CN112812409A - 一种抗菌抗病毒防霉母粒以及抗菌抗病毒防霉食品包装材料及其制备方法 - Google Patents
一种抗菌抗病毒防霉母粒以及抗菌抗病毒防霉食品包装材料及其制备方法 Download PDFInfo
- Publication number
- CN112812409A CN112812409A CN202110103599.1A CN202110103599A CN112812409A CN 112812409 A CN112812409 A CN 112812409A CN 202110103599 A CN202110103599 A CN 202110103599A CN 112812409 A CN112812409 A CN 112812409A
- Authority
- CN
- China
- Prior art keywords
- antibacterial
- antiviral
- mildewproof
- master batch
- coupling agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种抗菌抗病毒防霉母粒以及抗菌抗病毒防霉食品包装材料及其制备方法，所述抗菌抗病毒防霉母粒包括重量百分比如下的组分：高分子树脂70％‑80％、复合抗氧剂1％‑1.5％、无机载银抗菌剂8％‑12％、纳米银3‑6％和纳米氧化锌8‑12％。本发明中采用无机载银抗菌剂、纳米银和纳米氧化锌三者进行配合，协同作用，增强抗菌抗病毒防霉效果，使得得到的食品包装材料具有抗菌抗病毒防霉性能，并保持材料原有的力学性能，经检测抗菌率和抗病毒率均达到99％以上，防霉等级达到0级，且具有非常好的持久效果。
Description
技术领域
本发明属于包装材料技术领域，涉及一种抗菌抗病毒防霉母粒以及抗菌抗病毒防霉食品包装材料及其制备方法。
背景技术
目前，市场上直接与食品接触的食品包装大多以塑料薄膜包装为主，特别是高阻隔材料已成为食品包装的主体。所以选用时首先应考虑内装物保质、保鲜、保风味的要求。常用的塑料材料有聚乙烯(PE)、聚丙烯(PP)、聚酯(PET)、聚酰胺(PA)等。
目前，已有技术通过在聚乙烯膜表面涂覆化学防腐抗菌涂层的方式实现包装袋的抗菌性，但由于其涂层本身具有其他化学成分，对食品安全产生一定影响，且喷涂工艺将提高包装袋工艺复杂程度。
CN211843521U公开了一种新型抗菌冷冻食品包装膜，但其薄膜的最外层为清洁层不具有抗菌性能，很大程度上减弱了抗菌作用。
CN 111548537A公开了一种高强度防水抑菌食品包装膜的制备方法，解决了目前食品包装膜防水性能不佳、机械强度以及抗菌性能差的缺点。但该食品包装膜在制备过程用到了很多小分子有机溶剂，且不具有抗病毒防霉的作用。
因此，在本领域，期望开发一种具有更好的抗菌抗病毒防霉效果，且安全无污染的食品包装材料。
发明内容
针对现有技术的不足，本发明的目的在于提供一种抗菌抗病毒防霉母粒以及抗菌抗病毒防霉食品包装材料及其制备方法。本发明的抗菌抗病毒防霉母粒具有良好的抗菌抗病毒防霉性能，抗菌持久效果好，并保持较好的力学性能，且材料安全无污染。
为达此目的，本发明采用以下技术方案：
一方面，本发明提供一种抗菌抗病毒防霉母粒，所述抗菌抗病毒防霉母粒包括重量百分比如下的组分：
在本发明中，所述抗菌抗病毒防霉母粒中采用无机载银抗菌剂、纳米银和纳米氧化锌三者进行配合，协同作用，增强抗菌抗病毒防霉效果。
在本发明中，所述抗菌抗病毒防霉母粒中高分子树脂的含量为70％、71％、72％、73％、74％、75％、76％、77％、78％、79％或80％。
在本发明中，所述抗菌抗病毒防霉母粒中复合抗氧剂的含量为1％、1.1％、1.2％、1.3％、1.4％或1.5％。
在本发明中，所述抗菌抗病毒防霉母粒中无机载银抗菌剂的含量为8％、9％、10％、11％或12％。在本发明中，如果无机载银抗菌剂的含量太少，则会影响抗菌效果；如果含量太多，则会对母料的加工性能造成影响，并使抗菌剂粉末分散不均匀。
在本发明中，所述抗菌抗病毒防霉母粒中纳米银的含量为3％、3.5％、4％、4.5％、5％、5.5％或6％。在本发明中，添加纳米银是为了弥补无机载银抗菌剂抗病毒性能不足的缺点，如果纳米银的含量太少，则影响抗病毒效果，如果含量太多，则影响材料的物理性能。
在本发明中，所述抗菌抗病毒防霉母粒中纳米氧化锌的含量为8％、8.5％、9％、9.5％、10％、10.5％、11％、11.5％活12％。在本发明中，如果纳米氧化锌的含量太少，则会影响防霉效果，如果含量太多，则影响材料的物理性能。
优选地，所述高分子树脂为聚乙烯(PE)、聚丙烯(PP)、聚酯(PET)或聚酰胺(PA)中的任意一种。
优选地，所述复合抗氧剂为抗氧剂1010(四[β-(3,5-二叔丁基-4-羟基苯基)丙酸]季戊四醇酯)和抗氧剂168(三[2,4-二叔丁基苯基]亚磷酸酯)的组合。
优选地，所述无机载银抗菌剂中载体为沸石、磷酸锆或羟基磷酸钙中的任意一种。
优选地，所述无机载银抗菌剂为经过偶联剂改性的无机载银抗菌剂。
优选地，所述偶联剂为硅烷偶联剂KH-550、硅烷偶联剂KH-570或钛酸酯偶联剂201中的任意一种。
优选地，所述经过偶联剂改性的无机载银抗菌剂的制备方法为：将无机载银抗菌剂粉体溶于乙醇中，超声分散并搅拌均匀，而后向其中加入偶联剂/乙醇混合溶液，搅拌均匀，得到所述偶联剂改性的无机载银抗菌剂。
在本发明中，将无机载银抗菌剂经过偶联剂改性后，能够提高其在抗菌抗病毒防霉母粒中的分散度，改善无机抗菌剂与有机树脂之间的界面结合性能。
优选地，所述偶联剂的用量为无机载银抗菌剂粉体质量的1.5-2％，例如1.5％、1.6％、1.7％、1.8％、1.9％或2％。
优选地，所述偶联剂/乙醇混合溶液中偶联剂的质量浓度为10-20％，例如10％、12％、14％、16％、18％或20％。
优选地，所述混合在1000r/min的搅拌速度下进行。
优选地，所述混合的温度为50-70℃(例如50℃、53℃、55℃、58℃、60℃、63℃、65℃、68℃或70℃)恒温水浴。
优选地，所述混合的时间为1-2.5h，例如1h、1.3h、1.5h、1.8h、2h、2.2h或2.5h。
优选地，所述混合后，静置分层，取下层粉体，干燥研磨得到偶联剂改性的无机载银抗菌剂。
另一方面，本发明提供如上所述抗菌抗病毒防霉母粒的制备方法，所述制备方法包括以下步骤：将高分子树脂、复合抗氧剂、无机载银抗菌剂、纳米银以及纳米氧化锌进行混合，挤出，造粒，得到所述抗菌抗病毒防霉母粒。
优选地，所述混合的时间为30-60min，例如30min、35min、40min、45min、50min或60min。
另一方面，本发明提供一种抗菌抗病毒防霉食品包装材料，所述抗菌抗病毒防霉食品包装材料包括如上所述的抗菌抗病毒防霉母粒以及塑料高分子树脂原料。
优选地，所述抗菌抗病毒防霉食品包装材料中抗菌抗病毒防霉母粒的质量百分含量为5-7％，例如5％、5.3％、5.5％、5.8％、6％、6.3％、6.5％、6.8％或7％。
优选地，所述塑料高分子树脂原料包括聚乙烯(PE)、聚丙烯(PP)、聚酯(PET)或聚酰胺(PA)中的任意一种。
另一方面，本发明提供了如上所述的抗菌抗病毒防霉食品包装材料的制备方法，所述制备方法为：将抗菌抗病毒防霉母粒与塑料高分子树脂原料进行混合，而后挤出吹塑成型得到抗菌塑料薄膜，然后成型加工得到抗菌抗病毒防霉食品包装材料。
本发明得到的食品包装材料在使用过程中与细菌、霉菌以及病毒等微生物接触后，均起到抗菌抗病毒防霉的作用，且抗菌剂的使用不影响产品的外观、强度和耐磨性，使用过程无有害成分的产生，不污染环境。
相对于现有技术，本发明具有以下有益效果：
本发明中采用无机载银抗菌剂、纳米银和纳米氧化锌三者进行配合，协同作用，增强抗菌抗病毒防霉效果，使得得到的食品包装材料具有抗菌抗病毒防霉性能，并保持材料原有的力学性能，经检测抗菌率和抗病毒率均达到99％以上，防霉等级达到0级，具有非常好的持久效果，且使用过程无有害成分的产生，不污染环境。
具体实施方式
下面通过具体实施方式来进一步说明本发明的技术方案。本领域技术人员应该明了，所述实施例仅仅是帮助理解本发明，不应视为对本发明的具体限制。
在以下实施例中，使用的偶联剂改性无机载银抗菌剂，其改性方法为：称取一定量无机抗菌剂粉体溶于乙醇中，超声波分散并电磁搅拌至均匀。称量为无机载银抗菌剂粉末质量的2％的偶联剂(硅烷偶联剂KH-550)与适量乙醇混合均匀后加入如上所述机抗菌剂粉体溶液中，在1000r/min下60℃恒温水浴中搅拌1.5h后静置分层，取下层粉体干燥研磨得到改性后的无机载银抗菌剂。
实施例1
在本实施例中，提供一种抗菌抗病毒防霉母粒，所述抗菌抗病毒防霉母粒包括重量百分比如下的组分：
低密度聚乙烯(卡塔尔石化LDPE-FD0474，下同)70％
其中，复合抗氧剂为抗氧剂1010和抗氧剂168的组合，
将低密度聚乙烯、复合抗氧剂、偶联剂改性的无机载银抗菌剂、纳米银以及纳米氧化锌进行混合5min，打开出料口放料，再进行挤出造粒，得到所述抗菌抗病毒防霉母粒。
将该实施例的抗菌抗病毒防霉母粒以6％的添加量添加至塑料高分子树脂原料低密度聚乙烯中，充分混合，得到进行挤出吹塑成型制得抗菌塑料薄膜，再经过后续的成型加工制得抗菌抗病毒防霉食品包装材料。
实施例2
在本实施例中，提供一种抗菌抗病毒防霉母粒，所述抗菌抗病毒防霉母粒包括重量百分比如下的组分：
其中，复合抗氧剂为抗氧剂1010和抗氧剂168的组合，
将低密度聚乙烯、复合抗氧剂、偶联剂改性的无机载银抗菌剂、纳米银以及纳米氧化锌进行混合5min，打开出料口放料，再进行挤出造粒，得到所述抗菌抗病毒防霉母粒。
将该实施例的抗菌抗病毒防霉母粒以6％的添加量添加至塑料高分子树脂原料低密度聚乙烯中，充分混合，得到进行挤出吹塑成型制得抗菌塑料薄膜，再经过后续的成型加工制得抗菌抗病毒防霉食品包装材料。
实施例3
在本实施例中，提供一种抗菌抗病毒防霉母粒，所述抗菌抗病毒防霉母粒包括重量百分比如下的组分：
其中，复合抗氧剂为抗氧剂1010和抗氧剂168的组合，
将低密度聚乙烯、复合抗氧剂、偶联剂改性的无机载银抗菌剂、纳米银以及纳米氧化锌进行混合5min，打开出料口放料，再进行挤出造粒，得到所述抗菌抗病毒防霉母粒。
将该实施例的抗菌抗病毒防霉母粒以6％的添加量添加至塑料高分子树脂原料低密度聚乙烯中，充分混合，得到进行挤出吹塑成型制得抗菌塑料薄膜，再经过后续的成型加工制得抗菌抗病毒防霉食品包装材料。
实施例4
在本实施例中，提供一种抗菌抗病毒防霉母粒，所述抗菌抗病毒防霉母粒包括重量百分比如下的组分：
其中，复合抗氧剂为抗氧剂1010和抗氧剂168的组合，
将聚丙烯、复合抗氧剂、偶联剂改性的无机载银抗菌剂、纳米银以及纳米氧化锌进行混合5min，打开出料口放料，再进行挤出造粒，得到所述抗菌抗病毒防霉母粒。
将该实施例的抗菌抗病毒防霉母粒以6％的添加量添加至塑料高分子树脂原料聚丙烯中，充分混合，得到进行挤出吹塑成型制得抗菌塑料薄膜，再经过后续的成型加工制得抗菌抗病毒防霉食品包装材料。
实施例5
在本实施例中，提供一种抗菌抗病毒防霉母粒，所述抗菌抗病毒防霉母粒包括重量百分比如下的组分：
其中，复合抗氧剂为抗氧剂1010和抗氧剂168的组合，
将聚酯、复合抗氧剂、偶联剂改性的无机载银抗菌剂、纳米银以及纳米氧化锌进行混合5min，打开出料口放料，再进行挤出造粒，得到所述抗菌抗病毒防霉母粒。
将该实施例的抗菌抗病毒防霉母粒以6％的添加量添加至塑料高分子树脂原料聚酯中，充分混合，得到进行挤出吹塑成型制得抗菌塑料薄膜，再经过后续的成型加工制得抗菌抗病毒防霉食品包装材料。
实施例6
在本实施例中，提供一种抗菌抗病毒防霉母粒，所述抗菌抗病毒防霉母粒包括重量百分比如下的组分：
其中，复合抗氧剂为抗氧剂1010和抗氧剂168的组合，
将聚酰胺、复合抗氧剂、偶联剂改性的无机载银抗菌剂、纳米银以及纳米氧化锌进行混合5min，打开出料口放料，再进行挤出造粒，得到所述抗菌抗病毒防霉母粒。
将该实施例的抗菌抗病毒防霉母粒以6％的添加量添加至塑料高分子树脂原料聚酰胺中，充分混合，得到进行挤出吹塑成型制得抗菌塑料薄膜，再经过后续的成型加工制得抗菌抗病毒防霉食品包装材料。
对比例1
该对比例与实施例1不同之处仅在于，该对比例中不使用偶联剂改性的无机载银抗菌剂，其中纳米银用量为6.3％，纳米氧化锌用量为12.7％。
对比例2
该对比例与实施例1不同之处仅在于，该对比例中不使用纳米银，偶联剂改性的无机载银抗菌剂用量为5.4％，纳米氧化锌用量为13.6％。
对比例3
该对比例与实施例1不同之处仅在于，该对比例中不使用纳米氧化锌，偶联剂改性的无机载银抗菌剂用量为8.4％，纳米银用量为10.6％。
对实施例1-6以及对比例1-3的抗菌抗病毒防霉食品包装材料进行抗菌抗病毒防霉性能测试，性能测试根据如下标准进行：GB/T 31402-2015塑料表面抗菌性能试验方法，ISO21702-2019塑料和其他非多孔表面抗病毒活性的测定，GB/T 24128-2009塑料防霉性能试验方法，GB/T 1040.1-2018塑料拉伸性能的测定。
测试结果如表1所示。
表1
由表1可以看出，本发明的食品包装材料具有抗菌抗病毒防霉性能，抗菌率和抗病毒率均达到99％以上，防霉等级达到0级。
为了进行抗菌抗病毒防霉性能持久性的表征，对如上测试的实施例1-6以及对比例1-3的样品，间隔一周后再次进行抗菌抗病毒性能测试；对如上测试的实施例1-6以及对比例1-3的样品间隔40天后再次进行防霉等级测试。
测试结果如表2所示。
表2
表2的数据表明，本发明的食品包装材料的抗菌抗病毒防霉性能具有非常好的持久效果。
申请人声明，本发明通过上述实施例来说明本发明的抗菌抗病毒防霉母粒以及抗菌抗病毒防霉食品包装材料及其制备方法，但本发明并不局限于上述实施例，即不意味着本发明必须依赖上述实施例才能实施。所属技术领域的技术人员应该明了，对本发明的任何改进，对本发明产品各原料的等效替换及辅助成分的添加、具体方式的选择等，均落在本发明的保护范围和公开范围之内。
Claims (10)
1.一种抗菌抗病毒防霉母粒，其特征在于，所述抗菌抗病毒防霉母粒包括重量百分比如下的组分：
2.根据权利要求1所述的抗菌抗病毒防霉母粒，其特征在于，所述高分子树脂为聚乙烯、聚丙烯、聚酯或聚酰胺中的任意一种。
3.根据权利要求1或2所述的抗菌抗病毒防霉母粒，其特征在于，所述复合抗氧剂为抗氧剂1010和抗氧剂168的组合。
4.根据权利要求1-3中任一项所述的抗菌抗病毒防霉母粒，其特征在于，所述无机载银抗菌剂中载体为沸石、磷酸锆或羟基磷酸钙中的任意一种；
优选地，所述无机载银抗菌剂为经过偶联剂改性的无机载银抗菌剂；
优选地，所述偶联剂为硅烷偶联剂KH-550、硅烷偶联剂KH-570或钛酸酯偶联剂201中的任意一种。
5.根据权利要求1-4中任一项所述的抗菌抗病毒防霉母粒，其特征在于，所述经过偶联剂改性的无机载银抗菌剂的制备方法为：将无机载银抗菌剂粉体溶于乙醇中，超声分散并搅拌均匀，而后向其中加入偶联剂/乙醇混合溶液，搅拌均匀，得到所述偶联剂改性的无机载银抗菌剂；
优选地，所述偶联剂的用量为无机载银抗菌剂粉体质量的1.5-2％；
优选地，所述偶联剂/乙醇混合溶液中偶联剂的质量浓度为10-20％；
优选地，所述混合在1000r/min的搅拌速度下进行；
优选地，所述混合的温度为50-70℃恒温水浴；
优选地，所述混合的时间为1-2.5h；
优选地，所述混合后，静置分层，取下层粉体，干燥研磨得到偶联剂改性的无机载银抗菌剂。
6.根据权利要求1-5中任一项所述的抗菌抗病毒防霉母粒的制备方法，其特征在于，所述制备方法包括以下步骤：将高分子树脂、复合抗氧剂、无机载银抗菌剂、纳米银以及纳米氧化锌进行混合，挤出，造粒，得到所述抗菌抗病毒防霉母粒；
优选地，所述混合的时间为30-60min。
7.一种抗菌抗病毒防霉食品包装材料，其特征在于，所述抗菌抗病毒防霉食品包装材料包括如权利要求1-5中任一项所述的抗菌抗病毒防霉母粒以及塑料高分子树脂原料。
8.根据权利要求7所述的抗菌抗病毒防霉食品包装材料，其特征在于，所述抗菌抗病毒防霉食品包装材料中抗菌抗病毒防霉母粒的质量百分含量为5-7％。
9.根据权利要求7或8所述的抗菌抗病毒防霉食品包装材料，其特征在于，所述塑料高分子树脂原料包括聚乙烯、聚丙烯、聚酯或聚酰胺中的任意一种。
10.根据权利要求7-9中任一项所述的抗菌抗病毒防霉食品包装材料的制备方法，其特征在于，所述制备方法为：将抗菌抗病毒防霉母粒与塑料高分子树脂原料进行混合，而后挤出吹塑成型得到抗菌塑料薄膜，然后成型加工得到抗菌抗病毒防霉食品包装材料。