CN113503057A - 一种粮仓气密隔热性改造方法 - Google Patents
一种粮仓气密隔热性改造方法 Download PDFInfo
- Publication number
- CN113503057A CN113503057A CN202110930966.5A CN202110930966A CN113503057A CN 113503057 A CN113503057 A CN 113503057A CN 202110930966 A CN202110930966 A CN 202110930966A CN 113503057 A CN113503057 A CN 113503057A
- Authority
- CN
- China
- Prior art keywords
- air
- coating
- airtight
- heat insulation
- heat
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种粮仓气密隔热性改造方法,包括:地面气密隔热改造:清扫,对地坪L角、裂缝和伸缩缝进行气密性处理,打磨平整,喷涂高分子纳米渗透剂,用密闭涂料对地坪涂刷;墙面气密隔热改造:清理干净,一次刮涂腻子并铺贴网格布,固化后,喷涂高分子纳米渗透剂,固化后,再二次刮涂腻子,固化后,用密闭涂料对墙面涂刷;仓顶气密隔热改造:清扫,整体喷涂聚酰胺环氧树脂涂料;门窗气密隔热改造:安装双槽管,压入气调专用薄膜密封;粮面气密隔热改造:在装粮线处安装双槽管,压入气调专用薄膜密封;工艺孔洞气密隔热改造:在工艺孔洞处用硅酮密封胶进行密闭处理。本发明方法改造全面、气密隔热性强、保质降耗、工艺简单,成本低,适于现有粮仓改造。
Description
技术领域
本发明涉及一种气密隔热性改造方法,具体涉及一种粮仓气密隔热性改造方法。
背景技术
粮食安全始终是关系国计民生的重大问题,随着人们对绿色粮油食品需求的不断扩大,粮食储藏技术不断向“绿色健康”、“环保低碳”方向发展,以氮气气调、谷冷通风等工艺为主的“四合一”升级新技术得到了大量的推广应用。粮仓气密隔热性是储粮性能的重要指标之一,关系到储粮技术的应用效果和储粮成本,我国早期建设的粮仓平房仓的气密隔热性普遍较差,氮气气调过程中漏气严重,导致气调效果差且补气次数多,储粮成本居高不下,不能满足气调储粮等绿色储粮技术的要求,因此,提高现有粮仓的气密隔热性对粮食的绿色安全储藏至关重要。
CN205329876U公开了一种阻热隔气粮仓墙体,包括基体层和设置在基体层上表面的防水层,防水层的上表面还依次设有检漏基层、鳞片隔热阻气涂层和封孔保护层。虽然该墙体具有一定的阻热隔气性能,但是,综合隔热气密性较差,且对粮仓气密性能影响较大的门窗等部位未做处理,不能很好的满足气调低温储粮的要求。
CN203905574U公开了一种抗侧压气密性粮仓,是在粮仓吊顶底面设有聚氨酯喷涂发泡层;粮仓内墙上从主体墙往内依次为聚氨酯喷涂发泡层、加注砂浆的钢丝网层和腻子面层;粮仓地坪面由下至上依次为素土层、水泥碎石稳定层、高强度弹性密封卷材层和砼层。虽然该方案建设的粮仓具有较好的气密和抗侧压性能,但工艺复杂,成本高,且并未对门窗、工艺孔洞等重点漏气部位做处理,不能很好的满足气调低温储粮的要求。
目前,尚未有对粮仓地面、墙面、仓顶、门窗、粮面和工艺空洞等进行全面气密隔热处理的相关专利报道。
发明内容
本发明所要解决的技术问题是,克服现有技术存在的上述缺陷,提供一种改造全面、气密隔热性强、保质降耗、工艺简单,成本低,适宜于现有粮仓的系统化改造的粮仓气密隔热性改造方法。
本发明解决其技术问题所采用的技术方案如下:一种粮仓气密隔热性改造方法,包括:
地面气密隔热改造:清扫粮仓地坪基面的灰尘和杂物,对地坪L角、裂缝和伸缩缝进行气密性处理,将地面浮浆、起砂处打磨平整,清理干净后,喷涂高分子纳米渗透剂,最后用密闭涂料对地坪进行涂刷;
墙面气密隔热改造:将墙面基层原有墙漆铲除清理干净,一次刮涂腻子的过程中铺贴网格布,固化后,喷涂高分子纳米渗透剂,固化后,再二次刮涂腻子,固化后,用密闭涂料对墙面进行涂刷;
仓顶气密隔热改造:清扫仓顶内表面的灰尘和杂物,整体喷涂聚酰胺环氧树脂涂料;
门窗气密隔热改造:在大门和窗户上安装双槽管,并压入气调专用薄膜密封;
粮面气密隔热改造:在装粮线处安装双槽管,并压入气调专用薄膜密封;
工艺孔洞气密隔热改造:在工艺孔洞处用硅酮密封胶进行密闭处理。
优选地,所述地面气密隔热改造中,所述地坪L角进行气密性处理的方法是:将地坪L角原有的填充物清除,用气泵将L角内灰尘、杂物清理干净,基层表面喷涂高分子纳米渗透剂后,在L角内裂缝处用硅酮密封胶进行密封填充处理,再用聚合物防水抗裂砂浆填充成圆弧型L角,固化后,再在表面涂刷水泥防水粘连剂,铺贴聚乙烯丙纶防水卷材后,用水性环氧树脂涂料进行涂刷。粮仓地坪L角容易因仓房沉降产生大的裂缝,导致渗水漏气,严重影响仓房气密性,故需要重点对其做气密性处理。高分子纳米渗透剂可深入基材内部,形成透明防水结构层,有效阻隔水和气的渗入;聚合物防水抗裂砂浆可使地面和墙体紧密结合,再涂刷水泥防水粘连剂并铺贴聚乙烯丙纶防水卷材,可进一步防止裂缝的产生和加强防水效果,最后使用水性环氧树脂涂料可加强密闭性,使L角更美观和耐磨。
优选地,所述高分子纳米渗透剂的用量为0.1~0.2kg/m地坪L角线长。若用量过多,则会增加成本,若用量过少,则难以达到密闭效果。
优选地,所述高分子纳米渗透剂喷涂的地上高度为10~12cm,地面宽度为10~12cm。
优选地,所述高分子纳米渗透剂固含量为30~40%,其中,固体成分为质量比1:0.1~0.2:0.01~0.02的甲基硅醇钠、纳米级二氧化硅和三乙醇胺的混合物。所述高分子纳米渗透剂可与空气中的二氧化碳和水反应,形成防水膜,并且可渗透进建材内部形成致密的立体网状结构,堵塞毛细孔,具有长久的防水抗渗和密闭作用。
优选地,所述圆弧型L角的弧长为12~15cm,弧度为1.0~1.5°。圆弧型L角可减缓粮堆的压力,防止仓房的沉降,减少墙角裂缝的产生。
优选地,所述聚合物防水抗裂砂浆由水泥、砂子、聚合物胶粘剂和水以质量比1:1~3:0.005~0.015:1.0~1.5混合搅拌而成。所述聚合物防水抗裂砂浆具有较高的柔韧性、抗裂性和抗渗性,并且与地坪和墙体基层粘结牢固。
优选地,所述水泥防水粘连剂的涂刷厚度为8~12mm。
优选地,所述水泥防水粘连剂由水泥、胶粘剂和水以质量比1:0.02~0.03:0.4~0.6混合搅拌而成。更优选地,所述胶粘剂的型号为SBC120胶粘剂,购于长沙宝之暖保温材料有限公司。所述水泥防水粘连剂具有极强的粘结性,可使聚乙烯丙纶防水卷材紧密粘结在砂浆上。
优选地,所述聚乙烯丙纶防水卷材的厚度为0.6~1.0mm。若卷材太厚,则不易粘贴,若卷材太薄,则难以达到防水密闭效果。
优选地,所述聚乙烯丙纶防水卷材铺贴的地上高度为8~10cm,地面宽度为8~10cm。
优选地,所述水性环氧树脂涂料的涂刷厚度为0.4~0.6mm。
优选地,所述水性环氧树脂涂料涂刷的地上高度为10~12cm,地面宽度为10~12cm。
优选地,所述水性环氧树脂涂料的含水率为15~20%。
优选地,所述地面气密隔热改造中,所述裂缝和伸缩缝气密性处理的方法是:用角磨机将地坪裂缝和伸缩缝进行加宽处理,用气泵将缝内灰尘、杂物清理干净,缝内表面喷涂高分子纳米渗透剂,再用硅酮密封胶进行密封填充处理。
优选地,所述加宽处理的宽度为向裂缝两边各加宽0.3~0.5cm。
优选地,所述高分子纳米渗透剂的用量为0.02~0.05kg/m缝。
优选地,所述高分子纳米渗透剂固含量为30~40%,其中,固体成分为质量比1:0.1~0.2:0.01~0.02的甲基硅醇钠、纳米级二氧化硅和三乙醇胺的混合物。
优选地,所述墙面气密隔热改造中,所述一次刮涂腻子的厚度为0.4~0.6mm。若一次刮涂过厚,则会导致墙面开裂、起泡和脱落。
优选地,所述墙面气密隔热改造中,所述网格布下腻子层的厚度为0.2~0.4mm。
优选地,所述墙面气密隔热改造中,所述网格布的网格尺寸为3*3~5*5mm。
优选地,所述墙面气密隔热改造中,所述网格布的材质为聚酯纤维无纺布或玻纤布。聚酯纤维无纺布或玻纤布具有强度高、耐碱、抗裂、保温的特点。
优选地,所述墙面气密隔热改造中,所述二次刮涂腻子的厚度为0.3~0.5mm。
优选地,所述墙面气密隔热改造中,所述腻子为柔性防水腻子。
优选地,所述柔性防水腻子由水泥、重钙粉、石英砂、聚合物胶粉、羟丙基甲基纤维素和水以质量比1:0.8~1.2:0.4~0.6:0.2~0.4:0.04~0.06:1.0~1.5混合而成。
优选地,所述地面气密隔热改造和墙面气密隔热改造中,所述高分子纳米渗透剂的用量为0.2~0.5kg/m2。
优选地,所述地面气密隔热改造和墙面气密隔热改造中,所述密闭涂料的用量为0.4~1.0kg/m2。
优选地,所述地面气密隔热改造和墙面气密隔热改造中,所述密闭涂料为水性环氧树脂涂料。水性环氧树脂涂料具有良好的防水、防潮、阻气和隔热作用,并且环保、易施工。
优选地,所述地面气密隔热改造和墙面气密隔热改造中,采用两底两面工艺对密闭涂料进行涂刷。所述两底两面工艺是先用底漆进行横竖向交叉涂刷,固化后,再用面漆横向涂刷一遍,固化后,再使用面漆竖向涂刷一遍。通过横向和竖向交叉施工,使漆面具有更强的致密性。
优选地,所述仓顶气密隔热改造中,所述聚酰胺环氧树脂涂料的用量为0.5~1.0kg/m2。聚酰胺环氧树脂涂料具有很强的气密性和隔热、防潮作用。
优选地,所述门窗气密隔热改造和粮面气密隔热改造中,双槽管安装时,需在双槽管背面涂上硅酮密封胶,并用膨胀螺丝固定。
优选地,所述门窗气密隔热改造和粮面气密隔热改造中,所述气调专用薄膜的厚度为0.10~0.15mm,透氧率为500~2000mL/cm3。
优选地,所述门窗气密隔热改造和粮面气密隔热改造中,所述气调专用薄膜为三层共挤聚乙烯薄膜。
所述工艺孔洞包括气体检测管、测温电缆进线管、环流管等。
本发明方法的有益效果如下:
(1)本发明方法对粮仓地面、墙面、仓顶、门窗、粮面和工艺空洞进行全面气密隔热处理,充分考虑了所有可能的漏气点,使粮仓形成一个密闭体,有效避免了气体的泄露,大大增强粮仓的气密隔热性,可增加氮气气调时高浓度氮气的保持时间,降低充气次数,保证了气调效果,达到了保质降耗的目的;
(2)本发明方法改造后的粮仓气密性可高达472s,达到了气调储粮一级仓标准,大大提高了粮仓的气密性;在6~8月高温天气期间平均仓温可降低5.0~5.5℃,粮食平均温度可降低3~4℃,显著提升了仓房的隔热性;说明本发明方法改造全面、气密隔热性强、保质降耗、工艺简单,成本低,适宜于现有粮仓的系统化改造。
具体实施方式
下面结合实施例对本发明作进一步说明。
本发明实施例所使用的SBC120胶粘剂购于长沙宝之暖保温材料有限公司;本发明实施例所改造的粮仓为36×24m,装粮安全线高6m的高大平房仓;本发明实施例所使用的材料,如无特殊说明,均通过常规商业途径获得。
实施例1
地面气密隔热改造:清扫粮仓地坪基面的灰尘和杂物,对地坪L角、裂缝和伸缩缝进行气密性处理,将地面浮浆、起砂处打磨平整,清理干净后,喷涂高分子纳米渗透剂,最后用密闭涂料对地坪进行涂刷;
所述地坪L角进行气密性处理的方法是:将地坪L角原有的填充物清除,用气泵将L角内灰尘、杂物清理干净,基层表面喷涂高分子纳米渗透剂后,在L角内裂缝处用硅酮密封胶进行密封填充处理,再用聚合物防水抗裂砂浆填充成圆弧型L角,固化后,再在表面涂刷水泥防水粘连剂,铺贴聚乙烯丙纶防水卷材后,用水性环氧树脂涂料进行涂刷;所述高分子纳米渗透剂的用量为0.1kg/m地坪L角线长;所述高分子纳米渗透剂喷涂的地上高度为10cm,地面宽度为10cm;所述高分子纳米渗透剂固含量为30%,其中,固体成分为质量比1:0.2:0.02的甲基硅醇钠、纳米级二氧化硅和三乙醇胺的混合物;所述圆弧型L角的弧长为12cm,弧度为1.5°;所述聚合物防水抗裂砂浆由1重量份的水泥、2重量份的砂子、0.01重量份的聚合物胶粘剂和1.2重量份的水混合搅拌而成;所述水泥防水粘连剂的涂刷厚度为12mm;所述水泥防水粘连剂由1重量份的水泥、0.025重量份的SBC120胶粘剂和0.5重量份的水混合搅拌而成;所述聚乙烯丙纶防水卷材的厚度为0.8mm;所述聚乙烯丙纶防水卷材铺贴的地上高度为8cm,地面宽度为8cm;所述水性环氧树脂涂料的涂刷厚度为0.5mm;所述水性环氧树脂涂料涂刷的地上高度为10cm,地面宽度为10cm;所述水性环氧树脂涂料的含水率为15%。
所述裂缝和伸缩缝气密性处理的方法是:用角磨机将地坪裂缝和伸缩缝进行加宽处理,用气泵将缝内灰尘、杂物清理干净,缝内表面喷涂高分子纳米渗透剂,再用硅酮密封胶进行密封填充处理;所述加宽处理的宽度为向裂缝两边各加宽0.3cm;所述高分子纳米渗透剂的用量为0.03kg/m缝;
墙面气密隔热改造:将墙面基层原有墙漆铲除清理干净,一次刮涂柔性防水腻子的过程中铺贴网格布,固化后,喷涂高分子纳米渗透剂,固化后,再二次刮涂柔性防水腻子,固化后,用密闭涂料对墙面进行涂刷;所述一次刮涂柔性防水腻子的厚度为0.4mm;所述网格布下腻子层的厚度为0.2mm;所述网格布的网格尺寸为3*3mm;所述网格布的材质为聚酯纤维无纺布;所述二次刮涂柔性防水腻子的厚度为0.3mm;所述柔性防水腻子由水泥、重钙粉、石英砂、聚合物胶粉、羟丙基甲基纤维素和水以质量比1:1:0.5:0.3:0.05:1.2混合而成;
所述地面气密隔热改造和墙面气密隔热改造中,所述高分子纳米渗透剂的用量为0.2kg/m2;所述高分子纳米渗透剂固含量为30%,其中,固体成分为质量比1:0.2:0.02的甲基硅醇钠、纳米级二氧化硅和三乙醇胺的混合物;所述密闭涂料的用量为0.4kg/m2;所述密闭涂料为水性环氧树脂涂料;采用两底两面工艺对密闭涂料进行涂刷,所述两底两面工艺是先用底漆进行横竖向交叉涂刷,固化后,再用面漆横向涂刷一遍,固化后,再使用面漆竖向涂刷一遍;
仓顶气密隔热改造:清扫仓顶内表面的灰尘和杂物,整体喷涂聚酰胺环氧树脂涂料;所述聚酰胺环氧树脂涂料的用量为0.5kg/m2;
门窗气密隔热改造:在大门和窗户上安装双槽管,并压入气调专用薄膜密封;
粮面气密隔热改造:在装粮线处安装双槽管,并压入气调专用薄膜密封;
所述门窗气密隔热改造和粮面气密隔热改造中,双槽管安装时,需在双槽管背面涂上硅酮密封胶,并用膨胀螺丝固定;所述气调专用薄膜的厚度为0.1mm,透氧率为1500mL/cm3;所述气调专用薄膜为三层共挤聚乙烯薄膜;
工艺孔洞气密隔热改造:在工艺孔洞处用硅酮密封胶进行密闭处理;所述工艺孔洞包括气体检测管、测温电缆进线管、环流管等。
实施例2
地面气密隔热改造:清扫粮仓地坪基面的灰尘和杂物,对地坪L角、裂缝和伸缩缝进行气密性处理,将地面浮浆、起砂处打磨平整,清理干净后,喷涂高分子纳米渗透剂,最后用密闭涂料对地坪进行涂刷;
所述地坪L角进行气密性处理的方法是:将地坪L角原有的填充物清除,用气泵将L角内灰尘、杂物清理干净,基层表面喷涂高分子纳米渗透剂后,在L角内裂缝处用硅酮密封胶进行密封填充处理,再用聚合物防水抗裂砂浆填充成圆弧型L角,固化后,再在表面涂刷水泥防水粘连剂,铺贴聚乙烯丙纶防水卷材后,用水性环氧树脂涂料进行涂刷;所述高分子纳米渗透剂的用量为0.2kg/m地坪L角线长;所述高分子纳米渗透剂喷涂的地上高度为12cm,地面宽度为12cm;所述高分子纳米渗透剂固含量为40%,其中,固体成分为质量比为1:0.15:0.01的甲基硅醇钠、纳米级二氧化硅和三乙醇胺的混合物;所述圆弧型L角的弧长为15cm,弧度为1.0°;所述聚合物防水抗裂砂浆由1重量份的水泥、2.5重量份的砂子、0.012重量份的聚合物胶粘剂和1.4重量份的水混合搅拌而成;所述水泥防水粘连剂的涂刷厚度为10mm;所述水泥防水粘连剂由1重量份的水泥、0.03重量份的SBC120胶粘剂和0.4重量份的水混合搅拌而成;所述聚乙烯丙纶防水卷材的厚度为0.6mm;所述聚乙烯丙纶防水卷材铺贴的地上高度为10cm,地面宽度为10cm;所述水性环氧树脂涂料的涂刷厚度为0.6mm;所述水性环氧树脂涂料涂刷的地上高度为12cm,地面宽度为12cm;所述水性环氧树脂涂料的含水率为20%。
所述裂缝和伸缩缝气密性处理的方法是:用角磨机将地坪裂缝和伸缩缝进行加宽处理,用气泵将缝内灰尘、杂物清理干净,缝内表面喷涂高分子纳米渗透剂,再用硅酮密封胶进行密封填充处理;所述加宽处理的宽度为向裂缝两边各加宽0.5cm;所述高分子纳米渗透剂的用量为0.05kg/m缝;
墙面气密隔热改造:将墙面基层原有墙漆铲除清理干净,一次刮涂柔性防水腻子的过程中铺贴网格布,固化后,喷涂高分子纳米渗透剂,固化后,再二次刮涂柔性防水腻子,固化后,用密闭涂料对墙面进行涂刷;所述一次刮涂柔性防水腻子的厚度为0.6mm;所述网格布下腻子层的厚度为0.4mm;所述网格布的网格尺寸为5*5mm;所述网格布的材质为玻纤布;所述二次刮涂柔性防水腻子的厚度为0.5mm;所述柔性防水腻子由水泥、重钙粉、石英砂、聚合物胶粉、羟丙基甲基纤维素和水以质量比1:0.8:0.6:0.4:0.04:1.1混合而成;
所述地面气密隔热改造和墙面气密隔热改造中,所述高分子纳米渗透剂的用量为0.5kg/m2;所述高分子纳米渗透剂固含量为40%,其中,固体成分为质量比为1:0.15:0.01的甲基硅醇钠、纳米级二氧化硅和三乙醇胺的混合物;所述密闭涂料的用量为1.0kg/m2;所述密闭涂料为水性环氧树脂涂料;采用两底两面工艺对密闭涂料进行涂刷,所述两底两面工艺是先用底漆进行横竖向交叉涂刷,固化后,再用面漆横向涂刷一遍,固化后,再使用面漆竖向涂刷一遍;
仓顶气密隔热改造:清扫仓顶内表面的灰尘和杂物,整体喷涂聚酰胺环氧树脂涂料;所述聚酰胺环氧树脂涂料的用量为1.0kg/m2;
门窗气密隔热改造:在大门和窗户上安装双槽管,并压入气调专用薄膜密封;
粮面气密隔热改造:在装粮线处安装双槽管,并压入气调专用薄膜密封;
所述门窗气密隔热改造和粮面气密隔热改造中,双槽管安装时,需在双槽管背面涂上硅酮密封胶,并用膨胀螺丝固定;所述气调专用薄膜的厚度为0.15mm,透氧率为1000mL/cm3;所述气调专用薄膜为三层共挤聚乙烯薄膜;
工艺孔洞气密隔热改造:在工艺孔洞处用硅酮密封胶进行密闭处理;所述工艺孔洞包括气体检测管、测温电缆进线管、环流管等。
为了评价经实施例1、2改造后粮仓的气密性和隔热性,按照GB/25229-2010《粮油储藏 平房仓气密性要求》,采用负压压力衰减测试法(-300Pa~-150Pa的半衰期)测试其气密性,通过测定6~8月高温天气期间粮仓内的常温和粮食平均温度来测试其隔热性。
经检测,实施例1改造前粮仓的气密性为73s,经改造后的粮仓气密性为458s,实施例2改造前粮仓的气密性为65s,经改造后的粮仓气密性为472s,说明经过实施例1、2改造后的粮仓均达到了气调储粮一级仓标准,大大提高了粮仓的气密性。
经检测,实施例1在6~8月高温天气期间的平均仓温为29℃,粮食平均温度为15℃;实施例2在6~8月期间平均仓温为28.5℃,粮食平均温度为14℃;而粮库未经改造的同一仓型在6~8月期间平均仓温为34℃,粮食平均温度为18℃。说明经过实施例1、2改造后的粮仓比未改造的粮仓在6~8月期间平均仓温可降低5~5.5℃,粮食平均温度可降低3~4℃,显著提升了仓房的隔热性。
综上,经过本发明方法改造后的粮仓改造全面、气密隔热性强、工艺简单,成本低,适宜于现有粮仓的系统化改造。
Claims (7)
1.一种粮仓气密隔热性改造方法,其特征在于,包括:
地面气密隔热改造:清扫粮仓地坪基面的灰尘和杂物,对地坪L角、裂缝和伸缩缝进行气密性处理,将地面浮浆、起砂处打磨平整,清理干净后,喷涂高分子纳米渗透剂,最后用密闭涂料对地坪进行涂刷;
墙面气密隔热改造:将墙面基层原有墙漆铲除清理干净,一次刮涂腻子的过程中铺贴网格布,固化后,喷涂高分子纳米渗透剂,固化后,再二次刮涂腻子,固化后,用密闭涂料对墙面进行涂刷;
仓顶气密隔热改造:清扫仓顶内表面的灰尘和杂物,整体喷涂聚酰胺环氧树脂涂料;
门窗气密隔热改造:在大门和窗户上安装双槽管,并压入气调专用薄膜密封;
粮面气密隔热改造:在装粮线处安装双槽管,并压入气调专用薄膜密封;
工艺孔洞气密隔热改造:在工艺孔洞处用硅酮密封胶进行密闭处理。
2.根据权利要求1所述粮仓气密隔热性改造方法,其特征在于:所述地面气密隔热改造中,所述地坪L角进行气密性处理的方法是:将地坪L角原有的填充物清除,用气泵将L角内灰尘、杂物清理干净,基层表面喷涂高分子纳米渗透剂后,在L角内裂缝处用硅酮密封胶进行密封填充处理,再用聚合物防水抗裂砂浆填充成圆弧型L角,固化后,再在表面涂刷水泥防水粘连剂,铺贴聚乙烯丙纶防水卷材后,用水性环氧树脂涂料进行涂刷;所述高分子纳米渗透剂的用量为0.1~0.2kg/m地坪L角线长;所述高分子纳米渗透剂喷涂的地上高度为10~12cm,地面宽度为10~12cm;所述高分子纳米渗透剂固含量为30~40%,其中,固体成分为质量比1:0.1~0.2:0.01~0.02的甲基硅醇钠、纳米级二氧化硅和三乙醇胺的混合物;所述圆弧型L角的弧长为12~15cm,弧度为1.0~1.5°;所述聚合物防水抗裂砂浆由水泥、砂子、聚合物胶粘剂和水以质量比1:1~3:0.005~0.015:1.0~1.5混合搅拌而成;所述水泥防水粘连剂的涂刷厚度为8~12mm;所述水泥防水粘连剂由水泥、胶粘剂和水以质量比1:0.02~0.03:0.4~0.6混合搅拌而成;所述聚乙烯丙纶防水卷材的厚度为0.6~1.0mm;所述聚乙烯丙纶防水卷材铺贴的地上高度为8~10cm,地面宽度为8~10cm;所述水性环氧树脂涂料的涂刷厚度为0.4~0.6mm;所述水性环氧树脂涂料涂刷的地上高度为10~12cm,地面宽度为10~12cm;所述水性环氧树脂涂料的含水率为15~20%。
3.根据权利要求1或2所述粮仓气密隔热性改造方法,其特征在于:所述地面气密隔热改造中,所述裂缝和伸缩缝气密性处理的方法是:用角磨机将地坪裂缝和伸缩缝进行加宽处理,用气泵将缝内灰尘、杂物清理干净,缝内表面喷涂高分子纳米渗透剂,再用硅酮密封胶进行密封填充处理;所述加宽处理的宽度为向裂缝两边各加宽0.3~0.5cm;所述高分子纳米渗透剂的用量为0.02~0.05kg/m缝;所述高分子纳米渗透剂固含量为30~40%,其中,固体成分为质量比1:0.1~0.2:0.01~0.02的甲基硅醇钠、纳米级二氧化硅和三乙醇胺的混合物。
4.根据权利要求1~3之一所述粮仓气密隔热性改造方法,其特征在于:所述墙面气密隔热改造中,所述一次刮涂腻子的厚度为0.4~0.6mm;所述网格布下腻子层的厚度为0.2~0.4mm;所述网格布的网格尺寸为3*3~5*5mm;所述网格布的材质为聚酯纤维无纺布或玻纤布;所述二次刮涂腻子的厚度为0.3~0.5mm;所述腻子为柔性防水腻子;所述柔性防水腻子由水泥、重钙粉、石英砂、聚合物胶粉、羟丙基甲基纤维素和水以质量比1:0.8~1.2:0.4~0.6:0.2~0.4:0.04~0.06:1.0~1.5混合而成。
5.根据权利要求1~4之一所述粮仓气密隔热性改造方法,其特征在于:所述地面气密隔热改造和墙面气密隔热改造中,所述高分子纳米渗透剂的用量为0.2~0.5kg/m2;所述密闭涂料的用量为0.4~1.0kg/m2;所述密闭涂料为水性环氧树脂涂料;采用两底两面工艺对密闭涂料进行涂刷。
6.根据权利要求1~5之一所述粮仓气密隔热性改造方法,其特征在于:所述仓顶气密隔热改造中,所述聚酰胺环氧树脂涂料的用量为0.5~1.0kg/m2。
7.根据权利要求1~6之一所述粮仓气密隔热性改造方法,其特征在于:所述门窗气密隔热改造和粮面气密隔热改造中,双槽管安装时,需在双槽管背面涂上硅酮密封胶,并用膨胀螺丝固定;所述气调专用薄膜的厚度为0.10~0.15mm,透氧率为500~2000mL/cm3;所述气调专用薄膜为三层共挤聚乙烯薄膜。