CN112593221A - 一种抗氧化的铝合金表面处理剂 - Google Patents
一种抗氧化的铝合金表面处理剂 Download PDFInfo
- Publication number
- CN112593221A CN112593221A CN202011451285.2A CN202011451285A CN112593221A CN 112593221 A CN112593221 A CN 112593221A CN 202011451285 A CN202011451285 A CN 202011451285A CN 112593221 A CN112593221 A CN 112593221A
- Authority
- CN
- China
- Prior art keywords
- acid
- aluminum alloy
- alloy surface
- oxidation
- treating agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种抗氧化的铝合金表面处理剂，所述抗氧化的铝合金表面处理剂由以下质量百分含量的原料组成，5％～10％的氟化物、2％～7％的氧化剂、3％～8％的无机盐、3％～7％的稳定剂、0.5％～5％的成膜助剂、0.5％～5％的缓蚀剂以及水56％～88％混合而成，所述成膜助剂，具体为氟硼酸和氟硅酸的混合物，并且氟硼酸、和氟硅酸的比例为1:1，所述稳定剂为有机酸，具体为油酸和丙二酸的混合物，并且油酸和丙二酸的比例为1.5：1，所述缓蚀剂具体为柠檬酸铵和羟基乙酸，本发明涉及金属表面处理技术领域。该抗氧化的铝合金表面处理剂，解决了现有的铝合金表面抗氧化处理剂在颜色和形成保护膜的致密性上均有不足，且配置过程繁琐，污染性较强的问题。
Description
技术领域
本发明涉及金属表面处理技术领域，具体为一种抗氧化的铝合金表面处理剂。
背景技术
铝材和铝合金制品在使用或存放过程中其表面较为容易氧化，生成一层白色物质附着其表面，不仅影响美观也影响强度，所以优质的工业铝合金型材厂家都会在型材表面进行抗氧化处理。
现有技术进行抗氧化处理得当方法一般是极氧化哑光表面，就是通过处理剂对铝合金的表面进行处理，与其反应生成一层保护膜，起到隔绝空气和水的作用，但是现有的铝合金表面抗氧化处理剂在颜色和形成保护膜的致密性上均有不足，且配置过程繁琐，污染性较强。
发明内容
针对现有技术的不足，本发明提供了一种抗氧化的铝合金表面处理剂，解决了现有的铝合金表面抗氧化处理剂在颜色和形成保护膜的致密性上均有不足，且配置过程繁琐，污染性较强的问题。
为实现以上目的，本发明通过以下技术方案予以实现：一种抗氧化的铝合金表面处理剂，所述抗氧化的铝合金表面处理剂由以下质量百分含量的原料组成，5％～10％的氟化物、2％～7％的氧化剂、3％～8％的无机盐、3％～7％的稳定剂、0.5％～5％的成膜助剂、0.5％～5％的缓蚀剂以及水56％～88％混合而成。
优选的：所述成膜助剂，具体为氟硼酸和氟硅酸的混合物，并且氟硼酸、和氟硅酸的比例为1:1。
优选的：所述稳定剂为有机酸，具体为油酸和丙二酸的混合物，并且油酸和丙二酸的比例为1.5：1。
优选的：所述缓蚀剂具体为柠檬酸铵和羟基乙酸，并且柠檬酸铵和羟基乙酸的比例为1:1。
优选的：所述氟化物具体为氟化钠或者氟化镁，所述氧化剂具体为高锰酸钾。
优选的：所述无机盐为硝酸盐，具体为硝酸钠或者硝酸镁，配置溶液的水采用去离子水。
有益效果
本发明提供了一种抗氧化的铝合金表面处理剂。具备以下有益效果：
(1)、该抗氧化的铝合金表面处理剂，在对铝合金表面进行清洗风干后，将配置好的抗氧化的铝合金表面处理剂均匀的喷淋于铝合金的表面待其风干即可，风干后会在铝合金的表面形成一层钝化膜，且所形成膜薄具有致密均匀、光泽度好和抗氧化耐腐蚀的特性。
(2)、该抗氧化的铝合金表面处理剂，所用的原料从市场容易得到，只要将各种原料采用手工或机械搅匀即可使用，因而像已有技术那样经过繁琐的制作过程，使用方法简单，且污染性较低。
具体实施方式
下面将结合本发明实施例，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
本发明提供一种技术方案：一种抗氧化的铝合金表面处理剂，抗氧化的铝合金表面处理剂由以下质量百分含量的原料组成，5％～10％的氟化物、2％～7％的氧化剂、3％～8％的无机盐、3％～7％的稳定剂、0.5％～5％的成膜助剂、0.5％～5％的缓蚀剂以及水56％～88％混合而成。
进一步的：成膜助剂，具体为氟硼酸和氟硅酸的混合物，并且氟硼酸、和氟硅酸的比例为1:1。
进一步的：稳定剂为有机酸，具体为油酸和丙二酸的混合物，并且油酸和丙二酸的比例为1.5：1。
进一步的：缓蚀剂具体为柠檬酸铵和羟基乙酸，并且柠檬酸铵和羟基乙酸的比例为1:1。
进一步的：氟化物具体为氟化钠或者氟化镁，所述氧化剂具体为高锰酸钾。
进一步的：无机盐为硝酸盐，具体为硝酸钠或者硝酸镁，配置溶液的水采用去离子水。
实施例；采用6％氟化钠、4％高锰酸钾、5％硝酸钠、4％的油酸和丙二酸1.5：1混合物、4％的氟硼酸和氟硅酸1:1混合物、3％柠檬酸铵和羟基乙酸1:1混合物以及78％去离子水混合而成；
使用时，首先对铝合金表面进行清洗，以及去油脂处理，然后用水进行反复冲洗，去除铝合金表面的杂质以及脱脂剂，自然风干后将配置好的抗氧化的铝合金表面处理剂均匀的喷淋于铝合金的表面待其风干即可，风干后会在铝合金的表面形成一层钝化膜，且所形成膜薄具有致密均匀、光泽度好和抗氧化耐腐蚀的特性。
需要说明的是，在本文中，诸如第一和第二等之类的关系术语仅仅用来将一个实体或者操作与另一个实体或操作区分开来，而不一定要求或者暗示这些实体或操作之间存在任何这种实际的关系或者顺序。而且，术语“包括”、“包含”或者其任何其他变体意在涵盖非排他性的包含，从而使得包括一系列要素的过程、方法、物品或者设备不仅包括那些要素，而且还包括没有明确列出的其他要素，或者是还包括为这种过程、方法、物品或者设备所固有的要素。
尽管已经示出和描述了本发明的实施例，对于本领域的普通技术人员而言，可以理解在不脱离本发明的原理和精神的情况下可以对这些实施例进行多种变化、修改、替换和变型，本发明的范围由所附权利要求及其等同物限定。
Claims (6)
1.一种抗氧化的铝合金表面处理剂，其特征在于：所述抗氧化的铝合金表面处理剂由以下质量百分含量的原料组成，5％～10％的氟化物、2％～7％的氧化剂、3％～8％的无机盐、3％～7％的稳定剂、0.5％～5％的成膜助剂、0.5％～5％的缓蚀剂以及水56％～88％混合而成。
2.根据权利要求1所述的一种抗氧化的铝合金表面处理剂，其特征在于：所述成膜助剂，具体为氟硼酸和氟硅酸的混合物，并且氟硼酸、和氟硅酸的比例为1:1。
3.根据权利要求1所述的一种抗氧化的铝合金表面处理剂，其特征在于：所述稳定剂为有机酸，具体为油酸和丙二酸的混合物，并且油酸和丙二酸的比例为1.5：1。
4.根据权利要求1所述的一种抗氧化的铝合金表面处理剂，其特征在于：所述缓蚀剂具体为柠檬酸铵和羟基乙酸，并且柠檬酸铵和羟基乙酸的比例为1:1。
5.根据权利要求1所述的一种抗氧化的铝合金表面处理剂，其特征在于：所述氟化物具体为氟化钠或者氟化镁，所述氧化剂具体为高锰酸钾。
6.根据权利要求1所述的一种抗氧化的铝合金表面处理剂，其特征在于：所述无机盐为硝酸盐，具体为硝酸钠或者硝酸镁，配置溶液的水采用去离子水。