CN105839878A - Veneer composite tile and making process thereof - Google Patents
Veneer composite tile and making process thereof Download PDFInfo
- Publication number
- CN105839878A CN105839878A CN201610322000.2A CN201610322000A CN105839878A CN 105839878 A CN105839878 A CN 105839878A CN 201610322000 A CN201610322000 A CN 201610322000A CN 105839878 A CN105839878 A CN 105839878A
- Authority
- CN
- China
- Prior art keywords
- veneer
- material layer
- tile
- tack coat
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a veneer composite tile and a making method thereof. The veneer composite tile is an overall platy block which is mainly formed by a tile blank material, a first bonding layer, a veneer material layer, a second bonding layer and a transparent material layer which are arranged in sequence from bottom to top, and the veneer material layer is sealed between the transparent material layer and the tile blank material. According to the veneer composite tile and the making method thereof, the veneer material layer is sealed between the transparent material layer and the tile blank material, the veneer material layer is isolated from air and moisture, the service life of a veneer material is greatly prolonged, the effects of resisting moisture, mold and corrosion are achieved, the tile is flat, smooth, clean, easy to clean and durable, real veneer composite is achieved, the real feeling cannot be achieved through a printer, a better decorative effect can be achieved, and meanwhile the environmental protection effect is achieved. The intrinsic property of the tile is maintained, the tile can be cut freely to be applicable to different laying areas and different places, and meanwhile transportation is convenient.
Description
Technical field
The present invention relates to a kind of decoration compound tile, particularly to a kind of veneer compound tile, further relate to this wood
The processing technology of skin compound tile.
Background technology
Log veneer is widely used in composite furniture board industry typically as a kind of furniture material.Composite furniture
Plate is to use barbola work log veneer to be made with plank laminating, and this composite furniture plate can realize required
Graining effect, it is possible to be obviously improved the quality of furniture, increase aesthetic feeling.
But, the defects such as the wood decorative material such as plank has yielding, cracking, aberration, and veneer is direct
Patch method on the wall so that veneer often exist face get damp, go mouldy, damage by worms, laying dust, fade, corrosion etc.
Shortcoming, therefore, plank and veneer are extremely limited in the application of furnishing fields.It addition, wallpaper and wall paper
The ornament materials commonly used at present, it can not only decorated wall surface, protection metope, but also can promote
Life taste, is therefore widely used.But, wallpaper and wall paper generally use viscose glue paving at metope
On, so, often exist get damp, go mouldy, easy laying dust, the shortcoming such as easy to change, especially have the most easy to clean
Defect.Being additionally, since wallpaper directly to contact with room air with wall paper, its material is oxidizable, surface color and polish
Can gradually fade and become gloomy, seriously reduce decorative effect.
At present, due to ceramic tile have on-the-spot paving construction convenience, low cost, protection against the tide, waterproof, do not go mouldy, no
Variable color, the plurality of advantages such as easy to clean and be widely used in wall decoration.Existing wood grain ceramic tile, its quality is
Ceramic tile, it is the effect that the coloring of employing surface or the technology mode producing wood-grain texture reach to show wood grain.
But, wood grain ceramic tile is compared with real veneer, and its skin texture and texture have obvious difference.
Compound tile is ceramic tile industry latest developments a kind of forms more rapidly.It is multiple that compound tile is mainly glass
Close ceramic tile, be i.e. compound one layer of wired (or wallpaper) material between double glazing.But, this glass
Compound tile cannot be widely applied to wall decoration, this is because:
(1) glass has permeability so that it is be not widely deployed for wall decoration.
(2) glass has that paving construction is difficult, frangible, to be difficult to on-site cutting perforate fluting, inconvenience transport etc. many
Shortcoming, therefore, it is difficult to be widely used in wall decoration, it is also difficult to realizes batch production batch production.
(3), due to the restriction of ceramic tile Manufacturing Techniques, i.e. realize wood-grain texture and texture often through printer
Effect, its skin texture and texture are unable to reach texture and the decorative effect of veneer.
Summary of the invention
It is an object of the present invention to provide one to fully demonstrate veneer texture and texture, low cost, prevent
Damp, waterproof, do not go mouldy, invariant color, easy to clean, paving construction is convenient, production technology is simple, can be any
Cutting, convenient transport and the veneer compound tile of environmental protection.
The above-mentioned purpose of the present invention is realized by following technical measures: a kind of veneer compound tile, its feature
Be: it mainly by the ceramic tile base material set gradually from bottom to up, the first tack coat, veneer material layer, the
The overall tabular block that two tack coats and transparent material layer are formed, described veneer material layer seal is in described
Between transparent material layer and ceramic tile base material.
The veneer material layer seal of the present invention is between transparent material layer and ceramic tile base material so that veneer material layer with
Air, moisture are isolated, and significantly extend the service life of veneer material, it is achieved thereby that protection against the tide, mildew-resistant,
Antiseptical effect, and smooth, bright and clean, more easy to clean, durable, the present invention is that real veneer is combined, and it is true
True feeling is that printer is beyond one's reach, it is possible to realize more preferably also having environment protecting while decorative effect.Separately
Outward, the present invention maintains the self character of ceramic tile, can arbitrarily cut, to be adapted to the different area and not laid
Same place, also allows for transport simultaneously.The simple in construction of the present invention, with low cost, it is simple to mass production and wide
General popularization and be suitable for.
As one embodiment of the present invention, described first tack coat and the second tack coat all use hot melt adhesive layer,
Veneer material layer described in described hot melt adhesive layer hot melt seal.
As a kind of optimal way of the present invention, described hot melt adhesive layer is EVA hot-melt adhesive sheet, and thickness is
0.15～0.50mm.
As a kind of optimal way of the present invention, described transparent material layer is PET transparent resin sheet, and thickness is
0.25～0.50mm.
Ceramic tile base material of the present invention, the first tack coat, veneer material layer, the second tack coat and transparent material layer
Thickness be 0.2～0.5mm respectively.
Further object is that the processing technology that a kind of above-mentioned veneer compound tile is provided.
The above-mentioned purpose of the present invention is realized by following technical measures: the system of a kind of above-mentioned veneer compound tile
Make technique, it is characterised in that specifically include following steps:
(1) on ceramic tile base material, lay the first tack coat, veneer material layer, the second tack coat and transparent material successively
Layer forms compound tile semi-finished product；
(2) compound tile semi-finished product are placed in a vacuum chamber；
(3) compress compound tile semi-finished product and with fixing compound tile semi-finished product and make between its each layer snugly into each other；
(4) heat by the compound tile semi-finished product of step (3) gained, until the first tack coat and the second tack coat are heat
Molten state, makes veneer material layer seal between ceramic tile base material and transparent material layer, thus forms an integral slab
Shape block.
The processing technology of the present invention is simple, low production cost, it is simple to mass production and be widely popularized and be suitable for.
As a kind of optimal way of the present invention, the vacuum of vacuum chamber is more than or equal to 0.1MPa, the temperature of heating
Degree is 105～120 degree, and heat time heating time is 60～120 minutes, preferably 90 minutes.
As one embodiment of the present invention, described first tack coat and the second tack coat all use EVA hot melt
Film.
As one embodiment of the present invention, described transparent material layer is PET transparent resin film.
Compared with prior art, the present invention has a following significantly effect:
(1) the veneer material layer seal of the present invention is between transparent material layer and ceramic tile base material so that veneer material layer
It is isolated with air, moisture, significantly extends the service life of veneer material layer, it is achieved thereby that moistureproof,
Lightning protection, antiseptical effect.
(2) the compound tile of the present invention is smooth, bright and clean, more easy to clean, durable, and the present invention is that real veneer is multiple
Closing, embody the superficial makings of veneer own and color, its sense of reality is that printer is beyond one's reach, it is possible to realize more
The environment protecting also having while good decorative effect.
(3) the present invention maintains the self character of ceramic tile, can arbitrarily cut, be adapted to different lay area and
Different places, also allows for transport simultaneously.
(4) the simple in construction of the present invention, processing technology are simple, with low cost, it is simple to mass production.
(5) the compound tile of the present invention overcomes the various defects of existing ornament materials, and technique effect is very notable,
Be suitable to be widely popularized and be suitable for.
Accompanying drawing explanation
The present invention is described in further detail with specific embodiment below in conjunction with the accompanying drawings.
Fig. 1 is the perspective view of compound tile of the present invention；
Fig. 2 is the longitudinal section cross-sectional schematic of compound tile of the present invention；
Fig. 3 is the structural blast schematic diagram of compound tile of the present invention.
Detailed description of the invention
As shown in Figures 1 to 3, being one veneer compound tile of the present invention, it is mainly by setting gradually from bottom to up
Ceramic tile base material the 1, first tack coat 2, veneer material layer the 3, second tack coat 4 and 5 shapes of transparent material layer
The solid overall tabular block become, veneer material layer 3 is sealed in transparent material layer 5 and ceramic tile base material 1
Between.In the present embodiment, the first tack coat 2 and the second tack coat 4 all use hot melt adhesive layer, hot melt adhesive layer
Hot melt seal veneer material layer 3.Hot melt adhesive layer uses EVA hot-melt adhesive, and transparent material layer 5 uses PET transparent
Resin.
Veneer material seal is between transparent material layer 5 and ceramic tile base material 1 so that veneer material and air, tide
Gas phase completely cuts off, and significantly extends the service life of veneer material, it is achieved thereby that protection against the tide, lightning protection, antiseptical
Effect, and smooth, bright and clean, more easy to clean, durable, more preferably also has ring while decorative effect realizing
Protect effect.Veneer compound tile maintains the self character of ceramic tile, can arbitrarily cut, to be adapted to different paving
If area and different places, also allow for transport simultaneously.
The processing technology of a kind of above-mentioned veneer compound tile, specifically includes following steps:
(1) on ceramic tile base material 1, set gradually first tack coat 2 identical with ceramic tile base material 1 size, veneer material
The bed of material the 3, second tack coat 4 and transparent material layer 5, form compound tile semi-finished product；Wherein, the first tack coat
2 and second tack coat 4 be respectively adopted solid transparent EVA hot-melt adhesive sheet, transparent material layer 5 is the transparent tree of PET
Fat sheet.
(2) being placed in a vacuum chamber by compound tile semi-finished product, the vacuum of vacuum chamber is 0.1Mpa；
(3) compress compound tile semi-finished product and with fixing compound tile semi-finished product and make between its each layer snugly into each other；
Step vacuum lamination process (2) and (3) both can use vacuum equipment, utilizes clamping fixture to compound
Ceramic tile semi-finished product are fixed and compress, it would however also be possible to employ be placed in vacuum bag by compound tile semi-finished product, utilize
Negative pressure compresses vacuum bag, and with fixing compound tile semi-finished product and it is each to make vacuum bag extrusion cladding ceramic tile semi-finished product
Between Ceng snugly into each other.
(4) heating by the compound tile semi-finished product of step (3) gained, the temperature of heating is 105 degree, and heat time heating time is
90 minutes, until the first tack coat 2 and the second tack coat 4 are in hot melt state, veneer material layer 3 is made to be sealed in
Between ceramic tile base material 1 and transparent material layer 5, thus form an overall tabular block.
In other embodiments, the vacuum of vacuum chamber is more than 0.1MPa, and heating-up temperature is 105～120 degree, adds
The heat time is 60～120 minutes.Ceramic tile base material, the first tack coat, veneer material layer, the second tack coat and transparent
The thickness of material layer is 0.2～0.5mm respectively.
Embodiments of the present invention are not limited to this, according to the foregoing of the present invention, according to the ordinary skill of this area
Knowledge and customary means, without departing under the present invention above-mentioned basic fundamental thought premise, compound tile of the present invention
Each layer can also select other material to make, and the thickness of each layer can adjust with selectivity, wherein, and the first bonding
The thickness of layer and the second tack coat can regulate accordingly according to the thickness of veneer material layer；And, to compound tile
The method that semi-finished product carry out vacuum compound also has other embodiment.Therefore, can also to make other many for the present invention
The amendment of kind of form, replace or change, within the scope of all falling within rights protection of the present invention.
Claims (10)
1. a veneer compound tile, it is characterised in that: it is mainly by the ceramic tile base set gradually from bottom to up
The overall tabular that material, the first tack coat, veneer material layer, the second tack coat and transparent material layer are formed
Block, described veneer material layer seal is between described transparent material layer and ceramic tile base material.
Veneer compound tile the most according to claim 1, it is characterised in that: described first tack coat and
Two tack coats all use hot melt adhesive layer, veneer material layer described in described hot melt adhesive layer hot melt seal.
Veneer compound tile the most according to claim 2, it is characterised in that: described hot melt adhesive layer is EVA
Hot-melt film, thickness is 0.15～0.5mm.
Veneer compound tile the most according to claim 3, it is characterised in that: described transparent material layer is PET
Transparent resin sheet, thickness is 0.25～0.5mm.
Veneer compound tile the most according to claim 2, it is characterised in that: described ceramic tile base material, first
The thickness of tack coat, veneer material layer, the second tack coat and transparent material layer is 0.2～0.5mm respectively.
6. the processing technology of the veneer compound tile described in a claim 1, it is characterised in that specifically include with
Lower step:
(1) on ceramic tile base material, lay the first tack coat, veneer material layer, the second tack coat and transparent material successively
Layer forms compound tile semi-finished product；
(2) compound tile semi-finished product are placed in a vacuum chamber；
(3) compress compound tile semi-finished product and with fixing compound tile semi-finished product and make between its each layer snugly into each other；
(4) heat by the compound tile semi-finished product of step (3) gained, until the first tack coat and the second tack coat are heat
Molten state, makes veneer material layer seal between ceramic tile base material and transparent material layer, thus forms an integral slab
Shape block.
Processing technology the most according to claim 6, it is characterised in that: described first tack coat and second glues
Knot layer all uses EVA hot-melt adhesive sheet.
Processing technology the most according to claim 7, it is characterised in that: the vacuum of vacuum chamber more than or etc.
In 0.1Mpa.
Processing technology the most according to claim 8, it is characterised in that: the temperature of heating is 105～120
Degree, heat time heating time is 60～120 minutes.
Processing technology the most according to claim 8, it is characterised in that: described transparent material layer is PET
Transparent resin film.