CN113149602A - 一种强度高可塑性强综合性能优异的新型釉面瓷砖 - Google Patents
一种强度高可塑性强综合性能优异的新型釉面瓷砖 Download PDFInfo
- Publication number
- CN113149602A CN113149602A CN202110494030.2A CN202110494030A CN113149602A CN 113149602 A CN113149602 A CN 113149602A CN 202110494030 A CN202110494030 A CN 202110494030A CN 113149602 A CN113149602 A CN 113149602A
- Authority
- CN
- China
- Prior art keywords
- ceramic tile
- emulsion
- plasticity
- comprehensive performance
- glazed ceramic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明公布了一种强度高可塑性强综合性能优异的新型釉面瓷砖，涉及了釉面瓷砖的技术领域，以所述强度高可塑性强综合性能优异的新型釉面瓷砖质量为100％计包括有：粘土50‑60％，长石10‑25％，粉状石英5‑10％，丙烯酸乳液20‑30％，消泡剂1‑3％，润湿剂0.5‑2％，成膜助剂2‑8％，抛光废渣3‑10％，天然彩砂5‑8％，水2‑5％。本发明以粘土、长石和粉状石英为原材料并添加了丙烯酸乳液及天然彩砂制备成新型釉面瓷砖，有效提升了釉面瓷砖的强度及可塑性，改善了瓷砖的综合性能的问题。
Description
技术领域
本发明涉及釉面瓷砖技术领域，更具体的说，涉及一种强度高可塑性强综合性能优异的新型釉面瓷砖。
背景技术
釉面砖是砖的表面经过施釉高温高压烧制处理的瓷砖，这种瓷砖是由土胚和表面的釉面两个部分构成的，主体又分陶土和瓷土两种，陶土烧制出来的背面呈红色，瓷土烧制的背面呈灰白色。釉面砖表面可以做各种图案和花纹，比抛光砖色彩和图案丰富，因为表面是釉料，所以耐磨性不如抛光砖。
目前的釉面瓷砖各类性能都较为良好，且日常使用也无问题。但现有的釉面瓷砖在性能方面还存在强度不高、可塑性不强、综合性能还有提升空间的问题。
发明内容
本发明旨在于解决现有釉面瓷砖在性能方面还存在强度不高、可塑性不强、综合性能还有提升空间问题。
本发明一种强度高可塑性强综合性能优异的新型釉面瓷砖，由以下具体技术手段所达成：
一种强度高可塑性强综合性能优异的新型釉面瓷砖，以所述强度高可塑性强综合性能优异的新型釉面瓷砖质量为100％计包括有：
进一步的优选方案：所述粘土应选用硬质粘土或者半硬质粘土中的一种，或两者混合。
进一步的优选方案：所述丙烯酸乳液选用自交联或外交联共聚物乳液、丙烯酸酯类高分子共聚乳液、具有反应性基团的丙烯酸酯共聚物的高分子乳液、反应性丙烯酸酯多元共聚乳液、反应性自交联型丙烯酸酯乳液、甲基丙烯酸甲酯、丙烯酸丁酯、丙烯酰胺三元共聚乳液、丙烯酸丁酯与丙烯晴共聚物乳液、丙烯酸酯类的共聚物乳液、线性共聚物乳液或含官能基(羟基、羧基和氨基等)共聚物乳液其中的一种或多种。
进一步的优选方案：所述消泡剂选用C7-C9或C12-C22的高碳醇，其后者还应进行适当的乳化处理。
进一步的优选方案：所述丙烯酸乳液还可采用丙烯酸酯类共聚物或均聚物乳胶粉，其与适当量水按比例调制而成固含量为30-50％。
进一步的优选方案：所述优选固含量为35-45％的丙烯酸酯类高分子共聚物乳液，采用市售水性乳液类产品。
进一步的优选方案：所述用陶瓷抛光过程中产生的混合固体废弃物经干燥，粉碎，研磨，筛分之后得到的颗粒。本发明优选颗粒目数在250-800目的抛光废渣。
进一步的优选方案：所述天然彩砂采用天然带有颜色的砂粒，根据制品要求不同选用粒径不同的淡绿、白色等不同颜色的一种或几种彩砂的混合物。本发明优选彩砂的目数为200-300目。
本发明具有以下有益效果：
(1)通过在普通的瓷砖配方中添加的丙烯酸乳液，改良其性能，在其表面参与反应，同时瓷砖本有的粘土增强其整体新型釉面瓷砖烧制的可塑性。
(2)通过在普通的瓷砖配方添加的天然彩砂，经过多次的实验证明，其与普通瓷砖配方材料进行融合配比，加上其间具有的长石的高强度，提高其整体性能和美观程度。
(3)通过在普通的瓷砖配方中添加的粉状石英，能够有效增强其综合性能，使得普通釉面瓷砖更加优异。
附图说明
图1为本发明一种强度高可塑性强综合性能优异的新型釉面瓷砖的材料复合示意图。
具体实施方式
下面将结合本发明实施例中的附图，对本发明实施例中的技术方案进行清除，完整的描述，显然，所面熟的实施例仅仅是本发明一部分实施例，二部是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
如附图1所示：
本发明提供一种强度高可塑性强综合性能优异的新型釉面瓷砖质量为100％计包括有：
其中，所述粘土应选用硬质粘土或者半硬质粘土中的一种，或两者混合。
其中，所述丙烯酸乳液选用自交联或外交联共聚物乳液、丙烯酸酯类高分子共聚乳液、具有反应性基团的丙烯酸酯共聚物的高分子乳液、反应性丙烯酸酯多元共聚乳液、反应性自交联型丙烯酸酯乳液、甲基丙烯酸甲酯、丙烯酸丁酯、丙烯酰胺三元共聚乳液、丙烯酸丁酯与丙烯晴共聚物乳液、丙烯酸酯类的共聚物乳液、线性共聚物乳液或含官能基(羟基、羧基和氨基等)共聚物乳液其中的一种或多种。
其中，所述消泡剂选用C7-C9或C12-C22的高碳醇，其后者还应进行适当的乳化处理。
其中，所述丙烯酸乳液还可采用丙烯酸酯类共聚物或均聚物乳胶粉，其与适当量水按比例调制而成固含量为30-50％。
其中，所述优选固含量为35-45％的丙烯酸酯类高分子共聚物乳液，采用市售水性乳液类产品。
其中，所述用陶瓷抛光过程中产生的混合固体废弃物经干燥，粉碎，研磨，筛分之后得到的颗粒。本发明优选颗粒目数在250-800目的抛光废渣。
其中，所述天然彩砂采用天然带有颜色的砂粒，根据制品要求不同选用粒径不同的淡绿、白色等不同颜色的一种或几种彩砂的混合物。本发明优选彩砂的目数为200-300目。
本发明实施例：
最终光敏树脂材料的制作步骤：
1.首先，进行陶瓷主体的制备。将粘土进行破碎化，长石进行粉碎细化，然后添加SiO298.5％以上的粉状石英；
2.然后，进行添加剂的融合。以同等质量等级来称量，将相应的粘土50份，长石粉末10份，粉状石英5份进行混合，并且进行充分融合，在搅拌过程中依序加入丙烯酸乳液原料20份，消泡剂原料2份，润湿剂1份，成膜助剂原料2份，抛光废渣3份，天然彩砂5份，搅拌过程中逐渐加入水2份，将其完全搅拌进行混合，然后将其得到的泥浆注入水平放置的平板模具中，模具深度为6mm。刮平后，将盛有混合物泥浆的模具放入90℃的烘箱中，烘烤6小时，冷却后脱模即得。
3.最后，得到这种强度高可塑性强综合性能优异的新型釉面瓷砖。
Claims (8)
1.一种强度高可塑性强综合性能优异的新型釉面瓷砖，其特征在于：以所述强度高可塑性强综合性能优异的新型釉面瓷砖质量为100％计包括有：
2.根据权利要求1所述的一种强度高可塑性强综合性能优异的新型釉面瓷砖，其特征在于：所述粘土应选用硬质粘土或者半硬质粘土中的一种，或两者混合。
3.根据权利要求2所述的一种强度高可塑性强综合性能优异的新型釉面瓷砖，其特征在于：所述丙烯酸乳液选用自交联或外交联共聚物乳液、丙烯酸酯类高分子共聚乳液、具有反应性基团的丙烯酸酯共聚物的高分子乳液、反应性丙烯酸酯多元共聚乳液、反应性自交联型丙烯酸酯乳液、甲基丙烯酸甲酯、丙烯酸丁酯、丙烯酰胺三元共聚乳液、丙烯酸丁酯与丙烯晴共聚物乳液、丙烯酸酯类的共聚物乳液、线性共聚物乳液或含官能基(羟基、羧基和氨基等)共聚物乳液其中的一种或多种。
4.根据权利要求1所述的一种强度高可塑性强综合性能优异的新型釉面瓷砖，其特征在于：所述消泡剂选用C7-C9或C12-C22的高碳醇，其后者还应进行适当的乳化处理。
5.根据权利要求1所述的一种强度高可塑性强综合性能优异的新型釉面瓷砖，其特征在于：所述丙烯酸乳液还可采用丙烯酸酯类共聚物或均聚物乳胶粉，其与适当量水按比例调制而成固含量为30-50％。
6.根据权利要求1所述的一种强度高可塑性强综合性能优异的新型釉面瓷砖，其特征在于：所述优选固含量为35-45％的丙烯酸酯类高分子共聚物乳液，采用市售水性乳液类产品。
7.根据权利要求1所述的一种强度高可塑性强综合性能优异的新型釉面瓷砖，其特征在于：所述用陶瓷抛光过程中产生的混合固体废弃物经干燥，粉碎，研磨，筛分之后得到的颗粒。本发明优选颗粒目数在250-800目的抛光废渣。
8.根据权利要求1所述的一种强度高可塑性强综合性能优异的新型釉面瓷砖，其特征在于：所述天然彩砂采用天然带有颜色的砂粒，根据制品要求不同选用粒径不同的淡绿、白色等不同颜色的一种或几种彩砂的混合物。本发明优选彩砂的目数为200-300目。