CN1127286A - 炼焦的配煤方法 - Google Patents

炼焦的配煤方法 Download PDF

Info

Publication number
CN1127286A
CN1127286A CN 95110618 CN95110618A CN1127286A CN 1127286 A CN1127286 A CN 1127286A CN 95110618 CN95110618 CN 95110618 CN 95110618 A CN95110618 A CN 95110618A CN 1127286 A CN1127286 A CN 1127286A
Authority
CN
China
Prior art keywords
coal
coking
coke
blending method
quality
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 95110618
Other languages
English (en)
Inventor
李铁城
张桐生
赵静禅
谢春华
刘庆日
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Electric Coal Coking General Plant Zixing Mining Administration Hunan Prov (c
Original Assignee
Electric Coal Coking General Plant Zixing Mining Administration Hunan Prov (c
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Electric Coal Coking General Plant Zixing Mining Administration Hunan Prov (c filed Critical Electric Coal Coking General Plant Zixing Mining Administration Hunan Prov (c
Priority to CN 95110618 priority Critical patent/CN1127286A/zh
Publication of CN1127286A publication Critical patent/CN1127286A/zh
Pending legal-status Critical Current

Abstract

本发明涉及炼焦的配煤方法，它是在传统的烟煤配煤基础上，加入无烟煤，使配合煤的质量指标G为68～75、Y为15～20mm、其余质量指标与二级冶金焦的配合煤质量指标相同。采用加无烟煤炼焦后，焦炭质量不但没有下降，反而有所提高，较纯烟煤炼焦焦炭的块度大、裂纹少、反应性低。本发明提供的配煤方法对提高经济效益，扩大无烟煤应用范围、减轻运输压力起到了较好的作用。

Description

炼焦的配煤方法
本发明涉及炼焦的配煤方法。
传统的炼焦原料是采用烟煤，但在我国南方广大地区，缺少烟煤，因而南方炼焦的原料均由北方运来，增加了成本，加剧了运输紧张状况。另一方面，南方却有丰富优质的无烟煤。由于无烟煤本身的性质，使得不能只用无烟煤作为原料来进行炼焦。
除此之外，传统的用烟煤炼焦所得的焦炭，往往存在块度较小，裂纹多，结构不致密的缺点，并且反应性快。这对冶金、铸造行业的生产是极为不利的。
本发明的目的是提供一种炼焦的配煤方法，使得在原料中加入无烟煤后，仍能炼出二级冶金焦，并且增大焦炭的块度和致密度，降低焦炭的反应性。
为实现上述发明目的，本发明的关键在于调节配合煤的质量指标，使其中的G为68—75，V为15—20mm，其他质量指标达到二级冶金焦的配煤质量。
由于现有一般配煤工艺流程中，还没有配无烟煤的作业工序，因此，要完成配无烟煤炼焦，须采用现有的配煤工艺，加配无烟煤的工艺。其生产工艺流程如下：
Figure A9511061800031
→装煤→炼焦→出焦→焦炭筛分。
在上述炼焦工艺中，配煤比例要求控制准确，配比误差不大于±3％，粉碎细度要求d＜3mm的占80％以上，有利于烟煤与无烟煤混合均匀，提高结焦率。
本发明提供的配煤方法，将无烟煤加入烟煤中，其中的无烟煤起到了瘦化剂的作用。采用本发明配煤方法炼出的焦炭块度较大，裂纹少，结构致密，反应性低。
配无烟煤炼焦，不仅提高了经济效益，而且扩大了无烟煤的用途，拓宽了无烟煤的销售市场，缓解了缺煤地区炼焦煤紧张的局面，减轻了铁路运输的压力。
实施例1
所用各煤种的各项质量指标如下配比方案WB—01，肥煤25％，1/3焦煤30％，焦煤40％，无烟煤5％。配合煤质量指标：
Figure A9511061800042
生产工艺技术参数
 项目   焦饼中心温度(℃)   燃烧室标准温度(℃)    煤气总压(Pa)  推焦电流(A)  结焦时间(h)
 指标   1000±50    1140～1160   3000～4000     ＜30     14
按上述方案炼焦后，产品化验结果见表1。
实施例：
所用各煤种的各项质量指标同上例。
配比方案WB—02，肥煤30％，1/3焦煤25％，焦煤35％，无烟煤10％。
配合煤质量指标：
Figure A9511061800051
生产工艺技术参数同上例。
按上述方案炼焦后，产品质量结果见表1。
实施例3
所用各煤种的各项质量指标同上例。
配比方案WB—03肥煤30％，1/3焦煤25％，焦煤37％，无烟煤8％。
配合煤质量指标：
Figure A9511061800052
生产工艺技术参数同上例。
按上述方案炼焦后，产品质量结果见表1
表1：    试验焦炭化验结果
Figure A9511061800061

Claims (3)

1、一种炼焦的配煤方法，其特征在于在原来的烟煤中，加入了无烟煤，使配合煤质量指标中的G为68～75，V为15～20mm。
2、根据权利要求1所述配煤方法，其特征在于采用的烟煤是肥煤、1/3焦煤、焦煤。
3、根据权利要求1所述配煤方法，其特征在于粉碎细度要求d＜3mm的占80％以上。
CN 95110618 1995-01-17 1995-01-17 炼焦的配煤方法 Pending CN1127286A (zh)