CN113512796A - Ultra-smooth mink-wool-imitated silk fabric and preparation method thereof - Google Patents
Ultra-smooth mink-wool-imitated silk fabric and preparation method thereof Download PDFInfo
- Publication number
- CN113512796A CN113512796A CN202110494487.3A CN202110494487A CN113512796A CN 113512796 A CN113512796 A CN 113512796A CN 202110494487 A CN202110494487 A CN 202110494487A CN 113512796 A CN113512796 A CN 113512796A
- Authority
- CN
- China
- Prior art keywords
- parts
- smooth
- silk fabric
- mink
- ultra
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an ultra-smooth mink hair-imitated silk fabric and a preparation method thereof, wherein the ultra-smooth mink hair-imitated silk fabric comprises the following raw materials in parts by weight: the raw materials comprise the following components in parts by weight: the silk fabric prepared by the preparation method has the advantages of stiffness, smoothness, uneasiness in creasing and hooking, soft and elegant hand feeling, dense silk threads, good bulkiness and smoothness, color and hand feeling close to real wool, and meanwhile, the silver fibers are added into the silk fabric, so that the silk fabric has the capabilities of resisting bacteria, deodorizing, preventing radiation, resisting static electricity and pollution, and the wearing comfort level is improved.
Description
Technical Field
The invention relates to the technical field of spinning, in particular to an ultra-smooth mink hair-imitated real silk fabric and a preparation method thereof.
Background
The silk fabric is a pure mulberry silk fabric, which is classified into thin type and thick type according to the grammage of the fabric, and is classified into two types according to different dyeing and printing according to post-processing, the texture of the silk fabric is soft and smooth, the hand feeling is soft and light, the design and the color are rich and colorful, however, the smoothness of the existing mink hair-imitated real silk fabric is poor, and the comfort is general, so that a preparation method of the super-smooth mink hair-imitated real silk fabric is provided.
Disclosure of Invention
The invention aims to overcome the defects in the prior art, and provides the super-smooth mink-wool-imitated real silk fabric and the preparation method thereof.
In order to achieve the purpose, the invention provides the following technical scheme: the super-smooth mink hair-imitated real silk fabric comprises the following raw materials in parts by weight: 2-6 parts of tassels, 4-12 parts of master batches, 3-6 parts of peach skin black stripe yarns, 2-10 parts of empty tooth yarns, 12-26 parts of aramid fibers and 12-30 parts of silver fibers.
As a preferable technical scheme of the invention, the weight ratio of the aramid fiber to the silver fiber in the raw materials is 14-24: 14-28.
The fiber spinning machine further comprises melt spinning fibers and primary fibers, wherein the melt spinning fibers and the primary fibers are respectively 12-20 parts by weight and 3-8 parts by weight.
As a preferred technical scheme of the invention, in the raw materials, the weight ratio of melt-spun fibers to primary fibers is 14-18: 4-7.
The invention also discloses a preparation method of the ultra-smooth mink hair-imitated real silk fabric, which comprises the following steps of:
1) filament trimming: adding a taffy lattice, master batches, peach skin black stripe spinning, hollow tooth spinning, aramid fibers, melt-spun fibers and nascent fibers on a double-screw melt spinning device, uniformly mixing, extruding the high-temperature molten mixture by a screw, filtering, and extruding through a spinneret orifice to form a tow A;
2) preparing warp yarns: sequentially carrying out silk winding, double twisting, yarn steaming and shaping, rewinding and sectional warping on the tows A to obtain warps;
3) weft yarn preparation: sequentially carrying out double twisting, yarn steaming and shaping and rewinding procedures on the silver fibers to obtain weft yarns;
4) weaving the fabric: weaving the warp yarns and the weft yarns by adopting a weaving machine to obtain a fabric B;
5) dyeing and finishing: carrying out relaxation, refining, preshrinking, presetting, clear water wet setting, alkali decrement, dyeing, softening and setting processes on the fabric B to obtain a fabric C;
6) and (3) integration: and brushing the fabric C, ironing, shearing, cutting and sewing to obtain the mink hair-imitated real silk fabric.
As a preferable aspect of the present invention, the present invention is characterized in that: in the step 1), the tatting lattice, the peach skin black stripe spinning, the hollow tooth spinning, the aramid fiber, the melt-spun fiber and the nascent fiber are sliced and mixed, and the temperature of the molten mixture is 300-320 ℃.
As a preferable aspect of the present invention, the present invention is characterized in that: in the step 2), the temperature of the tows A in the process of steaming and shaping is 60-100 ℃, the boiling water shrinkage rate of the obtained warp yarn is 8-16%, and the filament number is 5.0-6.8 dpf.
As a preferable aspect of the present invention, the present invention is characterized in that: in the step 2), the temperature of the silver fiber in the steaming and shaping is 40-60 ℃.
As a preferable technical scheme of the invention, in the step 5), the temperature of the setting machine in the presetting is set to be 180-200 ℃, and the vehicle speed is 20-25 m/min.
As a preferred technical scheme of the invention, in the step 6), the temperature of the fabric C for ironing and cutting is 200-220 ℃.
Compared with the prior art, the invention has the beneficial effects that: the silver fiber fabric has the advantages of stiffness, smoothness, soft and elegant hand feeling, dense silk threads, high filling power and smoothness, color and hand feeling which are close to those of real hair, and simultaneously silver fibers are added in the silver fiber fabric, so that the silver fiber fabric has the capabilities of resisting bacteria, deodorizing, preventing radiation, resisting static electricity and pollution, and the wearing comfort level is improved.
Detailed Description
In order to make the objects, technical solutions and advantages of the present invention more apparent, the present invention is further described in detail with reference to the following embodiments. It should be understood that the specific embodiments described herein are merely illustrative of the invention and are not intended to limit the invention.
Example one
The super-smooth mink hair-imitated real silk fabric comprises the following raw materials in parts by weight: 2 parts of tassels, 4 parts of master batch, 3 parts of peach skin black stripe, 2 parts of open-end spinning, 12 parts of aramid fiber, 12 parts of silver fiber, 12 parts of melt-spun fiber and 3 parts of nascent fiber.
The invention also discloses a preparation method of the ultra-smooth mink hair-imitated real silk fabric, which comprises the following steps of:
1) filament trimming: adding a taffy lattice, master batches, peach skin black stripe spinning, hollow tooth spinning, aramid fibers, melt-spun fibers and nascent fibers on a double-screw melt spinning device, slicing and uniformly mixing, extruding a mixture with a melting temperature of 300 ℃ by a screw, filtering and extruding the mixture through a spinneret orifice to form a tow A;
2) preparing warp yarns: sequentially carrying out winding, double twisting, yarn steaming and setting, rewinding and sectional warping on the tows A, wherein the yarn steaming and setting temperature is 60 ℃, warp yarns are obtained, the boiling water shrinkage rate of the warp yarns is 8-16%, and the filament number is 5.0 dpf;
3) weft yarn preparation: sequentially carrying out two-for-one twisting, yarn steaming and shaping and rewinding procedures on the silver fibers to obtain weft yarns, wherein the temperature for yarn steaming and shaping is 40 ℃;
4) weaving the fabric: weaving the warp yarns and the weft yarns by adopting a weaving machine to obtain a fabric B;
5) dyeing and finishing: carrying out the working procedures of relaxation, refining, preshrinking, presetting, clear water wet setting, alkali decrement, dyeing, softening and setting on the fabric B, wherein the temperature of a setting machine in the presetting is set to be 180 ℃, and the vehicle speed is 20m/min, so as to obtain a fabric C;
6) and (3) integration: brushing the fabric C, ironing and shearing, cutting and sewing, wherein the ironing and shearing temperature is 200 ℃, and finally the mink hair-imitated real silk fabric is obtained.
In the embodiment, the ironing temperature of the real silk fabric is 200 ℃, and at the moment, the real silk fabric is general in comfort.
Example two
The super-smooth mink hair-imitated real silk fabric comprises the following raw materials in parts by weight: 3 parts of tassels, 6 parts of master batch, 4 parts of peach skin black stripe, 3 parts of open-end spinning, 15 parts of aramid fiber, 13 parts of silver fiber, 13 parts of melt-spun fiber and 4 parts of nascent fiber.
The invention also discloses a preparation method of the ultra-smooth mink hair-imitated real silk fabric, which comprises the following steps of:
1) filament trimming: adding a taffy lattice, master batches, peach skin black stripe spinning, hollow tooth spinning, aramid fibers, melt-spun fibers and nascent fibers on a double-screw melt spinning device, slicing and uniformly mixing, extruding a mixture with a melting temperature of 305 ℃ by a screw, filtering and extruding the mixture through a spinneret orifice to form a tow A;
2) preparing warp yarns: sequentially carrying out winding, double twisting, yarn steaming and setting, rewinding and sectional warping on the tows A, wherein the yarn steaming and setting temperature is 65 ℃, warp yarns are obtained, the boiling water shrinkage rate of the warp yarns is 10%, and the filament number is 5.5 dpf;
3) weft yarn preparation: sequentially carrying out two-for-one twisting, yarn steaming and shaping and rewinding procedures on the silver fibers to obtain weft yarns, wherein the temperature for yarn steaming and shaping is 45 ℃;
4) weaving the fabric: weaving the warp yarns and the weft yarns by adopting a weaving machine to obtain a fabric B;
5) dyeing and finishing: carrying out the working procedures of relaxation, refining, preshrinking, presetting, over-clear water wet setting, alkali decrement, dyeing, softening and setting on the fabric B, wherein the temperature of a setting machine in the presetting is set to be 190 ℃, and the vehicle speed is 22m/min, so as to obtain a fabric C;
6) and (3) integration: brushing the fabric C, ironing and shearing, cutting and sewing, wherein the ironing and shearing temperature is 210 ℃, and finally the mink hair-imitated real silk fabric is obtained.
In the embodiment, the ironing temperature is 210 ℃, and the silk fabric imitating mink hair is obtained finally, so that the real silk fabric is comfortable.
EXAMPLE III
The super-smooth mink hair-imitated real silk fabric comprises the following raw materials in parts by weight: 5 parts of tassels, 10 parts of master batches, 5 parts of peach skin black strips, 8 parts of empty teeth, 22 parts of aramid fibers, 16 parts of silver fibers, 19 parts of melt-spun fibers and 7 parts of nascent fibers.
The invention also discloses a preparation method of the ultra-smooth mink hair-imitated real silk fabric, which comprises the following steps of:
1) filament trimming: adding a taffy lattice, master batches, peach skin black stripe spinning, hollow tooth spinning, aramid fibers, melt-spun fibers and nascent fibers on a double-screw melt spinning device, slicing and uniformly mixing, extruding a mixture with a melting temperature of 315 ℃ by a screw, filtering and extruding the mixture through a spinneret orifice to form a tow A;
2) preparing warp yarns: sequentially carrying out winding, double twisting, yarn steaming and setting, rewinding and sectional warping on the tows A, wherein the yarn steaming and setting temperature is 90 ℃, warp yarns are obtained, the boiling water shrinkage rate of the warp yarns is 12%, and the filament number is 6.5 dpf;
3) weft yarn preparation: sequentially carrying out two-for-one twisting, yarn steaming and shaping and rewinding procedures on the silver fibers to obtain weft yarns, wherein the temperature for yarn steaming and shaping is 55 ℃;
4) weaving the fabric: weaving the warp yarns and the weft yarns by adopting a weaving machine to obtain a fabric B;
5) dyeing and finishing: carrying out the working procedures of relaxation, refining, preshrinking, presetting, over-clear water wet setting, alkali decrement, dyeing, softening and setting on the fabric B, wherein the temperature of a setting machine in the presetting is set to be 190 ℃, and the vehicle speed is 24m/min, so as to obtain a fabric C;
6) and (3) integration: brushing the fabric C, ironing and shearing, cutting and sewing, wherein the ironing and shearing temperature is 215 ℃, and finally the mink hair-imitated real silk fabric is obtained.
In the embodiment, the ironing temperature of the ironing and shearing is 215 ℃, and the smoothness of the silk fabric imitating the mink hair is improved, so that the comfort is general.
Example four
The super-smooth mink hair-imitated real silk fabric comprises the following raw materials in parts by weight: 6 parts of tassels, 12 parts of master batches, 6 parts of peach skin black strips, 10 parts of empty teeth, 26 parts of aramid fibers, 30 parts of silver fibers, 20 parts of melt-spun fibers and 8 parts of nascent fibers.
The invention also discloses a preparation method of the ultra-smooth mink hair-imitated real silk fabric, which comprises the following steps of:
1) filament trimming: adding a taffy lattice, master batches, peach skin black stripe spinning, hollow tooth spinning, aramid fibers, melt-spun fibers and nascent fibers on a double-screw melt spinning device, slicing and uniformly mixing, extruding a mixture with a melting temperature of 320 ℃ by a screw, filtering and extruding the mixture through a spinneret orifice to form a tow A;
2) preparing warp yarns: sequentially carrying out winding, double twisting, yarn steaming and setting, rewinding and sectional warping on the tows A, wherein the yarn steaming and setting temperature is 100 ℃, warp yarns are obtained, the boiling water shrinkage rate of the warp yarns is 8-16%, and the filament number is 6.8 dpf;
3) weft yarn preparation: sequentially carrying out two-for-one twisting, yarn steaming and shaping and rewinding procedures on the silver fibers to obtain weft yarns, wherein the temperature for yarn steaming and shaping is 60 ℃;
4) weaving the fabric: weaving the warp yarns and the weft yarns by adopting a weaving machine to obtain a fabric B;
5) dyeing and finishing: carrying out relaxation, refining, preshrinking, presetting, clear water wet setting, alkali decrement, dyeing, softening and setting processes on the fabric B, wherein the temperature of a setting machine in the presetting process is set to be 180-plus-one 200 ℃, and the vehicle speed is 25m/min, so as to obtain a fabric C;
6) and (3) integration: brushing the fabric C, ironing and shearing, cutting and sewing, wherein the ironing and shearing temperature is 220 ℃, and finally the mink hair-imitated real silk fabric is obtained.
In the embodiment, the ironing temperature of the ironing and shearing device is 220 ℃, and at the moment, the obtained silk fabric imitating the mink hair is good in comfort and smoothness.
The invention has the advantages of stiffness, uneasy crease and uneasy thread hooking, soft and elegant hand feeling, dense silk thread, better filling power and smoothness, and closer color and hand feeling to real hair, and simultaneously, the silver fiber is added in the invention, thereby the invention has the capabilities of antibiosis, deodorization, radiation protection, static resistance and pollution resistance, and improves the wearing comfort level.
Although embodiments of the present invention have been shown and described, it will be appreciated by those skilled in the art that changes, modifications, substitutions and alterations can be made in these embodiments without departing from the principles and spirit of the invention, the scope of which is defined in the appended claims and their equivalents.
Claims (10)
1. A super-smooth mink hair-imitated real silk fabric is characterized in that: the raw materials comprise the following components in parts by weight: 2-6 parts of tassels, 4-12 parts of master batches, 3-6 parts of peach skin black stripe yarns, 2-10 parts of empty tooth yarns, 12-26 parts of aramid fibers and 12-30 parts of silver fibers.
2. The ultra-smooth mink-wool-like silk fabric according to claim 1, characterized in that: in the raw materials, the weight ratio of aramid fiber to silver fiber is 14-24: 14-28.
3. The ultra-smooth mink-wool-like silk fabric according to claim 1, characterized in that: the fabric further comprises melt-spun fibers and primary fibers, wherein the weight parts of the melt-spun fibers and the primary fibers are 12-20 parts and 3-8 parts respectively.
4. The ultra-smooth mink-wool-like silk fabric according to claim 1, characterized in that: in the raw materials, the weight ratio of melt-spun fiber to nascent fiber is 14-18: 4-7.
5. A preparation method of an ultra-smooth mink hair-imitated real silk fabric is characterized by comprising the following steps of: the method comprises the following steps:
1) filament trimming: adding a taffy lattice, master batches, peach skin black stripe spinning, hollow tooth spinning, aramid fibers, melt-spun fibers and nascent fibers on a double-screw melt spinning device, uniformly mixing, extruding the high-temperature molten mixture by a screw, filtering, and extruding through a spinneret orifice to form a tow A;
2) preparing warp yarns: sequentially carrying out silk winding, double twisting, yarn steaming and shaping, rewinding and sectional warping on the tows A to obtain warps;
3) weft yarn preparation: sequentially carrying out double twisting, yarn steaming and shaping and rewinding procedures on the silver fibers to obtain weft yarns;
4) weaving the fabric: weaving the warp yarns and the weft yarns by adopting a weaving machine to obtain a fabric B;
5) dyeing and finishing: carrying out relaxation, refining, preshrinking, presetting, clear water wet setting, alkali decrement, dyeing, softening and setting processes on the fabric B to obtain a fabric C;
6) and (3) integration: and brushing the fabric C, ironing, shearing, cutting and sewing to obtain the mink hair-imitated real silk fabric.
6. The preparation method of the ultra-smooth mink-wool-imitated silk fabric according to claim 5, characterized in that: in the step 1), the tatting lattice, the peach skin black stripe spinning, the hollow tooth spinning, the aramid fiber, the melt-spun fiber and the nascent fiber are sliced and mixed, and the temperature of the molten mixture is 300-320 ℃.
7. The preparation method of the ultra-smooth mink-wool-imitated silk fabric according to claim 5, characterized in that: in the step 2), the temperature of the tows A in the process of steaming and shaping is 60-100 ℃, the boiling water shrinkage rate of the obtained warp yarn is 8-16%, and the filament number is 5.0-6.8 dpf.
8. The preparation method of the ultra-smooth mink-wool-imitated silk fabric according to claim 5, characterized in that: in the step 2), the temperature of the silver fiber in the steaming and shaping is 40-60 ℃.
9. The preparation method of the ultra-smooth mink-wool-imitated silk fabric according to claim 5, characterized in that: in step 5), the temperature of the setting machine in the presetting process is set to be 180-200 ℃, and the vehicle speed is 20-25 m/min.
10. The preparation method of the ultra-smooth mink-wool-imitated silk fabric according to claim 5, characterized in that: in the step 6), the light-ironing and shearing temperature of the fabric C is 200-220 ℃.