CN113215836A - 一种耐高温沥青复合防水卷材及其制备方法 - Google Patents
一种耐高温沥青复合防水卷材及其制备方法 Download PDFInfo
- Publication number
- CN113215836A CN113215836A CN202110409838.6A CN202110409838A CN113215836A CN 113215836 A CN113215836 A CN 113215836A CN 202110409838 A CN202110409838 A CN 202110409838A CN 113215836 A CN113215836 A CN 113215836A
- Authority
- CN
- China
- Prior art keywords
- parts
- temperature
- asphalt
- coiled material
- waterproof coiled
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种耐高温沥青复合防水卷材及其制备方法，该防水卷材包括以下重量份数的原料组成：基质沥青30～60份、氯化橡胶20～35份、古马隆树脂6～12份、季戊四醇硬脂酸酯3～5份、丙烯酸羟乙酯3～10份、凹凸棒土10～25份、功能填料10～20份、补强填料10～20份、十二烷基苯磺酸钠1～3份、甲基三甲氧基硅烷5～15份、磷酸二氢铝5～20份、防老剂15～25份、光稳定剂5～10份及改性剂5～10份。有益效果：本发明可以在保证较低成本的同时提高防水卷材的防水性能及耐高温性能，具有优异的耐高温性能、防水性能、阻燃性能、耐磨性能、防腐性能及耐紫外线性能。
Description
技术领域
本发明涉及防水材料制备技术领域，具体来说，涉及一种耐高温沥青复合防水卷材及其制备方法。
背景技术
随着经济的发展和社会的进步，各种建筑物如春笋般拔地而起，但在各种工程建设时，经常会出现屋面、地面、地下室渗水漏水等问题，为了解决这一问题，建筑防水工程应运而生，在建筑防水工程中广泛应用的建筑材料是高分子防水卷材。
目前，市场上的防水卷材类产品主要由三大系列组成，改性沥青防水材料，高分子塑料防水片材以及合成橡胶防水卷材。改性沥青防水卷材是以橡胶改性石油沥青为侵渍覆盖层，以聚酯纤维无纺布、黄麻布、玻纤毡等制作为胎基，以塑料薄膜为防粘隔离层，经选材、配料、共熔、侵渍、复合成型、卷曲等工序加工制作。
然而，现有的沥青复合防水卷材，在高温环境下使用，由于自身耐高温能力较差使得自身性能下降，且在使用过程中会受到光照，在光照条件下，沥青复合防水卷材会发生光化学反应，使得自身性能下降，进而使得使用寿命降低。
针对相关技术中的问题，目前尚未提出有效的解决方案。
发明内容
针对相关技术中的问题，本发明提出一种耐高温沥青复合防水卷材及其制备方法，以克服现有相关技术所存在的上述技术问题。
为此，本发明采用的具体技术方案如下：
根据本发明的一个方面，提供了一种耐高温沥青复合防水卷材，该防水卷材包括以下重量份数的原料组成：
基质沥青30～60份、氯化橡胶20～35份、古马隆树脂6～12份、季戊四醇硬脂酸酯3～5份、丙烯酸羟乙酯3～10份、凹凸棒土10～25份、功能填料10～20份、补强填料10～20份、十二烷基苯磺酸钠1～3份、甲基三甲氧基硅烷5～15份、磷酸二氢铝5～20份、防老剂15～25份、光稳定剂5～10份及改性剂5～10份。
进一步的，所述基质沥青由天然沥青和石油沥青按照2：1的重量比混合而成。
进一步的，所述功能填料由聚乙烯、聚酰胺、聚丙烯或聚酯类材料制成，且所述聚乙烯为线性低密度聚乙烯树脂。
进一步的，所述补强填料由氧化铈和三氧化锑按照1：1的重量比混合而成。
进一步的，所述防老剂由防老剂2246和防老剂4020按照3：2的重量比混合而成。
进一步的，所述光稳定剂由二苯甲酮和水杨酸甲酯按照任意比例混合而成。
进一步的，所述改性剂为SBS、APP、APAO、聚丙烯粉末和HDPE中的几种或多种混合而成。
根据本发明的另一方面，提供了一种耐高温沥青复合防水卷材的制备方法，该制备方法包括以下步骤：
S1、称取预设重量份数的耐高温沥青复合防水卷材的制备原料；
S2、将称取的基质沥青加入反应釜中进行加热直至基质沥青完全熔融；
S3、将称取的氯化橡胶和古马隆树脂加入粉碎机中进行粉碎处理；
S4、将熔融的基质沥青、粉碎的氯化橡胶和古马隆树脂、季戊四醇硬脂酸酯、丙烯酸羟乙酯及凹凸棒土加入搅拌釜中进行搅拌，直至搅拌均匀；
S5、向搅拌釜中继续加入功能填料、补强填料、十二烷基苯磺酸钠、甲基三甲氧基硅烷、磷酸二氢铝、防老剂、光稳定剂及改性剂，并不断搅拌直至搅拌均匀，得到混合料；
S6、利用高速剪切机对混合料剪切得到沥青防水材料，并将沥青防水材料倾倒在玻纤毡上，冷却至室温制得沥青复合防水卷材。
进一步的，所述加热温度为210～240℃，加热时间为40～60分钟，所述搅拌釜的搅拌速度为150～250rpm，搅拌时间为30分钟，搅拌温度为215-230℃。
进一步的，所述S6中利用高速剪切机对混合料剪切得到沥青防水材料具体包括以下步骤：
将混合料加入高速剪切机，在转速为4000～5000r/min，温度为215-230℃的条件下，进行剪切30-40min后，在转速为500～800r/min的条件下，继续搅拌1.5～2h制得沥青防水材料。
本发明的有益效果为：通过天然沥青和石油沥青的配合使用，使得其可以在保证较低成本的同时，有效地提高防水卷材的防水性能及耐高温性能；通过凹凸棒土、氯化橡胶及防老剂的使用，不仅可以有效地提高防水卷材的阻燃性能，而且还可以有效地提高防水卷材的耐磨及防腐性能；通过光稳定剂、补强填料、功能层、古马隆树脂及季戊四醇硬脂酸酯的配合使用，使得本发明的防水卷材具有优异的耐高温和耐紫外线性能；且本发明防水卷材的制备工艺具有工艺简单、原料易得及易于操作的优点。
附图说明
为了更清楚地说明本发明实施例或现有技术中的技术方案，下面将对实施例中所需要使用的附图作简单地介绍，显而易见地，下面描述中的附图仅仅是本发明的一些实施例，对于本领域普通技术人员来讲，在不付出创造性劳动的前提下，还可以根据这些附图获得其他的附图。
图1是根据本发明实施例的一种耐高温沥青复合防水卷材的制备方法的流程图。
具体实施方式
为进一步说明各实施例，本发明提供有附图，这些附图为本发明揭露内容的一部分，其主要用以说明实施例，并可配合说明书的相关描述来解释实施例的运作原理，配合参考这些内容，本领域普通技术人员应能理解其他可能的实施方式以及本发明的优点，图中的组件并未按比例绘制，而类似的组件符号通常用来表示类似的组件。
根据本发明的实施例，提供了一种耐高温沥青复合防水卷材及其制备方法。
现结合附图和具体实施方式对本发明进一步说明，根据本发明的一个方面，提供了一种耐高温沥青复合防水卷材，该防水卷材包括以下重量份数的原料组成：
基质沥青30～60份、氯化橡胶20～35份、古马隆树脂6～12份、季戊四醇硬脂酸酯3～5份、丙烯酸羟乙酯3～10份、凹凸棒土10～25份、功能填料10～20份、补强填料10～20份、十二烷基苯磺酸钠1～3份、甲基三甲氧基硅烷5～15份、磷酸二氢铝5～20份、防老剂15～25份、光稳定剂5～10份及改性剂5～10份。
其中，所述基质沥青由天然沥青和石油沥青按照2：1的重量比混合而成，在保证较低成本的同时，提高了卷材的防水性高和耐高温性能；
所述功能填料由聚乙烯、聚酰胺、聚丙烯或聚酯类材料制成，且所述聚乙烯为线性低密度聚乙烯树脂，其具有稳定的耐化学性、耐臭氧性、抗穿刺性，较高的抗冲击强度和耐环境应力开裂性等优点；
所述补强填料由氧化铈和三氧化锑按照1：1的重量比混合而成，利用了稀土氧化物的空轨道可以捕捉不稳定的游离基，使其失去活性，稀土元素暴露出未充满的4f电子，具有较强的配位络合作用，形成稳定的氧化物，能够吸收高能级的紫外线而以低能级的红外热能放出，并具有长效性，这就大大减少了紫外线的侵害，提高了本发明防水卷材的耐紫外线性能；
所述防老剂由防老剂2246和防老剂4020按照3：2的重量比混合而成；
所述光稳定剂由二苯甲酮和水杨酸甲酯按照任意比例混合而成；
所述改性剂为SBS、APP、APAO、聚丙烯粉末和HDPE中的几种或多种混合而成，能够有效地改善沥青各方面性能指标。
为了更好的理解上述技术方案，以下就本发明的具体实施例进行详细说明。
实施例一
一种耐高温沥青复合防水卷材，该防水卷材包括以下重量份数的原料组成：
基质沥青30份(天然沥青20份和石油沥青10份)、氯化橡胶20份、古马隆树脂6份、季戊四醇硬脂酸酯3份、丙烯酸羟乙酯3份、凹凸棒土10份、功能填料(线性低密度聚乙烯树脂)10份、补强填料10份(氧化铈5份和三氧化锑5份)、十二烷基苯磺酸钠1份、甲基三甲氧基硅烷5份、磷酸二氢铝5份、防老剂15份(10份防老剂2246和5份防老剂4020)、光稳定剂5份(二苯甲酮3份和水杨酸甲酯2份)及改性剂5份(SBS、APP及APAO)。
实施例二
一种耐高温沥青复合防水卷材，该防水卷材包括以下重量份数的原料组成：
基质沥青45份(天然沥青30份和石油沥青15份)、氯化橡胶25份、古马隆树脂8份、季戊四醇硬脂酸酯4份、丙烯酸羟乙酯6份、凹凸棒土15份、功能填料(聚酰胺树脂)15份、补强填料15份(氧化铈7份和三氧化锑8份)、十二烷基苯磺酸钠2份、甲基三甲氧基硅烷12份、磷酸二氢铝12份、防老剂20份(13份防老剂2246和7份防老剂4020)、光稳定剂7份(二苯甲酮4份和水杨酸甲酯3份)及改性剂(SBS、APP、APAO及聚丙烯粉末)7份。
实施例三
一种耐高温沥青复合防水卷材，该防水卷材包括以下重量份数的原料组成：
基质沥青60份(天然沥青40份和石油沥青20份)、氯化橡胶35份、古马隆树脂12份、季戊四醇硬脂酸酯5份、丙烯酸羟乙酯10份、凹凸棒土25份、功能填料(聚丙烯树脂)20份、补强填料20份(氧化铈10份和三氧化锑10份)、十二烷基苯磺酸钠3份、甲基三甲氧基硅烷15份、磷酸二氢铝20份、防老剂25份(16份防老剂2246和9份防老剂4020)、光稳定剂10份(二苯甲酮5份和水杨酸甲酯5份)及改性剂(SBS、APP、APAO、聚丙烯粉末和HDPE)10份。
对比例
本对比例为市场上一种常见的沥青复合防水卷材。
对实施例1-3和对比例制得的沥青复合防水卷材进行性能测试，测试结果如下表1所示；
耐高温：将实施例1-3和对比例制得沥青复合防水卷材，在温度为80℃的条件下，进行加热2h观察表面现象，进行多次试验，每次试验温度上升10℃。
抗老化：将实施例1-3和对比例制得沥青复合防水卷材在60℃的紫外老化箱进行3天的紫外老化，检测粘度。
表1
由上表1可知实施例1-3制得的沥青复合防水卷材在110℃时仍然不会出现位移、流淌、滴落的现象，而对比例制得的沥青复合防水卷材在100℃时就出现位移、流淌、滴落的现象，实施例1-3制得的沥青复合防水卷材的粘度老化指数在30.6-33.4％，而对比例的粘度老化指数为63.％，表明本发明制备的沥青复合防水卷材具有很好的耐高温和抗老化性。
根据本发明的另一个方面，如图1所示，提供了一种耐高温沥青复合防水卷材的制备方法，该制备方法包括以下步骤：
S1、称取预设重量份数的耐高温沥青复合防水卷材的制备原料；
S2、将称取的基质沥青加入反应釜中进行加热直至基质沥青完全熔融；
S3、将称取的氯化橡胶和古马隆树脂加入粉碎机中进行粉碎处理；
S4、将熔融的基质沥青、粉碎的氯化橡胶和古马隆树脂、季戊四醇硬脂酸酯、丙烯酸羟乙酯及凹凸棒土加入搅拌釜中进行搅拌，直至搅拌均匀；
S5、向搅拌釜中继续加入功能填料、补强填料、十二烷基苯磺酸钠、甲基三甲氧基硅烷、磷酸二氢铝、防老剂、光稳定剂及改性剂，并不断搅拌直至搅拌均匀，得到混合料；
其中，所述加热温度为210～240℃，加热时间为40～60分钟，所述搅拌釜的搅拌速度为150～250rpm，搅拌时间为30分钟，搅拌温度为215-230℃。
S6、利用高速剪切机对混合料剪切得到沥青防水材料，并将沥青防水材料倾倒在玻纤毡上，冷却至室温制得沥青复合防水卷材。
其中，所述S6中利用高速剪切机对混合料剪切得到沥青防水材料具体包括以下步骤：
将混合料加入高速剪切机，在转速为4000～5000r/min，温度为215-230℃的条件下，进行剪切30-40min后，在转速为500～800r/min的条件下，继续搅拌1.5～2h制得沥青防水材料。
综上所述，借助于本发明的上述技术方案，通过天然沥青和石油沥青的配合使用，使得其可以在保证较低成本的同时，有效地提高防水卷材的防水性能及耐高温性能；通过凹凸棒土、氯化橡胶及防老剂的使用，不仅可以有效地提高防水卷材的阻燃性能，而且还可以有效地提高防水卷材的耐磨及防腐性能；通过光稳定剂、补强填料、功能层、古马隆树脂及季戊四醇硬脂酸酯的配合使用，使得本发明的防水卷材具有优异的耐高温和耐紫外线性能；且本发明防水卷材的制备工艺具有工艺简单、原料易得及易于操作的优点。
以上所述仅为本发明的较佳实施例而已，并不用以限制本发明，凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (10)
1.一种耐高温沥青复合防水卷材，其特征在于，该防水卷材包括以下重量份数的原料组成：
基质沥青30～60份、氯化橡胶20～35份、古马隆树脂6～12份、季戊四醇硬脂酸酯3～5份、丙烯酸羟乙酯3～10份、凹凸棒土10～25份、功能填料10～20份、补强填料10～20份、十二烷基苯磺酸钠1～3份、甲基三甲氧基硅烷5～15份、磷酸二氢铝5～20份、防老剂15～25份、光稳定剂5～10份及改性剂5～10份。
2.根据权利要求1所述的一种耐高温沥青复合防水卷材，其特征在于，所述基质沥青由天然沥青和石油沥青按照2：1的重量比混合而成。
3.根据权利要求2所述的一种耐高温沥青复合防水卷材，其特征在于，所述功能填料由聚乙烯、聚酰胺、聚丙烯或聚酯类材料制成，且所述聚乙烯为线性低密度聚乙烯树脂。
4.根据权利要求3所述的一种耐高温沥青复合防水卷材，其特征在于，所述补强填料由氧化铈和三氧化锑按照1：1的重量比混合而成。
5.根据权利要求4所述的一种耐高温沥青复合防水卷材，其特征在于，所述防老剂由防老剂2246和防老剂4020按照3：2的重量比混合而成。
6.根据权利要求5所述的一种耐高温沥青复合防水卷材，其特征在于，所述光稳定剂由二苯甲酮和水杨酸甲酯按照任意比例混合而成。
7.根据权利要求6所述的一种耐高温沥青复合防水卷材，其特征在于，所述改性剂为SBS、APP、APAO、聚丙烯粉末和HDPE中的几种或多种混合而成。
8.一种耐高温沥青复合防水卷材的制备方法，用以实现权利要求7中所述的耐高温沥青复合防水卷材的制备，其特征在于，该制备方法包括以下步骤：
S1、称取预设重量份数的耐高温沥青复合防水卷材的制备原料；
S2、将称取的基质沥青加入反应釜中进行加热直至基质沥青完全熔融；
S3、将称取的氯化橡胶和古马隆树脂加入粉碎机中进行粉碎处理；
S4、将熔融的基质沥青、粉碎的氯化橡胶和古马隆树脂、季戊四醇硬脂酸酯、丙烯酸羟乙酯及凹凸棒土加入搅拌釜中进行搅拌，直至搅拌均匀；
S5、向搅拌釜中继续加入功能填料、补强填料、十二烷基苯磺酸钠、甲基三甲氧基硅烷、磷酸二氢铝、防老剂、光稳定剂及改性剂，并不断搅拌直至搅拌均匀，得到混合料；
S6、利用高速剪切机对混合料剪切得到沥青防水材料，并将沥青防水材料倾倒在玻纤毡上，冷却至室温制得沥青复合防水卷材。
9.根据权利要求8所述的一种耐高温沥青复合防水卷材的制备方法，其特征在于，所述加热温度为210～240℃，加热时间为40～60分钟，所述搅拌釜的搅拌速度为150～250rpm，搅拌时间为30分钟，搅拌温度为215-230℃。
10.根据权利要求8所述的一种耐高温沥青复合防水卷材的制备方法，其特征在于，所述S6中利用高速剪切机对混合料剪切得到沥青防水材料具体包括以下步骤：
将混合料加入高速剪切机，在转速为4000～5000r/min，温度为215-230℃的条件下，进行剪切30-40min后，在转速为500～800r/min的条件下，继续搅拌1.5～2h制得沥青防水材料。