CN113510803A - Brand-new natural wood grain glass brick and manufacturing process thereof - Google Patents
Brand-new natural wood grain glass brick and manufacturing process thereof Download PDFInfo
- Publication number
- CN113510803A CN113510803A CN202010552704.5A CN202010552704A CN113510803A CN 113510803 A CN113510803 A CN 113510803A CN 202010552704 A CN202010552704 A CN 202010552704A CN 113510803 A CN113510803 A CN 113510803A
- Authority
- CN
- China
- Prior art keywords
- putting
- glass brick
- manufacturing process
- adhesive sheet
- melt adhesive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a brand-new natural wood grain glass brick and a manufacturing process thereof, wherein the manufacturing process comprises the following steps: firstly, performing anti-cracking treatment on purchased veneers, cutting purchased massive glass into the specification of a glass brick to be processed, and firing the cut glass in a kiln; then putting the transparent glass brick on a mould of a laminating furnace, then putting a layer of EVA hot-melt adhesive sheet, then putting natural veneer, then putting a layer of EVA hot-melt adhesive sheet, and finally putting a layer of white waterproof protective film. The invention has simple manufacturing process and high production efficiency, the produced product has natural color, different timbers have different colors and textures, the pattern is rich, the product can not generate oxidation discoloration phenomenon, the problem of monotonous color of the doubling product on the market can be effectively solved, the problem of high pattern repetition rate is solved, the phenomenon of film oxidation is solved, the stability of the product is ensured, and the using environment is rich in artistic sense.
Description
Technical Field
The invention relates to the technical field of glass brick manufacturing, in particular to a brand-new natural wood grain glass brick and a manufacturing process thereof.
Background
The current market does not have like product, this product has adopted natural veneer as the base colour, do not process any colour processing, the product effect of coming out is exactly ligneous primary colour, each veneer all has different line, it is very natural and beautiful, develop this product and be exactly for letting the product colour seem to press close to nature more, the oxidation discoloration can not appear in the colour of veneer, can guarantee that the product can use for a long time, mosaic glass brick is exactly one has artistic nature product, let the people seem more comfortable, bring higher artistic embodiment for the space of using.
Laminated glass brick that has imitative stone material line above the market all prints with the film, and the colour is dull, and the pattern repetition rate is very high moreover, forms the product pattern and comparatively dies, and the rubber is easy to be oxidized, and the film will become yellow and change colour after the film oxidation, and the printing layer also can follow the oxidation and fade, and the production process of film produces the shrink fracture bubble easily, can not have good quality assurance.
Disclosure of Invention
The invention aims to provide a brand-new natural wood grain glass brick and a manufacturing process thereof so as to solve the problems in the background technology.
In order to achieve the purpose, the invention provides the following technical scheme: the brand new natural wood grain glass brick and the manufacturing process thereof comprise the following steps:
A. firstly, performing anti-cracking treatment on purchased veneers, cutting purchased massive glass into the specification of a glass brick to be processed, and firing the cut glass in a kiln;
B. then putting the transparent glass brick on a mould of a laminating furnace, then putting a layer of EVA hot-melt adhesive sheet, then putting a natural veneer, then putting a layer of EVA hot-melt adhesive sheet, and finally putting a layer of white waterproof protective film;
C. putting the mold into a laminating furnace, starting to work after the laminating furnace is sealed, starting to vacuumize the machine, and starting to heat a heating facility in the machine;
D. and (3) removing the vacuum state of the laminating furnace, taking the mold out of the laminating furnace, and removing the veneer and the EVA hot melt adhesive sheet at the edge of the glass brick in time when the temperature is reduced to 45-55 ℃, so that the natural wood grain glass brick is manufactured.
Preferably, the following production materials are prepared before the step A production: the waterproof coating comprises a natural veneer with the thickness of 0.4mm-0.5mm, an EVA hot melt adhesive sheet with the thickness of 0.2mm-0.3mm, a transparent glass brick fired at high temperature and a white waterproof protective film with the thickness of 0.1mm, wherein the natural veneer and the EVA hot melt adhesive sheet are processed and synthesized together.
Preferably, the glass passes through 850 ℃ in the kiln in the step A, and the final whole manufacturing process flow can be completed by requiring 2 hours of firing time.
Preferably, the temperature in step C is raised to 90-105 deg.C, and the temperature is maintained for two hours in such a state.
Compared with the prior art, the invention has the following beneficial effects:
1. the invention has simple manufacturing process and high production efficiency, the produced product has natural color, different timbers have different colors and textures, the pattern is rich, the product can not generate oxidation discoloration phenomenon, the problem of monotonous color of the doubling product on the market can be effectively solved, the problem of high pattern repetition rate is solved, the phenomenon of film oxidation is solved, the stability of the product is ensured, and the using environment is rich in artistic sense.
Detailed Description
The technical solutions in the embodiments of the present invention will be clearly and completely described below with reference to the embodiments of the present invention, and it is obvious that the described embodiments are only a part of the embodiments of the present invention, and not all of the embodiments. All other embodiments, which can be derived by a person skilled in the art from the embodiments given herein without making any creative effort, shall fall within the protection scope of the present invention.
In order to achieve the purpose, the invention provides the following technical scheme: the brand new natural wood grain glass brick and the manufacturing process thereof comprise the following steps:
A. firstly, performing anti-cracking treatment on purchased veneers, cutting purchased massive glass into the specification of a glass brick to be processed, and firing the cut glass in a kiln;
B. then putting the transparent glass brick on a mould of a laminating furnace, then putting a layer of EVA hot-melt adhesive sheet, then putting a natural veneer, then putting a layer of EVA hot-melt adhesive sheet, and finally putting a layer of white waterproof protective film;
C. putting the mold into a laminating furnace, starting to work after the laminating furnace is sealed, starting to vacuumize the machine, and starting to heat a heating facility in the machine;
D. and (3) removing the vacuum state of the laminating furnace, taking the mold out of the laminating furnace, and removing the veneer and the EVA hot melt adhesive sheet at the edge of the glass brick in time when the temperature is reduced to 45-55 ℃, so that the natural wood grain glass brick is manufactured.
The first embodiment is as follows:
the brand new natural wood grain glass brick and the manufacturing process thereof comprise the following steps:
A. firstly, performing anti-cracking treatment on purchased veneers, cutting purchased massive glass into the specification of a glass brick to be processed, and firing the cut glass in a kiln;
B. then putting the transparent glass brick on a mould of a laminating furnace, then putting a layer of EVA hot-melt adhesive sheet, then putting a natural veneer, then putting a layer of EVA hot-melt adhesive sheet, and finally putting a layer of white waterproof protective film;
C. putting the mold into a laminating furnace, starting to work after the laminating furnace is sealed, starting to vacuumize the machine, and starting to heat a heating facility in the machine;
D. and (3) removing the vacuum state of the laminating furnace, taking the mold out of the laminating furnace, and removing the veneer and the EVA hot melt adhesive sheet at the edge of the glass brick in time when the temperature is reduced to 45-55 ℃, so that the natural wood grain glass brick is manufactured.
Example two:
in the first embodiment, the following steps are added:
the following production materials need to be prepared before the production in step A: the waterproof coating comprises a natural veneer with the thickness of 0.4mm-0.5mm, an EVA hot melt adhesive sheet with the thickness of 0.2mm-0.3mm, a transparent glass brick fired at high temperature and a white waterproof protective film with the thickness of 0.1mm, wherein the natural veneer and the EVA hot melt adhesive sheet are processed and synthesized together.
The brand new natural wood grain glass brick and the manufacturing process thereof comprise the following steps:
A. firstly, performing anti-cracking treatment on purchased veneers, cutting purchased massive glass into the specification of a glass brick to be processed, and firing the cut glass in a kiln;
B. then putting the transparent glass brick on a mould of a laminating furnace, then putting a layer of EVA hot-melt adhesive sheet, then putting a natural veneer, then putting a layer of EVA hot-melt adhesive sheet, and finally putting a layer of white waterproof protective film;
C. putting the mold into a laminating furnace, starting to work after the laminating furnace is sealed, starting to vacuumize the machine, and starting to heat a heating facility in the machine;
D. and (3) removing the vacuum state of the laminating furnace, taking the mold out of the laminating furnace, and removing the veneer and the EVA hot melt adhesive sheet at the edge of the glass brick in time when the temperature is reduced to 45-55 ℃, so that the natural wood grain glass brick is manufactured.
Example three:
in the second embodiment, the following steps are added:
in the step A, the glass is subjected to 850 ℃ high temperature in a kiln, and finally the whole manufacturing process flow can be finished by requiring 2 hours of firing time.
The brand new natural wood grain glass brick and the manufacturing process thereof comprise the following steps:
A. firstly, performing anti-cracking treatment on purchased veneers, cutting purchased massive glass into the specification of a glass brick to be processed, and firing the cut glass in a kiln;
B. then putting the transparent glass brick on a mould of a laminating furnace, then putting a layer of EVA hot-melt adhesive sheet, then putting a natural veneer, then putting a layer of EVA hot-melt adhesive sheet, and finally putting a layer of white waterproof protective film;
C. putting the mold into a laminating furnace, starting to work after the laminating furnace is sealed, starting to vacuumize the machine, and starting to heat a heating facility in the machine;
D. and (3) removing the vacuum state of the laminating furnace, taking the mold out of the laminating furnace, and removing the veneer and the EVA hot melt adhesive sheet at the edge of the glass brick in time when the temperature is reduced to 45-55 ℃, so that the natural wood grain glass brick is manufactured.
Example four:
in the third embodiment, the following steps are added:
the temperature in step C was raised up to 90-105 ℃ and held for two hours under such conditions.
The brand new natural wood grain glass brick and the manufacturing process thereof comprise the following steps:
A. firstly, performing anti-cracking treatment on purchased veneers, cutting purchased massive glass into the specification of a glass brick to be processed, and firing the cut glass in a kiln;
B. then putting the transparent glass brick on a mould of a laminating furnace, then putting a layer of EVA hot-melt adhesive sheet, then putting a natural veneer, then putting a layer of EVA hot-melt adhesive sheet, and finally putting a layer of white waterproof protective film;
C. putting the mold into a laminating furnace, starting to work after the laminating furnace is sealed, starting to vacuumize the machine, and starting to heat a heating facility in the machine;
D. and (3) removing the vacuum state of the laminating furnace, taking the mold out of the laminating furnace, and removing the veneer and the EVA hot melt adhesive sheet at the edge of the glass brick in time when the temperature is reduced to 45-55 ℃, so that the natural wood grain glass brick is manufactured.
Although embodiments of the present invention have been shown and described, it will be appreciated by those skilled in the art that changes, modifications, substitutions and alterations can be made in these embodiments without departing from the principles and spirit of the invention, the scope of which is defined in the appended claims and their equivalents.
Claims (4)
1. The brand new natural wood grain glass brick and the manufacturing process thereof are characterized in that: the preparation process comprises the following steps:
A. firstly, performing anti-cracking treatment on purchased veneers, cutting purchased massive glass into the specification of a glass brick to be processed, and firing the cut glass in a kiln;
B. then putting the transparent glass brick on a mould of a laminating furnace, then putting a layer of EVA hot-melt adhesive sheet, then putting a natural veneer, then putting a layer of EVA hot-melt adhesive sheet, and finally putting a layer of white waterproof protective film;
C. putting the mold into a laminating furnace, starting to work after the laminating furnace is sealed, starting to vacuumize the machine, and starting to heat a heating facility in the machine;
D. and (3) removing the vacuum state of the laminating furnace, taking the mold out of the laminating furnace, and removing the veneer and the EVA hot melt adhesive sheet at the edge of the glass brick in time when the temperature is reduced to 45-55 ℃, so that the natural wood grain glass brick is manufactured.
2. The novel natural wood grain glass brick and the manufacturing process thereof as claimed in claim 1, wherein: the following production materials need to be prepared before the production in step A: the waterproof coating comprises a natural veneer with the thickness of 0.4mm-0.5mm, an EVA hot melt adhesive sheet with the thickness of 0.2mm-0.3mm, a transparent glass brick fired at high temperature and a white waterproof protective film with the thickness of 0.1mm, wherein the natural veneer and the EVA hot melt adhesive sheet are processed and synthesized together.
3. The novel natural wood grain glass brick and the manufacturing process thereof as claimed in claim 1, wherein: in the step A, the glass is subjected to 850 ℃ high temperature in a kiln, and finally the whole manufacturing process flow can be finished by requiring 2 hours of firing time.
4. The novel natural wood grain glass brick and the manufacturing process thereof as claimed in claim 1, wherein: the temperature in step C is raised to 90-105 deg.C, and the temperature is maintained for two hours in the state.