳胶原液与抗菌剂混合搅拌均匀。
步骤3、将混合原液与水混合搅拌均匀，得到液体。
步骤4、将纤维分批放入容器中，同时分批注入混合液体。
步骤5、将混合液体与纤维通过蒸汽升温至50度，保温30分钟。
步骤6、将纤维取出，脱水、烘干，得到天然乳胶晴纶短纤维。
实施例三
一种天然乳胶纤维包括锦纶纤维100份，天然乳胶原液3份，亲水210份，抗菌剂0.5份。
上述天然乳胶纤维的制备方法如下：
步骤1、将称取各原料备用。
步骤2、将天然乳胶原液与抗菌剂混合搅拌均匀。
步骤3、将混合原液与水混合搅拌均匀，得到液体。
步骤4、将纤维分批放入容器中，同时分批注入混合液体。
步骤5、将混合液体与纤维通过蒸汽升温至55度，保温30分钟。
步骤6、将纤维取出，脱水、烘干，得到天然乳胶锦纶短纤维。
实施例四
一种天然乳胶纤维包括莫代尔纤维100份，天然乳胶原液4份，亲水220份，抗菌剂0.6份。
上述天然乳胶纤维的制备方法如下：
步骤1、将称取各原料备用。
步骤2、将天然乳胶原液与抗菌剂混合搅拌均匀。
步骤3、将混合原液与水混合搅拌均匀，得到液体。
步骤4、将纤维分批放入容器中，同时分批注入混合液体。
步骤5、将混合液体与纤维通过蒸汽升温至55度，保温30分钟。
步骤6、将纤维取出，脱水、烘干，得到天然乳胶莫代尔短纤维。
实施例五
一种天然乳胶纤维包括竹纤维100份，天然乳胶原液6份，亲水230份，抗菌剂0.6份。
上述天然乳胶纤维的制备方法如下：
步骤1、将称取各原料备用。
步骤2、将天然乳胶原液与抗菌剂混合搅拌均匀。
步骤3、将混合原液与水混合搅拌均匀，得到液体。
步骤4、将纤维分批放入容器中，同时分批注入混合液体。
步骤5、将混合液体与纤维通过蒸汽升温至58度，保温35分钟。
步骤6、将纤维取出，脱水、烘干，得到天然乳胶竹短纤维。
实施例六
一种天然乳胶纤维包括聚乳酸纤维100份，天然乳胶原液8份，亲水240份，抗菌剂0.7份。
上述天然乳胶纤维的制备方法如下：
步骤1、将称取各原料备用。
步骤2、将天然乳胶原液与抗菌剂混合搅拌均匀。
步骤3、将混合原液与水混合搅拌均匀，得到液体。
步骤4、将纤维分批放入容器中，同时分批注入混合液体。
步骤5、将混合液体与纤维通过蒸汽升温至58度，保温35分钟。
步骤6、将纤维取出，脱水、烘干，得到天然乳胶聚乳酸短纤维。
实施例七
一种天然乳胶纤维包括羊毛纤维100份，天然乳胶原液5份，亲水260份，抗菌剂0.9份。
上述天然乳胶纤维的制备方法如下：
步骤1、将称取各原料备用。
步骤2、将天然乳胶原液与抗菌剂混合搅拌均匀。
步骤3、将混合原液与水混合搅拌均匀，得到液体。
步骤4、将纤维分批放入容器中，同时分批注入混合液体。
步骤5、将混合液体与纤维通过蒸汽升温至58度，保温35分钟。
步骤6、将纤维取出，脱水、烘干，得到天然乳胶羊毛短纤维。
实施例八
一种天然乳胶纤维包括莱赛尔纤维100份，天然乳胶原液6份，亲水280份，抗菌剂1.1份。
上述天然乳胶纤维的制备方法如下：
步骤1、将称取各原料备用。
步骤2、将天然乳胶原液与抗菌剂混合搅拌均匀。
步骤3、将混合原液与水混合搅拌均匀，得到液体。
步骤4、将纤维分批放入容器中，同时分批注入混合液体。
步骤5、将混合液体与纤维通过蒸汽升温至60度，保温40分钟。
步骤6、将纤维取出，脱水、烘干，得到天然乳胶莱赛尔短纤维。
实施例九
一种天然乳胶纤维包括棉花纤维100份，天然乳胶原液4份，亲水300份，抗菌剂1.3份。
上述天然乳胶纤维的制备方法如下：
步骤1、将称取各原料备用。
步骤2、将天然乳胶原液与抗菌剂混合搅拌均匀。
步骤3、将混合原液与水混合搅拌均匀，得到液体。
步骤4、将纤维分批放入容器中，同时分批注入混合液体。
步骤5、将混合液体与纤维通过蒸汽升温至60度，保温40分钟。
步骤6、将纤维取出，脱水、烘干，得到天然乳胶棉花短纤维。
实施例十
一种天然乳胶纤维包括粘胶纤维100份，天然乳胶原液8份，亲水300份，抗菌剂1.3份。
上述天然乳胶纤维的制备方法如下：
步骤1、将称取各原料备用。
步骤2、将天然乳胶原液与抗菌剂混合搅拌均匀。
步骤3、将混合原液与水混合搅拌均匀，得到液体。
步骤4、将纤维分批放入容器中，同时分批注入混合液体。
步骤5、将混合液体与纤维通过蒸汽升温至60度，保温40分钟。
步骤6、将纤维取出，脱水、烘干，得到天然乳胶粘胶短纤维。
本发明的一种天然乳胶纤维，从感观上有一种轻微的乳香味，手感比普通的纤维更柔软更有弹性。
以上所述仅为本发明的优选实施方式而已，并不用于限制本发明。对于本领域的技术人员来说，本发明可以有各种更改和变化，凡在本发明的精神和原则之内所作的任何修改、等同替换、改进等均应包含在本发明的保护范围之内。
Claims (4)
1.一种天然乳胶纤维的制备方法，其特征在于天然乳胶将短纤维包覆。
2.根据权利要求1所述的一种天然乳胶纤维，其特征在于，天然乳胶纤维的份数配比为纤维100份、天然乳胶原液2-8份，亲水200-300份，抗菌剂0.5-1.5份。
3.根据权利要求1-2所述的一种天然乳胶纤维，其特征在于为涤纶、晴纶、锦纶、羽绒、蚕丝、羊毛、莫代尔、莱赛尔、棉花、竹纤维、聚乳酸、粘胶的纤维。
4.跟据权利要求1-3所述的一种天然乳胶纤维制备方法，包括以下步骤：
步骤1、将称取各原料备用。
步骤2、将天然乳胶原液与抗菌剂混合搅拌均匀。
步骤3、将混合原液与水混合搅拌均匀，得到液体。
步骤4、将纤维分批放入容器中，同时分批注入混合液体。
步骤5、将混合液体与纤维通过蒸汽升温至50-60度，保温30-45分钟。
步骤6、将纤维取出，脱水、烘干，得到天然乳胶短纤维。