CN112842965A - 一种高效补水的再生纤维素面膜及其制备方法 - Google Patents
一种高效补水的再生纤维素面膜及其制备方法 Download PDFInfo
- Publication number
- CN112842965A CN112842965A CN202110243380.1A CN202110243380A CN112842965A CN 112842965 A CN112842965 A CN 112842965A CN 202110243380 A CN202110243380 A CN 202110243380A CN 112842965 A CN112842965 A CN 112842965A
- Authority
- CN
- China
- Prior art keywords
- cellulose
- mask
- solution
- facial mask
- mulberry bark
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及护肤品中面膜的制作技术领域，特别是桑树皮浆纤维素再生面膜及其制备方法。本发明的制备方法包括：桑树皮通过机械和化学相结合的方法且利用PFI磨浆机制备成桑树皮浆；将桑树皮浆溶解到硫脲溶液中再倒入模具中制成规定形状的面膜基材；制备含玻尿酸的补水精华；将面膜和精华一起装入包装袋中，进行封口、灭菌、包装。本发明制得的面膜天然成分高、易吸收。玻尿酸可保持皮肤滋润光滑、细腻柔嫩、富有弹性，具有防皱、抗皱、美容保健和恢复皮肤生理功能的作用。
Description
技术领域
本发明涉及护肤品中面膜的制作技术领域，具体是桑树皮浆纤维素再生面膜及其制备方法。
背景技术
面膜是护肤品的一个类别，用于皮肤补水，也具有保湿、滋润、营养、改善外观、深层清洁等多种功能。它在水分挥发的干燥过程中，使皮肤产生适度的收缩，且封闭效果使皮肤温度暂时性上升，促进血液循环。面膜的功能和面膜的安全环保性一直是面膜市场发展的趋势，利用成本低且安全无害的材料制备面膜是面膜发展的一个重要方面。随着生活水平的提高，人们越来越注重肌肤的保养，同时也越来越注意产品的安全环保性。目前市场上有的面膜制备周期长，有的面膜价格偏贵，有的面膜使用感就差，所以经济实惠，使用感良好且安全环保的面膜是人们的首选。
目前市场上的主流面膜还是以纸质面膜为主，但这类面膜延展性不好，持水性能差，而市面上生物纤维素面膜也只有少数几款，并且大部分为进口，价格昂贵，市场均价元盒，一盒三片，生物纤维素面膜昂贵的价格使其消费群体极其有限。本发明的纤维素再生面膜在满足面膜的基本的特性的前提下，既能弥补纸质面膜的缺点又能使其价格方面偏低且工艺方法简单。
发明内容
本发明的目的是提供一种再生纤维素面膜，在低成本的条件下享受高效补水的舒适感。因此，本发明提供了一种高效补水的纤维素再生面膜及其制备方法。一种高效补水的纤维素再生面膜，所述纤维素再生面膜包括纤维素再生面膜基材和面膜基液。所述面膜基材的原料为100％桑树皮浆再生纤维素。所述面膜基液各组分原料包括：玻尿酸1％原液：维他命原B5：蒸馏水：甘草酸浓缩粉：复方抗菌剂比例为10(ml)：2.5(ml)：37(ml)：0.25(g)：0.3(ml)。
本发明所采用的技术方案包括如下步骤：
(1)先将面膜模具置入75％酒精中浸泡30min，然后进行紫外灭菌30min。
(2)将均匀的桑树皮浆纤维素溶液倒入灭菌后的面膜模具中，用玻璃棒推开，直至均匀填满模具，并留出五官，成形。
步骤(2)中所述的桑树皮浆纤维素溶液的制作方法为：桑树皮浆首先分散为直径1-3cm小颗粒，按4-6％质量比加入预冻好的硫脲溶液中；再经高强超声波粉碎处理，放入-20℃冰柜静置3-4h；最后取出经次高强超声波分散处理，放入-20℃冰柜静置2-3h，得到纤维素溶液，再向纤维素溶液中加入不溶的ZnO，存放在5℃条件下备用。
进一步的，所述的桑树皮浆的制作步骤为：桑树皮浆经化学机械法制备，桑树皮去掉表层黑皮，再经8-10％氢氧化钠和2-3％在85-95℃预处理1小时，控制质量百分比10-15％，再经PFI磨浆。
进一步的，所述的PFI磨浆为PFI磨浆机进行打浆时采用10000转时，游离度356±35，打浆时一次30克绝干浆料，浓度10％。
进一步的，所述的硫脲溶液体系制备，硫脲溶液按6：7：9：9：90比例称取NaOH、硫脲、尿素和去离子水配制碱尿溶液，将溶液放入冰箱中预冻2-3h，桑树皮浆纤维素的溶解质量百分比为7％-9％。
进一步的，所述的高强超声波粉碎处理功率为900W，频率为20KHz，总处理时间为15-20min，每隔1s工作5s。
进一步的，所述的次高强超声波分散处理功率为600W，频率为20KHz，处理时间为10-15min，每隔1s工作5s。
(3)将装有溶液的模具一起放入WHCI＝6％的水溶液中凝固成膜，再将模具放入WNaOH＝6％的水溶液中浸泡30min。
(4)浸泡后取出放入乙醇凝固浴中凝固成膜30min，再用去离子水浸泡30min，再用甘油浸泡1-4h。最后从模具中取出面膜用超纯水反复洗涤或浸泡直至中性，得到白色透明纤维素再生面膜基材。
(5)将面膜放入冰箱中，冷冻24h，后进行真空干燥24h，得纤维素再生干面膜。
(6)面膜浸泡包装：将纤维素再生干面膜放入精华液中充分浸泡15min后面膜和精华液一起进行包装。
步骤(6)中所述的精华液的制备步骤是：
i将玻尿酸溶液、蒸馏水和维他命原B5加入烧杯中，搅拌均匀；
ii再将甘草酸浓缩粉加入烧杯中溶解后搅拌均匀；
iii再加入复方抗菌剂，混合均匀，即得玻尿酸抗敏修复精华液。
与现有技术相比，本发明具有以下优点及有益效果：
本发明是以环境友好型、可生物降解的桑树皮浆为原料，具有优异的生物降解性与相容性，采用清洁高效的溶解再生方法制备纤维素再生膜，具有亲水性高、渗透性好、柔湿度敏感、耐折性好、韧性高等特性。本发明中纤维素的溶解和再生是物理过程，未发生复杂化学反应，遵循可持续发展战略，符合当今社会可持续发展的要求。
本发明在制浆时采用PFI磨浆，将桑树皮浆纤维分解成单根纤维，并且在桑树皮浆纤维溶解过程中借助超声波处理破坏其结晶结构，都提高了桑树皮浆在硫脲溶液中的溶解效率。纤维素溶液成膜前加入ZnO，后续除掉，虽增大了膜的孔径，但仍小于皮肤的毛孔，促进了面膜基布的吸水。本发明制得的玻尿酸精华无添加且纯度高，具有防皱、抗皱、美容保健和恢复皮肤生理功能的作用。
因此，本发明所提供的一种高效补水的纤维素再生面膜及其制备方法，制备方法简单可行、条件温和，解决了目前反应条件苛刻、制备方法复杂等问题，还有效提高了润湿状态下的强度。
具体实施方式
以下将结合具体实施例对本发明做进一步的说明。
实施例一
一种高效补水的再生纤维素面膜的制备方法，包括以下步骤：
(1)先将面膜模具置入75％酒精中浸泡30min，然后进行紫外灭菌30min。
(2)将均匀的桑树皮浆纤维素溶液倒入灭菌后的面膜模具中，用玻璃棒推开，直至均匀填满模具，并留出五官，成形。
(3)将装有溶液的模具一起放入WHCI＝6％的水溶液中凝固成膜，再将模具放入WNaOH＝6％的水溶液中浸泡30min。
(4)浸泡后取出放入乙醇凝固浴中凝固成膜30min，再用去离子水浸泡30min，再用甘油浸泡2h。最后从模具中取出面膜用超纯水反复洗涤或浸泡直至中性，得到白色透明纤维素再生面膜基材。
(5)将面膜放入冰箱中，冷冻24h，后进行真空干燥24h，得纤维素再生干面膜。
(6)精华液的制备：将玻尿酸溶液、蒸馏水和维他命原B5加入烧杯中，搅拌均匀；再将甘草酸浓缩粉加入烧杯中溶解后搅拌均匀；再加入复方抗菌剂，混合均匀，即得玻尿酸抗敏修复精华液。
(7)面膜浸泡包装：将纤维素再生干面膜放入精华液中充分浸泡15min后面膜和精华液一起进行包装。
上述步骤(2)中所述的桑树皮纤维素溶液的制作步骤为：桑树皮浆首先分散为直径1-3cm小颗粒，按4％质量比加入预冻好的硫脲溶液中；再经高强超声波粉碎处理，放入-20℃冰柜静置3h；最后取出经次高强超声波分散处理，放入-20℃冰柜静置2h，得到纤维素溶液，再向纤维素溶液中加入不溶的ZnO，存放在5℃条件下备用。
所述的桑树皮浆的制作步骤为：桑树皮浆经化学机械法制备，桑树皮去掉表层黑皮，再经8％氢氧化钠和2％H2O2在90℃预处理1小时，控制质量百分比10-15％，再经PFI磨浆机磨浆。
所述PFI磨浆机进行打浆时采用10000转时，游离度356±35，打浆时一次30克绝干浆料，浓度10％。
硫脲溶液体系制备，硫脲溶液按6：7：9：9：90比例称取NaOH、硫脲、尿素和去离子水配制碱尿溶液，将溶液放入冰箱中预冻2h，桑树皮浆纤维素的溶解质量百分比为7％。
所述高强超声波粉碎处理功率为900W，频率为20KHz，总处理时间为15min，每隔1s工作5s。
所述次高强超声波分散处理功率为600W，频率为20KHz，处理时间为10min，每隔1s工作5s。
实施例二
一种高效补水的再生纤维素面膜的制备方法，包括以下步骤：
(1)先将面膜模具置入75％酒精中浸泡30min，然后进行紫外灭菌30min。
(2)将均匀的桑树皮浆纤维素溶液倒入灭菌后的面膜模具中，用玻璃棒推开，直至均匀填满模具，并留出五官，成形。
(3)将装有溶液的模具一起放入WHCI＝6％的水溶液中凝固成膜，再将模具放入WNaOH＝6％的水溶液中浸泡30min。
(4)浸泡后取出放入乙醇凝固浴中凝固成膜30min，再用去离子水浸泡30min，再用甘油浸泡3h。最后从模具中取出面膜用超纯水反复洗涤或浸泡直至中性，得到白色透明纤维素再生面膜基材。
(5)将面膜放入冰箱中，冷冻24h，后进行真空干燥24h，得纤维素再生干面膜。
(6)精华液的制备：将玻尿酸溶液、蒸馏水和维他命原B5加入烧杯中，搅拌均匀；再将甘草酸浓缩粉加入烧杯中溶解后搅拌均匀；再加入复方抗菌剂，混合均匀，即得玻尿酸抗敏修复精华液。
(7)面膜浸泡包装：将纤维素再生干面膜放入精华液中充分浸泡15min后面膜和精华液一起进行包装。
上述步骤(2)中所述的桑树皮纤维素溶液的制作步骤为：桑树皮浆首先分散为直径1-3cm小颗粒，按5％质量比加入预冻好的硫脲溶液中；再经高强超声波粉碎处理，放入-20℃冰柜静置3.5h；最后取出经次高强超声波分散处理，放入-20℃冰柜静置3h，得到纤维素溶液，再向纤维素溶液中加入不溶的ZnO，存放在5℃条件下备用。
所述的桑树皮浆的制作步骤为：桑树皮浆经化学机械法制备，桑树皮去掉表层黑皮，再经9％氢氧化钠和2％H2O2在92℃预处理1小时，控制质量百分比10-15％，再经PFI磨浆机磨浆。
所述PFI磨浆机进行打浆时采用10000转时，游离度356±35，打浆时一次30克绝干浆料，浓度10％。
所述的硫脲溶液体系制备，硫脲溶液按6：7：9：9：90比例称取NaOH、硫脲、尿素和去离子水配制碱尿溶液，将溶液放入冰箱中预冻2.5h，桑树皮浆纤维素的溶解质量百分比为8％。
所述高强超声波粉碎处理功率为900W，频率为20KHz，总处理时间为17min，每隔1s工作5s。
所述次高强超声波分散处理功率为600W，频率为20KHz，处理时间为12min，每隔1s工作5s。
实施例三
一种高效补水的再生纤维素面膜的制备方法，包括以下步骤：
(1)先将面膜模具置入75％酒精中浸泡30min，然后进行紫外灭菌30min。
(2)将均匀的桑树皮浆纤维素溶液倒入灭菌后的面膜模具中，用玻璃棒推开，直至均匀填满模具，并留出五官，成形。
(3)将装有溶液的模具一起放入WHCI＝6％的水溶液中凝固成膜，再将模具放入WNaOH＝6％的水溶液中浸泡30min。
(4)浸泡后取出放入乙醇凝固浴中凝固成膜30min，再用去离子水浸泡30min，再用甘油浸泡4h。最后从模具中取出面膜用超纯水反复洗涤或浸泡直至中性，得到白色透明纤维素再生面膜基材。
(5)将面膜放入冰箱中，冷冻24h，后进行真空干燥24h，得纤维素再生干面膜。
(6)精华液的制备：将玻尿酸溶液、蒸馏水和维他命原B5加入烧杯中，搅拌均匀；再将甘草酸浓缩粉加入烧杯中溶解后搅拌均匀；再加入复方抗菌剂，混合均匀，即得玻尿酸抗敏修复精华液。
(7)面膜浸泡包装：将纤维素再生干面膜放入精华液中充分浸泡15min后面膜和精华液一起进行包装。
上述步骤(2)中所述的桑树皮纤维素溶液的制作步骤为：桑树皮浆首先分散为直径1-3cm小颗粒，按6％质量比加入预冻好的硫脲溶液中；再经高强超声波粉碎处理，放入-20℃冰柜静置4h；最后取出经次高强超声波分散处理，放入-20℃冰柜静置3h，得到纤维素溶液，再向纤维素溶液中加入不溶的ZnO，存放在5℃条件下备用。
所述的桑树皮浆的制作步骤为：桑树皮浆经化学机械法制备，桑树皮去掉表层黑皮，再经10％氢氧化钠和3％H2O2在95℃预处理1小时，控制质量百分比10-15％，再经PFI磨浆机磨浆。
所述PFI磨浆机进行打浆时采用10000转时，游离度356±35，打浆时一次30克绝干浆料，浓度10％。
所述的硫脲溶液体系制备，硫脲溶液按6：7：9：9：90比例称取NaOH、硫脲、尿素和去离子水配制碱尿溶液，将溶液放入冰箱中预冻3h，桑树皮浆纤维素的溶解质量百分比为9％。
所述高强超声波粉碎处理功率为900W，频率为20KHz，总处理时间为20min，每隔1s工作5s。
所述次高强超声波分散处理功率为600W，频率为20KHz，处理时间为15min，每隔1s工作5s。
从表1可以看出，实施例1～3所得再生纤维素膜基布的克重在40g/m2左右，厚度为0.49～0.51mm。该面膜基布在干态下的断裂强力在40.5N以上，断裂伸长率在32％以上；在湿态下的断裂强力在31.0N以上，断裂伸长率在31％以上，干湿状态下的机械力学性能良好，具备相当的抗拉强度和伸长率。该面膜基布的持液率在1360％以上，持液能力强；透气率不低于2751mm/s，透气性好，使用时舒适性强。
表1实施例1～3所得再生纤维素面膜基布的性能检测结果
Claims (10)
1.一种高效补水的纤维素再生面膜，其特征在于：所述纤维素再生面膜包括纤维素再生面膜基材和面膜基液，所述面膜基材的原料为100％桑树皮浆再生纤维素，所述面膜基液各组分原料包括：玻尿酸1％原液：维他命原B5：蒸馏水：甘草酸浓缩粉：复方抗菌剂比例为10(ml)：2.5(ml)：37(ml)：0.25(g)：0.3(ml)。
2.权利要求1所述的一种纤维素再生面膜的制备方法，其步骤是：
(1)先将面膜模具置入75％酒精中浸泡30min，然后进行紫外灭菌30min；
(2)将均匀的桑树皮浆纤维素溶液倒入灭菌后的面膜模具中，用玻璃棒推开，直至均匀填满模具，并留出五官，成形；
(3)将装有溶液的模具一起放入WHCI＝6％的水溶液中凝固成膜，再将模具放入WNaOH＝6％的水溶液中浸泡30min；
(4)浸泡后取出放入乙醇凝固浴中凝固成膜30min，再用去离子水浸泡30min，再用甘油浸泡1-4h，最后从模具中取出面膜用超纯水反复洗涤或浸泡直至中性，得到白色透明纤维素再生面膜基材；
(5)将面膜放入冰箱中，冷冻24h，后进行真空干燥24h，得纤维素再生干面膜；
(6)面膜浸泡包装：将纤维素再生干面膜放入精华液中充分浸泡15min后面膜和精华液一起进行包装。
3.如权利要求2所述的一种纤维素再生面膜的制备方法，其特征在于：步骤(2)所述的桑树皮浆纤维素溶液经超声硫脲溶液体系制备，硫脲溶液按6：7：9：9：90质量比称取NaOH、硫脲、尿素和去离子水配制碱尿溶液，将溶液放入冰箱中预冻2-3h，桑树皮浆纤维素的溶解质量百分比为7-9％。
4.如权利要求3所述的一种纤维素再生面膜的制备方法，其特征在于：所述桑树皮浆纤维素溶液的超声硫脲溶液体系制备方法为将桑树皮浆首先分散为直径1-3cm小颗粒，按4-6％质量比加入预冻好的硫脲溶液中；再经高强超声波粉碎处理，放入-20℃冰柜静置3-4h；最后取出经次高强超声波分散处理，放入-20℃冰柜静置2-3h，得到纤维素溶液，再向纤维素溶液中加入不溶的ZnO，搅拌均匀，存放在5℃条件下备用。
5.如权利要求4所述的一种纤维素再生面膜的制备方法，其特征在于：桑树皮浆经化学机械法制备，桑树皮去掉表层黑皮，再经8-10％氢氧化钠和2-3％H2O2在85-95℃预处理1小时，控制质量百分比10-15％，再经PFI磨浆机磨浆。
6.如权利要求4所述的一种纤维素再生面膜的制备方法，其特征在于：所述高强超声波粉碎处理功率为900W，频率为20KHz，总处理时间为15-20min，每隔1s工作5s。
7.如权利要求4所述的一种纤维素再生面膜的制备方法，其特征在于：所述次高强超声波分散处理功率为600W，频率为20KHz，处理时间为10-15min，每隔1s工作5s。
8.如权利要求4所述的一种纤维素再生面膜的制备方法，其特征在于：所使用的ZnO的粒径大小为0.1-5μm，白色固体，无嗅无味，无砂性。
9.如权利要求5所述的一种纤维素再生面膜的制备方法，其特征在于：PFI磨浆机进行打浆时采用10000转时，游离度控制356±35，打浆时一次30克绝干浆料，浓度10％。
10.如权利要求2所述的一种纤维素再生面膜的制备方法，其特征在于：步骤(6)所述精华液的制备方法，其步骤是：将玻尿酸溶液、蒸馏水和维他命原B5加入烧杯中，搅拌均匀；再将甘草酸浓缩粉加入烧杯中溶解后搅拌均匀；再加入复方抗菌剂，混合均匀，即得玻尿酸抗敏修复精华液。