CN113561697A - Preparation method of cinnabar picture - Google Patents
Preparation method of cinnabar picture Download PDFInfo
- Publication number
- CN113561697A CN113561697A CN202110850904.3A CN202110850904A CN113561697A CN 113561697 A CN113561697 A CN 113561697A CN 202110850904 A CN202110850904 A CN 202110850904A CN 113561697 A CN113561697 A CN 113561697A
- Authority
- CN
- China
- Prior art keywords
- glue
- cinnabar
- picture
- brushing
- mass ratio
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a preparation method of a cinnabar picture, which comprises the following steps: painting on the bottom plate by using oil painting pigment; after the picture is dried completely, brushing a layer of glue 1 in sequence to bond white sand; after the glue 1 is dried completely, brushing a layer of glue 1, bonding cinnabar and drying; and (3) applying glue 2 again, brushing the glue 2 on the place where the original stone and the tree branches need to be bonded, framing, and finishing the cinnabar picture. The cinnabar picture is mainly combined with an oil painting drawing technique, the artistic conception of the wash painting is infiltrated, cinnabar, original stone, branches, white sand and glue are contained, the wash painting has a thick three-dimensional effect, the artistic conception of the picture is not lost, after the picture is completely processed, the glue is added in proportion to glue cinnabar, in order to reflect the crystal feeling of cinnabar, the cinnabar picture is manufactured by firstly brushing glue, then gluing sand, adding the original stone and the branches after drying, and adopting different glues to glue.
Description
Technical Field
The invention belongs to the technical field of industrial art, and particularly relates to a preparation method of a cinnabar painting.
Background
Cinnabar is generally called cinnabar, which is also called Binxian cinnabar, dansha, red lead and mercurous chloride, and is a mineral of mercuric sulfide (HgS). The crystal belongs to trigonal system and is homogeneous and multiple images with cinnabar of isometric system. Often in the shape of a rhombohedron or a short cylinder; usually throughout the twins. Complete cleavage with parallel cylindrical surfaces. The aggregate is in the form of granules, blocks or films. Mohs hardness is 2.5, and specific gravity is 8.10. The color is red, and the crystal surface has streaky red and is semitransparent. The pure cinnabar is golden and bright and vermilion; when the pigment contains impurities, the pigment is dull and brownish red.
At present, cinnabar paintings are made by painting on special painting paper and gluing, and the method needs a lot of time, and the pictures have poor artistic sense and poor stereoscopic impression.
The present invention has been made in view of the above circumstances.
Disclosure of Invention
In order to solve the problems in the prior art, the cinnabar picture provided by the invention mainly combines a technique of drawing an oil picture, permeates the artistic conception of a wash painting, has stereoscopic impression, does not lose the primary colors of original sand and original stone, and can embody the crystal color of cinnabar.
In order to achieve the purpose, the invention adopts the following technical scheme:
a preparation method of the cinnabar picture comprises the following steps:
(1) painting on the bottom plate by using oil painting pigment;
(2) after the picture is dried completely, brushing a layer of glue 1 in sequence to bond white sand;
(3) after the glue 1 is dried completely, brushing a layer of glue 1, bonding cinnabar and drying;
(4) and (3) applying glue 2 again, brushing the glue 2 on the place where the original stone and the tree branches need to be bonded, framing, and finishing the cinnabar picture.
Further, the glue 1 in the steps (1) and (2) is AB glue.
The AB glue is a different name of two-liquid mixed hardening glue, one liquid is the glue, the other liquid is the hardening agent, the two liquids can be hardened after being mixed, and the glue can be hardened without depending on temperature, so the AB glue is one of normal-temperature hardening glue, can be used for making models sometimes and is generally used in industry.
The component A is acrylic modified epoxy or epoxy resin or contains catalyst and other assistants, and the component B is modified amine or other hardener or contains catalyst and other assistants. Mixing at a certain ratio. The catalyst may control the cure time and other adjuvants may control properties (e.g., viscosity, stiffness, flexibility, adhesion, etc.).
The modified acrylic acid modified epoxy or epoxy resin adhesive has the characteristic of quick drying, and can be dried completely within 5 minutes at 25 ℃ after A \ B is mixed, and the drying time is shorter when the temperature is higher. The adhesive can be used for bonding plastics and plastics, plastics and metal, and after bonding, peeling needs a cutter or hot melting separation. The plastic and the plastic have good bonding effect, almost equal to the strength of ABS, and can be widely used for manual manufacturing improvement.
Further, the mass ratio of the glue 1 to the white sand in the step (2) is 1: 2-4.
Further, the mass ratio of the glue 1 to the white sand in the step (2) is 1:3.
The white sand in the invention is quartz sand.
Further, the mass ratio of the glue 1 to the cinnabar in the step (3) is 1: 1.5-2.5.
Further, the mass ratio of the glue 1 to the cinnabar in the step (3) is 1:2.
Cinnabar is generally called cinnabar, which is also called Binxian cinnabar, dansha, red lead and mercurous chloride, and is a mineral of mercuric sulfide (HgS). The crystal belongs to trigonal system and is homogeneous and multiple images with cinnabar of isometric system. Often in the shape of a rhombohedron or a short cylinder; usually throughout the twins. Complete cleavage with parallel cylindrical surfaces. The aggregate is in the form of granules, blocks or films. Mohs hardness is 2.5, and specific gravity is 8.10. The color is red, and the crystal surface has streaky red and is semitransparent. The pure cinnabar is golden and bright and vermilion; when the pigment contains impurities, the pigment is dull and brownish red.
Further, the glue 2 in the step (4) is a mixture of a molding paste and white latex.
The white latex is one of the most widely used, most used and long-term water-soluble adhesives, and is a thermoplastic adhesive prepared by the polymerization reaction of vinyl acetate monomers under the action of an initiator. The adhesive can be cured at normal temperature, is cured quickly, has high adhesive strength, and has good toughness and durability and is not easy to age.
The white latex is one of the adhesive varieties which have the widest application and the largest use amount at present. It is prepared by emulsion polymerization with water as a dispersion medium, and is a water-based environment-friendly adhesive. The adhesive has the characteristics of good film forming property, high bonding strength, high curing speed, good dilute acid and alkali resistance, convenient use, low price, no organic solvent and the like, is widely applied to the industries of wood, furniture, decoration, printing, textile, leather, paper making and the like, and becomes a familiar adhesive.
Further, the mass ratio of the molding paste to the white latex is 3-5: 1.
Further, the mass ratio of the molding paste to the white latex is 4: 1.
The molding paste of the present invention is a white hard clay mass, which is sold as a molding material along with various brands of polymeric pigments. The molding compound is essentially a harder, less fluid polymeric base.
All the raw materials required in the invention are commercial products.
Further, the mass ratio of the raw stone, the glue 2 and the branches in the step (4) is 3-5:1-3: 1.
Further, the mass ratio of the raw stone, the glue 2 and the branches in the step (4) is 4:2: 1.
Raw stone refers to a certain natural ore without processing, including jade raw stone, agate raw stone, crystal raw stone, diamond raw stone, etc.
Compared with the prior art, the invention has the beneficial effects that:
the cinnabar picture is mainly combined with an oil painting drawing technique, the artistic conception of the wash painting is infiltrated, cinnabar, original stone, branches, white sand and glue are contained, so that the wash painting has a thick three-dimensional effect, the artistic conception of the picture is not lost, after the picture is completely processed, the glue is added in proportion to glue cinnabar, and in order to reflect the crystal feeling of cinnabar, when the cinnabar picture is manufactured, the sand and the glue are not stirred, but the sand is firstly brushed and then pasted, the original stone and the branches are added after the sand is dried completely, and the cinnabar picture is formed by pasting different glues.
Detailed Description
In order to make the objects, technical solutions and advantages of the present invention more apparent, the technical solutions of the present invention will be described in detail below. It is to be understood that the described embodiments are merely exemplary of the invention, and not restrictive of the full scope of the invention. All other embodiments, which can be derived by a person skilled in the art from the examples given herein without any inventive step, are within the scope of the present invention.
Example 1
The preparation method of the cinnabar picture comprises the following steps:
(1) painting on the bottom plate by using oil painting pigment;
(2) after the picture is dried completely, brushing a layer of AB glue on the picture, and bonding white sand, wherein the mass ratio of the AB glue to the white sand is 1: 2;
(3) after the AB glue is dried completely, brushing a layer of AB glue, bonding cinnabar, and drying in the air, wherein the mass ratio of the AB glue to the cinnabar is 1: 1.5;
(4) and (3) applying glue 2 again, brushing the glue 2 on the place where the original stone and the tree branches need to be bonded, framing, and finishing the cinnabar picture, wherein the glue 2 is a mixture of a molding paste and white latex, the mass ratio of the molding paste to the white latex is 3:1, and the mass ratio of the original stone, the glue 2 to the tree branches is 3:1: 1.
Example 2
The preparation method of the cinnabar picture comprises the following steps:
(1) painting on the bottom plate by using oil painting pigment;
(2) after the picture is dried completely, brushing a layer of AB glue on the picture, and bonding white sand, wherein the mass ratio of the AB glue to the white sand is 1: 3;
(3) after the AB glue is dried completely, brushing a layer of AB glue, bonding cinnabar, and drying in the air, wherein the mass ratio of the AB glue to the cinnabar is 1: 2;
(4) and (3) applying glue 2 again, brushing the glue 2 on the place where the original stone and the tree branches need to be bonded, framing, and finishing the cinnabar picture, wherein the glue 2 is a mixture of a molding paste and white latex, the mass ratio of the molding paste to the white latex is 4:1, and the mass ratio of the original stone, the glue 2 to the tree branches is 4:2: 1.
Example 3
The preparation method of the cinnabar picture comprises the following steps:
(1) painting on the bottom plate by using oil painting pigment;
(2) after the picture is dried completely, brushing a layer of AB glue on the picture, and bonding white sand, wherein the mass ratio of the AB glue to the white sand is 1: 4;
(3) after the AB glue is dried completely, brushing a layer of AB glue, bonding cinnabar, and drying in the air, wherein the mass ratio of the AB glue to the cinnabar is 1: 2.5;
(4) and (3) applying glue 2 again, brushing the glue 2 on the place where the original stone and the tree branches need to be bonded, framing, and finishing the cinnabar picture, wherein the glue 2 is a mixture of a molding paste and white latex, the mass ratio of the molding paste to the white latex is 5:1, and the mass ratio of the original stone, the glue 2 to the tree branches is 5:3: 1.
Example 4
The preparation method of the cinnabar picture comprises the following steps:
(1) painting on the bottom plate by using oil painting pigment;
(2) after the picture is dried completely, brushing a layer of AB glue on the picture, and bonding white sand, wherein the mass ratio of the AB glue to the white sand is 1: 2.5;
(3) after the AB glue is dried completely, brushing a layer of AB glue, bonding cinnabar, and drying in the air, wherein the mass ratio of the AB glue to the cinnabar is 1: 1.8;
(4) and (3) applying glue 2 again, brushing the glue 2 on the place where the original stone and the tree branches need to be bonded, framing, and finishing the cinnabar picture, wherein the glue 2 is a mixture of a molding paste and white latex, the mass ratio of the molding paste to the white latex is 3.5:1, and the mass ratio of the original stone, the glue 2 to the tree branches is 3.5:1.5: 1.
Example 6
The preparation method of the cinnabar picture comprises the following steps:
(1) painting on the bottom plate by using oil painting pigment;
(2) after the picture is dried completely, brushing a layer of AB glue on the picture, and bonding white sand, wherein the mass ratio of the AB glue to the white sand is 1: 3.5;
(3) after the AB glue is dried completely, brushing a layer of AB glue, bonding cinnabar, and drying in the air, wherein the mass ratio of the AB glue to the cinnabar is 1: 2.3;
(4) and (3) applying glue 2 again, brushing the glue 2 on the place where the original stone and the tree branches need to be bonded, framing, and finishing the cinnabar picture, wherein the glue 2 is a mixture of a molding paste and white latex, the mass ratio of the molding paste to the white latex is 4.5:1, and the mass ratio of the original stone, the glue 2 to the tree branches is 4.5:2.5: 1.
The above description is only for the specific embodiments of the present invention, but the scope of the present invention is not limited thereto, and any person skilled in the art can easily conceive of the changes or substitutions within the technical scope of the present invention, and all the changes or substitutions should be covered within the scope of the present invention. Therefore, the protection scope of the present invention shall be subject to the protection scope of the appended claims.
Claims (10)
1. The preparation method of the cinnabar picture is characterized by comprising the following steps of:
(1) painting on the bottom plate by using oil painting pigment;
(2) after the picture is dried completely, brushing a layer of glue 1 in sequence to bond white sand;
(3) after the glue 1 is dried completely, brushing a layer of glue 1, bonding cinnabar and drying;
(4) and (3) applying glue 2 again, brushing the glue 2 on the place where the original stone and the tree branches need to be bonded, framing, and finishing the cinnabar picture.
2. The preparation method of the cinnabar picture as claimed in claim 1, wherein the glue 1 in steps (1) and (2) is AB glue.
3. The preparation method of the cinnabar picture as claimed in claim 1 or 2, wherein the mass ratio of the glue 1 to the white sand in the step (2) is 1: 2-4.
4. The preparation method of the cinnabar picture as claimed in claim 3, wherein the mass ratio of the glue 1 to the white sand in the step (2) is 1:3.
5. The preparation method of the cinnabar picture as claimed in claim 1, wherein the mass ratio of the glue 1 to the cinnabar in the step (3) is 1: 1.5-2.5.
6. The preparation method of the cinnabar picture as claimed in claim 5, wherein the mass ratio of the glue 1 to the cinnabar in the step (3) is 1:2.
7. The method for preparing the cinnabar picture as claimed in claim 1, wherein the glue 2 in step (4) is a mixture of a molding paste and a white latex.
8. The preparation method of the cinnabar picture as claimed in claim 7, wherein the mass ratio of the molding paste to the white latex is 3-5:1, preferably 4: 1.
9. The preparation method of the cinnabar picture as claimed in claim 1, wherein the mass ratio of the raw stone, the glue 2 and the branches in step (4) is 3-5:1-3: 1.
10. The preparation method of the cinnabar picture as claimed in claim 9, wherein the mass ratio of the raw stone, the glue 2 and the branches in step (4) is 4:2: 1.