CN112574676A - 一种隔热消音管用粘结剂及其使用方法 - Google Patents
一种隔热消音管用粘结剂及其使用方法 Download PDFInfo
- Publication number
- CN112574676A CN112574676A CN202011349659.XA CN202011349659A CN112574676A CN 112574676 A CN112574676 A CN 112574676A CN 202011349659 A CN202011349659 A CN 202011349659A CN 112574676 A CN112574676 A CN 112574676A
- Authority
- CN
- China
- Prior art keywords
- parts
- heat
- adhesive
- sound
- binder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种隔热消音管用粘结剂及其使用方法,包括三型聚丙烯10‑15份、耐热聚乙烯20‑23份、马来酸酐1‑3份、二氧化硅2‑6份、环氧树脂10~38份、丙丁二烯基三乙氧基硅烷1~5份、固化剂8‑26份、三氮化硼乙胺2‑3份、聚硫橡胶增韧剂2‑2.5份、烯酸树脂5‑25份、导热剂10~41份、促进剂1‑3份和调节剂5‑12份。固化剂用于增加固化效果,通过导热剂可以使吸收的热量快速分散,然后通过所述促进剂和所述调节剂改善粘结剂的交联速度和粘度,使得更加容易进行使用,从而使得本产品具有较好的耐热性能而不容易燃烧和脱落使得使用本粘结剂粘结的消音管可以在高温环境下稳定地工作,从而解决现有的粘结剂热稳定性不好使得消音管在高温环境下消音效果降低的问题。
Description
技术领域
本发明涉及粘结剂领域,尤其涉及一种隔热消音管用粘结剂及其使用方法。
背景技术
在水排放过程中,由于水流量太大,流速太快,会产生较大的噪声,从而会对周围环境造成恶劣影响,因此需要消音管进行排水,消音管一般由管体和外部的隔音层组成,在高温环境下工作时在外部还需要隔热层,他们之间主要由粘接剂进行连接,但是现有的粘结剂热稳定性不好使得隔音层容易脱落,从而会使消音管在高温环境下降低消音效果。
发明内容
本发明的目的在于提供一种隔热消音管用粘结剂及其使用方法,旨在解决现有的粘结剂热稳定性不好使得消音管在高温环境下消音效果降低的问题。
为实现上述目的,第一方面,本发明提供了一种隔热消音管用粘结剂,其组分按重量计包括:三型聚丙烯10-15份、耐热聚乙烯20-23份、马来酸酐1-3份、二氧化硅2-6份、环氧树脂10~38份、丙丁二烯基三乙氧基硅烷1~5份、固化剂8-26份、三氮化硼乙胺2-3份、聚硫橡胶增韧剂2-2.5份、烯酸树脂5-25份、导热剂10~41份、促进剂1-3份和调节剂5-12份。
其中,所述导热剂组分按重量计包括氮化硼8-33份和导热硅脂2-8份。
其中,所述固化剂组分按重量计包括二乙烯基三胺1-3份、二氨基环己烷2-7份、亚甲基双环己烷胺3-10份和三乙烯四胺3-5份。
其中,所述促进剂组分按重量计包括亚磷酸三苯酯0.5-0.8份和水杨酸0.5-2.2份。
其中,所述组分按重量计还包括石墨3-5份、异戊四醇5-7份、二异成四醇2-4份和聚异成四醇2-4份。
其中,所述组分按重量计还包括三聚氰胺焦磷酸2-7份、磷酸胍尿素5-6份、正礴酸10-15份和三聚磷酸8-17份。
第二方面,本发明还提供一种隔热消音管用粘结剂的使用方法,包括:在隔音层内侧敷设隔热消音管用粘结剂;将隔热层和隔音层连接,并采用圆辊滚动压合;在隔热层内侧敷设隔热消音管用粘结剂;将管体和隔热层连接,并采用气压机进行密封压合,保持1-3min。
其中,所述气压机进行密封压合的压力为0.8-1.2MPa。
本发明的一种隔热消音管用粘结剂及其使用方法,三型聚丙烯是由PP和PE由气相法合成的无规共聚聚丙烯,其结构特点是PE分子无规则的链接在PP分子当中,分子量从30万~80万不等,为粘结剂的主材之一;耐热聚乙烯是乙烯(ethylene)和辛烯的单体经茂金属催化共聚而成,具有良好的耐温性能和优良的隔热性能,同样作为粘结剂的主材之一,用于提升粘结剂的耐热性能;马来酸酐又称顺丁烯二酸酐,简称顺酐,是顺丁烯二酸的酸酐,室温下为有酸味的无色或白色固体,用于合成中间体;二氧化硅是一种无机物,化学式为SiO2,硅原子和氧原子长程有序排列形成晶态二氧化硅,短程有序或长程无序排列形成非晶态二氧化硅,用于和耐热聚乙烯进行组合以加强耐热性能;环氧树脂是一种高分子聚合物,是指分子中含有两个以上环氧基团的一类聚合物的总称。它是环氧氯丙烷与双酚A或多元醇的缩聚产物。由于环氧基的化学活性,可用多种含有活泼氢的化合物使其开环,固化交联生成网状结构,因此它是一种热固性树脂,用于增加各种材料之间的粘结性,使得分布更加稳定;固化剂用于增加固化效果,通过导热剂可以使吸收的热量快速分散,然后通过所述促进剂和所述调节剂改善粘结剂的交联速度和粘度,使得更加容易进行使用,从而使得本产品具有较好的耐热性能而不容易燃烧和脱落使得使用本粘结剂粘结的消音管可以在高温环境下稳定地工作,从而解决现有的粘结剂热稳定性不好使得消音管在高温环境下消音效果降低的问题。
附图说明
为了更清楚地说明本发明实施例或现有技术中的技术方案,下面将对实施例或现有技术描述中所需要使用的附图作简单地介绍,显而易见地,下面描述中的附图仅仅是本发明的一些实施例,对于本领域普通技术人员来讲,在不付出创造性劳动的前提下,还可以根据这些附图获得其他的附图。
图1是本发明的一种隔热消音管用粘结剂的使用方法的流程图。
具体实施方式
下面详细描述本发明的实施例,所述实施例的示例在附图中示出,其中自始至终相同或类似的标号表示相同或类似的元件或具有相同或类似功能的元件。下面通过参考附图描述的实施例是示例性的,旨在用于解释本发明,而不能理解为对本发明的限制。
本发明提供一种隔热消音管用粘结剂,其组分按重量计包括:三型聚丙烯10-15份、耐热聚乙烯20-23份、马来酸酐1-3份、二氧化硅2-6份、环氧树脂10~38份、丙丁二烯基三乙氧基硅烷1~5份、固化剂8-26份、三氮化硼乙胺2-3份、聚硫橡胶增韧剂2-2.5份、烯酸树脂5-25份、导热剂10~41份、促进剂1-3份和调节剂5-12份。
在本实施方式中,三型聚丙烯是由PP和PE由气相法合成的无规共聚聚丙烯,其结构特点是PE分子无规则的链接在PP分子当中,分子量从30万~80万不等,为粘结剂的主材之一;耐热聚乙烯是乙烯(ethylene)和辛烯的单体经茂金属催化共聚而成,具有良好的耐温性能和优良的隔热性能,同样作为粘结剂的主材之一,用于提升粘结剂的耐热性能;马来酸酐又称顺丁烯二酸酐,简称顺酐,是顺丁烯二酸的酸酐,室温下为有酸味的无色或白色固体,用于合成中间体;二氧化硅是一种无机物,化学式为SiO2,硅原子和氧原子长程有序排列形成晶态二氧化硅,短程有序或长程无序排列形成非晶态二氧化硅,用于和耐热聚乙烯进行组合以加强耐热性能;环氧树脂是一种高分子聚合物,是指分子中含有两个以上环氧基团的一类聚合物的总称。它是环氧氯丙烷与双酚A或多元醇的缩聚产物。由于环氧基的化学活性,可用多种含有活泼氢的化合物使其开环,固化交联生成网状结构,因此它是一种热固性树脂,用于增加各种材料之间的粘结性,使得分布更加稳定;固化剂用于增加固化效果,通过导热剂可以使吸收的热量快速分散,然后通过所述促进剂和所述调节剂改善粘结剂的交联速度和粘度,使得更加容易进行使用,从而使得本产品具有较好的耐热性能而不容易燃烧和脱落使得使用本粘结剂粘结的消音管可以在高温环境下稳定地工作,从而解决现有的粘结剂热稳定性不好使得消音管在高温环境下消音效果降低的问题。
其中,所述导热剂组分按重量计包括氮化硼8-33份和导热硅脂2-8份。
在本实施方式中,氮化硼通常为黑色、棕色或暗红色晶体,为闪锌矿结构,具有良好的导热性,导热硅脂以有机硅酮为主要原料,添加耐热、导热性能优异的材料,制成的导热型有机硅脂状复合物,通过氮化硼和导热硅脂可以使吸收的热量可以更快地在粘结剂中传递,避免热量集中而造成粘结效果下降,使得可以均匀地受热和散热。
其中,所述固化剂组分按重量计包括二乙烯三胺1-3份、二氨基环己烷2-7份、亚甲基双环己烷胺3-10份和三乙烯四胺3-5份。
在本实施方式中,二乙烯基三胺,是一种有机物,分子量为103.17,是黄色具有吸湿性的透明粘稠液体,有刺激性氨臭,可燃,呈强碱性。溶于水、丙酮、苯、乙醇、甲醇等,难溶于正庚烷,对铜及其合金有腐蚀性,可以作为固化剂,用于增加固化反应,使得反应过程不可逆而形成更加稳定的化合物,二氨基环己烷、亚甲基双环己烷胺和三乙烯四胺用于加强固化效果。
其中,所述促进剂组分按重量计包括亚磷酸三苯酯0.5-0.8份和水杨酸0.5-2.2份。
在本实施方式中,亚磷酸三苯酯是一种性能优良的辅助抗氧剂,添加型阻燃增塑剂及塑料制品防老剂。广泛用于各种聚烯烃、聚酯、ABS树脂、环氧树脂制品中。能有效增强制品的光稳定性及保持其透明度。水杨酸是一种脂溶性的有机酸,化学式为C7H6O3。外观是白色的结晶粉状物,熔点是158~161℃。存在于自然界的柳树皮、白珠树叶及甜桦树中,是重要的精细化工原料,可以提高交联速度。
其中,所述调节剂包括石蜡、微晶蜡、聚乙烯蜡、氧化聚乙烯蜡、聚丙烯蜡。
在本实施方式中,石蜡,又称晶形蜡,是一种溶于汽油、二硫化碳、二甲苯、乙醚、苯、氯仿、四氯化碳、石脑油等一类非极性溶剂,不溶于水和甲醇等极性溶剂。微晶蜡,白色无定形非晶状固体蜡,以C31-70的支链饱和烃为主,含少量的环状、直链烃,无臭无味。不溶于乙醇,略溶于热乙醇,可溶于苯、氯仿、乙醚等;可与各种矿物蜡、植物蜡及热脂肪油互溶。聚乙烯蜡(PE蜡),又称高分子蜡简称聚乙烯蜡。因其优良的耐寒性、耐热性、耐化学性和耐磨性而得到广泛的应用。正常生产中,这部分蜡作为一种添加剂可直接加到聚烯烃加工中,它可以增加产品的光泽和加工性能。作为润滑剂,其化学性质稳定、电性能良好。聚乙烯蜡与聚乙烯、聚丙烯、聚醋酸乙烯、乙丙橡胶、丁基橡胶相溶性好,氧化聚乙烯蜡和聚丙烯蜡与聚乙烯蜡的作用类似,可以加入到粘结剂中对粘结剂的粘度进行调整,使得在使用粘结剂时,使得粘度合适而更加便于对隔热层和消音层进行组装。
其中,所述组分按重量计还包括石墨3-5份、异戊四醇5-7份、二异成四醇2-4份和聚异成四醇2-4份。
在本实施方式中,异戊四醇为白色粉末状洁净,常温下性质稳定,受热会脱水,排气消音管的热量较高,有可能使温度太高使粘结剂燃烧而发生事故,因此设置石墨在粘结剂中,在受热时,粘结剂表面的异戊四醇、二异戊四醇和聚异戊四醇脱水会形成一层炭壳层,而石墨受热会膨胀,从而形成绝热和阻燃层,从而可以防火阻燃,避免粘结剂发生燃烧而引起安全事故。
其中,述组分按重量计还包括三聚氰胺焦磷酸2-7份、磷酸胍尿素5-6份、正礴酸10-15份和三聚磷酸8-17份。
在本实施方式中,三聚氰胺焦磷酸,又称三聚氰胺焦磷酸盐,是一种含氮和含磷的阻燃剂,产品为白色、微细粉体,其突出的优点是热稳定性好,不溶于水,发烟性小,不吸湿。而磷酸胍尿素、正礴酸和三聚磷酸作为活性成分,可以对异戊四醇的碳化成活起催化作用,从而提高碳化效率,
第二方面,本发明还提供一种隔热消音管用粘结剂的使用方法,包括:
S101在隔音层内侧敷设隔热消音管用粘结剂;
使用本粘结剂的隔热消音管由内部的管体、中间的隔热层和外部的隔音层组成,需要在每两层之间使用粘结剂进行贴合以达到好的隔热消音效果。
S102将隔热层和隔音层连接,并采用圆辊滚动压合;
隔热层主要采用石棉材料制成,通过圆辊伸入管内的方式可以充分进行压合,避免留下缝隙。
S103在隔热层内侧敷设隔热消音管用粘结剂;
S104将管体和隔热层连接,并采用气压机进行密封压合,保持1-3min。
采用气压机进行密封压合,控制压合压力为0.8-1.2MPa,并保持一段时间,使得可以充分接触并粘接,从而可以使得隔热消音管达到良好的耐热性和连接性而不容易在高温环境下损坏。
以上所揭露的仅为本发明一种较佳实施例而已,当然不能以此来限定本发明之权利范围,本领域普通技术人员可以理解实现上述实施例的全部或部分流程,并依本发明权利要求所作的等同变化,仍属于发明所涵盖的范围。
Claims (8)
1.一种隔热消音管用粘结剂,其特征在于,
其组分按重量计包括:三型聚丙烯10-15份、耐热聚乙烯20-23份、马来酸酐1-3份、二氧化硅2-6份、环氧树脂10~38份、丙丁二烯基三乙氧基硅烷1~5份、固化剂8-26份、三氮化硼乙胺2-3份、聚硫橡胶增韧剂2-2.5份、烯酸树脂5-25份、导热剂10~41份、促进剂1-3份和调节剂5-12份。
2.如权利要求1所述的一种隔热消音管用粘结剂,其特征在于,
所述导热剂组分按重量计包括氮化硼8-33份和导热硅脂2-8份。
3.如权利要求1所述的一种隔热消音管用粘结剂,其特征在于,
所述固化剂组分按重量计包括二乙烯基三胺1-3份、二氨基环己烷2-7份、亚甲基双环己烷胺3-10份和三乙烯四胺3-5份。
4.如权利要求1所述的一种隔热消音管用粘结剂,其特征在于,
所述促进剂组分按重量计包括亚磷酸三苯酯0.5-0.8份和水杨酸0.5-2.2份。
5.如权利要求1所述的一种隔热消音管用粘结剂,其特征在于,
所述组分按重量计还包括石墨3-5份、异戊四醇5-7份、二异成四醇2-4份和聚异成四醇2-4份。
6.如权利要求5所述的一种隔热消音管用粘结剂,其特征在于,
所述组分按重量计还包括三聚氰胺焦磷酸2-7份、磷酸胍尿素5-6份、正礴酸10-15份和三聚磷酸8-17份。
7.一种隔热消音管用粘结剂的使用方法,其特征在于,
包括:在隔音层内侧敷设隔热消音管用粘结剂;
将隔热层和隔音层连接,并采用圆辊滚动压合;
在隔热层内侧敷设隔热消音管用粘结剂;
将管体和隔热层连接,并采用气压机进行密封压合,保持1-3min。
8.如权利要求7所述的一种隔热消音管用粘结剂及其使用方法,其特征在于,
所述气压机进行密封压合的压力为0.8-1.2MPa。