CN1132880C - Method for making normal temperature plasticine - Google Patents
Method for making normal temperature plasticine Download PDFInfo
- Publication number
- CN1132880C CN1132880C CN 00123233 CN00123233A CN1132880C CN 1132880 C CN1132880 C CN 1132880C CN 00123233 CN00123233 CN 00123233 CN 00123233 A CN00123233 A CN 00123233A CN 1132880 C CN1132880 C CN 1132880C
- Authority
- CN
- China
- Prior art keywords
- plasticine
- normal temperature
- microcrystalline wax
- rosin
- white vaseline
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to the improvement of a sculpturing material. Microcrystalline wax, white vaseline and rosin are proportionally put and heated in a metal container to achieve a certain melting point, and then powdery fillers are poured and uniformly stirred in the metal container; the sculpturing material can be obtained by cooling. The sculpturing material has the advantages of high density, good viscidity, good handle, easy molding, little possibility of hand pollution with plasticine and colors, little possibility of deformation at normal temperature, no bacterium or toxicity and no pollution. The sculpturing material is not only suitable for sculpture, but is also suitable for industrial molding design, building design, industrial art, mold fabrication, art education, children' s toys, etc.
Description
The present invention relates to the improvement of carving material.
Plasticine claims greasy filth, oily soil, oily clay again.Present homemade plasticine is soft partially when operation, the easy foundry loam of hand, and sticking look, yielding under the normal temperature.External import plasticine is also undesirable, though influenced by temperature as Korea S's plasticine, the still easy foundry loam of hand, sticking look when using; Japan's like product has only moulding instability, also contains certain toxic substance.The oily clay of producing as Japanese toy association clear and definite prompting in specification sheets: " on hand, arm etc., have when hindering swollen, eczema etc., please do not use." even when operation, can not contact nose, eyes and mouth.This shows the above-mentioned comparatively desirable material that all can not become at present.Purpose of the present invention just provides a kind of good hand touch, normal temperature plasticine that normal temperature is yielding, nontoxic.
The object of the present invention is achieved like this: Microcrystalline Wax 140-155g, white vaseline 90-110g, rosin 18-20g are put into metal vessel heat, when fusing point rises to 120-140 ℃,, pour powder filler 300-450g into and stir evenly from fire, after the cooling promptly.
According to this area weather condition and actual needs, can in the limit proportional range, arbitrarily reconcile.Strengthen Microcrystalline Wax and rosin ratio and can increase strength of materials height, the ratio that strengthens vaseline can make material hardness weaken.Its color difference depends on filler.
Below to material therefor explanation of the present invention:
(1) Microcrystalline Wax
Microcrystalline Wax has two kinds, and a kind of is oxidized microcrystalline wax, and another kind is 80
#The pure white Microcrystalline Wax.Oxidized microcrystalline wax is light yellow, and the solid of flexible, dropping point are 70-115 ℃.80
#The pure white Microcrystalline Wax is the yellow cereous deep processing of China, and dropping point is 82.5 ℃.Both density is at 0.85-0.95g/cm
3About.The effect of Microcrystalline Wax in prescription is after utilization is softened, density at normal temperatures, viscosity, hardness, extensional viscosity and kinematic viscosity and peculiar avidity.
(2) white vaseline
White vaseline belongs to medical strict control acid number, sulphur content and does not contain a kind of paste petroleum products of fused ring compound.Fusing point is 38-56 ℃.Its effect is to make Microcrystalline Wax etc. softening, forms the plasticity-feel.
(3) rosin
Rosin is commonly called as ripe rosin or ripe perfume (or spice).Transparent glass shape crumbly mass has rosin fat fragrance.Density 1.05-1.10g/cm
3Fusing point 110-135 ℃.Warm deliquescing and gluing.Effect in prescription is to increase viscosity, density and hardness.
(4) powder filler
Powder filler is as mud powder, cement flour, chalk powder, various ore powders etc.Generally 200
#It below all is available object.In prescription, fleut is the matrix of plasticine.
Major advantage of the present invention: the present invention is the sculptor according to the practice development of oneself, and its advantage is the density height, good hand touch, moulding sure, hand is difficult for foundry loam, sticking look, and is not yielding at normal temperatures, aseptic nontoxic, do not pollute.The present invention is applicable to that also Industrial Moulding Design, architectural design, artwork design, mould turn over system, art education and toy for children etc. except that being used for sculpture.
Embodiment 1:
Microcrystalline Wax 150g
White vaseline 100g
Rosin 19g
Powder filler 400g
Embodiment 2:
Microcrystalline Wax 145g
White vaseline 90g
Rosin 18g
Powder filler 370g
Embodiment 3:
Microcrystalline Wax 152g
White vaseline 105g
Rosin 18g
Powder filler 380g
Claims (4)
1, a kind of making method of normal temperature plasticine, Microcrystalline Wax 140-155g, white vaseline 90-110g, rosin 18-20g are put into metal vessel to be heated, when fusing point rises to 120-140 ℃ from fire, the powder filler 300-450g that pours mud powder, cement flour, chalk powder and ore powder into stirs evenly, after the cooling promptly.
2, the making method of a kind of normal temperature plasticine according to claim 1 is characterized in that Microcrystalline Wax 150g, white vaseline 100g, rosin 19g, powder filler 400g.
3, the making method of a kind of normal temperature plasticine according to claim 1 is characterized in that Microcrystalline Wax 145g, white vaseline 90g, rosin 18g, powder filler 370g.
4, the making method of a kind of normal temperature plasticine according to claim 1 is characterized in that Microcrystalline Wax 152g, white vaseline 105g, rosin 18g, powder filler 380g.