CN1132881C - Method for making normal temperature stone imitating plasticine - Google Patents
Method for making normal temperature stone imitating plasticine Download PDFInfo
- Publication number
- CN1132881C CN1132881C CN 00123234 CN00123234A CN1132881C CN 1132881 C CN1132881 C CN 1132881C CN 00123234 CN00123234 CN 00123234 CN 00123234 A CN00123234 A CN 00123234A CN 1132881 C CN1132881 C CN 1132881C
- Authority
- CN
- China
- Prior art keywords
- microcrystalline wax
- plasticine
- normal temperature
- rosin
- white vaseline
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to an improved sculpturing material. Microcrystalline wax, white vaseline and rosin are heated according to a certain proportion and then mixed with mineral powder stuffing and purified sand, and then the sculpturing material is obtained. The present invention has the main advantages of high density, good viscosity, sterile state, no toxicity and real stone imitating effect.
Description
The present invention relates to the improvement of carving material.
At present, China does not still have the producer that produces this material.Japan is existing with the imitative stone clay of natural clay synthetic water-based.But need after doing could realize imitative stone effect through polishing, it makes the sculpture technology complexity.
The objective of the invention is to solve the sculptor and can simplify sculpture making processes, improve the normal temperature stone imitating plasticine of looking effect that to realize stone carving in the first draft.
The object of the present invention is achieved like this: Microcrystalline Wax 140-160g, white vaseline 90-110g, rosin 15-20g are put into metal vessel heat, when fusing point rises to 130-140 ℃,, pour mineral powder filling materials 200-220g, pure sand 180-220g into from fire, stir evenly, after the cooling promptly.
Can arbitrarily reconcile by formula rate according to actual needs.Strengthen Microcrystalline Wax and rosiny ratio, can increase hardness, strengthen the ratio of Vaseline, can reduce hardness.Its color depends on filler.
The material therefor explanation:
(1) Microcrystalline Wax
Microcrystalline Wax has two kinds, and a kind of is oxidized microcrystalline wax, and another kind is 80
#The pure white Microcrystalline Wax.Oxidized microcrystalline wax is the solid of light yellow flexible, and dropping point is 70-115 ℃.80
#The pure white Microcrystalline Wax is the yellow cereous deep processing of China, and dropping point is at 82.5 ℃, and both density is at 0.85-0.95g/em
3About.The effect of Microcrystalline Wax in prescription is after utilization is softened, density at normal temperatures, viscosity, hardness, extensional viscosity and kinematic viscosity and distinctive avidity.
(2) white vaseline
White vaseline belongs to medical strict control acid number, sulphur content and do not contain a kind of paste petroleum products of fused ring compound.Fusing point is 38-56 ℃.Effect of the present invention is to make Microcrystalline Wax etc. softening, forms the plasticity-feel.
(3) rosin
Rosin is commonly called as ripe rosin or ripe perfume (or spice).Transparent glass shape crumbly mass has rosin fat fragrance.Density
1.05-1.10g/cm
3Fusing point 110-135 ℃, the chance thermal change is soft and sticking, and the effect in prescription is to increase viscosity, hardness and density.
(4) powder filler
Powder filler, as mud powder, cement flour, chalk powder and various ore powder, general requirement is 200
#More than, all be available object.In prescription, fleut is the matrix of plasticine.The color of the color decision plasticine of filler.
(5) pure sand
Pure sand promptly refers to the ore sand and the artificial sand (silicon carbide) of various looks.It would be desirable luminously to have sand.50-120
#For good.Effect in plasticine is to form the sandstone sense with the filler unification.
Advantage of the present invention:
The net effect of material of the present invention has the density height, and viscosity is good, and hand is the sticking look of foundry loam not, does not do, does not split, and is nontoxic aseptic, not yielding, and imitative stone effect is true.
Embodiment 1:
Microcrystalline Wax 150g
White vaseline 100g
Rosin 15g
Powder filler 200g
Pure sand 200g
Embodiment 2:
Microcrystalline Wax 140g
White vaseline 95g
Rosin 16g
Powder filler 210g
Pure sand 190g
Embodiment 3:
Microcrystalline Wax 145g
White vaseline 98g
Rosin 18g
Powder filler 215g
Pure sand 180g
Claims (4)
1, a kind of making method of normal temperature stone imitating plasticine, Microcrystalline Wax 140-160g, white vaseline 90-110g, rosin 15-20g are put into metal vessel to be heated, when fusing point rises to 130-140 ℃, from fire, pour the powder filler 200-220g of mud powder, cement flour, chalk powder and various ore powders, pure sand 180-200g into, stir evenly, after the cooling promptly.
2, the making method of a kind of normal temperature stone imitating plasticine according to claim 1 is characterized in that Microcrystalline Wax 150g, white vaseline 100g, rosin 15g, powder filler 200g, pure sand 200g.
3, the making method of a kind of normal temperature stone imitating plasticine according to claim 1 is characterized in that Microcrystalline Wax 140g, white vaseline 95g, rosin 16g, powder filler 210g, pure sand 190g.
4, the making method of a kind of normal temperature stone imitating plasticine according to claim 1 is characterized in that Microcrystalline Wax 145g, white vaseline 98g, rosin 18g, powder filler 215g, pure sand 180g.