CN112494345A - 一种含有生物活性玻璃成分牙膏及其制备方法 - Google Patents
一种含有生物活性玻璃成分牙膏及其制备方法 Download PDFInfo
- Publication number
- CN112494345A CN112494345A CN202011446117.4A CN202011446117A CN112494345A CN 112494345 A CN112494345 A CN 112494345A CN 202011446117 A CN202011446117 A CN 202011446117A CN 112494345 A CN112494345 A CN 112494345A
- Authority
- CN
- China
- Prior art keywords
- bioactive glass
- toothpaste
- parts
- humectant
- surfactant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明属于牙膏技术领域，尤其为一种含有生物活性玻璃成分牙膏及其制备方法，包括以下原料：生物活性玻璃、摩擦剂、增溶剂、保湿剂、表面活性剂、甜味剂和防腐剂。本发明通过生物活性玻璃的使用，可以使得牙膏不仅具有抗敏方蛀、固齿美白、止血消炎、清除异味等传统功效，还具有修复浅喁坑点、解决口腔溃疡问题，摩擦剂是牙膏中能够和牙刷共同作用，擦去牙齿表面牙垢，减轻牙渍、牙菌斑、牙结石等外来物质的固体原料成分，增稠剂能够使牙膏具有适当的粘度和稠度，又不感到粘腻；使牙膏具有骨架，挤出的牙膏能停留在牙刷上不会塌下；在刷牙时牙膏容易分散，有良好的扩散性能；而且使膏体细腻光泽，磨料分散均匀，不结粘返粗。
Description
技术领域
本发明涉及牙膏技术领域，具体为一种含有生物活性玻璃成分牙膏及其制备方法。
背景技术
生物活性玻璃是由SiO2、Na2O、CaO和P2O5等组成的硅酸盐玻璃。生物活性玻璃植入人体后，其表面组成和结构随时间变化，形成具有生物活性的碳酸羟基磷灰石层，为骨头和软组织恢复和生长提供了键合界面，可用于骨置换、修复和再生，不引起细胞损伤、无降解产物、无感染性风险，将生物活性玻璃加入牙膏，可以促进口腔溃疡创面的愈合、封闭牙本质小管、消除牙本质过敏症等作用，由申请号为CN201210561547.X，本发明涉及生活日用品领域中的一种终止龋齿病变的牙膏，其组分为摩擦剂、保湿剂、粘合剂、表面活性剂、甜味剂、其他活性添加剂、芳香剂和水，其特征在于其他活性添加剂为鱼脑石粉、煅自然铜、硫酸镁、氧化锌、煅鱼鳞钙、生物活性玻璃、S-羟基磷灰石、β-磷酸三钙和硼砂，以牙膏总重量为100％计，其用量重量百分数为：鱼脑石粉7％～24％，煅自然铜0.3％～1％，硫酸镁1％～1.5％，氧化锌1％～3％，煅鱼鳞钙0～10％，生物活性玻璃0～8％，S-羟基磷灰石0～6％，β-磷酸三钙0～12％，硼砂0～1％。本发明提供的牙膏具有对2、3度龋齿消炎、修复、止痛作用，贮存稳定，可使2、3度龋齿矿化成病变静止状态，有效终止龋齿向4、5度龋齿发展。
目前市面上的牙膏往往存在效果单一，牙体自身修复较差和口腔抗菌不理想等问题，为了解决以上问题，本发明提供一种含有生物活性玻璃成分牙膏及其制备方法。
发明内容
(一)解决的技术问题
针对现有技术的不足，本发明提供了一种含有生物活性玻璃成分牙膏及其制备方法，解决了该牙膏牙体自身修复较差和口腔抗菌不理想的问题。
(二)技术方案
为实现上述目的，本发明提供如下技术方案：一种含有生物活性玻璃成分牙膏，包括以下原料：生物活性玻璃、摩擦剂、增溶剂、保湿剂、表面活性剂、甜味剂和防腐剂。
作为本发明的一种优选技术方案，所述生物活性玻璃1-15份、摩擦剂10-30份、增稠剂0.5-1份、保湿剂10-15份、表面活性剂1-4份、甜味剂0.1-0.5份和防腐剂0.1-0.3份。
作为本发明的一种优选技术方案，所述生物活性玻璃的制备原料按重量份包括40～50份SiO、15～25份CaO、1～30份KO、1～25份NaO和4～6份PO。
作为本发明的一种优选技术方案，所述生物活性玻璃的制备方法为：按所需重量份称取各原料，将各原料混合后置于1400～1500℃温度下熔化60～90min得到均一的混合物，将所述混合物置于常温水浴中使其骤冷，烘干后研磨至粒径为10～50nm的颗粒，即得到所述生物活性玻璃。
作为本发明的一种优选技术方案，所述摩擦剂选自碳酸钙、碳酸氢钙、焦磷酸钙、水合硅酸、二氧化硅、氢氧化铝、珍珠粉、钛白粉中的一种或多种。
作为本发明的一种优选技术方案，所述增溶剂选自聚甘油脂肪酸酯、PEG-60氢化蓖麻油类、聚山梨醇酯类中的至少一种，所述保湿剂选自甘油、丙二醇、聚乙二醇、山梨醇中的一种或多种。
作为本发明的一种优选技术方案，所述表面活性剂选自十二烷基硫酸钠、十二醇硫酸钠、月桂醇硫酸钠中的一种、两种或三种。
作为本发明的一种优选技术方案，所述甜味剂选自甘油、环己胺磺酸钠和糖精钠中的一种或其组合，所述防腐剂选自苯甲酸钠、脱氢醋酸钠和尼泊金酯类中的一种或多种。
本发明还提供一种含有生物活性玻璃成分牙膏的制备方法，包括以下步骤：
S1、按以下各组分及重量份进行备料；
S2、将增稠剂加入配制罐搅拌均匀，再加入保湿剂进行搅拌，且加热温度为40-60℃，然后加入三分之一摩擦剂充分搅拌均匀，得到混合液A；
S3、将生物活性玻璃、表面活性剂、甜味剂和防腐剂依次加入步骤S2混合液A中搅拌均匀，然后将剩余三分之二的摩擦剂加入并搅拌均匀，并停止加热得到混合液B；
S4、最后对混合液B抽真空搅拌，抽真空搅拌时间为1～2h，即可得到生物活性玻璃成分牙膏。
(三)有益效果
与现有技术相比，本发明提供了一种含有生物活性玻璃成分牙膏及其制备方法，具备以下有益效果：
该含有生物活性玻璃成分牙膏及其制备方法，通过生物活性玻璃的使用，可以使得牙膏不仅具有抗敏方蛀、固齿美白、止血消炎、清除异味等传统功效，还具有修复浅喁坑点、解决口腔溃疡问题，摩擦剂是牙膏中能够和牙刷共同作用，擦去牙齿表面牙垢，减轻牙渍、牙菌斑、牙结石等外来物质的固体原料成分，增稠剂能够使牙膏具有适当的粘度和稠度，又不感到粘腻；使牙膏具有骨架，挤出的牙膏能停留在牙刷上不会塌下；在刷牙时牙膏容易分散，有良好的扩散性能；而且使膏体细腻光泽，磨料分散均匀，不结粘返粗，保湿剂可防止牙膏在软管中固化变硬，使膏体具有光泽，并能降低膏体的冰点，使牙膏在寒冷地区亦能正常使用，表面活性剂有洁净、发泡能力，可以渗透、疏松牙面污物，使之成为乳化状或悬乳状，易被牙刷和摩擦剂从牙面上洗刷下来，随漱口水吐掉。此外，它还具有轻微的灭菌作用，并且与摩擦剂具有较好的相容性，甜味剂加入到牙膏中，使刷牙者感到爽口舒适，并有助于减轻口臭，防腐剂可用于预防龋齿和牙周疾病，本发明通过上述特殊配方比制备的生物活性玻璃成分牙膏，具有良好的牙体自身修复和口腔抗菌性能较理想的性能。
附图说明
图1为本发明性能测试图。
具体实施方式
下面将结合本发明实施例中的附图，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例1
请参阅图1，本发明提供以下技术方案：一种含有生物活性玻璃成分牙膏，包括以下原料：生物活性玻璃、摩擦剂、增溶剂、保湿剂、表面活性剂、甜味剂和防腐剂。
具体的，生物活性玻璃5份、摩擦剂10份、增稠剂0.5份、保湿剂10份、表面活性剂2份、甜味剂0.1份和防腐剂0.1份。
具体的，生物活性玻璃的制备原料按重量份包括40份SiO、15份CaO、20份KO、21份NaO和4份PO。
具体的，生物活性玻璃的制备方法为：按所需重量份称取各原料，将各原料混合后置于1400℃温度下熔化60min得到均一的混合物，将所述混合物置于常温水浴中使其骤冷，烘干后研磨至粒径为10nm的颗粒，即得到所述生物活性玻璃。
具体的，摩擦剂为碳酸钙。
具体的，增溶剂为聚甘油脂肪酸酯，保湿剂为聚乙二醇。
具体的，表面活性剂为十二烷基硫酸钠。
具体的，甜味剂为甘油，防腐剂为脱氢醋酸钠。
本发明还提供一种含有生物活性玻璃成分牙膏的制备方法，包括以下步骤：
S1、按以下各组分及重量份进行备料；
S2、将增稠剂加入配制罐搅拌均匀，再加入保湿剂进行搅拌，且加热温度为40℃，然后加入三分之一摩擦剂充分搅拌均匀，得到混合液A；
S3、将生物活性玻璃、表面活性剂、甜味剂和防腐剂依次加入步骤S2混合液A中搅拌均匀，然后将剩余三分之二的摩擦剂加入并搅拌均匀，并停止加热得到混合液B；
S4、最后对混合液B抽真空搅拌，抽真空搅拌时间为1h，即可得到生物活性玻璃成分牙膏。
实施例2
请参阅图1，本发明提供以下技术方案：一种含有生物活性玻璃成分牙膏，包括以下原料：生物活性玻璃、摩擦剂、增溶剂、保湿剂、表面活性剂、甜味剂和防腐剂。
具体的，生物活性玻璃8份、摩擦剂15份、增稠剂0.6份、保湿剂12份、表面活性剂2.2份、甜味剂0.2份和防腐剂0.15份。
具体的，生物活性玻璃的制备原料按重量份包括44份SiO、20份CaO、25份KO、7份NaO和4份PO。
具体的，生物活性玻璃的制备方法为：按所需重量份称取各原料，将各原料混合后置于1420℃温度下熔化70min得到均一的混合物，将所述混合物置于常温水浴中使其骤冷，烘干后研磨至粒径为20nm的颗粒，即得到所述生物活性玻璃。
具体的，摩擦剂为碳酸氢钙。
具体的，增溶剂为PEG-60氢化蓖麻油类，保湿剂位丙二醇。
具体的，表面活性剂为十二醇硫酸钠。
具体的，甜味剂为环己胺磺酸钠，防腐剂为脱氢醋酸钠。
本发明还提供一种含有生物活性玻璃成分牙膏的制备方法，包括以下步骤：
S1、按以下各组分及重量份进行备料；
S2、将增稠剂加入配制罐搅拌均匀，再加入保湿剂进行搅拌，且加热温度为45℃，然后加入三分之一摩擦剂充分搅拌均匀，得到混合液A；
S3、将生物活性玻璃、表面活性剂、甜味剂和防腐剂依次加入步骤S2混合液A中搅拌均匀，然后将剩余三分之二的摩擦剂加入并搅拌均匀，并停止加热得到混合液B；
S4、最后对混合液B抽真空搅拌，抽真空搅拌时间为1.2h，即可得到生物活性玻璃成分牙膏。
实施例3
请参阅图1，本发明提供以下技术方案：一种含有生物活性玻璃成分牙膏，包括以下原料：生物活性玻璃、摩擦剂、增溶剂、保湿剂、表面活性剂、甜味剂和防腐剂。
具体的，生物活性玻璃10份、摩擦剂20份、增稠剂0.8份、保湿剂14份、表面活性剂2.8份、甜味剂0.3份和防腐剂0.2份。
具体的，生物活性玻璃的制备原料按重量份包括45份SiO、20份CaO、20份KO、10份NaO和5份PO。
具体的，生物活性玻璃的制备方法为：按所需重量份称取各原料，将各原料混合后置于1450℃温度下熔化80min得到均一的混合物，将所述混合物置于常温水浴中使其骤冷，烘干后研磨至粒径为30nm的颗粒，即得到所述生物活性玻璃。
具体的，摩擦剂为珍珠粉。
具体的，增溶剂为聚山梨醇酯类，保湿剂为丙二醇。
具体的，表面活性剂为十二醇硫酸钠。
具体的，甜味剂为环己胺磺酸钠，防腐剂为脱氢醋酸钠。
本发明还提供一种含有生物活性玻璃成分牙膏的制备方法，包括以下步骤：
S1、按以下各组分及重量份进行备料；
S2、将增稠剂加入配制罐搅拌均匀，再加入保湿剂进行搅拌，且加热温度为50℃，然后加入三分之一摩擦剂充分搅拌均匀，得到混合液A；
S3、将生物活性玻璃、表面活性剂、甜味剂和防腐剂依次加入步骤S2混合液A中搅拌均匀，然后将剩余三分之二的摩擦剂加入并搅拌均匀，并停止加热得到混合液B；
S4、最后对混合液B抽真空搅拌，抽真空搅拌时间为1.5h，即可得到生物活性玻璃成分牙膏。
实施例4
请参阅图1，本发明提供以下技术方案：一种含有生物活性玻璃成分牙膏，包括以下原料：生物活性玻璃、摩擦剂、增溶剂、保湿剂、表面活性剂、甜味剂和防腐剂。
具体的，生物活性玻璃15份、摩擦剂30份、增稠剂1份、保湿剂15份、表面活性剂3份、甜味剂0.5份和防腐剂0.3份。
具体的，生物活性玻璃的制备原料按重量份包括50份SiO、25份CaO、10份KO、10份NaO和5份PO。
具体的，生物活性玻璃的制备方法为：按所需重量份称取各原料，将各原料混合后置于1500℃温度下熔化90min得到均一的混合物，将所述混合物置于常温水浴中使其骤冷，烘干后研磨至粒径为50nm的颗粒，即得到所述生物活性玻璃。
具体的，摩擦剂为钛白粉。
具体的，增溶剂为聚山梨醇酯类，保湿剂为山梨醇。
具体的，表面活性剂为月桂醇硫酸钠。
具体的，甜味剂为糖精钠，防腐剂为尼泊金酯类。
本发明还提供一种含有生物活性玻璃成分牙膏的制备方法，包括以下步骤：
S1、按以下各组分及重量份进行备料；
S2、将增稠剂加入配制罐搅拌均匀，再加入保湿剂进行搅拌，且加热温度为60℃，然后加入三分之一摩擦剂充分搅拌均匀，得到混合液A；
S3、将生物活性玻璃、表面活性剂、甜味剂和防腐剂依次加入步骤S2混合液A中搅拌均匀，然后将剩余三分之二的摩擦剂加入并搅拌均匀，并停止加热得到混合液B；
S4、最后对混合液B抽真空搅拌，抽真空搅拌时间为2h，即可得到生物活性玻璃成分牙膏。
对比例1
请参阅图1，本发明提供以下技术方案：一种含有生物活性玻璃成分牙膏，包括以下原料：生物活性玻璃、摩擦剂、增溶剂、保湿剂、表面活性剂、甜味剂和防腐剂。
具体的，生物活性玻璃1份、摩擦剂9份、增稠剂0.5份、保湿剂10份、表面活性剂1份、甜味剂0.1份和防腐剂0.4份。
具体的，生物活性玻璃的制备原料按重量份包括40份SiO、15份CaO、20份KO、21份NaO和4份PO。
具体的，生物活性玻璃的制备方法为：按所需重量份称取各原料，将各原料混合后置于1400℃温度下熔化60min得到均一的混合物，将所述混合物置于常温水浴中使其骤冷，烘干后研磨至粒径为10nm的颗粒，即得到所述生物活性玻璃。
具体的，摩擦剂为碳酸钙。
具体的，增溶剂为聚甘油脂肪酸酯，保湿剂为聚乙二醇。
具体的，表面活性剂为十二烷基硫酸钠。
具体的，甜味剂为甘油，防腐剂为脱氢醋酸钠。
本发明还提供一种含有生物活性玻璃成分牙膏的制备方法，包括以下步骤：
S1、按以下各组分及重量份进行备料；
S2、将增稠剂加入配制罐搅拌均匀，再加入保湿剂进行搅拌，且加热温度为40℃，然后加入三分之一摩擦剂充分搅拌均匀，得到混合液A；
S3、将生物活性玻璃、表面活性剂、甜味剂和防腐剂依次加入步骤S2混合液A中搅拌均匀，然后将剩余三分之二的摩擦剂加入并搅拌均匀，并停止加热得到混合液B；
S4、最后对混合液B抽真空搅拌，抽真空搅拌时间为1h，即可得到生物活性玻璃成分牙膏。
通过图1中可知，由实施例1-4制备的牙膏中耐磨值、抗菌值要优于对比例1中的耐磨值和抗菌值，对牙膏耐磨值可根据GB/T35832-2018检测方法进行测试，抗菌测试可参考QB/T2738-2012进行测试，对牙膏功效测试，可选择受试者90人，其中牙渍组30人、有口气组30人和健康组30人，男女各半。随机分为9组，每组10人，受试者分别用实施例1-4和对比例1制备的牙膏刷牙，每日两次，每次2min，一个月后测试，受试者根据使用效果进行感官评价。评分标准如下：10分制，0分最差，10分最好，结果见图1。
本发明由实施例1-4制备的生物活性玻璃成分牙膏，通过生物活性玻璃的使用，可以使得牙膏不仅具有抗敏方蛀、固齿美白、止血消炎、清除异味等传统功效，还具有修复浅喁坑点、解决口腔溃疡问题，摩擦剂是牙膏中能够和牙刷共同作用，擦去牙齿表面牙垢，减轻牙渍、牙菌斑、牙结石等外来物质的固体原料成分，增稠剂能够使牙膏具有适当的粘度和稠度，又不感到粘腻；使牙膏具有骨架，挤出的牙膏能停留在牙刷上不会塌下；在刷牙时牙膏容易分散，有良好的扩散性能；而且使膏体细腻光泽，磨料分散均匀，不结粘返粗，保湿剂可防止牙膏在软管中固化变硬，使膏体具有光泽，并能降低膏体的冰点，使牙膏在寒冷地区亦能正常使用，表面活性剂有洁净、发泡能力，可以渗透、疏松牙面污物，使之成为乳化状或悬乳状，易被牙刷和摩擦剂从牙面上洗刷下来，随漱口水吐掉。此外，它还具有轻微的灭菌作用，并且与摩擦剂具有较好的相容性，甜味剂加入到牙膏中，使刷牙者感到爽口舒适，并有助于减轻口臭，防腐剂可用于预防龋齿和牙周疾病，本发明通过上述特殊配方比制备的生物活性玻璃成分牙膏，具有良好的牙体自身修复和口腔抗菌性能较理想的性能。
最后应说明的是：以上所述仅为本发明的优选实施例而已，并不用于限制本发明，尽管参照前述实施例对本发明进行了详细的说明，对于本领域的技术人员来说，其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换。凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (9)
1.一种含有生物活性玻璃成分牙膏，其特征在于：包括以下原料：生物活性玻璃、摩擦剂、增溶剂、保湿剂、表面活性剂、甜味剂和防腐剂。
2.根据权利要求1所述的一种含有生物活性玻璃成分牙膏，其特征在于：所述生物活性玻璃1-15份、摩擦剂10-30份、增稠剂0.5-1份、保湿剂10-15份、表面活性剂1-4份、甜味剂0.1-0.5份和防腐剂0.1-0.3份。
3.根据权利要求1所述的一种含有生物活性玻璃成分牙膏，其特征在于：所述生物活性玻璃的制备原料按重量份包括40～50份SiO、15～25份CaO、1～30份KO、1～25份NaO和4～6份PO。
4.根据权利要求3所述的一种含有生物活性玻璃成分牙膏，其特征在于：所述生物活性玻璃的制备方法为：按所需重量份称取各原料，将各原料混合后置于1400～1500℃温度下熔化60～90min得到均一的混合物，将所述混合物置于常温水浴中使其骤冷，烘干后研磨至粒径为10～50nm的颗粒，即得到所述生物活性玻璃。
5.根据权利要求1所述的一种含有生物活性玻璃成分牙膏，其特征在于：所述摩擦剂选自碳酸钙、碳酸氢钙、焦磷酸钙、水合硅酸、二氧化硅、氢氧化铝、珍珠粉、钛白粉中的一种或多种。
6.根据权利要求1所述的一种含有生物活性玻璃成分牙膏，其特征在于：所述增溶剂选自聚甘油脂肪酸酯、PEG-60氢化蓖麻油类、聚山梨醇酯类中的至少一种，所述保湿剂选自甘油、丙二醇、聚乙二醇、山梨醇中的一种或多种。
7.根据权利要求1所述的一种含有生物活性玻璃成分牙膏，其特征在于：所述表面活性剂选自十二烷基硫酸钠、十二醇硫酸钠、月桂醇硫酸钠中的一种、两种或三种。
8.根据权利要求1所述的一种含有生物活性玻璃成分牙膏，其特征在于：所述甜味剂选自甘油、环己胺磺酸钠和糖精钠中的一种或其组合，所述防腐剂选自苯甲酸钠、脱氢醋酸钠和尼泊金酯类中的一种或多种。
9.根据权利要求1-8任一项所述的一种含有生物活性玻璃成分牙膏的制备方法，其特征在于：包括以下步骤：
S1、按以下各组分及重量份进行备料；
S2、将增稠剂加入配制罐搅拌均匀，再加入保湿剂进行搅拌，且加热温度为40-60℃，然后加入三分之一摩擦剂充分搅拌均匀，得到混合液A；
S3、将生物活性玻璃、表面活性剂、甜味剂和防腐剂依次加入步骤S2混合液A中搅拌均匀，然后将剩余三分之二的摩擦剂加入并搅拌均匀，并停止加热得到混合液B；
S4、最后对混合液B抽真空搅拌，抽真空搅拌时间为1～2h，即可得到生物活性玻璃成分牙膏。