CN112605325B - 一种偏心锻件成型工艺 - Google Patents

一种偏心锻件成型工艺 Download PDF

Info

Publication number
CN112605325B
CN112605325B CN202011381503.XA CN202011381503A CN112605325B CN 112605325 B CN112605325 B CN 112605325B CN 202011381503 A CN202011381503 A CN 202011381503A CN 112605325 B CN112605325 B CN 112605325B
Authority
CN
China
Prior art keywords
blank
hole
inclined hole
eccentric forging
eccentric
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN202011381503.XA
Other languages
English (en)
Other versions
CN112605325A (zh
Inventor
赵晓光
张明桥
冉雄波
付朝政
傅明娇
李卓林
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guizhou Aerospace Xinli Technology Co ltd
Original Assignee
Guizhou Aerospace Xinli Technology Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guizhou Aerospace Xinli Technology Co ltd filed Critical Guizhou Aerospace Xinli Technology Co ltd
Priority to CN202011381503.XA priority Critical patent/CN112605325B/zh
Publication of CN112605325A publication Critical patent/CN112605325A/zh
Application granted granted Critical
Publication of CN112605325B publication Critical patent/CN112605325B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种偏心锻件成型工艺，使用了偏心锻件成型模具结构进行，步骤包括如下：步骤一、取316H奥氏体材质的胚料，胚料的外径尺寸根据和成型后的外径尺寸比变形量在18％～20％取，而后加温至1050℃±5℃；步骤二、胚料底部经斜孔顶部的倒角挤压至斜孔内，胚料小端整体拔长在斜孔内完成变形，此时，闷孔的斜孔内胚料小端温度约为1000℃，沿着导热孔的热空气保证胚料大端温度为约980℃±0.5℃；步骤三、以在斜孔内成型的小端为基础，使胚料大端发生镦粗变形，使得偏心锻件的大端成型，变形量为25％～30％，胚料大端完全将导热孔填充完毕，取出偏心锻件直接进行入水冷却，得到满足要求的大角度偏心锻件，解决了机械加工表面晶粒度容易长大的问题。

Description

一种偏心锻件成型工艺
技术领域
本发明涉及一种偏心锻件成型工艺，属于锻件成型技术领域。
背景技术
对于使用316H奥氏体不锈钢制成的偏心锻件，偏心锻件的结构参见图1至图2所示，目前对偏心锻件的加工工艺是：取316H奥氏体规则的圆棒或者矩形锻件，通过机械加工成型，在加工时，316H奥氏体不锈钢变形抗力大，在机械加工时存在变形升温，偏心锻件表面的晶粒度在高温下容易长大，生产后的偏心锻件力学性能发生改变。
发明内容
为解决上述技术问题，本发明提供了一种偏心锻件成型工艺。
本发明通过以下技术方案得以实现。
本发明提供的一种偏心锻件成型工艺，使用了偏心锻件成型模具结构进行，步骤包括如下：
步骤一、取316H奥氏体材质的胚料，胚料的外径尺寸根据和成型后的外径尺寸比变形量在18％～20％取，而后加温至1050℃±5℃；
步骤二、胚料底部经斜孔顶部的倒角挤压至斜孔内，胚料小端整体拔长在斜孔内完成变形，此时，闷孔的斜孔内胚料小端温度约为1000℃，沿着导热孔的热空气保证胚料大端温度为约980℃±0.5℃；
步骤三、以在斜孔内成型的小端为基础，使胚料大端发生镦粗变形，使得偏心锻件的大端成型，变形量为25％～30％，胚料大端完全将导热孔填充完毕，取出偏心锻件直接进行入水冷却，得到满足要求的大角度偏心锻件。
本发明的有益效果在于：由于在模具块内的斜孔及导热孔一次成型，解决了机械加工成型偏心锻件表面的晶粒度在高温下容易长大的问题，避免了偏心锻件力学性能发生改变。
附图说明
图1是偏心锻件主视图；
图2是图1偏心锻件的俯视图；
图3是本发明模具块与偏心锻件成型状态剖面图；
图4是本发明偏心锻件在模具块内成型受力分析；
图中：1-模具块；11-斜孔；12-导热孔；2-胚料小端；3-胚料大端。
具体实施方式
下面进一步描述本发明的技术方案，但要求保护的范围并不局限于所述。
参见图3至图4所示。
本发明的一种偏心锻件成型模具结构，包括：模具块1，模具块1上设用供偏心锻件变形成型的斜孔11。
模具块1放在锻造液压机上，将胚料加温后，对准模具块1上的斜孔11进行一次锻造成型，而后水冷成型，解决了316H奥氏体为规则的圆棒或者矩形锻件机械加工成型生产效率低的问题，提高了生产效率。
所述斜孔11底部为密封的闷孔，先变形的偏心锻件底部的温度在闷孔内对模具块1进行加热膨胀，加快偏心锻件在斜孔11内的变形速率。
所述斜孔11的顶端模具块1体上设用导热孔12，导热孔12直径大于斜孔11及偏心锻件的胚料，胚料在导热孔12与斜孔11接触处发生变形，变形及胚料本身散发的热量沿着导热孔12不会向四方直接散发到空气中，而是沿着导热孔12对未变形的胚料进行保温，避免未变形的胚料散热而过快冷却。
所述斜孔11顶部的中心点与导热孔12中心点重合，保证胚料变形成型后的偏心锻件的零件形状和尺寸。
所述导热孔12顶部边为倒角斜边，避免出现棱边对操作工人刮伤。
所述斜孔11顶边与导热孔12底边交接处为倒角斜边，便于对胚料进入提供导向。
所述模具块1外部底面为平面，便于放置在锻造液压机上进行稳定受力。
所述模具块1外部两个相对的两个侧面为平面，便于在锻造液压机进行加持固定。
一种偏心锻件成型工艺，使用了偏心锻件成型模具结构进行，步骤包括如下：
步骤一、取316H奥氏体材质的胚料，胚料的外径尺寸根据和成型后的外径尺寸比变形量在18％～20％取，而后加温至1050℃±5℃；
步骤二、胚料底部经斜孔11顶部的倒角挤压至斜孔11内，胚料小端2整体拔长在斜孔11内完成变形，此时，闷孔的斜孔11内胚料小端2温度约为1000℃，沿着导热孔12的热空气保证胚料大端温度为约980℃±0.5℃；
步骤三、以在斜孔11内成型的小端为基础，使胚料大端发生镦粗变形，使得偏心锻件的大端成型，变形量为25％～30％，胚料大端3完全将导热孔12填充完毕，取出偏心锻件直接进行入水冷却，得到满足要求的大角度偏心锻件。
由于在模具块1内的斜孔11及导热孔12一次成型，解决了机械加工成型偏心锻件表面的晶粒度在高温下容易长大的问题，避免了偏心锻件力学性能发生改变。

Claims (2)

1.一种偏心锻件成型工艺，使用了偏心锻件成型模具结构进行，其特征在于，
所述偏心锻件成型模具结构，包括：模具块(1)，模具块(1)上设用供偏心锻件变形成型的斜孔(11)；
所述斜孔(11)底部为密封的闷孔；
所述斜孔(11)的顶端模具块(1)体上设用导热孔(12)，导热孔(12)直径大于斜孔(11)及偏心锻件的胚料；
所述斜孔(11)顶边与导热孔(12)底边交接处为倒角斜边；
步骤包括如下：
步骤一、取316H奥氏体材质的胚料，而后加温至1050℃±5℃；
步骤二、胚料底部经斜孔(11)顶部的倒角挤压至斜孔(11)内，胚料小端(2)整体拔长在斜孔(11)内完成变形，此时，为密封的闷孔形式的斜孔(11)内胚料小端(2)温度为1000℃，沿着导热孔(12)的热空气保证胚料大端温度为980℃±0.5℃；
步骤三、以在斜孔(11)内成型的小端为基础，使胚料大端发生镦粗变形，使得偏心锻件的大端成型，变形量为25％～30％，胚料大端(3)完全将导热孔(12)填充完毕，取出水冷。
2.如权利要求1所述的偏心锻件成型工艺，其特征在于：在所述步骤一中，胚料的外径尺寸根据和成型后的外径尺寸比变形量在18％～20％取。
CN202011381503.XA 2020-11-30 2020-11-30 一种偏心锻件成型工艺 Active CN112605325B (zh)