CN108821674A - A kind of ceramic tile bond and preparation method thereof - Google Patents
A kind of ceramic tile bond and preparation method thereof Download PDFInfo
- Publication number
- CN108821674A CN108821674A CN201810478140.8A CN201810478140A CN108821674A CN 108821674 A CN108821674 A CN 108821674A CN 201810478140 A CN201810478140 A CN 201810478140A CN 108821674 A CN108821674 A CN 108821674A
- Authority
- CN
- China
- Prior art keywords
- parts
- ceramic tile
- cellulose ether
- tile bond
- mixture
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of ceramic tile bond and preparation method thereof, the raw material of the binder includes ordinary portland cement, quartz sand, powdered whiting, cellulose ether, land plaster, redispersable latex powder, polyvinyl alcohol, wood fibre, water-reducing agent, defoaming agent and enuatrol.Preparation method is that powdered whiting and land plaster are first modified enhancing with coupling agent, it is added in the mixture of ordinary portland cement and quartz sand again, then cellulose ether, redispersable latex powder, wood fibre, polyvinyl alcohol, water-reducing agent, defoaming agent and enuatrol are sequentially added, ceramic tile adhesive is obtained.Ceramic tile bond of the invention has excellent water resistance, weatherability, solvent resistant and chemical corrosivity, the stickup suitable for various marbles, vitrified tile, ceramic tile, glass.
Description
Technical field
The invention belongs to technical field of construction and decoration materials, and in particular to a kind of ceramic tile bond and preparation method thereof.
Background technique
With the development of national economy, requirement of the people to beauty of architecture is also higher and higher, the walls such as ceramic tile, mosaic tile, mosaic
The requirement of face ornament materials is higher and higher.Some problems of construction and application aspect are also brought as a result, such as construction effect
Rate, useful life longevity and safety etc..The cement mortar that traditional barbola work uses inlays patch, can not meet construction industry hair
The needs of exhibition.
Ceramic tile has a wide range of applications in decorative material for wall surface, and ceramic tile bond majority applied currently on the market is water
The shortcomings that cement mortar, cement mortar, is that cohesive force is weak, durability is poor, is easy to peel off, when stirring at the scene, the mode of thick-layer construction
It not only matches unstable, but also biggish pollution can be caused to environment, speed of application is slow, also will cause the waste of material.For
The problems of traditional cement mortar, it has been proposed that the ceramic tile bond of polymer modification, incorporation polymer can be significantly
The adhesion strength and non-deformability for improving mortar, make a kind of high-quality environment protective type polyalcohol cement basis compoiste adhering material
Material.However, the ceramic tile bond for being added to polymer still remains durability, defect anti-aging, weatherability is poor.
Summary of the invention
The object of the present invention is to provide a kind of ceramic tile bond and preparation method thereof, which has excellent water-fast
Property, weatherability, solvent resistant and chemical corrosivity.
A kind of ceramic tile bond, raw material include in parts by weight：20-40 parts of ordinary portland cement, 5-10 parts of quartz sand,
20-30 parts of powdered whiting, 3-6 parts of cellulose ether, 5-10 parts of land plaster, 9-12 parts of redispersable latex powder, polyvinyl alcohol 2-5
Part, 3-7 parts of wood fibre, 1-2 parts of water-reducing agent, 2-3 parts of defoaming agent, 2-4 parts of enuatrol.
Further, the granularity of the quartz sand is in 20-100 mesh.
Further, the cellulose ether is the mixture of methyl cellulose ether and hydroxypropyl methyl cellulose ether, methyl
The weight ratio of cellulose ether and hydroxypropyl methyl cellulose ether is 1-2：3-5.
Further, the water-reducing agent is sulfonated melamine.
Further, the defoaming agent is mineral oil or silicone oil defoaming agent.
Further, the powdered whiting and land plaster are obtained by coupling agent modified.
The preparation method of above-mentioned ceramic tile bond, includes the following steps：
Step 1, powdered whiting and land plaster are mixed, addition accounts for mixture weight 0.5-1wt.% coupling agent, grinds, obtains
Modified mixture；
Step 2, ordinary portland cement, modified mixture, quartz sand are mixed, is stirred evenly；
Step 3, cellulose ether, redispersable latex powder, wood fibre are added in the mixture that step 2 obtains, is stirred evenly；
Step 4, polyvinyl alcohol, water-reducing agent, defoaming agent and enuatrol are added in the mixture that step 3 obtains, is passed through CO2, fill
Divide sealing and standing 30min after grinding, obtains ceramic tile bond.
Ceramic tile bond of the invention has excellent water resistance, weatherability, solvent resistant and chemical corrosivity, is suitable for each
The stickup of kind marble, vitrified tile, ceramic tile, glass.
Specific embodiment
Embodiment 1
A kind of ceramic tile bond, raw material include in parts by weight：20 parts of ordinary portland cement, 5 parts of quartz sand, powdered whiting
20 parts, 3 parts of cellulose ether, 5 parts of land plaster, 9 parts of redispersable latex powder, 2 parts of polyvinyl alcohol, 3 parts of wood fibre, water-reducing agent 1
Part, 2 parts of defoaming agent, 2 parts of enuatrol.
Wherein, the granularity of the quartz sand has 20-40 mesh and two kinds of 50-70 mesh.
The cellulose ether is the mixture of methyl cellulose ether and hydroxypropyl methyl cellulose ether, methyl cellulose ether and
The weight ratio of hydroxypropyl methyl cellulose ether is 1：3.
The water-reducing agent is sulfonated melamine.The defoaming agent is mineral oil.
The powdered whiting and land plaster are obtained by coupling agent modified.
The preparation method of above-mentioned ceramic tile bond, includes the following steps：
Step 1, powdered whiting and land plaster are mixed, addition accounts for mixture weight 0.5wt.% silane coupling agent, grinds, obtains
To modified mixture；
Step 2, ordinary portland cement, modified mixture, quartz sand are mixed, is stirred evenly；
Step 3, cellulose ether, redispersable latex powder, wood fibre are added in the mixture that step 2 obtains, is stirred evenly；
Step 4, polyvinyl alcohol, water-reducing agent, defoaming agent and enuatrol are added in the mixture that step 3 obtains, is passed through CO2, fill
Divide sealing and standing 30min after grinding, obtains ceramic tile bond.
According to JC/T547-2005《Ceramic wall and floor bricks binder》Standard, gained binder stretch gluing original intensity and are
Stretching adhesive strength after 4.8MPa, immersion is that the stretching adhesive strength after 3.6 MPa, heat ageing is 4.3 MPa, Frozen-thawed cycled
Stretching adhesive strength afterwards is 3.2MPa.
Embodiment 2
A kind of ceramic tile bond, raw material include in parts by weight：30 parts of ordinary portland cement, 7 parts of quartz sand, powdered whiting
24 parts, 5 parts of cellulose ether, 7 parts of land plaster, 10 parts of redispersable latex powder, 3 parts of polyvinyl alcohol, 5 parts of wood fibre, water-reducing agent
1.5 parts, 2.5 parts of defoaming agent, 3 parts of enuatrol.
Wherein, the granularity of the quartz sand has 20-40 mesh and two kinds of 50-70 mesh.
The cellulose ether is the mixture of methyl cellulose ether and hydroxypropyl methyl cellulose ether, methyl cellulose ether and
The weight ratio of hydroxypropyl methyl cellulose ether is 1：4.
The water-reducing agent is sulfonated melamine.The defoaming agent is mineral oil.
The powdered whiting and land plaster are obtained by coupling agent modified.
The preparation method of above-mentioned ceramic tile bond, includes the following steps：
Step 1, powdered whiting and land plaster are mixed, addition accounts for mixture weight 0.5wt.% silane coupling agent, grinds, obtains
To modified mixture；
Step 2, ordinary portland cement, modified mixture, quartz sand are mixed, is stirred evenly；
Step 3, cellulose ether, redispersable latex powder, wood fibre are added in the mixture that step 2 obtains, is stirred evenly；
Step 4, polyvinyl alcohol, water-reducing agent, defoaming agent and enuatrol are added in the mixture that step 3 obtains, is passed through CO2, fill
Divide sealing and standing 30min after grinding, obtains ceramic tile bond.
According to JC/T547-2005《Ceramic wall and floor bricks binder》Standard, gained binder stretch gluing original intensity and are
Stretching adhesive strength after 4.7MPa, immersion is that the stretching adhesive strength after 3.7 MPa, heat ageing is 4.2 MPa, Frozen-thawed cycled
Stretching adhesive strength afterwards is 3.1MPa.
Embodiment 3
A kind of ceramic tile bond, raw material include in parts by weight：40 parts of ordinary portland cement, 10 parts of quartz sand, heavy carbonic acid
30 parts of calcium, 6 parts of cellulose ether, 10 parts of land plaster, 12 parts of redispersable latex powder, 5 parts of polyvinyl alcohol, 7 parts of wood fibre, diminishing
2 parts of agent, 3 parts of defoaming agent, 4 parts of enuatrol.
Wherein, the granularity of the quartz sand has 20-40 mesh and two kinds of 50-70 mesh.
The cellulose ether is the mixture of methyl cellulose ether and hydroxypropyl methyl cellulose ether, methyl cellulose ether and
The weight ratio of hydroxypropyl methyl cellulose ether is 2：5.
The water-reducing agent is sulfonated melamine.The defoaming agent is mineral oil.
The powdered whiting and land plaster are obtained by coupling agent modified.
The preparation method of above-mentioned ceramic tile bond, includes the following steps：
Step 1, powdered whiting and land plaster are mixed, addition accounts for mixture weight 0.5wt.% silane coupling agent, grinds, obtains
To modified mixture；
Step 2, ordinary portland cement, modified mixture, quartz sand are mixed, is stirred evenly；
Step 3, cellulose ether, redispersable latex powder, wood fibre are added in the mixture that step 2 obtains, is stirred evenly；
Step 4, polyvinyl alcohol, water-reducing agent, defoaming agent and enuatrol are added in the mixture that step 3 obtains, is passed through CO2, fill
Divide sealing and standing 30min after grinding, obtains ceramic tile bond.
According to JC/T547-2005《Ceramic wall and floor bricks binder》Standard, gained binder stretch gluing original intensity and are
Stretching adhesive strength after 4.4MPa, immersion is 3.2MPa, the stretching adhesive strength after heat ageing is 4.1 MPa, Frozen-thawed cycled
Stretching adhesive strength afterwards is 3.4MPa.
Claims (7)
1. a kind of ceramic tile bond, it is characterised in that：Raw material includes in parts by weight：20-40 parts of ordinary portland cement, quartz
5-10 parts of sand, 20-30 parts of powdered whiting, 3-6 parts of cellulose ether, 5-10 parts of land plaster, 9-12 parts of redispersable latex powder, gather
2-5 parts of vinyl alcohol, 3-7 parts of wood fibre, 1-2 parts of water-reducing agent, 2-3 parts of defoaming agent, 2-4 parts of enuatrol.
2. ceramic tile bond according to claim 1, it is characterised in that：The granularity of the quartz sand is in 20-100 mesh.
3. ceramic tile bond according to claim 1, it is characterised in that：The cellulose ether is methyl cellulose ether and hydroxyl
The weight ratio of the mixture of propyl methocel ether, methyl cellulose ether and hydroxypropyl methyl cellulose ether is 1-2：3-5.
4. ceramic tile bond according to claim 1, it is characterised in that：The water-reducing agent is sulfonated melamine.
5. ceramic tile bond according to claim 1, it is characterised in that：The defoaming agent is that mineral oil or silicone oil disappear
Infusion.
6. ceramic tile bond according to claim 1, it is characterised in that：The powdered whiting and land plaster are by idol
Connection agent modification obtains.
7. the preparation method of ceramic tile bond described in claim 1, it is characterised in that：Include the following steps：
Step 1, powdered whiting and land plaster are mixed, addition accounts for mixture weight 0.5-1wt.% coupling agent, grinds, obtains
Modified mixture；
Step 2, ordinary portland cement, modified mixture, quartz sand are mixed, is stirred evenly；
Step 3, cellulose ether, redispersable latex powder, wood fibre are added in the mixture that step 2 obtains, is stirred evenly；
Step 4, polyvinyl alcohol, water-reducing agent, defoaming agent and enuatrol are added in the mixture that step 3 obtains, is passed through CO2, sufficiently
Sealing and standing 30min after grinding, obtains ceramic tile bond.