CN112457742A - Preparation method of 3D artistic floor - Google Patents
Preparation method of 3D artistic floor Download PDFInfo
- Publication number
- CN112457742A CN112457742A CN202011292807.9A CN202011292807A CN112457742A CN 112457742 A CN112457742 A CN 112457742A CN 202011292807 A CN202011292807 A CN 202011292807A CN 112457742 A CN112457742 A CN 112457742A
- Authority
- CN
- China
- Prior art keywords
- floor
- artistic
- primer
- parts
- component
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a preparation method of a 3D artistic floor, belonging to the technical field of artistic floors, wherein the preparation method comprises the steps of uniformly mixing a primer and a curing agent according to the mass ratio of 2:1, and adding different color pastes in two parts to obtain A, B components; paving the component A on the ground to form a floor primer, spraying the component B on the floor primer, and naturally curing to obtain a 3D artistic floor; the primer comprises an epoxy resin dispersion, dipropylene glycol butyl ether, a wetting agent, a defoaming agent, 5% RD sol, a thickening agent and a pearlescent filler. The preparation method can form blocky textures with different sizes, the pearl powder in the blocky textures is scattered from the center to the periphery to form a raised 3D effect, so that the cured artistic floor can visually present a 3D stereoscopic effect, and meanwhile, the surface is flat and smooth, and the 3D stereoscopic effect which cannot be presented by a common artistic floor is presented.
Description
Technical Field
The invention belongs to the technical field of artistic terraces, and particularly relates to a preparation method of a 3D artistic terrace.
Background
The terrace is a ground which is constructed and treated by using specific materials and processes and presents certain decoration and functionality. Common epoxy self-leveling terraces, carborundum wear-resistant terraces, epoxy terrazzo terraces, cement-based terrazzo, epoxy color sand terraces, epoxy anti-static terraces, epoxy anti-skid terraces, polyurea anti-corrosion terraces, polyurethane terraces, silicon PU terraces, concrete sealing curing agent terraces and the like. The ground that utilizes the terrace to lay compares in the ground that ordinary ceramic tile laid, and the seam is few, the wholeness is strong, changes in the cleaning and disinfecting, and is long shorter when laying the time of being under construction. The artistic floor refers to a floor with a strong decorative effect, and can be laid in shopping malls, hotels, office buildings and other areas. Terrace on the market at present can not present the 3D effect after laying.
Disclosure of Invention
In order to overcome the defects of the prior art, the technical problems to be solved by the invention are as follows: the preparation method of the 3D artistic floor capable of generating the 3D effect is provided.
In order to solve the technical problems, the invention adopts the technical scheme that: a preparation method of a 3D artistic floor comprises the following steps:
step 1, uniformly mixing a primer and a curing agent according to a mass ratio of 2:1, then evenly dividing the mixture into two parts, and respectively adding different color pastes to obtain a component A and a component B;
step 2, paving the component A on the ground to form a floor primer, then spraying the component B on the floor primer, and naturally curing to obtain the 3D artistic floor;
the primer comprises, by weight, 800-1000 parts of epoxy resin dispersoid, 50-100 parts of dipropylene glycol butyl ether, 1-10 parts of wetting agent, 1-10 parts of defoaming agent, 50-100 parts of 5% RD sol, 10-100 parts of thickening agent and 5-50 parts of pearlescent filler;
the curing agent is an epoxy resin curing agent.
The invention has the beneficial effects that: according to the preparation method of the 3D artistic floor, the 5% of RD sol and the pearl filler are added into the primer, the RD sol can wrap the pearl filler, the wrapped pearl filler can be refracted and reflected by magnesium in a hexahedral structure and silicon in an octahedral structure in the RD sol through light, blocky textures with different sizes can be formed after point spraying, pearl powder in the blocky textures is scattered from the center to the periphery to form a raised 3D effect, so that the cured artistic floor can visually present a 3D stereoscopic effect, the surface is flat and smooth, and the 3D stereoscopic effect which cannot be presented by a common artistic floor is presented.
Drawings
Fig. 1 shows a 3D art floor prepared by the method for preparing a 3D art floor according to the embodiment of the present invention;
fig. 2 shows a 3D art floor prepared by the method for preparing a 3D art floor according to the embodiment of the present invention;
fig. 3 shows a 3D art floor prepared by the method for preparing a 3D art floor according to the embodiment of the present invention;
fig. 4 shows a 3D art floor prepared by the preparation method of the 3D art floor according to the embodiment of the invention.
Detailed Description
In order to explain technical contents, achieved objects, and effects of the present invention in detail, the following description is made with reference to the accompanying drawings in combination with the embodiments.
The invention discloses a preparation method of a 3D artistic floor, which comprises the following steps:
step 1, uniformly mixing a primer and a curing agent according to a mass ratio of 2:1, then evenly dividing the mixture into two parts, and respectively adding different color pastes to obtain a component A and a component B;
step 2, paving the component A on the ground to form a floor primer, then spraying the component B on the floor primer, and naturally curing to obtain the 3D artistic floor;
the primer comprises, by weight, 800-1000 parts of epoxy resin dispersoid, 50-100 parts of dipropylene glycol butyl ether, 1-10 parts of wetting agent, 1-10 parts of defoaming agent, 50-100 parts of 5% RD sol, 10-100 parts of thickening agent and 5-50 parts of pearlescent filler;
the curing agent is an epoxy resin curing agent.
From the above description, the beneficial effects of the present invention are: according to the preparation method of the 3D artistic floor, 5% of RD sol and pearl filler are added into the primer, the RD sol can wrap the pearl filler, the wrapped pearl filler can be refracted and reflected by magnesium in a hexahedral structure and silicon in an octahedral structure in the RD sol through light, blocky textures with different sizes can be formed after spot spraying, pearl powder in the blocky textures is scattered from the center to the periphery to form a raised 3D effect, so that the cured artistic floor can visually present a 3D stereoscopic effect, and meanwhile, the surface is flat and smooth, and the 3D stereoscopic effect which cannot be presented by a common artistic floor is presented; by selecting the specific epoxy resin dispersion, the excellent self-leveling performance of the system can be provided, and finally the self-leveling can form a smooth plane while the lumpy 3D texture can be kept without being blurred and deformed.
Further, the epoxy resin dispersion is
0901 epoxy resin dispersion.
Further, the wetting agent is SURFYNOL 104E wetting agent.
Further, the antifoaming agent is a RHODOLINE DF691 antifoaming agent.
Further, the 5% RD sol consists of 5% RD rubber powder, 0.1% preservative and the balance of water, wherein the RD rubber powder is LAPONITE RD.
LAPONITE RD rubber powder has excellent thixotropy and yield value, independent slab structure can be produced after the fine slab-shaped structure is dispersed in water, different slab edges have different charges, a small amount of divalent cations exist after sol is formed in water, the mutual connection of the edges between slabs can be promoted, then a 'card house-shaped structure' is formed, the pearlescent filler is wrapped in the slab-shaped structure, and the three-dimensional effect is produced through refraction and reflection of magnesium in a hexahedral structure and silicon in an octahedral structure.
Further, the thickener is a U905 thickener.
Further, the pearlescent filler is KC8100 color pearlescent pigment.
As can be appreciated from the above description,
example 1:
the preparation method of the 3D artistic floor comprises the following steps:
step 1, uniformly mixing a primer and a curing agent according to a mass ratio of 2:1, then evenly dividing the mixture into two parts, and respectively adding different color pastes to obtain a component A (white) and a component B (blue);
step 2, paving the component A on the ground to form a floor primer, then spraying the component B on the floor primer, and naturally curing to obtain a 3D artistic floor as shown in figure 1;
the primer comprises 800kg of
0901 epoxy resin dispersion, 50kg DPn, 1kg SURFYNOL 104E wetting agent, 3kg RHODOLINE DF691 defoamer, 50kg 5% RD sol, 30kg U905 thickener and 20kg KC8100 color pearlescent pigment;
the 5% RD sol consists of 5% RD rubber powder, 0.1% LEX preservative and the balance of water, wherein the RD rubber powder is LAPONITE RD;
the curing agent is
332 curing agent.
Example 2:
the preparation method of the 3D artistic floor comprises the following steps:
step 1, uniformly mixing a primer and a curing agent according to a mass ratio of 2:1, then evenly dividing the mixture into two parts, and respectively adding white and blue color pastes to obtain a component A (white) and a component B (black);
step 2, paving the component A on the ground to form a floor primer, then spraying the component B on the floor primer, and naturally curing to obtain a 3D artistic floor as shown in figure 2;
the primer comprises 900kg of
0901 epoxy resin Dispersion, 80kg DPn, 5kg SURFYNOL 104E wetting agent, 1kg RHODOLINE DF691 defoaming agent, 70kg 5% RD sol, 10kgU905 thickener and 5kg of KC8100 color pearlescent pigment;
the 5% RD sol consists of 5% RD rubber powder, 0.1% LEX preservative and the balance of water, wherein the RD rubber powder is LAPONITE RD;
the curing agent is
332 curing agent.
Example 3:
the preparation method of the 3D artistic floor comprises the following steps:
step 1, uniformly mixing a primer and a curing agent according to a mass ratio of 2:1, then evenly dividing the mixture into two parts, and respectively adding white and black color pastes to obtain a component A (white) and a component B (black);
step 2, paving the component A on the ground to form a floor primer, then spraying the component B on the floor primer, and naturally curing to obtain a 3D artistic floor as shown in figure 3;
the primer comprises 900kg of
0901 epoxy resin dispersion, 90kg DPn, 10kg SURFYNOL 104E wetting agent, 9kg RHODOLINE DF691 defoamer, 90kg 5% RD sol, 100kg U905 thickener and 40kg KC8100 color pearlescent pigment;
the 5% RD sol consists of 5% RD rubber powder, 0.1% LEX preservative and the balance of water, wherein the RD rubber powder is LAPONITE RD;
the curing agent is
332 curing agent.
Example 4:
the preparation method of the 3D artistic floor comprises the following steps:
step 1, uniformly mixing a primer and a curing agent according to a mass ratio of 2:1, then evenly dividing the mixture into two parts, and adding white and yellow-green color paste into one part to obtain a component A (white) and a component B (yellow-green);
step 2, paving the component A on the ground to form a floor primer, then spraying the component B on the floor primer, and naturally curing to obtain a 3D artistic floor as shown in figure 4;
the primer comprises 1000kg of
0901 epoxy resin dispersion, 100kg DPn, 8kg SURFYNOL 104E wetting agent, 10kg RHODOLINE DF691 defoamer, 100kg 5% RD sol, 90kg U905 thickener and 50kg KC8100 color pearlescent pigment;
the 5% RD sol consists of 5% RD rubber powder, 0.1% LEX preservative and the balance of water, wherein the RD rubber powder is LAPONITE RD;
the curing agent is
332 curing agent.
The 3D artistic floor obtained in the embodiment 1-4 is detected to meet the standard of GB 50209-2002.
Comparative example 1:
comparative example 1 differs from example 1 only in that 5% RD rubber powder was not added. The obtained artistic terrace has no third dimension, and the edge of the component B is gradually mixed with the component A after the component B is sprayed.
Comparative example 2:
comparative example 2 differed from example 1 only in that an equivalent amount of 8% RD sol was used instead of 5% RD sol, the 8% RD sol powder consisting of 8% RD sol powder, 0.1% LEX preservative, and the balance water. In the process of preparing the artistic terrace, the component B can not be spread out after point spraying and can not smoothly form blocky textures.
In summary, according to the preparation method of the 3D artistic floor provided by the invention, 5% of RD sol and pearlescent filler are added into the primer, the RD sol can wrap the pearlescent filler, the wrapped pearlescent filler can be refracted and reflected by magnesium in a hexahedral structure and silicon in an octahedral structure in the RD sol through light, blocky textures with different sizes can be formed after spot spraying, and the pearlescent powder in the blocky textures is scattered from the center to the periphery to form a raised 3D effect, so that the cured artistic floor can visually present a 3D stereoscopic effect, and meanwhile, the surface is flat and smooth, and a 3D stereoscopic effect which cannot be presented by a common artistic floor is presented.
The above description is only an embodiment of the present invention, and not intended to limit the scope of the present invention, and all equivalent changes made by using the contents of the present specification and the drawings, or applied directly or indirectly to the related technical fields, are included in the scope of the present invention.
Claims (7)
1. The preparation method of the 3D artistic floor is characterized by comprising the following steps of:
step 1, uniformly mixing a primer and a curing agent according to a mass ratio of 2:1, then evenly dividing the mixture into two parts, and respectively adding different color pastes to obtain a component A and a component B;
step 2, paving the component A on the ground to form a floor primer, then spraying the component B on the floor primer, and naturally curing to obtain the 3D artistic floor;
the primer comprises, by weight, 800-1000 parts of epoxy resin dispersoid, 50-100 parts of dipropylene glycol butyl ether, 1-10 parts of wetting agent, 1-10 parts of defoaming agent, 50-100 parts of 5% RD sol, 10-100 parts of thickening agent and 5-50 parts of pearlescent filler;
the curing agent is an epoxy resin curing agent.
2. The method for preparing a 3D artistic floor according to claim 1, wherein the epoxy resin dispersion is
0901 epoxy resin dispersion.
3. The method for preparing a 3D artistic floor as claimed in claim 1, wherein the wetting agent is SURFYNOL 104E wetting agent.
4. The method for preparing a 3D artistic floor according to claim 1, wherein the defoamer is a RHODOLINE DF691 defoamer.
5. The preparation method of the 3D artistic floor as claimed in claim 1, wherein the 5% RD sol consists of 5% RD glue powder, 0.1% preservative and the balance of water, and the RD glue powder is LAPONITE RD.
6. The method for preparing a 3D artistic floor according to claim 1, wherein the thickener is a U905 thickener.
7. The preparation method of the 3D artistic floor, according to claim 1, characterized in that the pearlescent filler is KC8100 color pearlescent pigment.