CN106980229A - A kind of preparation method of cambered surface eyeglass - Google Patents
A kind of preparation method of cambered surface eyeglass Download PDFInfo
- Publication number
- CN106980229A CN106980229A CN201710328626.9A CN201710328626A CN106980229A CN 106980229 A CN106980229 A CN 106980229A CN 201710328626 A CN201710328626 A CN 201710328626A CN 106980229 A CN106980229 A CN 106980229A
- Authority
- CN
- China
- Prior art keywords
- cambered surface
- plate
- surface eyeglass
- preparation
- screen
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of preparation method of cambered surface eyeglass, according to the film of cambered surface eyeglass to carrying out silk-screen for the plate for making cambered surface eyeglass, processing then is dried to the plate after silk-screen；The front and back of plate after drying process sticks diaphragm respectively, then carries out arc cutting to the plate of coated with protective film；Plate after arc cutting is processed by shot blasting, then the plate after polishing cut, more than two cambered surface eyeglasses are obtained.Being different from traditional cambered surface eyeglass can only be molded by way of injection, the present invention to plate by first carrying out silk-screen, then arc cutting, polishing are carried out successively, cut to be molded cambered surface eyeglass, there is provided a kind of new method for being molded cambered surface eyeglass, molding cycle is substantially shorter, production cost is saved.
Description
Technical field
The present invention relates to processing technique field, more particularly to a kind of preparation method of cambered surface eyeglass.
Background technology
The preparation method of existing cambered surface eyeglass generally comprises the steps such as injection, silk-screen, stiffened and cutting, during due to injection
A product can only be once molded, when needing to produce in enormous quantities, producing efficiency is low, the market for being unfavorable for being lifted manufacturer is competing
Strive power.
The content of the invention
The technical problems to be solved by the invention are：A kind of preparation method of new cambered surface eyeglass is provided, production can be lifted
Efficiency.
In order to solve the above-mentioned technical problem, the technical solution adopted by the present invention is：
A kind of preparation method of cambered surface eyeglass, is carried out according to the film of cambered surface eyeglass to the plate for making cambered surface eyeglass
Silk-screen, is then dried processing to the plate after silk-screen；The front and back of plate after drying process sticks guarantor respectively
Cuticula, then carries out arc cutting to the plate of coated with protective film；Plate after arc cutting is processed by shot blasting, it is then right
Plate after polishing is cut, and obtains more than two cambered surface eyeglasses.
The beneficial effects of the present invention are：Being different from traditional cambered surface eyeglass can only be molded by way of injection, this
Invention by first to plate carry out silk-screen, then successively carry out arc cutting, polishing, cutting come be molded cambered surface eyeglass there is provided
A kind of new method for being molded cambered surface eyeglass, is substantially shorter molding cycle, saves production cost, also, can select as needed
The plate of suitable size, while being molded multiple cambered surface eyeglasses, further improves production efficiency.
Embodiment
To describe technology contents, the objects and the effects of the present invention in detail, it is explained below in conjunction with embodiment.
The design of most critical of the present invention is：It is direct to plate to carry out the radian that arc cutting obtains cambered surface eyeglass, can be big
It is big to shorten molding cycle, save production cost.
A kind of preparation method of cambered surface eyeglass, is carried out according to the film of cambered surface eyeglass to the plate for making cambered surface eyeglass
Silk-screen, is then dried processing to the plate after silk-screen；The front and back of plate after drying process sticks guarantor respectively
Cuticula, then carries out arc cutting to the plate of coated with protective film；Plate after arc cutting is processed by shot blasting, it is then right
Plate after polishing is cut, and obtains more than two cambered surface eyeglasses.
It was found from foregoing description, the beneficial effects of the present invention are：Being different from traditional cambered surface eyeglass can only be by injection
Mode be molded, the present invention carries out by first carrying out silk-screen to plate, then arc cutting, polishing, cutting and is molded successively
Cambered surface eyeglass is substantially shorter molding cycle there is provided a kind of new method for being molded cambered surface eyeglass, saves production cost, also,
The plate of suitable size can be selected as needed, while being molded multiple cambered surface eyeglasses, improve production efficiency.
Further, the drying process is specially：Plate after silk-screen is heated into 30- under the conditions of 60-70 DEG C
45min。
Seen from the above description, silk-screen effect can be improved by processing being dried to the plate after silk-screen, can be as needed
Select suitable drying temperature and time.
Further, the diaphragm is PET film, and the thickness of the PET film is 0.1-0.2mm.
Seen from the above description, can be with PET film as diaphragm, the thickness of PET film can be selected as needed.
Further, arc cutting is carried out to the plate of coated with protective film using R angles knife.
Further, the radian of R angles knife is 45-120 °.
Seen from the above description, when carrying out arc cutting using R angles knife, R angles knife is selected according to the radian of cambered surface eyeglass
Radian.
Further, the plate after arc cutting is polished using polishing wheel.
Seen from the above description, cambered surface is polished, is conducive to improving formed precision, first rough polishing can be carried out again during polishing
Carry out smart throwing.
Further, the plate after polished processing is cut using carving machine.
Seen from the above description, when being cut using carving machine, cutting accuracy can be improved.
Further, the plate is acrylic board.
Seen from the above description, cambered surface eyeglass is molded using acrylic board, production cost is advantageously reduced.
Further, the plate for making cambered surface eyeglass, the size of the plate are obtained according to the size of cambered surface eyeglass
More than the size sum of two cambered surface eyeglasses.
Seen from the above description, select larger-size plate to make multiple cambered surface eyeglasses simultaneously, improve production effect
Rate.
Embodiments of the invention one are：
A kind of preparation method of cambered surface eyeglass, can reduce production cost, greatly promote production efficiency.
First, the plate for making cambered surface eyeglass is obtained according to the size of cambered surface eyeglass, the size of the plate is more than
The size sum of two cambered surface eyeglasses, can select the size of plate as needed, and such as one went out for six, one coldest days of the year end or one goes out 12
Deng in the present embodiment, plate is acrylic board.Then the plate for making cambered surface eyeglass is entered according to the film of cambered surface eyeglass
Row silk-screen, can the different film of pre-production as needed, required half tone is then produced with the film, is carried out using web plate
Silk-screen.Then processing the plate after silk-screen is dried, the actual conditions of the drying process is：Plate after silk-screen is existed
30-45min is heated under the conditions of 60-70 DEG C, it is preferred that 30-45min is dried under the conditions of 65 DEG C, the dry time can be according to need
It is adjusted.During to silk-screen multilayer ink, such as three layers of ink of silk-screen, then 10min is dried after the complete first layer of silk-screen,
Then the silk-screen second layer, dries silk-screen third layer, last re-dry 30-45min after 10min.Plate after drying process
Front and back sticks diaphragm respectively, and diaphragm is PET film, and the thickness of the PET film is 0.1-0.2mm, it is preferred that PET
The thickness of film is 0.15mm.Then arc cutting, the radian of R angles knife are carried out to the plate of coated with protective film using R angle knives
For 45-120 °, the radian of R angles knife can be selected according to the radian of cambered surface eyeglass.Using polishing wheel to the plate after arc cutting
Material is processed by shot blasting, when being processed by shot blasting, can first carry out rough polishing, then carries out smart throwing, and the specification of polishing wheel can be as needed
Selected.Finally the plate after polishing is cut using carving machine, more than two cambered surface eyeglasses are obtained.
In the present embodiment, the size of plate can be selected as needed, and the multiple cambered surface eyeglasses of one-shot forming improve production effect
There is provided a kind of new method of globoidal mirror sheetmolding for rate.
In summary, the preparation method for a kind of cambered surface eyeglass that the present invention is provided, being different from traditional cambered surface eyeglass can only
It is molded by way of injection, the present invention directly carries out arc cutting shaping cambered surface eyeglass on plate, can reduce production
Cost, improves production efficiency.
Embodiments of the invention are the foregoing is only, are not intended to limit the scope of the invention, it is every to utilize this hair
The equivalents that bright description is made, or the technical field of correlation is directly or indirectly used in, similarly it is included in this hair
In bright scope of patent protection.
Claims (9)
1. a kind of preparation method of cambered surface eyeglass, it is characterised in that according to the film of cambered surface eyeglass to for making cambered surface eyeglass
Plate carry out silk-screen, processing then is dried to the plate after silk-screen；The front and back of plate after drying process
Diaphragm is sticked respectively, and arc cutting then is carried out to the plate of coated with protective film；Plate after arc cutting is polished
Processing, then cuts to the plate after polishing, obtains more than two cambered surface eyeglasses.
2. the preparation method of cambered surface eyeglass according to claim 1, it is characterised in that the drying process is specially：Will
Plate after silk-screen heats 30-45min under the conditions of 60-70 DEG C.
3. the preparation method of cambered surface eyeglass according to claim 1, it is characterised in that the diaphragm is PET film, described
The thickness of PET film is 0.1-0.2mm.
4. the preparation method of cambered surface eyeglass according to claim 1, it is characterised in that using R angles knife to coated with protective film
Plate carry out arc cutting.
5. the preparation method of cambered surface eyeglass according to claim 4, it is characterised in that the radian of R angles knife is 45-
120°。
6. the preparation method of cambered surface eyeglass according to claim 1, it is characterised in that using polishing wheel to through arc cutting
Plate afterwards is polished.
7. the preparation method of cambered surface eyeglass according to claim 1, it is characterised in that using carving machine to polished processing
Plate afterwards is cut.
8. the preparation method of cambered surface eyeglass according to claim 1, it is characterised in that the plate is acrylic board.
9. the preparation method of cambered surface eyeglass according to claim 1, it is characterised in that obtained according to the size of cambered surface eyeglass
Plate for making cambered surface eyeglass, the size of the plate is more than the size sum of two cambered surface eyeglasses.