CN112979274A - 紫砂制品及其制备方法 - Google Patents
紫砂制品及其制备方法 Download PDFInfo
- Publication number
- CN112979274A CN112979274A CN202110424688.6A CN202110424688A CN112979274A CN 112979274 A CN112979274 A CN 112979274A CN 202110424688 A CN202110424688 A CN 202110424688A CN 112979274 A CN112979274 A CN 112979274A
- Authority
- CN
- China
- Prior art keywords
- purple sand
- mud
- sand product
- jade
- tourmaline
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明属于紫砂制品领域，具体涉及一种紫砂制品及其制备方法。本发明的紫砂制品,由以下配比的原料制成:玉石0.1～0.2％、稀晶石0.1～0.5％、电气石5～8％，余量为紫砂泥。本发明的紫砂制品的制备方法为将玉石、稀晶石和电气石分解成若干小块，然后分别投入球磨机，然后用100目的过滤网进行过滤，把过滤下来的三种浆料与紫砂泥进行真空练泥，得到泥料；最后用所得到的泥料进行高温烧制，得到紫砂制品。使用本发明的紫砂制品泡茶、冲饮咖啡等口感滑爽滋润、生津回味，利于人体吸收营养物质。使用后可使人体经络通畅、清肝明目健脑、利尿排便、抗疲劳、增强免疫力、消除自由基。
Description
技术领域
本发明属于紫砂制品领域，具体涉及一种紫砂制品及其制备方法。
背景技术
紫砂壶是中国特有的陶土工艺品，紫砂壶是用于泡茶煮茶的。紫砂壶以宜兴紫砂壶最为出名，宜兴紫砂壶泡茶既不夺茶真香，又无熟汤气，能较长时间保持茶叶的色、香、味。紫砂茶具还因其造型古朴别致、气质特佳，经茶水泡、手摩挲，会变为古玉色而倍受人们青睐。从显微观察发现，紫泥主要矿物为石英、粘土、云母和赤铁矿。合理的化学、矿物、颗粒组成，使紫泥俱备了可塑性好、生坯强度高、干燥收缩小等良好的工艺性能。紫泥粉碎的细度，以过60目筛为宜。
紫砂陶所用的原料，包括紫泥、绿泥及红泥三种，统称紫砂泥。紫泥是甲泥矿层的一个夹层，矿体呈薄层状、透镜状，矿层厚度一般在几十公分到一公尺左右，稳定性差，原料外观颜色呈紫色、紫红色，并带有浅绿色斑点，烧后外观颜色则呈紫色、紫棕色、紫黑色。紫泥主要成份为水云母，并含有不等量的高岭土、石英、云母屑及铁质等。综合分析，紫砂泥属于粒土--石英云母系，颇类制瓷原料的特点，因此单种原料即具有理想的可塑性，泥坯强度高，干燥收缩率小，为多种造型提供了良好的工艺条件。绿泥是紫砂泥中的夹脂，故有“泥中泥”之称。绿泥产量不多，泥质较嫩，耐火力也比紫泥为低，一般多用作胎身外面的粉料或涂料，使紫砂陶器皿的颜色更为多彩。
红泥，或称朱泥，则是位于嫩泥和矿层底部的泥料，矿形琐碎，需经手工挑选。周高起云：“石黄泥，出赵庄山，即未触风日之石骨也，陶乃变朱砂色。”因其含铁量多寡不等，烧成之后变朱砂色、朱砂紫或海棠红等色。因为产量少，早期除销往南洋的水平小壶用朱泥制作胎身外，一般只用作化妆土装饰在紫砂泥坯上。至于朱泥的胎土，不过是制壶陶手，为了求得更精细的泥料，将红泥以洗泥沉淀，得到约140目到180目细孔的泥料，制成细如滑脂的朱泥壶。朱泥的土质成份，最大的特色是含有极高的氧化铁，约在14％到18％之间，这是朱泥所以烧成后壶身成为红色的主要原因。由于朱泥的泥性甚娇，成型工艺难度亦高，而朱泥由生坯至烧成，因收缩率高达30％至40％，故一般成品良率约仅七成
对于紫砂壶的性能“色香味皆蕴”过去早有定论。而且，科学机构也对砂壶的“暑月越宿不馊”一事，较砂壶与陶瓷做了详细测试，的确证实了砂壶较陶瓷优越了许多，这一结论是基于紫砂原料的独特性。紫砂壶实用性强，乃在于它具有比较高的气孔率，使其具有透气性好的优点。
虽然紫砂壶具有诸多优点，但是随着人们对生活品质的追求，单纯的紫砂壶已不能满足人们的需要。
发明内容
本发明的目的在于提供一种紫砂制品。
本发明的再一目的在于提供上述紫砂制品的制备方法。
根据本发明具体实施方式的一种紫砂制品,其由以下配比的原料制成:玉石0.1～0.2％、稀晶石0.1～0.5％、电气石5～8％，余量为紫砂泥。
本发明中所用的紫砂泥包括各种紫砂泥料，如紫泥、绿泥、红泥等。
玉石(Nephrite)是一种矿物质，玉石包括软、硬两种，本发明所用玉石为软玉。软玉包括和田玉、岫岩玉，南阳玉，酒泉玉等十多种软玉。
电气石(tourmaline)，又名碧玺，是电气石族矿物的总称，化学成分较复杂，是以含硼为特征的铝、钠、铁、镁、锂的环状结构硅酸盐矿物。电气石分为镁铁锂电气石、钙镁电气石、钠锰电气石、布格电气石四个矿物种。
稀晶石，是一种由多种稀有矿石复合而成的人造晶石。其原材料主要包括生物炭基硅化物质、火山岩矿物质、和田玉、能量稀土等。稀晶石释放负氧离子的能力源于其复杂而独特的矿物原材料组合，除了部分能自然而然的释放出负氧离子的物质(如：火山岩矿物质)，还有一些是通过不同元素之间的化学反应，不同分子之间的排列组合而产生的。
根据本发明具体实施方式的一种紫砂制品,所述玉石、稀晶石、电气石的粒径小于100目。
根据本发明具体实施方式的一种紫砂制品,所述紫砂制品由以下重量比的原料制成:玉石0.1％、稀晶石0.1％、电气石5％，余量为紫砂泥。
根据本发明具体实施方式的一种紫砂制品,所述紫砂制品由以下重量比的原料制成:玉石0.2％、稀晶石0.5％、电气石8％，余量为紫砂泥。
根据本发明具体实施方式的一种紫砂制品,所述紫砂制品由以下重量比的原料制成:玉石0.1％、稀晶石0.2％、电气石7％，余量为紫砂泥。
根据本发明具体实施方式的紫砂制品的制备方法,包括以下步骤：
(1)分别将玉石、稀晶石和电气石进行球磨，用100目的过滤网进行过滤，取筛下的原料，得到石粉；
(2)将石粉与紫砂泥混合，进行真空炼泥，得到泥料；
(3)将泥料进行高温烧制，得到紫砂制品。
不同的紫砂泥料所需要的烧制温度不同，其中，紫泥的烧制温度为1200℃左右，红泥烧制的温度为1160℃左右，本山绿泥的烧制温度为1170℃左右。
本发明的紫砂制品的制备方法为将玉石、稀晶石和电气石分解成若干小块，然后分别投入球磨机，球磨48h，在球磨过程中加入适量清水。然后用100目的过滤网进行过滤，把过滤下来的三种浆料，按比例放在一起充分搅拌。在将搅拌后的材料按比例与紫砂泥进行练泥，得到泥料。最后用所得到的泥料进行高温烧制，得到紫砂制品。
其中炼泥的方法可以采用传统的手动炼泥、或真空炼泥机进行炼泥，即用手动或机械方式得到器坯，并阴干备用。其中，真空炼泥机可选用的种类较多，以HK-SC为优选。
高温烧制过程即可以选择传统的龙窑，也可以采用现代的电窑。
根据本发明具体实施方式的紫砂制品的制备方法,步骤(1)中，玉石、稀晶石和电气石进行球磨的时间为48小时。
根据本发明具体实施方式的紫砂制品的制备方法,步骤(1)中，对玉石、稀晶石和电气石进行球磨过程中加入少量水。
根据本发明具体实施方式的紫砂制品的制备方法,步骤(3)中，高温烧制包括以下步骤：
(3-1)将窑在95～105℃条件下预热1～2h；
(3-2)将窑温度升高至1030～1050℃后，保持5～6h；
(3-3)窑温自然冷却，24小时后取出，得到紫砂制品。
本发明的有益效果：
1.本发明紫砂制品发射负氧离子浓度可达2000左右，用本发明的紫砂制品浸泡的水，pH检测范围为7.3～7.4，符合碱性水标准，并且饮用水由酸性变成碱性的时间小于1min，满足人们的饮用要求。
2.本发明的紫砂制品能在水中溶解多种微量元素、钙、买、锌、硒等，达到补充人体所需、平衡人体微环境的作用；本发明的紫砂制品能够释放负氧离子，长期使用可以提高人体免疫力、调节血糖、调节血脂。
具体实施方式
为使本发明的目的、技术方案和优点更加清楚，下面将对本发明的技术方案进行详细的描述。显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动的前提下所得到的所有其它实施方式，都属于本发明所保护的范围。
实施例1
本发明的紫砂制品包括原料：玉石0.1％、稀晶石0.1％、电气石5％，余量为红泥。
本发明的紫砂制品的制备方法包括以下步骤：
(1)分别将玉石、稀晶石和电气石进行球磨，用100目的过滤网进行过滤，取筛下的原料，得到石粉；
(2)将石粉与红泥混合，放入真空炼泥机(真空度<-735pa,电机功率1.5～2.2kw,出泥速度30kg/h)中，共同搅拌，通过三次往返均匀搅拌，得到泥料；
(3)将泥料进行高温烧制：
(3-1)将窑在95℃条件下预热1h；
(3-2)将窑温度升高至1030℃后，保持5h；
(3-3)窑温自然冷却，24小时后取出，得到紫砂制品。
实施例2
本发明的紫砂制品包括原料：玉石0.2％、稀晶石0.5％、电气石8％，余量为绿泥。
本发明的紫砂制品的制备方法包括以下步骤：
(1)分别将玉石、稀晶石和电气石进行球磨，用100目的过滤网进行过滤，取筛下的原料，得到石粉；
(2)将石粉与绿泥混合，放入真空炼泥机(真空度<-735pa,电机功率1.5～2.2kw,出泥速度30kg/h)，共同搅拌，通过三次往返均匀搅拌，得到泥料；
(3)将泥料进行高温烧制：
(3-1)将窑在105℃条件下预热2h；
(3-2)将窑温度升高至1040℃后，保持6h；
(3-3)窑温自然冷却，24小时后取出，得到紫砂制品。
实施例3
本发明的紫砂制品包括原料：玉石0.1％、稀晶石0.2％、电气石7％，余量为紫砂泥。
本发明的紫砂制品的制备方法包括以下步骤：
(1)分别将玉石、稀晶石和电气石进行球磨，用100目的过滤网进行过滤，取筛下的原料，得到石粉；
(2)将石粉与紫砂泥混合，放入真空炼泥机(真空度<-735pa,电机功率1.5～2.2kw,出泥速度30kg/h)，共同搅拌，通过三次往返均匀搅拌，得到泥料；
(3)将泥料进行高温烧制：
(3-1)将窑在100℃条件下预热2h；
(3-2)将窑温度升高至1050℃后，保持6h；
(3-3)窑温自然冷却，24小时后取出，得到紫砂制品。
使用本发明的紫砂制品泡茶、冲饮咖啡等口感滑爽滋润、生津回味，利于人体吸收营养物质。使用后可使人体经络通畅、清肝明目健脑、利尿排便、抗疲劳、增强免疫力、消除自由基。小孩、老人使用本发明的紫砂制品后伤风感冒减少、体力增强。本发明的紫砂制品尤其适合高血压、通风患者长期使用。
使用注意事项：长时间使用后，本发明的紫砂制品表面产生水垢，用刷子清洗干净即可。注意水壶中的水不要烧干，防止高温中使紫砂制品破裂。
实施例4
将清水倒入本发明实施例1～3所得的紫砂制品中，1min内，用负氧离子检测仪(MODEL COM-3010PRO)和pH仪分别进行测定，测定结果如下：
表1负氧离子和pH检测情况
| 实施例1 | 实施例2 | 实施例3 | 清水 | |
| 负氧离子 | 1989 | 2016 | 1889 | 56 |
| pH值 | 7.3 | 7.4 | 7.3 | 6.2 |
由表1可知，本发明紫砂制品发射负氧离子浓度为1889～2016，用本发明的紫砂制品浸泡的水，pH检测范围为7.3～7.4，符合碱性水标准，并且饮用水由酸性变成碱性的时间小于1min。
本发明的紫砂制品的负氧离子的释放效果与改善水样pH的效果，与烧制过程密切相关。本发明进行相关实验：
实验组：实施例3的制备方法所得的紫砂制品；
对比组1：未将窑在100℃条件下预热，直接进行升温烧制，其他步骤同实施例3；
对比组2：步骤(3-2)中，将窑温度升高至1150℃，其他步骤同实施例3；
对比组3：步骤(3-3)中，窑温自然冷却，18小时后取出，其他步骤同实施例3；
对比例4：传统紫砂烧制方法：将窑温度升至1150℃，保温8h，并于18小时后，出炉。
用负氧离子检测仪(MODEL COM-3010PRO)和pH仪对产品的性能进行检测，结果如下：
表2各紫砂制品的性能比较
如表2所述，当紫砂泥中加入玉石、电气石、稀晶石后，按照传统的烧制方法，紫砂制品坍塌严重，无法成型，对比组2中，当烧制温度达到1150℃时，同样造成产品形变。对比组1、3虽然可以烧制成紫砂成品，与实验组相比，负氧离子发射能力较弱，将饮用水由酸性变成弱碱性的能力减弱，尤其是，将水由酸性变成弱碱性的时间大大延长，超过了3min，而过长的等待时间将影响人们使用紫砂壶的体验。因此，按照本发明的烧制方法得到的紫砂制品不但能够发生高浓度的负氧离子，而且能够在短时间内将饮用水由弱酸性变成弱碱性，满足人们的饮用需求。
以上所述，仅为本发明的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本技术领域的技术人员在本发明揭露的技术范围内，可轻易想到变化或替换，都应涵盖在本发明的保护范围之内。因此，本发明的保护范围应以所述权利要求的保护范围为准。
Claims (9)
1.一种紫砂制品,其特征在于,所述紫砂制品由以下重量比的原料制成:玉石0.1～0.2％、稀晶石0.1～0.5％、电气石5～8％，余量为紫砂泥。
2.根据权利要求1所述的紫砂制品,其特征在于,所述玉石、稀晶石、电气石的粒径小于100目。
3.根据权利要求1所述的紫砂制品,其特征在于,所述紫砂制品由以下重量比的原料制成:玉石0.1％、稀晶石0.1％、电气石5％，余量为紫砂泥。
4.根据权利要求1所述的紫砂制品,其特征在于,所述紫砂制品由以下重量比的原料制成:玉石0.2％、稀晶石0.5％、电气石8％，余量为紫砂泥。
5.根据权利要求1所述的紫砂制品,其特征在于,所述紫砂制品由以下重量比的原料制成:玉石0.1％、稀晶石0.2％、电气石7％，余量为紫砂泥。
6.权利要求1～5任一项所述的紫砂制品的制备方法,其特征在于,所述制备方法包括以下步骤：
(1)分别将玉石、稀晶石和电气石进行球磨，用100目的过滤网进行过滤，取筛下的原料，得到石粉；
(2)将石粉与紫砂泥混合，进行炼泥，得到泥料；
(3)将泥料进行高温烧制，得到紫砂制品。
7.权利要求6所述的紫砂制品的制备方法,其特征在于，步骤(1)中，玉石、稀晶石和电气石进行球磨的时间为48小时。
8.权利要求6所述的紫砂制品的制备方法,其特征在于，步骤(1)中，对玉石、稀晶石和电气石进行球磨过程中加入少量水。
9.权利要求6所述的紫砂制品的制备方法,其特征在于，步骤(3)中，高温烧制包括以下步骤：
(3-1)将窑在95～105℃条件下预热1～2h；
(3-2)将窑温度升高至1030～1050℃后，保持5～6h；
(3-3)窑温自然冷却，24小时后取出，得到紫砂制品。