CN113510227B - 一种控制连铸坯尾保护渣卷渣的方法 - Google Patents

一种控制连铸坯尾保护渣卷渣的方法 Download PDF

Info

Publication number
CN113510227B
CN113510227B CN202110401492.5A CN202110401492A CN113510227B CN 113510227 B CN113510227 B CN 113510227B CN 202110401492 A CN202110401492 A CN 202110401492A CN 113510227 B CN113510227 B CN 113510227B
Authority
CN
China
Prior art keywords
tail
roll gap
continuous casting
blank
slag
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN202110401492.5A
Other languages
English (en)
Other versions
CN113510227A (zh
Inventor
王峦涛
陈宇
高洪涛
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Angang Steel Co Ltd
Original Assignee
Angang Steel Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Angang Steel Co Ltd filed Critical Angang Steel Co Ltd
Priority to CN202110401492.5A priority Critical patent/CN113510227B/zh
Publication of CN113510227A publication Critical patent/CN113510227A/zh
Application granted granted Critical
Publication of CN113510227B publication Critical patent/CN113510227B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种控制连铸坯尾保护渣卷渣的方法，1)降低尾坯拉速率，尾坯拉速率控制在0.05m/min2以下，减少尾坯对保护渣的吸力；2)扇形段对连铸板坯最后3‑4m从恒定辊缝改为渐缩辊缝控制，渐缩辊缝的渐缩量为1.5‑3mm；增加尾坯内部钢液压力，减少向尾坯内部抽吸保护渣。本发明的方法减少连铸坯尾钢水凝固收缩时对保护渣的吸入，提高连铸坯尾质量，避免生产的钢卷出现坯尾夹杂分层缺陷。

Description

一种控制连铸坯尾保护渣卷渣的方法
技术领域
本发明涉及钢铁冶金领域特别涉及一种控制连铸坯尾保护渣卷渣的方法。
背景技术
板坯连铸生产过程中，连铸坯尾坯易产生的夹杂缺陷，且此类缺陷通常位于板坯厚度中心位置，在成品钢卷表面无法有效识别，在用户加工过程中发生开裂分层，无论对企业效益还是对企业品牌形象都造成一定影响。本发明通过调整连铸停浇阶段尾坯输出辊缝控制，减少坯尾钢水凝固收缩时对保护渣的吸入，提高连铸尾坯质量。
发明内容
本发明所要解决的技术问题是提供一种控制连铸坯尾保护渣卷渣的方法，解决连铸坯尾中保护渣卷渣缺陷。
为实现上述目的，本发明采用以下技术方案实现：
一种控制连铸坯尾保护渣卷渣的方法，包括：
1)降低尾坯拉速率，减少尾坯对保护渣的吸力；
2)扇形段对连铸板坯最后3-4m从恒定辊缝改为渐缩辊缝控制，增加尾坯内部钢液压力，减少向尾坯内部抽吸保护渣。
步骤1)中尾坯拉速率控制在0.05m/min2以下；
步骤2)中渐缩辊缝的渐缩量为1.5-3mm；按钢种具体为：
低碳钢,渐缩辊缝的渐缩量为1.5-2.2mm；
中碳钢,渐缩量为2.3-2.6mm；
高碳钢,渐缩量为2.7-3.0mm。
与现有的技术相比，本发明的有益效果是：
本发明的方法减少连铸坯尾钢水凝固收缩时对保护渣的吸入，提高连铸坯尾质量，避免生产的钢卷出现坯尾夹杂分层缺陷。
具体实施方式
下面结合实施例对本发明进一步说明：
以下实施例对本发明进行详细描述。这些实施例仅是对本发明的最佳实施方案进行描述，并不对本发明的范围进行限制。
一种控制连铸坯尾保护渣卷渣的方法，包括：
1)降低尾坯拉速率在0.05m/min2以下，减少尾坯对保护渣的吸力；
2)扇形段对连铸板坯最后3-4m从恒定辊缝改为渐缩辊缝控制，增加尾坯内部钢液压力，减少向尾坯内部抽吸保护渣。
实施例1
控制高碳钢连铸坯尾保护渣卷渣的方法，包括：
1)降低尾坯拉速率为0.04m/min2；
2)扇形段对连铸板坯最后3m从恒定辊缝改为渐缩辊缝控制，渐缩辊缝的渐缩量设定为3.0mm,具体辊缝数据调整方案见表1；
表1：
距离坯尾米数 渐缩辊缝值
1m 0mm
1.5m -0.7mm
2.0m -1.5mm
2.5m -2.3mm
3.0m -3.0mm
实施例2
控制中碳钢连铸坯尾保护渣卷渣的方法，包括：
1)降低尾坯拉速率为0.05m/min2；
2)扇形段对连铸板坯最后3m从恒定辊缝改为渐缩辊缝控制，渐缩辊缝的渐缩量设定为2.3mm,具体辊缝数据调整方案见表2；
表2：
Figure BDA0003020503100000021
Figure BDA0003020503100000031
实施例3
控制中碳钢连铸坯尾保护渣卷渣的方法，包括：
1)降低尾坯拉速率为0.04m/min2；
2)扇形段对连铸板坯最后3m从恒定辊缝改为渐缩辊缝控制，渐缩辊缝的渐缩量设定为1.5mm,具体辊缝数据调整方案见表3；
表3：
距离坯尾米数 渐缩辊缝值
1m 0mm
1.5m -0.4mm
2.0m -0.8mm
2.5m -1.2mm
3.0m -1.5mm
。

Claims (1)

1.一种控制连铸坯尾保护渣卷渣的方法，其特征在于，减少连铸坯尾钢水凝固收缩时对保护渣的吸入，避免生产的钢卷出现坯尾夹杂分层缺陷，包括：
1)尾坯拉速率降低为0.04m/min2；
2)扇形段对连铸板坯最后3m从恒定辊缝改为渐缩辊缝控制，渐缩辊缝的渐缩量设定为3.0mm,具体辊缝数据调整：
距离坯尾1m，渐缩辊缝值0；
距离坯尾1.5m，渐缩辊缝值-0.7mm；
距离坯尾2m，渐缩辊缝值-1.5mm；
距离坯尾2.5m，渐缩辊缝值-2.3mm；
距离坯尾3m，渐缩辊缝值-3.0mm。
CN202110401492.5A 2021-04-14 2021-04-14 一种控制连铸坯尾保护渣卷渣的方法 Active CN113510227B (zh)