CN112457053B - 一种改性硅酸钙板及其表面处理方法以及应用 - Google Patents

一种改性硅酸钙板及其表面处理方法以及应用 Download PDF

Info

Publication number
CN112457053B
CN112457053B CN202011251691.4A CN202011251691A CN112457053B CN 112457053 B CN112457053 B CN 112457053B CN 202011251691 A CN202011251691 A CN 202011251691A CN 112457053 B CN112457053 B CN 112457053B
Authority
CN
China
Prior art keywords
calcium silicate
silicate board
sizing
modified calcium
drying
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN202011251691.4A
Other languages
English (en)
Other versions
CN112457053A (zh
Inventor
丁永平
顾海兵
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangsu Langyuan Meisheng New Material Technology Co ltd
Original Assignee
Jiangsu Langyuan Meisheng New Material Technology Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangsu Langyuan Meisheng New Material Technology Co ltd filed Critical Jiangsu Langyuan Meisheng New Material Technology Co ltd
Priority to CN202011251691.4A priority Critical patent/CN112457053B/zh
Publication of CN112457053A publication Critical patent/CN112457053A/zh
Priority to US17/614,516 priority patent/US20220348512A1/en
Priority to PCT/CN2021/127223 priority patent/WO2022100453A1/zh
Application granted granted Critical
Publication of CN112457053B publication Critical patent/CN112457053B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种改性硅酸钙板，属于地板、装饰板技术领域，改性方法是将硅酸钙板浸渍于固含量在95%以上的二氧化硅溶液中,完全吸透至饱和,再将浸渍后的硅酸钙板干燥处理；在改性完成的硅酸钙板的任一面上进行施胶硬化，获得硅酸钙板，能使三胺浸渍纸与其直接热压贴合，表结合强度达到1MPa；木皮、防火板等材料与其冷贴，产品剥离强度均符合要求，有效提高了硅酸钙板的实用性。

Description

一种改性硅酸钙板及其表面处理方法以及应用
技术领域
本发明属于地板、装饰板技术领域，尤其涉及复合装饰板材的制备技术。
背景技术
随着人民生活水平的提高，对装饰材料的环保、阻燃、美观等要求愈来愈高。硅酸钙板是一种新颖装饰材料，它的稳定性、阻燃性、无甲醛、低成本等优势越来越迎合市场的需求。
但已知的硅酸钙板，多以无机材料如硅酸钙或碳酸钙等无机材料的粉末制成，更详细地说，以硅酸质与石灰质为主要成分，经制浆、抄制、 蒸养等工序制成，由于在高温高压下反应结晶而成，故实质上为众多的硅酸钙结晶粉末；也或是以水泥、硅沙、石绵等纤维加入添加物经抄取法或流浆法高压蒸养压制而成，然而，由于粉末间的结合力弱，当要在此类硅酸钙板的表面贴覆一表材时，较为靠近表材的粉末易被表材撕起而剥离，使表材难以牢固地贴合，也即表材相当容易被剥离，而细究其原因，即是因为硅酸钙板的结构松散，各粉末间的结合力小于粘胶的粘合力，使拉扯的力量直接传递至较为靠近的粉末，造成表材易将较为靠近的粉末一同剥离，实为施工上的困难之处。
中国专利公告号CN105859323B，公开了一种硅酸钙板表层处理方法，包含以下步骤：一、备一硅酸钙板：其中该硅酸钙板具有相对的一第一面与一第二面；二、涂布第一次水玻璃溶液：在该硅酸钙板的第一面涂布或喷洒重量百分浓度为a的水玻璃溶液，使水玻璃溶液渗入该硅酸钙板一预定厚度；三、涂布第二次水玻璃溶液：在该硅酸钙板的第一面涂布或喷洒重量百分浓度为b的水玻璃溶液，使水玻璃溶液渗入该硅酸钙板一预定厚度；其中，a小于b，且a与b皆分别大于30％但小于55％。该技术方案能使硅酸钙板表层结构密实而易于贴覆表材，表材可牢固地粘贴于硅酸钙板上不易剥离，也是对硅酸钙板的一种改性方法，但其只是简单的在需要与表材贴合的贴合面进行水玻璃涂布，让水玻璃浸入基板表面，长、宽尺寸为2400mm、1200mm的硅酸钙板也只涂布50克至60克，进入的深度只停留在浅表层，只能防止初级剥离，离现在市面上要求的抗剥落，抗弯折的硅酸钙板才存在技术问题，而且发现，这种基材处理后的硅酸钙板，用三胺浸渍纸与其热压是完全粘不住的。
发明内容
本发明针对现有技术的不足，提供了一种可整体强化硅酸钙板的结构和密实度，方便与各种表材复合的改性硅酸钙板以及表层处理方法，能使三胺浸渍纸与基材直接热压贴合，表结合强度达到1MPa；木皮、防火板等材料与其冷贴，产品剥离强度均符合要求，有效提高了硅酸钙板的实用性。
为实现本发明目的，提供了以下技术方案：一种改性硅酸钙板，其特征在于改性方法是：将硅酸钙板浸渍于固含量在95%以上的二氧化硅溶液中,直至完全吸透至饱和,再将浸渍后的硅酸钙板干燥处理。通过完全浸渍基材来改性硅酸钙板，比现有技术中仅在表面涂覆涂层改性相比，提高了基材的内结合强度。
上述改性硅酸钙板的表面处理方法，包括在改性完成的硅酸钙板的任一面上进行施胶硬化，其特征在于施胶硬化包括涂胶、流平渗透、烘干、冷却、抛光。
作为优选，施胶硬化具体为：
（1）第一道施胶:一次涂胶、一次流平渗透、一次烘干、一次冷却、一次抛光；
（2）在第一道施胶后的面上进行第二道施胶:二次涂胶、二次烘干、二次抛光。
作为优选，第一道施胶中一次涂胶的上胶量为：当板材密度在900~950kg/m³，上胶量110-120g/m2；当板材密度在950~1100kg/m³，上胶量在90-100g/m2；当板材密度在1100~1300kg/m³，上胶量75-85g/m2。
作为优选，一次涂胶采用水性双组份环氧胶,与基材有更好的适用性。
作为优选，一次烘干以10~12m/min的速度进烘道，烘道设置温度130~150℃，烘道长度为10~15m。
作为优选，二次涂胶的上胶量为40~50g/m2。
作为优选，二次烘干以8-10m/min的速度进烘道，烘道设置温度130~150℃，烘道长度为10~15m。
作为优选，二次涂胶采用水性丙烯酸胶加固化剂异氰酸酯, 水性丙烯酸胶与异氰酸酯的重量配比为3.5-10：1,最佳配比为6-7:1,强度最高，便于量产化。
为实现本发明目的，提供了一种硅酸钙板的应用，其特征在于任一面上贴覆表材。
作为优选，表材包括：三胺浸渍纸，木皮，防火板。
作为优选，表材的贴覆方法包括高温热压，冷压。
本发明有益效果：
1. 通过对硅酸钙板改性，提高了基材的内结合强度；
2. 通过基材表面的涂胶处理，可使基材与其它各种表材相复合，不仅能使三胺浸渍纸与基材直接热压贴合，表结合强度达到1MPa以上，而且木皮、防火板等材料与其冷贴，产品剥离强度均符合要求，有效提高了硅酸钙板的实用性，适用范围更加广泛。
3. 贴覆表材后的终产品,降低了消费成本，环保无毒。
具体实施方式
实施例1
一种改性硅酸钙板，将硅酸钙板浸渍于固含量在95%以上的二氧化硅溶液中,完全吸透至饱和,再将浸渍后的硅酸钙板干燥处理。
分别对改性前的硅酸钙板和改性后的硅酸钙板进行内结合力检测，改性前为40kg/f，改性后为70 kg/f。
实施例2
将实施例1改性得到的硅酸钙板进行表面处理：即在改性完成的硅酸钙板的任一面上进行施胶硬化：
（1）第一道施胶:一次涂胶、一次流平渗透、一次烘干、一次冷却、一次抛光，第一道施胶中一次涂胶的上胶量为：当板材密度在910kg/m³，上胶量120g/m2，一次涂胶采用水性双组份环氧胶,一次烘干以10m/min的速度进烘道，烘道设置温度150℃，烘道长度为10m。
（2）在第一道施胶后的面上进行第二道施胶:二次涂胶、二次烘干、二次抛光，二次涂胶的上胶量为40g/m2，二次烘干以8m/min的速度进烘道，烘道设置温度150℃，烘道长度为10m，二次涂胶采用水性丙烯酸胶加固化剂异氰酸酯, 水性丙烯酸胶与异氰酸酯的重量配比为3.5：1。
实施例3-7，参考实施例2，第一道施胶和第二道施胶的参数调控如表一。
表一
Figure DEST_PATH_IMAGE001
实施例8-16，在上述实施2-7的硅酸钙板上贴覆表材，对成品进行剥离强度检测，具体见表二。
Figure 639950DEST_PATH_IMAGE002

Claims (7)

1.一种改性硅酸钙板，其特征在于，制备方法包括改性、改性硅酸钙板的表面处理，其中：
改性：将硅酸钙板浸渍于固含量在95%以上的二氧化硅溶液中 ,直至完全吸透至饱和,再将 浸渍后的硅酸钙板干燥处理；
改性硅酸钙板的表面处理：包括在改性完成的硅酸钙板的任一面上进行施胶硬化，施胶硬化包括涂胶、流平渗透、烘干、冷却、抛光。
2.根据权利要求1所述的一种改性硅酸钙板，其特征在于施胶硬化具体为：
（1）第一道施胶:一次涂胶、一次流平渗透、一次烘干、一次冷却、一次抛光；
（2）在第一道施胶后的面上进行第二道施胶:二次涂胶、二次烘干、二次抛光。
3.根据权利要求2所述的一种改性硅酸钙板，其特征在于第一道施胶中一次涂胶的上胶量为：当板材密度在900 ~ 950kg/m³，上胶量110-120g/m2；当板材密度在950 ~ 1100kg/m³，上胶量在90-100g/m2；当板材密度在1100 ~ 1300kg/m³，上胶量75-85g/m2；一次涂胶采用水性双组份环氧胶 ,与基材有更好的适用性，一次烘干以10 ~ 12m/min的速度进烘道，烘道设置温度130 ~ 150℃，烘道长度为10 ~ 15m。
4.根据权利要求2所述的一种改性硅酸钙板，其特征在于二次涂胶的上胶量为40 ~50g/m2。
5.根据权利要求2所述的一种改性硅酸钙板，其特征在于二次烘干以8- 10m/min的速度进烘道，烘道设置温度130 ~ 150℃，烘道长度为10 ~ 15m。
6.根据权利要求2所述的一种改性硅酸钙板，其特征在于二次涂胶采用水性丙烯酸胶加固化剂异氰酸酯 , 水性丙烯酸胶与异氰酸酯的重量配比为3 .5-10：1。
7.根据权利要求6所述的一种改性硅酸钙板，其特征在于水性丙烯酸胶与异氰酸酯的重量配比为6-7:1。
CN202011251691.4A 2020-11-11 2020-11-11 一种改性硅酸钙板及其表面处理方法以及应用 Active CN112457053B (zh)