CN113717688A - 一种漆膜黏合剂及其制备方法和漆膜回贴处理方法 - Google Patents
一种漆膜黏合剂及其制备方法和漆膜回贴处理方法 Download PDFInfo
- Publication number
- CN113717688A CN113717688A CN202110991172.XA CN202110991172A CN113717688A CN 113717688 A CN113717688 A CN 113717688A CN 202110991172 A CN202110991172 A CN 202110991172A CN 113717688 A CN113717688 A CN 113717688A
- Authority
- CN
- China
- Prior art keywords
- paint film
- adhesive
- paint
- parts
- lacquer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本公开涉及一种漆膜黏合剂，所述黏合剂中含有如下重量百分含量的各组分：40‑80重量份的透明漆、0‑50重量份的粳米糊、0‑30重量份的生漆、2‑5重量份的一氧化铅和0‑2重量份的Rocima342。该黏结剂可将起翘、脱落的漆膜快速牢固地粘贴到漆器上，并且主成分与漆器本体材质一致，能够使漆器的外观协调，具有较高粘接强度，在各种环境下施工方便，且在自然环境下长久保存而不脱落。
Description
技术领域
本公开涉及漆器文物保护修复技术领域，具体地，涉及一种漆膜黏合剂及其制备方法和漆膜回贴处理方法。
背景技术
漆器是指采用天然生漆或精制漆等涂饰在各种胎体(包括木胎、夹纻胎、陶胎等)上的器物。漆器在中国的创造和使用历史源远流长。据《韩非子·十过》中记载“尧禅天下，虞舜受之，作为食器，斩山而财之，削踞修之迹，流漆墨其上，输之于宫，为食器”。8000年前的跨湖桥，7000年前的河姆渡，5000年前的良渚遗址直至元明清的都有大量考古出土和传世漆器的实物例证。出土或传世漆器由于漆膜降解老化、环境温湿度突变、水分散失等原因常导致漆膜脆化、起翘，甚至脱落，破坏了漆器文物的美观和完整性。
漆膜是彩绘图案的重要载体，也是漆器文物的精华所在。将漆膜展平后回贴到器物原位是漆器修复保护的要点。漆器修复中漆膜回贴成功的关键在于选择适用的黏合剂以及起翘、脱落漆膜的回贴方法。《中国传统工艺全集·漆艺》记载了“漆工艺所用的黏合剂，主要有干性油、动物胶、生漆等”。干性油、动物胶粘接强度较低，且与漆器本体材质差异大。传统的天然生漆对施工环境的温湿度要求高，常温常湿下固化慢，需要在特定环境下(如放置于温度为20～30℃，相对湿度为60～80％湿度的荫房)才能干燥固化。曾用于漆皮回贴的化学合成胶粘剂有FS-101、D-801、505树脂、聚苯乙烯、Paraloid B72、环氧树脂、白乳胶等，化学合成材料虽施工方便，但合成材料普遍耐老化性较差，仅能保持20～30年时间。因此，研究开发在各种条件下施工方便，具有良好粘结性能的黏合剂及其应用方法具有重要的实际意义。
因此，亟需提供一种有效的科学保护手段，可将起翘、脱落的漆膜快速牢固地粘贴到漆器上，并且漆器本体相容性好，能够使漆器的外观协调，具有较高粘接强度，在各种环境下施工方便，且在自然环境下长久保存而不脱落。
发明内容
本公开的目的是提供一种漆膜黏合剂及其制备方法和漆膜回贴处理方法，可将起翘、脱落的漆膜快速牢固地粘贴到漆器上，且在自然环境下长久保存而不脱落。
为了实现上述目的，本公开第一方面提供了一种漆膜黏合剂，所述黏合剂中包括：40-80重量份的透明漆、0-50重量份的粳米糊、0-30重量份的生漆、2-5重量份的一氧化铅和0-2重量份的Rocima342(二氯辛基异噻唑啉酮防霉防藻剂)。
本公开第二方面提供了第一方面所述黏合剂的制备方法，其中，所述方法包括如下步骤：将粳米糊调入透明漆和生漆中，一次混匀；再加入一氧化铅粉末，二次混匀；加入Rocima342，三次混匀；5-10min后产生黏性，形成黏合剂。
本公开第三方面提供了第一方面所述的黏合剂在漆膜回贴处理中的应用。
本公开第四方面提供了一种漆膜回贴处理方法，所述方法包括如下步骤：
S1、擦除漆膜待粘贴面表面污渍，利用第一方面所述黏合剂将起翘或脱落的漆膜按压回漆器本体；
S2、取无尘纸蘸取酒精擦除回贴漆膜边缘渗出的黏合剂；
S3、利用保湿剂润湿的生宣纸覆盖在漆膜回贴处，再将生宣纸下的气泡按压挤出；
S4、再利用泡沫软垫按压在生宣纸上，固定回贴的漆膜；
S5、1-3min后将生宣纸和泡沫软垫取下，将漆膜表面擦拭干净。
本公开第五方面提供了上述方法在漆膜回贴处理中的应用。
通过上述技术方案，本公开可对传世或出土漆器起翘、脱落漆膜进行有效、快速回贴修复，黏合剂能在各种环境条件下较快固化，可将起翘、脱落的漆膜快速牢固地粘贴到漆器上，与漆器本体相容性好，外观协调，具有较高粘接强度，在各种环境下施工方便，且在自然环境下长久保存而不脱落。
本公开的其他特征和优点将在随后的具体实施方式部分予以详细说明。
附图说明
附图是用来提供对本公开的进一步理解，并且构成说明书的一部分，与下面的具体实施方式一起用于解释本公开，但并不构成对本公开的限制。在附图中：
图1是利用扫描电镜观察黏合剂中各成分的表面微观形貌特征；
图2是实施例1和实施例2分别制备的大漆加粳米糊前后黏合剂的红外光谱对比(a.生漆；b.粳米糊；c.漆糊)；
图3是利用生漆、红锦漆、本公开自制黏合剂I对自制漆膜模拟样品以及本公开自制黏合剂II对考古出土带漆灰层的剥离强度对比情况；
图4是起翘漆膜回贴示意图；
图5是回贴漆膜固定示意图；
图6是考古出土彩绘漆棺修复前的起翘漆膜；
图7是考古出土彩绘漆棺修复后的漆膜情况。
具体实施方式
以下对本公开的具体实施方式进行详细说明。应当理解的是，此处所描述的具体实施方式仅用于说明和解释本公开，并不用于限制本公开。
本公开第一方面提供了一种漆膜黏合剂，所述黏合剂中包括：40-80重量份的透明漆、0-50重量份的粳米糊、0-30重量份的生漆、2-5重量份的一氧化铅和0-2重量份的Rocima342。
根据本公开，其中，所述黏合剂中包括：50-60重量份的透明漆、40-50重量份的粳米糊、2-5重量份的生漆、2-3重量份的一氧化铅和0.5-1重量份的Rocima342。
本公开第二方面提供了第一方面所述黏合剂的制备方法，其中，所述方法包括如下步骤：将粳米糊调入透明漆和生漆中，一次混匀；再加入一氧化铅粉末，二次混匀；加入Rocima342，三次混匀；5-10min后产生黏性，形成黏合剂。
材料的性能与其微观结构息息相关，利用扫描电镜观察黏合剂中各成分的表面微观形貌特征，结果如图1：粳米淀粉的颗粒大小不均匀，颗粒形态主要有圆形、椭圆形及不规则形，椭圆形颗粒存在明显的凹陷；粳米糊颗粒较小，相对较为细腻，粘接层较薄，干燥稍快一些。生漆和透明漆混合后作为胶粘剂成膜后表面会存在大量的孔隙，可能是在干燥过程中漆中的水分散失所致。漆与粳米糊混合在一起，均匀包覆在淀粉颗粒表面，混合物呈现网络结构，从而起到胶黏剂的作用。
如图2所示，生漆样品在3328cm-1处的吸收峰属于漆酚苯环上羟基(-O H)的吸收峰，3011cm-1附近处弱吸收峰为＝CH-键的伸缩振动，993cm-1为苯环上不饱和侧链C＝C平面弯曲伸缩振动，1622cm-1是苯环烯烃C＝C的伸缩振动吸收峰，1018cm-1附近是芳香基醚(C-O-C)引起的对称伸缩振动吸收峰。当生漆中加入粳米糊后(图2c)，对比生漆(图2a)及粳米糊(图2b)的红外光谱，谱峰数量及强度发生了变化，图2c中993cm-1处C＝C吸收峰强度降低，可见粳米糊的加入促使生漆干燥成膜中的氧化聚合反应。相对于生漆3328cm-1处的羟基(O-H)吸收峰的强度增加，并向低波数移动，表明漆酚的羟基与粳米糊的羟基或者羧基能形成众多的分子间的氢键，从而可提高大漆的力学强度和粘接性能。
本公开第三方面提供了第一方面所述黏合剂在漆膜回贴处理中的应用。
如图3所示，生漆、红锦漆、本公开自制黏合剂(自制黏合剂I)对自制漆膜模拟样品以及本公开自制黏合剂(自制黏合剂II)对考古出土带漆灰层的粘接性能比较。对比黏合后的漆膜的剥离强度，可见，本公开自制的黏合剂I和II的剥离强度均大于传统的大漆黏合剂如生漆和红锦漆；本公开自制的漆膜模拟样品无漆灰层的粘接性能相比于考古出土带漆灰层弱一些，因为漆层较薄，配制的黏合剂剥离强度也稍弱，避免了黏合剂粘性过强导致的漆皮起皱。
本公开第四方面提供了一种漆膜回贴处理方法，所述方法包括如下步骤：
S1、擦除漆膜待粘贴面表面污渍，利用第一方面所述黏合剂将起翘或脱落的漆膜按压回漆器本体；
S2、取无尘纸蘸取酒精擦除回贴漆膜边缘渗出的黏合剂；
S3、利用保湿剂润湿的生宣纸覆盖在漆膜回贴处，再将生宣纸下的气泡按压挤出；
S4、再利用泡沫软垫按压在生宣纸上，固定回贴的漆膜；
S5、1-3min后将生宣纸和泡沫软垫取下，将漆膜表面擦拭干净。
根据本公开，其中，步骤S1中所述黏合剂的用量为80-500g/m2。
根据本公开，其中，步骤S3中所述保湿剂为PEG200保湿剂，用量为20mL-150mL/m2。
根据本公开，其中，步骤S4中所述泡沫软垫的厚度为0.5-3cm。
本公开第五方面提供了第四方面所述的方法在漆膜回贴处理中的应用。
下面通过实施例来进一步举例说明本公开，但是本公开并不因此而受到任何限制。
实施例1
以自制无漆灰层漆膜模拟样品为实施对象，将自制漆膜回贴到松木块表面。
无漆灰层漆膜模拟样品制备：在通风橱中将红色推光漆液倾倒适量至干净的聚四氟乙烯薄膜上，用刮漆板反复刮平，直至目测表面完全平整没有明显缺陷或局部不均匀状态；将涂好的漆片放入饱和盐水湿度发生器中(装有氯化钾饱和盐水的干燥器，T＝25℃，RH＝85％)干燥一周后取出、剥离，获得完整的漆膜样品，厚度约为0.1～0.2mm，裁成大小为2cm×2cm的漆片回贴。
回贴步骤及效果：该黏合剂(自制黏合剂I)的组成包括：65重量份的透明漆、30重量份的生漆、5重量份的一氧化铅。用棉签沾取30％的乙醇水溶液对漆膜的背面及木板回贴处轻轻擦拭清理表面污渍；取无尘纸轻轻吸附已清理处残余的乙醇水溶液；用小号平头勾线笔蘸取配好的大漆黏合剂涂在漆膜回贴处，涂抹均匀，涂抹厚度为0.2mm，黏合剂用量为200g/m2；等待5min后待黏合剂产生黏性，用镊子轻轻夹起漆膜，用小号塑料刮楸将漆膜轻轻按压回漆器本体，按压服帖；取无尘纸蘸少许酒精擦掉边缘渗出的大漆黏合剂；取一片大小合适的生宣纸，喷上30体积％的PEG200保湿剂，让保湿剂自然晕染整片宣纸，用吸水性滤纸吸掉多余的保湿剂，不让保湿剂滴下来；将宣纸覆盖在漆膜回贴处，用脱脂棉球将宣纸下的气泡按压挤出；1-3分钟之后观察回贴的漆膜边缘处有无透明黏合剂渗出，把边缘处有黏合剂渗出的地方的宣纸轻轻揭下，取干净棉签蘸取酒精擦拭干净，避免黏合剂干后留下一圈黑线；取一片大小合适的生宣纸，喷上30体积％的PEG200保湿剂，让保湿剂自然晕染整片宣纸，用吸水性滤纸吸掉多余的保湿剂，不让保湿剂滴下来；将宣纸覆盖在漆膜回贴处，用脱脂棉球将宣纸下的气泡按压挤出；用泡沫软垫按在漆膜回贴处，泡沫软垫会在保湿剂的吸附作用下紧紧吸贴在宣纸上，起到固定漆膜的作用；3min后将生宣纸和泡沫软垫取下，将漆膜表面擦拭干净。
实施例2
以考古出土漆膜残块为实施对象，回贴带漆灰彩绘漆膜，厚度约为0.37-3mm。
黏合剂(自制黏合剂II)的制备过程包括：50重量份的透明漆、20重量份的粳米糊、17重量份的生漆、2.5重量份的一氧化铅、0.5重量份的Ro cima342；粳米糊制备方法为：将8g的粳米粉与24mL蒸馏水倒入RVA Sup er4型快速黏度分析仪(澳大利亚NewportScientific)的金属杯中混合，并搅拌均匀，在960r/min下搅拌形成均匀悬浊液后，保持160r/min转速搅拌13min；黏度分析仪在初始温度30℃下保持1min，再以12℃/min提高到温度95℃，95℃下恒温搅拌5min，再以12℃/min降到30℃，保温2min，粳米糊制备完成；然后将制备好的粳米糊按比例调入透明漆和生漆中，用刮楸将漆糊在白瓷板上调制均匀；加入一氧化铅粉末，再次调制均匀；最后加入Roc ima342(二氯辛基异噻唑啉酮)防霉剂，用刮楸混匀待用，10min后黏合剂产生黏性即可使用。
回贴步骤及效果：用棉签沾30体积％的乙醇水溶液对回贴胎体处轻轻擦拭清理，取无尘纸轻轻吸附已清理处残余的乙醇水溶液，用斜头勾线笔蘸取配好的的黏合剂涂在漆膜漆灰层，涂抹均匀，涂抹厚度为0.5mm；用镊子轻轻夹起漆片，用小号塑料刮楸(或有弹性的软竹片)将漆膜轻轻按压回木胎，按压服帖；取无尘纸蘸取少许酒精擦掉边缘渗出的黏合剂；取一片大小合适的生宣纸，喷上35体积％的PEG200保湿剂，让保湿剂自然晕染整片宣纸，用吸水性滤纸吸掉多余的保湿剂，不让保湿剂滴下来；将宣纸覆盖在漆膜回贴处，用脱脂棉球将宣纸下的气泡按压挤出；1-3分钟之后观察回贴的漆膜边缘处有无透明漆渗出，把边缘处有黏合剂渗出的地方的宣纸轻轻揭下，取干净棉签蘸取酒精擦拭干净，避免漆液干后留下一圈黑线；取一片大小合适的生宣纸，喷上35体积％的PEG200保湿剂，让保湿剂自然晕染整片宣纸，用吸水性滤纸吸掉多余的保湿剂，不让保湿剂滴下来。将宣纸覆盖在漆膜回贴处，用脱脂棉球将宣纸下的气泡按压挤出；用泡沫软垫按在漆膜回贴处，泡沫软垫会在保湿剂的吸附作用下紧紧吸贴在宣纸上，起到固定漆膜的作用；待3min后将生宣纸和泡沫软垫取下，将漆膜表面擦拭干净。
实施例3
北方考古出土彩绘漆棺
以北京石景山五里坨明墓出土彩绘漆棺为实施对象，回贴画面无漆灰彩绘漆膜，漆膜厚度约为0.1-0.75mm。
回贴步骤及效果：用棉签蘸取50体积％的乙醇水溶液对漆膜的背面及回贴胎体处轻轻擦拭清理；取无尘纸轻轻吸附已清理处残余的乙醇水溶液；利用与实施例2相同的方法制备黏合剂，不同的是本实施例的黏合剂中不含有粳米糊和Rocima342；等待5分钟后待黏合剂产生黏性，用镊子轻轻夹起漆膜，用小号斜面勾线笔蘸取配好的黏合剂涂在漆膜回贴处，涂抹均匀，涂抹厚度为0.2mm；用小号塑料刮楸将漆膜轻轻按压回漆器本体，按压服帖；取无尘纸蘸取少许酒精擦掉边缘渗出的黏合剂，取一片大小合适的生宣纸，喷上40体积％的PEG200保湿剂，让保湿剂自然晕染整片宣纸，用吸水性滤纸吸掉多余的保湿剂，不让保湿剂滴下来；将宣纸覆盖在漆膜回贴处，用脱脂棉球将宣纸下的气泡按压挤出；1-3分钟之后观察回贴的漆膜边缘处有无透明漆渗出，把边缘处有黏合剂渗出的地方的宣纸轻轻揭下，取干净棉签蘸取酒精擦拭干净，避免漆液干后留下一圈黑线；取一片大小合适的生宣纸，喷上40体积％的PEG200保湿剂，让保湿剂自然晕染整片宣纸，用吸水性滤纸吸掉多余的保湿剂，不让保湿剂滴下来；将宣纸覆盖在漆膜回贴处，用脱脂棉球将宣纸下的气泡按压挤出；用泡沫软垫按在漆膜回贴处，泡沫软垫会在保湿剂的吸附作用下紧紧吸贴在宣纸上，采用竹签和木支架进行支护，起到固定漆膜的作用；待3min后将生宣纸和泡沫软垫取下，将漆膜表面擦拭干净。
通过上述技术方案，本公开所制备的黏合剂可将起翘、脱落的漆膜快速牢固地粘贴到漆器上，并且主成分与漆器本体材质一致，能够使漆器的外观协调，具有较高粘接强度，在各种环境下施工方便，且在自然环境下长久保存而不脱落。
以上结合附图详细描述了本公开的优选实施方式，但是，本公开并不限于上述实施方式中的具体细节，在本公开的技术构思范围内，可以对本公开的技术方案进行多种简单变型，这些简单变型均属于本公开的保护范围。
另外需要说明的是，在上述具体实施方式中所描述的各个具体技术特征，在不矛盾的情况下，可以通过任何合适的方式进行组合，为了避免不必要的重复，本公开对各种可能的组合方式不再另行说明。
此外，本公开的各种不同的实施方式之间也可以进行任意组合，只要其不违背本公开的思想，其同样应当视为本公开所公开的内容。
Claims (9)
1.一种漆膜黏合剂，其特征在于，所述黏合剂中包括：40-80重量份的透明漆、0-50重量份的粳米糊、0-30重量份的生漆、2-5重量份的一氧化铅和0-2重量份的Rocima342。
2.根据权利要求1所述的黏合剂，其中，所述黏合剂中包括：50-60重量份的透明漆、40-50重量份的粳米糊、2-5重量份的生漆、2-3重量份的一氧化铅和0.5-1重量份的Rocima342。
3.权利要求1或2所述黏合剂的制备方法，其中，所述方法包括如下步骤：将粳米糊调入透明漆和生漆中，一次混匀；再加入一氧化铅粉末，二次混匀；加入Rocima342，三次混匀；5-10min后产生黏性，形成黏合剂。
4.权利要求1或2所述的黏合剂在漆膜回贴处理中的应用。
5.一种漆膜回贴处理方法，其特征在于，所述方法包括如下步骤：
S1、擦除漆膜待粘贴面表面污渍，利用权利要求1或2所述黏合剂将起翘或脱落的漆膜按压回漆器本体；
S2、取无尘纸蘸取酒精擦除回贴漆膜边缘渗出的黏合剂；
S3、利用保湿剂润湿的生宣纸覆盖在漆膜回贴处，再将生宣纸下的气泡按压挤出；
S4、再利用泡沫软垫按压在生宣纸上，固定回贴的漆膜；
S5、1-3min后将生宣纸和泡沫软垫取下，将漆膜表面擦拭干净。
6.根据权利要求5所述的方法，其中，步骤S1中所述黏合剂的用量为80-500g/m2。
7.根据权利要求5所述的方法，其中，步骤S3中所述保湿剂为PEG200保湿剂，用量为20mL-150mL/m2。
8.根据权利要求5所述的方法，其中，步骤S4中所述泡沫软垫的厚度为0.5-3cm。
9.权利要求5-8任意一项所述的方法在漆膜回贴处理中的应用。