CN112694684A - 一种含有负离子远红外线的护心卡及其制备方法 - Google Patents
一种含有负离子远红外线的护心卡及其制备方法 Download PDFInfo
- Publication number
- CN112694684A CN112694684A CN202110077649.3A CN202110077649A CN112694684A CN 112694684 A CN112694684 A CN 112694684A CN 202110077649 A CN202110077649 A CN 202110077649A CN 112694684 A CN112694684 A CN 112694684A
- Authority
- CN
- China
- Prior art keywords
- heart
- card
- meshes
- protection card
- percent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种含有负氧离子远红外线的护心卡及其制备方法。所述的护心卡，其由下列重量比的原料配置而成：三元乙丙橡胶：保健添加剂：流动剂：色料：促进剂=70：30：1：10：5。护心卡可以制成各种人们喜欢的颜色以及喜闻乐见的图形。当人们佩戴本发明提供的护心卡时，护心卡内的保健添加剂释放出的高氧负离子和远红外线，具有辅助改善呼吸、平稳心律跳动正常、防止心律跳动加速、防止心律跳动衰弱、提高心脏供氧量、提高心脏供血量、防止新血管堵塞和老化及钙化之积极功能。
Description
技术领域
本发明涉及保健产品技术领域，尤其涉及一种辅助缓解、减轻和调节人体心血管、呼吸等疾病的临床状态的护心卡及其制备方法。
背景技术
由于工作生活节奏的加快以及随着年龄的增长，人体容易产生心血管、呼吸等疾病。比如，呼吸困难，心口疼痛，心律不整；心血管硬化，心血管钙化，心血管堵塞，心肌肿胀；心脏支架患者， 心脏搭桥患者。这种心血管、呼吸等慢性疾病严重影响人们的身体健康，降低人们的生活质量，甚至危害人们的生命安全。针对所述慢性疾病，一般需要通过长期服药要控制，病情严重的患者甚至需要通过手术来医治。在通过服药和手术医治疾病的同时，人们还在积极开拓一些办法来辅助健康。比如，合理吸氧、做保健拳操、传统中医的保健等。随着社会发展，人们还希望还有更加方便的辅助医疗队保健方式出现。
因此，如何克服现有对心血管、呼吸等疾病的辅助保健方式不方便的缺陷是业界亟待解决的问题。
发明内容
本发明为了解决现有对心血管、呼吸等疾病的辅助保健方式不便的问题，提出一种含有负离子远红外线的护心卡及其制备方法。本发明提供的护心卡可以方便的吊挂与人们的胸前，保健效果永久，并可辅助缓解、减轻和调节人体心血管、呼吸等疾病的临床状态。
本发明提出的一种含有负氧离子远红外线的护心卡，其由下列重量比的原料配置而成 ：三元乙丙橡胶(EPDM)：保健添加剂：流动剂：色料：促进剂 = 70：30：1：10：5。
优选的，所述的保健添加剂，其由下列重量百分含量的原料配置而成 ：
钙 2% ～ 8%；磷4% ～ 12%；铈15% ～ 35%；钛3% ～ 12%、
钇1% ～ 10%；钕9% ～ 17%；镧 11%～19%；锗3% ～ 10%。
优选的，所述保健添加剂的原料的粒度 ：钙为 800 目、磷为 1200、铈为 1500目、钛为 450 目、钇为目 550、钕为 600 目、镧为3000 目、锗为 550 目。
优选的，所述流动剂为植物类环保多元醇。
优选的，所述色料为食品级色母。
优选的，所述促进剂为纳米级氧化锌。
本发明提供一种所述含有负氧离子远红外线的护心卡的制备方法，其步骤如下：
步骤1、根据所述护心卡的原料配比称取各原料，先将所述的三元乙丙橡胶放入100℃温度的烤炉中，开始边搅拌边升温到 130℃，保持130℃混练搅拌均匀，共一小时；
步骤2：在130℃的温度下，向所述烤炉中加入所述的流动剂、色料、促进剂，并保持在130℃的温度混炼搅拌均匀一小时，制得混合料；
步骤3：利用0.5小时，将所述混合料的温度提升到140℃，再加入所述的保健添加剂粉，保持140℃高温混炼搅拌均匀一小时，得混炼均匀的胶料；
步骤4：将所述混炼均匀的胶料拉成薄片，高温塑化,然后将所述薄片自然冷却7~9小时，得护心卡材料；
步骤5：将所述护心卡材料放入除湿机中在100℃下烤四小时，在将除湿后的护心卡材料自然冷却1.5~2.5小时；
步骤6：将除湿冷却后的所述护心卡材料，按每一护心卡的设计称取所需的重量，逐个放入模具里，并经过225~235秒的180℃的高温硫化成型；
步骤7：将硫化成型后的护心卡胚体取出模具，修除毛边、披风，制得所述的护心卡。
优选的，所述步骤4中，用开炼机将所述混炼均匀的胶料拉成15cm ×60cm的薄片。
优选的，所述步骤6中，该产品设计称取所述护心卡材料的重量为19~21克。
优选的，所述步骤7中，制得长×宽×厚为90mm×55mm×4mm的护心卡。
本发明提供的护心卡可以根据需要制成各种人们喜欢的颜色，而且还可以利用模具在护心卡的表面模压出各种人们喜闻乐见的图形。人们可以根据自己的喜欢选择不同颜色和可以调节长短的挂绳，将护心卡当作装饰品吊挂于胸前。当人们佩戴本发明提供的护心卡时，护心卡内的保健添加剂释放出的高氧负离子和远红外线，具有辅助改善呼吸、平稳心律跳动正常、防止心律跳动加速、防止心律跳动衰弱、提高心脏供氧量、提高心脏供血量、防止新血管堵塞和老化及钙化之积极功能。
具体实施方式
下面通过实施例对本发明作进一步的说明。
本发明提供的一种含有负氧离子远红外线的护心卡，其由下列重量比的原料配置而成，EPDM三元乙丙橡胶：保健添加剂：流动剂：色料：促进剂 = 70：30：1：10：5。
其中，所述流动剂优选为植物类环保多元醇；色料优选为食品级色母；促进剂优选为纳米级氧化锌。
根据需要可以选择不同颜色的色料，也可以使用单一色料或混合色料。所述护心卡原料用量的配比，为如下实施例：
70 kg 的三元乙丙橡胶（EPDM）；30 kg的保健添加剂；1 kg流动剂：10 kg的橘红色料；5 kg的促进剂 。
所述的保健添加剂，其由下列重量百分含量的原料配置而成 ：
钙 2% ～ 8%；磷4% ～ 12%；铈15% ～ 35%；钛3% ～ 12%、
钇1% ～ 10%；钕9% ～ 17%；镧 11%～19%；锗3% ～ 10%。
所述保健添加剂的原料的粒度为：钙为 800 目、磷为 1200、铈为 1500 目、钛为450 目、钇为目 550、钕为 600 目、镧为3000 目、锗为 550 目。
根据不同功效的要求，可以选用保健添加剂原料用量的配比，在此不多赘述。所述化工原料：三元乙丙橡胶、流动剂、色料以及保健添加剂的原料---钙、磷、铈、钛、钇、钕、镧和锗均可以在化工原料商店或化工厂购买得到。
本发明提供一种所述含有负氧离子远红外线的护心卡的制备方法，其步骤如下：
步骤1、根据所述护心卡的原料配比称取各原料，本实施例为：
70 kg 的三元乙丙橡胶（EPDM）；30 kg的保健添加剂；1 kg流动剂：10 kg的橘红色料；5 kg的促进剂 。其中保健添加剂中的：钙为 800 目 ；磷为 1200 ；铈为 1500 目 ；钛为 450 目 ；钇为目 550 ；钕为 600 目 ；镧为 3000 目 ；锗为 550 目。
先将容量300升的熔炉用高温瓦斯烧烤达到100℃高温后，再将70kg 的EPDM三元乙丙橡胶放入烤炉中，开始边搅拌边升温到 130℃，保持130℃混练搅拌均匀。前后搅拌共计一小时。
步骤2：在130℃的温度下，向所述烤炉中加入所述的1kg的流动剂、10kg的色料和5kg的促进剂，并保持在130℃的温度下再混炼搅拌均匀一小时，制得混合料。
步骤3：利用0.5小时，将所述混合料的温度提升到140℃，再加入所述的保健添加剂粉，保持在140℃的高温下混炼搅拌均匀一小时，得混炼均匀的胶料
步骤4：用开炼机将所述混炼均匀的胶料拉成15cm x 60cm的薄片，在高温塑化下使得五种原料分子完全溶合为一种具有特定功能的新型材料。然后将所述薄片自然冷却7~9小时，得护心卡材料；
步骤5：将所述护心卡材料放入除湿机中在100℃下烤四小时，确保完全干燥，在将除湿后的护心卡材料自然冷却1.5~2.5小时；
步骤6：将除湿冷却后的所述护心卡材料，按每一护心卡的设计称取所需的重量为19~21克，逐个放入模具里，并经过225~235秒的180℃的高温硫化成型；
步骤7：将硫化成型后的护心卡胚体取出模具，修除毛边、披风，制得长×宽×厚为90mm×55mm×4mm的护心卡。
针对本发明提供的护心卡进行有关临床实验如下：
一、实验结果
由马来西亚IONSPEC慈善基金会和亚洲中医技术学院招募100名心脏疾病和呼吸困难使 用患者，分为三组：
A组： 呼吸困难，心口疼痛，心律不整，
B组：心血管硬化，心血管钙化，心血管堵塞，心肌肿胀，
C组：心脏支架患者， 心脏搭桥患者。
佩戴护心卡 产品12个月后，55%以上的心脏疾病患者得到改善。
| 样本 | 人数 | 改善呼吸系统，呼吸顺畅，步行更远，活动时间更长 | 上下楼梯轻松，不气喘，饭后精神部困睡，记忆力集中，手脚有力，不麻痹 |
| A组：呼吸困难，心口疼痛，心律不整患者 | 74 | 78.38% | 55.41% |
| B组：心血管硬化，心血管钙化，心血管堵塞，心肌肿胀患者 | 15 | 53.33% | 46.67% |
| C组：心脏支架患者， 心脏搭桥患者 | 11 | 36.36% | 45.45% |
上述A，B，C三组佩戴方法；
A组患者佩戴三片：左肺和右肺各一片，胸口心脏处一片。每天连续使用10小时。
B 组患者佩戴四片：前胸口心脏处二片，后背胸口处二片。每天连续使用10小时。
C 组患者佩戴五片：前胸口心脏处二片，后背胸口处二片，颈后部一片。每天连续使用10小时。
结论：实验的科目表示满意;提供佩戴的护心卡改善了他们的心脏疾病和呼吸问题。评估结果表明，护心卡有助于改善受试者的心脏疾病和呼吸问题。对照组在不佩戴本发明提供的护心卡，估计他们的心脏疾病和呼吸问题在3-12个月后保持相同或恶化。比较实验组（佩戴本发明提供的护心卡的患者）和对照组（不佩戴）。那些实验组的心脏和呼吸功能有所提高。因此，本发明提供的护心卡具有帮助患者改善心脏疾病和呼吸问题的积极效果。所有研究对象均来自亚洲中医技术学院（ASIA SKILLS COLLEGE）。
以上所述实施例主要是为了说明本发明的创作构思，应当指出的是，对于本领域的普通技术人员来说，在不脱离本发明构思的前提下，还可以做出若干变形和改进，这些都属于本发明的保护范围。
Claims (10)
1.一种含有负氧离子远红外线的护心卡，其由下列重量比的原料配置而成 ：
三元乙丙橡胶：保健添加剂：流动剂：色料：促进剂 = 70：30：1：10：5。
2.如权利要求1所述的护心卡，其特征在于，所述的保健添加剂，其由下列重量百分含量的原料配置而成 ：
钙 2% ～ 8%；磷4% ～ 12%；铈15% ～ 35%；钛3% ～ 12%、
钇1% ～ 10%；钕9% ～ 17%；镧 11%～19%；锗3% ～ 10%。
3.如权利要求2所述的护心卡，其特征在于，所述保健添加剂的原料的粒度 ：
钙为 800 目、磷为 1200、铈为 1500 目、钛为 450 目、钇为目 550、钕为 600 目、
镧为3000 目、锗为 550 目。
4.如权利要求1所述的护心卡，其特征在于，所述流动剂为植物类环保多元醇。
5.如权利要求1所述的护心卡，其特征在于，所述色料为食品级色母。
6.如权利要求1所述的护心卡，其特征在于，所述促进剂为纳米级氧化锌。
7.一种如权利要求1至6任一项所述的护心卡的制备方法，其步骤如下：
步骤1、根据所述护心卡的原料配比称取各原料，先将所述的三元乙丙橡胶放入100℃温度的烤炉中，开始边搅拌边升温到 130℃，保持130℃混练搅拌均匀，共一小时；
步骤2：在130℃的温度下，向所述烤炉中加入所述的流动剂、色料、促进剂，并保持在130℃的温度混炼搅拌均匀一小时，制得混合料；
步骤3：利用0.5小时，将所述混合料的温度提升到140℃，再加入所述的保健添加剂粉，保持140℃高温混炼搅拌均匀一小时，得混炼均匀的胶料；
步骤4：将所述混炼均匀的胶料拉成薄片，高温塑化,然后将所述薄片自然冷却7~9小时，得护心卡材料；
步骤5：将所述护心卡材料放入除湿机中在100℃下烤四小时，在将除湿后的护心卡材料自然冷却1.5~2.5小时；
步骤6：将除湿冷却后的所述护心卡材料，按每一护心卡的设计称取所需的重量，逐个放入模具里，并经过225~235秒的180℃的高温硫化成型；
步骤7：将硫化成型后的护心卡胚体取出模具，修除毛边、披风，制得所述的护心卡。
8.如权利要求7所述的制备方法，其特征在于，所述步骤4中，用开炼机将所述混炼均匀的胶料拉成15cm x 60cm的薄片。
9.如权利要求1所述的制备方法，其特征在于，所述步骤6中，该产品设计称取所述护心卡材料的重量为19~21克。
10.如权利要求1所述的制备方法，其特征在于，所述步骤7中，制得长×宽×厚为90mm×55mm×4mm的护心卡。