CN112626530A - 一种不锈钢表面处理剂及其表面处理工艺 - Google Patents
一种不锈钢表面处理剂及其表面处理工艺 Download PDFInfo
- Publication number
- CN112626530A CN112626530A CN202011451219.5A CN202011451219A CN112626530A CN 112626530 A CN112626530 A CN 112626530A CN 202011451219 A CN202011451219 A CN 202011451219A CN 112626530 A CN112626530 A CN 112626530A
- Authority
- CN
- China
- Prior art keywords
- stainless steel
- agent
- degreasing
- mass
- surface treatment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种不锈钢表面处理剂及其表面处理工艺，具体为脱脂剂，所述脱脂剂由以下质量百分含量的原料组成，8～10％的表面活性剂、3～6％的不锈钢螯合剂、16～20％的无机碱、4～7％的络合剂、8～10％的有机碱、0～1％的渗透剂、0.5～1％的缓蚀剂以及49～63％的水混合而成，表面活性剂为非离子型表面活性剂，具体为2‑十四烷醇，不锈钢螯合剂具体为柠檬酸铵和羟基乙酸，并且柠檬酸铵和羟基乙酸的比例为1:1，本发明涉及不锈钢表面处理技术领域。该不锈钢表面处理剂及其表面处理工艺，脱脂剂的所有原料从市场容易得到，只要将各种原料采用手工或机械搅匀即可使用，能满足镀锌企业在生产线上自制自用的便捷性和节省时间的要求。
Description
技术领域
本发明涉及不锈钢表面处理技术领域，具体为一种不锈钢表面处理剂及其表面处理工艺。
背景技术
钢铁制品在加工涂漆前要对其表面进行去油、除锈处理以防止中间过程的腐蚀，改善涂漆质量、延长钢铁的使用寿命，现有的处理方法一般都是通过使用脱脂剂去除不锈钢表面的油脂和锈，
但是现有脱脂剂对原料要求苛刻，从而给制造构成麻烦，具体表现为制造工艺复杂，例如需要使用反应釜蒸汽加热搅拌，制造过程长，能源消耗大。
发明内容
针对现有技术的不足，本发明提供了一种不锈钢表面处理剂及其表面处理工艺。
为实现以上目的，本发明通过以下技术方案予以实现：一种不锈钢表面处理剂及其表面处理工艺，具体为脱脂剂，所述脱脂剂由以下质量百分含量的原料组成，8～10％的表面活性剂、3～6％的不锈钢螯合剂、16～20％的无机碱、4～7％的络合剂、8～10％的有机碱、0～1％的渗透剂、0.5～1％的缓蚀剂以及49～63％的水混合而成。
优选的：所述表面活性剂为非离子型表面活性剂，具体为2-十四烷醇，化学式是C14H30O。
优选的：所述不锈钢螯合剂具体为柠檬酸铵和羟基乙酸，并且柠檬酸铵和羟基乙酸的比例为1:1。
优选的：所述无机碱具体为硅酸钠和氢氧化钠，并且硅酸钠和氢氧化钠的比例为2:1。
优选的：所述有机碱具体为三乙醇胺，所述络合剂具体为葡萄糖酸钠。
优选的：所述渗透剂具体为聚氧乙烯聚氧丙烯单丁基醚，所述缓蚀剂具体为苯甲酸钠。
一种不锈钢表面处理工艺，具体为；
第一步；预处理：通过毛刷或者棉布清理不锈钢表面的灰尘等杂物
第二步；脱脂：单位面积内使用1.5PT的脱脂剂，喷淋于不锈钢的表面，对不锈钢表面进行脱脂，出去不锈钢表面的油脂，此步骤重复三次；
第三步；水洗：使用PH小于8的纯水对不锈钢表面进行反复冲洗，且冲洗次数不少于三次，将不锈钢表面的油脂以及脱脂剂冲刷掉；
第四步；硅烷处理：单位面积内使用3‰的硅烷皮膜剂，涂覆与不锈钢的表面，与不锈钢反应在不锈钢表面生成一层不溶于水、牢固附着的保护膜。
有益效果
本发明提供了一种不锈钢表面处理剂及其表面处理工艺。具备以下有益效果：
该不锈钢表面处理剂及其表面处理工艺，构成脱脂剂的所有原料从市场容易得到；只要将各种原料采用手工或机械搅匀即可使用，因而无需象已有技术那样经过繁琐的制作过程，从而能满足镀锌企业在生产线上自制自用的便捷性和节省时间的要求，并且该脱脂剂使用起来污染较小。
具体实施方式
下面对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
本发明提供一种技术方案：一种不锈钢表面处理剂及其表面处理工艺，具体为脱脂剂，其特征在于：所述脱脂剂由以下质量百分含量的原料组成，8～10％的表面活性剂、3～6％的不锈钢螯合剂、16～20％的无机碱、4～7％的络合剂、8～10％的有机碱、0～1％的渗透剂、0.5～1％的缓蚀剂以及49～63％的水混合而成。
进一步的：所述表面活性剂为非离子型表面活性剂，具体为2-十四烷醇，化学式是C14H30O。
进一步的：所述不锈钢螯合剂具体为柠檬酸铵和羟基乙酸，并且柠檬酸铵和羟基乙酸的比例为1:1。
进一步的：所述无机碱具体为硅酸钠和氢氧化钠，并且硅酸钠和氢氧化钠的比例为2:1。
进一步的：所述有机碱具体为三乙醇胺，所述络合剂具体为葡萄糖酸钠。
进一步的：所述渗透剂具体为聚氧乙烯聚氧丙烯单丁基醚，所述缓蚀剂具体为苯甲酸钠。
一种不锈钢表面处理工艺，具体为；
第一步；预处理：通过毛刷或者棉布清理不锈钢表面的灰尘等杂物
第二步；脱脂：单位面积内使用1.5PT的脱脂剂，喷淋于不锈钢的表面，对不锈钢表面进行脱脂，出去不锈钢表面的油脂，此步骤重复三次；
第三步；水洗：使用PH小于8的纯水对不锈钢表面进行反复冲洗，且冲洗次数不少于三次，将不锈钢表面的油脂以及脱脂剂冲刷掉；
第四步；硅烷处理：单位面积内使用3‰的硅烷皮膜剂，涂覆与不锈钢的表面，与不锈钢反应在不锈钢表面生成一层不溶于水、牢固附着的保护膜。
使用注意事项；
该产品在使用时应远离食品、饮料和饲料，使用后应除去所有的不洁的和被污染的衣服，在休息之前和工作完成之后需要洗手，避免皮肤和眼睛直接接触到该产品。
需要说明的是，在本文中，诸如第一和第二等之类的关系术语仅仅用来将一个实体或者操作与另一个实体或操作区分开来，而不一定要求或者暗示这些实体或操作之间存在任何这种实际的关系或者顺序。而且，术语“包括”、“包含”或者其任何其他变体意在涵盖非排他性的包含，从而使得包括一系列要素的过程、方法、物品或者设备不仅包括那些要素，而且还包括没有明确列出的其他要素，或者是还包括为这种过程、方法、物品或者设备所固有的要素。
尽管已经示出和描述了本发明的实施例，对于本领域的普通技术人员而言，可以理解在不脱离本发明的原理和精神的情况下可以对这些实施例进行多种变化、修改、替换和变型，本发明的范围由所附权利要求及其等同物限定。
Claims (7)
1.一种不锈钢表面处理剂，具体为脱脂剂，其特征在于：所述脱脂剂由以下质量百分含量的原料组成，8～10％的表面活性剂、3～6％的不锈钢螯合剂、16～20％的无机碱、4～7％的络合剂、8～10％的有机碱、0～1％的渗透剂、0.5～1％的缓蚀剂以及49～63％的水混合而成。
2.根据权利要求1所述的一种不锈钢表面处理剂，其特征在于：所述表面活性剂为非离子型表面活性剂，具体为2-十四烷醇，化学式是C14H30O。
3.根据权利要求1所述的一种不锈钢表面处理剂，其特征在于：所述不锈钢螯合剂具体为柠檬酸铵和羟基乙酸，并且柠檬酸铵和羟基乙酸的比例为1:1。
4.根据权利要求1所述的一种不锈钢表面处理剂，其特征在于：所述无机碱具体为硅酸钠和氢氧化钠，并且硅酸钠和氢氧化钠的比例为2:1。
5.根据权利要求1所述的一种不锈钢表面处理剂，其特征在于：所述有机碱具体为三乙醇胺，所述络合剂具体为葡萄糖酸钠。
6.根据权利要求1所述的一种不锈钢表面处理剂，其特征在于：所述渗透剂具体为聚氧乙烯聚氧丙烯单丁基醚，所述缓蚀剂具体为苯甲酸钠。
7.根据权利要求1-6所述的一种不锈钢表面处理工艺，具体为；
第一步；预处理，通过毛刷或者棉布清理不锈钢表面的灰尘等杂物
第二步；脱脂，单位面积内使用1.5PT的脱脂剂，喷淋于不锈钢的表面，对不锈钢表面进行脱脂，出去不锈钢表面的油脂，此步骤重复三次；
第三步；水洗，使用PH小于8的纯水对不锈钢表面进行反复冲洗，且冲洗次数不少于三次，将不锈钢表面的油脂以及脱脂剂冲刷掉；
第四步；硅烷处理，单位面积内使用3‰的硅烷皮膜剂，涂覆与不锈钢的表面，与不锈钢反应在不锈钢表面生成一层不溶于水、牢固附着的保护膜。