CN113663465A - 一种能够祛除甲醛净化空气的湿巾 - Google Patents
一种能够祛除甲醛净化空气的湿巾 Download PDFInfo
- Publication number
- CN113663465A CN113663465A CN202110959058.9A CN202110959058A CN113663465A CN 113663465 A CN113663465 A CN 113663465A CN 202110959058 A CN202110959058 A CN 202110959058A CN 113663465 A CN113663465 A CN 113663465A
- Authority
- CN
- China
- Prior art keywords
- parts
- wet tissue
- cellulose
- aloe gel
- purifying air
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及空气净化技术领域，且公开了一种能够祛除甲醛净化空气的湿巾；本能够祛除甲醛净化空气的湿巾包括如下原料：芦荟胶纤维素、乙醇、渗透剂、去离子水和二氧化钛，本发明擦拭家具表面后，在水份渗透的带动下进入板材等污染物释放通道中，将脲醛树脂中的不稳定结构的氧脱除，继而发生中和反应(高分子聚合反应)，改变分子结构，生成稳定的树脂类固体物质，反应产生的树脂固体物质留存在游离甲醛挥发必须的细微孔隙中，阻止外界的潮气进入，杜绝脲醛树脂胶遇潮分解的问题，同时添加二氧化钛光触媒成分，可以在光的照射下可以产生催化作用，从而起到基材表面抗菌的作用。
Description
技术领域
本发明属于空气净化技术领域，具体为一种能够祛除甲醛净化空气的湿巾。
背景技术
新装修的室内空间，甲醛最大的污染源通常是家具，柜体，木饰面板等。因为其中板材使用的粘合剂主要成份是脲醛树脂，而脲醛树脂的部分结构不稳定，遇到空气中的水分子会发生水解，析出甲醛，这种结构特性是潮湿环境中室内甲醛浓度会升高的主要原因。由于在污染源的板材内部不是以甲醛分子的形式存在的，所以甲醛释放期会长达3-15年。
现有的祛除甲醛的方法多为自然通风祛除，但是此种方法一来效率较慢，二来在房屋空置的过程中，家具表面会积灰，时间较长的情况下，可能结成污垢，影响后期使用的美观性；因此，针对目前的状况，现需对其进行改进。
发明内容
针对上述情况，为克服现有技术的缺陷，本发明提供一种能够祛除甲醛净化空气的湿巾，有效的解决了现有的祛除甲醛的方法多为自然通风祛除，但是此种方法一来效率较慢，二来在房屋空置的过程中，家具表面会积灰，时间较长的情况下，可能结成污垢，影响后期使用的美观性的问题。
为实现上述目的，本发明提供如下技术方案：一种能够祛除甲醛净化空气的湿巾，包括如下原料：芦荟胶纤维素、乙醇、渗透剂、去离子水、二氧化钛，所述各原料的重量份数为：芦荟胶纤维素6-8份、乙醇2-3份、渗透剂1-1.5份、去离子水90-95份和二氧化钛2-4份。
优选的，所述芦荟胶纤维素占总分量比例为3-4％、所述乙醇占总分量比例为0.5-1％、所述渗透剂占总分量比例为0.3-1％、所述去离子水占总分量比例为90-95％和所述二氧化钛占总分量比例为1-2％。
优选的，所述芦荟胶纤维素具体为芦荟胶和纤维素的聚合物，所述纤维素为细菌纤维素，且所述芦荟胶和所述纤维素的聚合比例为6:4。
优选的，所述渗透剂具体为硫酸化蓖麻油、烷基磺酸钠、烷基苯磺酸钠、烷基硫酸酯钠、仲烷基磺酸钠、仲烷基硫酸酯钠、α一烯基磺酸钠、烷基萘磺酸钠、琥珀酸烷基酯磺酸钠、胰加漂T、氨基磺酸钠、脂肪醇聚氧乙烯醚、烷基酚聚氧乙烯醚、聚醚和磷酸酯类化合物中一种或几种的组合。
优选的，所述能够祛除甲醛净化空气的湿巾的制备方法包括以下步骤：
S1：准备材料：准备芦荟胶4-5份、细菌纤维素2-3份、乙醇2-3份、渗透剂1-1.5份、去离子水90-95份、二氧化钛2-4份和干巾200-300份放置备用；
S2：聚合混合：将芦荟胶4-5份和细菌纤维素2-3份放入搅拌釜中进行混合搅拌，搅拌时控制搅拌转速为700-850r/min，且控制搅拌时间为2-3min，使得芦荟胶和细菌纤维素完全混合；
S3：原料混合：在步骤S2的基础上，向搅拌釜中加入乙醇2-3份、渗透剂1-1.5份、去离子水90-95份、和二氧化钛2-4份，搅拌时控制搅拌转速为1000-1200r/min，且控制搅拌时间为10-12min，直至原料完全混合后倒出至盛放容器；
S4：干巾浸泡：将干巾200-300份放入步骤S3中盛放了混合原料的容器中，使干巾完全浸泡入混合原料中，浸泡时间控制在15-18min，浸泡完全后，得到湿巾，将湿巾经过杀菌后再包装，即得到能够祛除甲醛净化空气的湿巾。
优选的，所述干巾材质为粘胶纤维和涤纶纤维混合而成，且所述粘胶纤维和涤纶纤维的混合比例为3:7，所述粘胶纤维和涤纶纤维采用交叉铺网的成型工艺，且所述干巾表面设置有均匀分布的凸点。
优选的，所述步骤S2-S3中，搅拌釜采用3000L型搪瓷开式恒温恒压反应釜，且在使用反应釜时控制反应压力在0.30-0.35Mpa，反应温度控制在22-24℃。
优选的，所述步骤S4中，湿巾杀菌采用磁力杀菌机，且杀菌时间为2-3min，湿巾包装采用QX-260型全自动单片湿巾包装机。
与现有技术相比，本发明的有益效果是：1、本发明，擦拭家具表面后，在水份渗透的带动下进入板材等污染物释放通道中，将脲醛树脂中的不稳定结构的氧脱除，继而发生中和反应(高分子聚合反应)，改变分子结构，生成稳定的树脂类固体物质，反应产生的树脂固体物质留存在游离甲醛挥发必须的细微孔隙中，阻止外界的潮气进入，杜绝脲醛树脂胶遇潮分解的问题，同时添加二氧化钛光触媒成分，可以在光的照射下可以产生催化作用，从而起到基材表面抗菌的作用；
2、本发明，细菌纤维素是一种天然的、对环境友好、性能优异的纳米生态纤维功能材料，它具有良好的纳米纤维三网络状结构特征，它的多孔结构，具有表面积大、孔隙多的特点，且对甲醛具有一定的吸附效果，通过将芦荟胶和细菌纤维素聚合得到的芦荟胶纤维素，可通过湿巾擦拭家具表面后残留在家具表面，对空气中的甲醛进行吸附，从而避免空气中残留甲醛对人体造成伤害；
3、本发明，在对基材表面的无腐蚀性，对人皮肤无刺激无伤害的基本条件下，可以减少家具表面脲醛树脂遇水释放甲醛的问题，同时基材有长效抗菌的作用，并能够实现批量生产，且生产过程简单，易于推广。
附图说明
附图用来提供对本发明的进一步理解，并且构成说明书的一部分，与本发明的实施例一起用于解释本发明，并不构成对本发明的限制。
在附图中：
图1为本发明流程图；
具体实施方式
下面将结合本发明实施例中的附图，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例；基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
为实现上述目的，本发明提供如下技术方案：一种能够祛除甲醛净化空气的湿巾，包括如下原料：芦荟胶纤维素、乙醇、渗透剂、去离子水和二氧化钛，各原料的重量份数为：芦荟胶纤维素6-8份、乙醇2-3份、渗透剂1-1.5份、去离子水90-95份和二氧化钛2-4份。
芦荟胶纤维素占总分量比例为3-4％、乙醇占总分量比例为0.5-1％、渗透剂占总分量比例为0.3-1％、去离子水占总分量比例为90-95％、二氧化钛占总分量比例为1-2％。
| 材料名 | 单位(份) | 占总分量比(％) |
| 芦荟胶纤维素 | 6-8份 | 3-4％ |
| 乙醇 | 2-3份 | 0.5-1％ |
| 渗透剂 | 1-1.5份 | 0.3-1％ |
| 去离子水 | 90-95份 | 90-95％ |
| 二氧化钛 | 2-4份 | 1-2％ |
芦荟胶纤维素具体为芦荟胶和纤维素的聚合物，纤维素为细菌纤维素，且芦荟胶和纤维素的聚合比例为6:4。
渗透剂具体为硫酸化蓖麻油、烷基磺酸钠、烷基苯磺酸钠、烷基硫酸酯钠、仲烷基磺酸钠、仲烷基硫酸酯钠、α一烯基磺酸钠、烷基萘磺酸钠、琥珀酸烷基酯磺酸钠、胰加漂T、氨基磺酸钠、脂肪醇聚氧乙烯醚、烷基酚聚氧乙烯醚、聚醚和磷酸酯类化合物中一种或几种的组合。
如图1所示，一种能够祛除甲醛净化空气的湿巾的制备方法，包括以下步骤：
S1：准备材料：准备芦荟胶4-5份、细菌纤维素2-3份、乙醇2-3份、渗透剂1-1.5份、去离子水90-95份、二氧化钛2-4份和干巾200-300份放置备用；
S2：聚合混合：将芦荟胶4-5份和细菌纤维素2-3份放入搅拌釜中进行混合搅拌，搅拌时控制搅拌转速为700-850r/min，且控制搅拌时间为2-3min，使得芦荟胶和细菌纤维素完全混合；
S3：原料混合：在步骤S2的基础上，向搅拌釜中加入乙醇2-3份、渗透剂1-1.5份、去离子水90-95份和二氧化钛2-4份，搅拌时控制搅拌转速为1000-1200r/min，且控制搅拌时间为10-12min，直至原料完全混合后倒出至盛放容器；
S4：干巾浸泡：将干巾200-300份放入步骤S3中盛放了混合原料的容器中，使干巾完全浸泡入混合原料中，浸泡时间控制在15-18min，浸泡完全后，得到湿巾，将湿巾经过杀菌后再包装，即得到能够祛除甲醛净化空气的湿巾。
其中，干巾材质为粘胶纤维和涤纶纤维混合而成，且粘胶纤维和涤纶纤维的混合比例为3:7，粘胶纤维和涤纶纤维采用交叉铺网的成型工艺，且干巾表面设置有均匀分布的凸点；步骤S2-S3中，搅拌釜采用3000L型搪瓷开式恒温恒压反应釜，且在使用反应釜时控制反应压力在0.30-0.35Mpa，反应温度控制在22-24℃；步骤S4中，湿巾杀菌采用磁力杀菌机，且杀菌时间为2-3min，湿巾包装采用QX-260型全自动单片湿巾包装机。
实施例一
一种能够祛除甲醛净化空气的湿巾的制备方法，包括以下步骤：
S1：准备材料：准备芦荟胶4份、细菌纤维素2份、乙醇2份、渗透剂1份、去离子水90份、二氧化钛2份和干巾200份放置备用；
S2：聚合混合：将芦荟胶4份和细菌纤维素2份放入搅拌釜中进行混合搅拌，搅拌时控制搅拌转速为700r/min，且控制搅拌时间为3min，使得芦荟胶和细菌纤维素完全混合；
S3：原料混合：在步骤S2的基础上，向搅拌釜中加入乙醇2份、渗透剂1份、去离子水90份和二氧化钛2份，搅拌时控制搅拌转速为1000r/min，且控制搅拌时间为10min，直至原料完全混合后倒出至盛放容器；
S4：干巾浸泡：将干巾200份放入步骤S3中盛放了混合原料的容器中，使干巾完全浸泡入混合原料中，浸泡时间控制在15min，浸泡完全后，得到湿巾，将湿巾经过杀菌后再包装，即得到能够祛除甲醛净化空气的湿巾。
通过上述方法制备能够祛除甲醛净化空气的湿巾，擦拭家具表面后，在水份渗透的带动下进入板材等污染物释放通道中，将脲醛树脂中的不稳定结构的氧脱除，继而发生中和反应(高分子聚合反应)，改变分子结构，生成稳定的树脂类固体物质，反应产生的树脂固体物质留存在游离甲醛挥发必须的细微孔隙中，阻止外界的潮气进入，杜绝脲醛树脂胶遇潮分解的问题，同时添加二氧化钛光触媒成分，可以在光的照射下可以产生催化作用，从而起到基材表面抗菌的作用。
实施例二
一种能够祛除甲醛净化空气的湿巾的制备方法，包括以下步骤：
S1：准备材料：准备芦荟胶5份、细菌纤维素3份、乙醇3份、渗透剂1.5份、去离子水95份、二氧化钛4份和干巾300份放置备用；
S2：聚合混合：将芦荟胶5份和细菌纤维素3份放入搅拌釜中进行混合搅拌，搅拌时控制搅拌转速为850r/min，且控制搅拌时间为2min，使得芦荟胶和细菌纤维素完全混合；
S3：原料混合：在步骤S2的基础上，向搅拌釜中加入乙醇3份、渗透剂1.5份、去离子水95份、和二氧化钛4份，搅拌时控制搅拌转速为1200r/min，且控制搅拌时间为12min，直至原料完全混合后倒出至盛放容器；
S4：干巾浸泡：将干巾300份放入步骤S3中盛放了混合原料的容器中，使干巾完全浸泡入混合原料中，浸泡时间控制在18min，浸泡完全后，得到湿巾，将湿巾经过杀菌后再包装，即得到能够祛除甲醛净化空气的湿巾。
通过上述方法制备能够祛除甲醛净化空气的湿巾，细菌纤维素是一种天然的、对环境友好、性能优异的纳米生态纤维功能材料，它具有良好的纳米纤维三网络状结构特征，它的多孔结构，具有表面积大、孔隙多的特点，且对甲醛具有一定的吸附效果，通过将芦荟胶和细菌纤维素聚合得到的芦荟胶纤维素，可通过湿巾擦拭家具表面后残留在家具表面，对空气中的甲醛进行吸附，从而避免空气中残留甲醛对人体造成伤害。
实施例三
一种能够祛除甲醛净化空气的湿巾的制备方法，包括以下步骤：
S1：准备材料：准备芦荟胶4.5份、细菌纤维素2.5份、乙醇2.5份、渗透剂1.25份、去离子水93份、二氧化钛3份和干巾250份放置备用；
S2：聚合混合：将芦荟胶4.5份和细菌纤维素2.5份放入搅拌釜中进行混合搅拌，搅拌时控制搅拌转速为850r/min，且控制搅拌时间为2min，使得芦荟胶和细菌纤维素完全混合；
S3：原料混合：在步骤S2的基础上，向搅拌釜中加入乙醇2.5份、渗透剂1.25份、去离子水93份和二氧化钛3份，搅拌时控制搅拌转速为1200r/min，且控制搅拌时间为12min，直至原料完全混合后倒出至盛放容器；
S4：干巾浸泡：将干巾250份放入步骤S3中盛放了混合原料的容器中，使干巾完全浸泡入混合原料中，浸泡时间控制在18min，浸泡完全后，得到湿巾，将湿巾经过杀菌后再包装，即得到能够祛除甲醛净化空气的湿巾。
通过上述方法制备能够祛除甲醛净化空气的湿巾，在对基材表面的无腐蚀性，对人皮肤无刺激无伤害的基本条件下，可以减少家具表面脲醛树脂遇水释放甲醛的问题，同时基材有长效抗菌的作用，并能够实现批量生产，且生产过程简单，易于推广。
需要说明的是，在本文中，诸如第一和第二等之类的关系术语仅仅用来将一个实体或者操作与另一个实体或操作区分开来，而不一定要求或者暗示这些实体或操作之间存在任何这种实际的关系或者顺序。而且，术语“包括”、“包含”或者其任何其他变体意在涵盖非排他性的包含，从而使得包括一系列要素的过程、方法、物品或者设备不仅包括那些要素，而且还包括没有明确列出的其他要素，或者是还包括为这种过程、方法、物品或者设备所固有的要素。
尽管已经示出和描述了本发明的实施例，对于本领域的普通技术人员而言，可以理解在不脱离本发明的原理和精神的情况下可以对这些实施例进行多种变化、修改、替换和变型，本发明的范围由所附权利要求及其等同物限定。
Claims (8)
1.一种能够祛除甲醛净化空气的湿巾，其特征在于：包括如下原料：芦荟胶纤维素、乙醇、渗透剂、去离子水和二氧化钛，所述各原料的重量份数为：芦荟胶纤维素6-8份、乙醇2-3份、渗透剂1-1.5份、去离子水90-95份和二氧化钛2-4份。
2.根据权利要求1所述的一种能够祛除甲醛净化空气的湿巾，其特征在于：所述芦荟胶纤维素占总分量比例为3-4％、所述乙醇占总分量比例为0.5-1％、所述渗透剂占总分量比例为0.3-1％、所述去离子水占总分量比例为90-95％％和所述二氧化钛占总分量比例为1-2％。
3.根据权利要求1所述的一种能够祛除甲醛净化空气的湿巾，其特征在于：所述芦荟胶纤维素具体为芦荟胶和纤维素的聚合物，所述纤维素为细菌纤维素，且所述芦荟胶和所述纤维素的聚合比例为6:4。
4.根据权利要求1所述的一种能够祛除甲醛净化空气的湿巾，其特征在于：所述渗透剂具体为硫酸化蓖麻油、烷基磺酸钠、烷基苯磺酸钠、烷基硫酸酯钠、仲烷基磺酸钠、仲烷基硫酸酯钠、α一烯基磺酸钠、烷基萘磺酸钠、琥珀酸烷基酯磺酸钠、胰加漂T、氨基磺酸钠、脂肪醇聚氧乙烯醚、烷基酚聚氧乙烯醚、聚醚和磷酸酯类化合物中一种或几种的组合。
5.根据权利要求1所述的一种能够祛除甲醛净化空气的湿巾，其特征在于：所述能够祛除甲醛净化空气的湿巾的制备方法包括以下步骤：
S1：准备材料：准备芦荟胶4-5份、细菌纤维素2-3份、乙醇2-3份、渗透剂1-1.5份、去离子水90-95份、二氧化钛2-4份和干巾200-300份放置备用；
S2：聚合混合：将芦荟胶4-5份和细菌纤维素2-3份放入搅拌釜中进行混合搅拌，搅拌时控制搅拌转速为700-850r/min，且控制搅拌时间为2-3min，使得芦荟胶和细菌纤维素完全混合；
S3：原料混合：在步骤S2的基础上，向搅拌釜中加入乙醇2-3份、渗透剂1-1.5份、去离子水90-95份和二氧化钛2-4份，搅拌时控制搅拌转速为1000-1200r/min，且控制搅拌时间为10-12min，直至原料完全混合后倒出至盛放容器；
S4：干巾浸泡：将干巾200-300份放入步骤S3中盛放了混合原料的容器中，使干巾完全浸泡入混合原料中，浸泡时间控制在15-18min，浸泡完全后，得到湿巾，将湿巾经过杀菌后再包装，即得到能够祛除甲醛净化空气的湿巾。
6.根据权利要求5所述的一种能够祛除甲醛净化空气的湿巾，其特征在于：所述干巾材质为粘胶纤维和涤纶纤维混合而成，且所述粘胶纤维和涤纶纤维的混合比例为3:7，所述粘胶纤维和涤纶纤维采用交叉铺网的成型工艺，且所述干巾表面设置有均匀分布的凸点。
7.根据权利要求5所述的一种能够祛除甲醛净化空气的湿巾，其特征在于：所述步骤S2-S3中，搅拌釜采用3000L型搪瓷开式恒温恒压反应釜，且在使用反应釜时控制反应压力在0.30-0.35Mpa，反应温度控制在22-24℃。
8.根据权利要求5所述的一种能够祛除甲醛净化空气的湿巾，其特征在于：所述步骤S4中，湿巾杀菌采用磁力杀菌机，且杀菌时间为2-3min，湿巾包装采用QX-260型全自动单片湿巾包装机。