CN112359464A - Production method of cotton-covered polyester shirt fabric - Google Patents
Production method of cotton-covered polyester shirt fabric Download PDFInfo
- Publication number
- CN112359464A CN112359464A CN202011196386.XA CN202011196386A CN112359464A CN 112359464 A CN112359464 A CN 112359464A CN 202011196386 A CN202011196386 A CN 202011196386A CN 112359464 A CN112359464 A CN 112359464A
- Authority
- CN
- China
- Prior art keywords
- cotton
- temperature
- fabric
- percent
- polyester
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a production method of a fabric, in particular to a production method of a cotton-covered polyester shirt fabric. The process route is as follows: grey cloth preparation → scouring and bleaching → drying → singeing → mercerizing → high temperature dyeing polyester → active dyeing cotton fiber → dehydration scutching → drying → soft finishing → can steaming → inspection and packing. The invention selects polyester cotton core-spun yarn to weave, then carries out pretreatment and dyeing in an overflow dyeing machine, and the subsequent process goes through a wool spinning decating route, and the fabric produced by the method has the advantages that: the yarn structure is formed by wrapping polyester filaments with cotton fibers; the finished product has the advantages that: the polyester filament yarn is wrapped inside the cotton fiber, the cotton fiber is in contact with the skin of a human body when the fabric is worn, the fabric is comfortable and skin-friendly, and the polyester filament yarn is wrapped inside the fabric to form a framework.
Description
Technical Field
The invention relates to a production method of a fabric, in particular to a production method of a cotton-covered polyester shirt fabric.
Background
The conventional shirt fabric is generally produced by weaving pure cotton or polyester-cotton blended yarns, wherein the pure cotton fabric has the advantages of skin friendliness, moisture absorption and comfortable wearing, and has the disadvantages of low strength and poor crease resistance. The polyester-cotton blended fabric has the advantages that the characteristics of low pure cotton strength and poor pure polyester hygroscopicity are made up, but the polyester-cotton blended fabric is not good in skin friendliness when worn next to the skin.
Disclosure of Invention
Aiming at the defects of the prior art, the invention aims to provide a production method of a cotton-covered polyester shirt fabric, the prepared fabric polyester filament yarns are wrapped inside cotton fibers, the cotton fibers are in contact with the skin of a human body when the cotton-covered polyester shirt fabric is worn, the skin is comfortable and the polyester filament yarns are wrapped inside to form a framework, and the finished product of the fabric polyester shirt fabric is high in strength, good in rebound resilience, anti-wrinkle, skin-friendly and stiff and smooth.
The invention relates to a production method of cotton-covered polyester shirt fabric, which comprises the following process routes: grey cloth preparation → scouring and bleaching → drying → singeing → mercerizing → high temperature dyeing polyester → active dyeing cotton fiber → dehydration scutching → drying → soft finishing → can steaming → inspection and packing.
The method comprises the following specific steps:
(1) preparing a grey fabric: the polyester-cotton core-spun yarn plain cloth consists of 50% of terylene and 50% of cotton fiber, wherein the cotton fiber is wound outside the terylene filament, the gram weight is 210g/m, and each cylinder is 800-1200 meters;
(2) boiling and bleaching: treating the fabric by using a high-temperature high-pressure overflow dyeing machine and adopting mixed liquor of caustic soda, hydrogen peroxide, a refined deoiling agent, a high-efficiency penetrating agent and a chelating dispersant;
(3) shaping and drying;
(4) singeing: a natural gas singeing machine is adopted, singeing is carried out on a fire hole in a forward direction and a reverse direction, and the speed is 80-100 m/min;
(5) mercerizing:
(6) dyeing:
the formula of the disperse dye dyed terylene comprises: 0.3 percent of disperse blue, 0.02 percent of disperse orange, 0.04 percent of disperse red jade, 1g/l of acetic acid, 2g/l of level dyeing dispersant and 1g/l of water softener;
the temperature is 130 ℃, and the time is 30-50 min;
the formula of the cotton dyed by the reactive dye comprises the following steps: 0.01 percent of reactive red, 0.02 percent of reactive yellow, 0.21 percent of reactive brilliant blue, 20g/l of anhydrous sodium sulphate, 10g/l of soda ash and 1g/l of water softener;
the temperature is 60 ℃, and the time is 30-50 min;
the soaping formula comprises: soaping agent 1g/l, acetic acid 1g/l, temperature 80 deg.C, time 20 min;
(7) dehydrating and scutching;
(8) shaping and drying;
(9) softening and finishing: the temperature is 160 ℃, the speed is 40m/min, the overfeed is 1%, the hydrophilic softening agent is 20-40g/l, and the moisture absorption and sweat releasing finishing agent is 10-50 g/l;
(10) decating;
(11) and (6) checking and packaging.
Wherein:
in the step (2), the boiling and bleaching specifically comprises the following steps: the high-temperature high-pressure overflow dyeing machine is used, and the mixed solution of 2g/l of caustic soda, 4g/l of hydrogen peroxide, 1.5g/l of refined degreaser, 1g/l of high-efficiency penetrant and 3g/l of chelating dispersant is adopted for processing at the temperature of 100 ℃ for 40 min. The refined deoiling agent is DR-N6, the high-efficiency penetrating agent is TX, and the chelating dispersant is DR-99.
In the step (3), the shaping and drying are carried out at the temperature of 180 ℃ for 30-50s, the speed of 40m/min and the overfeeding is 2%.
In the step (5), the mercerizing is as follows: the treatment is carried out by adopting 220g/l caustic soda solution, and the vehicle speed is 50 m/min.
In the step (6), the soaping agent is a soaping agent 535.
In the step (8), the shaping and drying are carried out at the temperature of 160 ℃, the vehicle speed of 50m/min and the overfeeding is 0.5 percent.
In the step (10), the decating is as follows: a KD series of pot steamers are adopted, the steam temperature is 160 ℃, the pressure is 0.6bar, the steam temperature is 120s from inside to outside, the steam temperature is 150s from outside to inside, and the decating temperature is 100 ℃.
Compared with the prior art, the invention has the following beneficial effects:
the invention selects polyester cotton core-spun yarn to weave, then carries out pretreatment and dyeing in an overflow dyeing machine, and the subsequent process goes through a wool spinning decating route, and the fabric produced by the method has the advantages that: the yarn adopts cotton fiber to wrap the polyester filament yarn, and the finished product has the advantages that: the polyester filament yarn is wrapped inside the cotton fiber, the cotton fiber is in contact with the skin of a human body when the fabric is worn, the fabric is comfortable and skin-friendly, and the polyester filament yarn is wrapped inside the fabric to form a framework.
Detailed Description
The present invention is further illustrated by, but is not limited to, the following examples.
All the starting materials used in the examples are commercially available, except where otherwise indicated.
Example 1
The production method of the cotton-covered polyester shirt fabric comprises the following specific implementation steps:
(1) preparing a grey fabric: the polyester-cotton core-spun yarn plain cloth is composed of 50% of polyester and 50% of cotton fibers, wherein the cotton fibers are wound outside polyester filaments, the gram weight is 210g/m, and each cylinder is 800 meters.
(2) Boiling and bleaching: the high-temperature high-pressure overflow dyeing machine is used, and the mixed solution of 2g/l of caustic soda, 4g/l of hydrogen peroxide, 1.5g/l of refined degreaser (DR-N6), 1g/l of high-efficiency penetrating agent (TX) and 3g/l of chelating dispersant (DR-99) is adopted for treatment, the temperature is 100 ℃, and the time is 40 min.
(3) Shaping and drying: the temperature is 180 ℃, the time is 50s, the vehicle speed is 40m/min, and the overfeeding is 2 percent.
(4) Singeing: a natural gas singeing machine is adopted, singeing is carried out on a fire hole in a forward direction and a reverse direction, and the speed is 80 m/min.
(5) Mercerizing: the treatment is carried out by adopting 220g/l caustic soda solution, and the vehicle speed is 50 m/min.
(6) Dyeing:
the formula of the disperse dye dyed terylene comprises: 0.3 percent of disperse blue, 0.02 percent of disperse orange, 0.04 percent of disperse ruby, 1g/l of acetic acid, 2g/l of level dyeing dispersant and 1g/l of water softener.
The temperature is 130 ℃ and the time is 30 min.
The formula of the cotton dyed by the reactive dye comprises the following steps: 0.01 percent of reactive red, 0.02 percent of reactive yellow, 0.21 percent of reactive brilliant blue, 20g/l of anhydrous sodium sulphate, 10g/l of soda ash and 1g/l of water softener
The temperature is 60 deg.C, and the time is 30 min.
The soaping formula comprises: soaping agent (535)1g/l, acetic acid 1 g/l. The temperature is 80 deg.C, and the time is 20 min.
(7) Dehydrating and scutching;
(8) shaping and drying: the temperature is 160 ℃, the vehicle speed is 50m/min, and the overfeeding is 0.5 percent.
(9) Softening and finishing: the temperature is 160 ℃, the speed is 40m/min, the overfeed is 1%, the hydrophilic softening agent is 20g/l, and the moisture absorption and sweat releasing finishing agent is 20 g/l.
(10) Decating: a KD series of pot steamers are adopted, the steam temperature is 160 ℃, the pressure is 0.6bar, the steam temperature is 120s from inside to outside, the steam temperature is 150s from outside to inside, and the decating temperature is 100 ℃.
(11) And (6) checking and packaging.
Example 2
The production method of the cotton-covered polyester shirt fabric comprises the following specific implementation steps:
(1) preparing a grey fabric: the polyester-cotton core-spun yarn plain cloth is composed of 50% of polyester and 50% of cotton fibers, wherein the cotton fibers are wound outside polyester filaments, the gram weight of the polyester-cotton core-spun yarn plain cloth is 210g/m, and each cylinder is 1200 meters.
(2) Boiling and bleaching: the high-temperature high-pressure overflow dyeing machine is used, and the mixed solution of 2g/l of caustic soda, 4g/l of hydrogen peroxide, 1.5g/l of refined degreaser (DR-N6), 1g/l of high-efficiency penetrating agent (TX) and 3g/l of chelating dispersant (DR-99) is adopted for treatment, the temperature is 100 ℃, and the time is 40 min.
(3) Shaping and drying: the temperature is 180 ℃, the time is 30s, the vehicle speed is 40m/min, and the overfeeding is 2 percent.
(4) Singeing: a natural gas singeing machine is adopted, singeing is carried out on a fire hole in a forward direction and a reverse direction, and the vehicle speed is 100 m/min.
(5) Mercerizing: the treatment is carried out by adopting 220g/l caustic soda solution, and the vehicle speed is 50 m/min.
(6) Dyeing:
the formula of the disperse dye dyed terylene comprises: 0.3 percent of disperse blue, 0.02 percent of disperse orange, 0.04 percent of disperse ruby, 1g/l of acetic acid, 2g/l of level dyeing dispersant and 1g/l of water softener.
The temperature is 130 ℃ and the time is 50 min.
The formula of the cotton dyed by the reactive dye comprises the following steps: 0.01 percent of reactive red, 0.02 percent of reactive yellow, 0.21 percent of reactive brilliant blue, 20g/l of anhydrous sodium sulphate, 10g/l of soda ash and 1g/l of water softener
The temperature is 60 deg.C, and the time is 50 min.
The soaping formula comprises: soaping agent (535)1g/l, acetic acid 1 g/l. The temperature is 80 deg.C, and the time is 20 min.
(7) Dehydrating and scutching;
(8) shaping and drying: the temperature is 160 ℃, the vehicle speed is 50m/min, and the overfeeding is 0.5 percent.
(9) Softening and finishing: the temperature is 160 ℃, the vehicle speed is 40m/min, the overfeed is 1 percent, the hydrophilic softening agent is 40g/l, and the moisture absorption and sweat releasing finishing agent is 40 g/l.
(10) Decating: a KD series of pot steamers are adopted, the steam temperature is 160 ℃, the pressure is 0.6bar, the steam temperature is 120s from inside to outside, the steam temperature is 150s from outside to inside, and the decating temperature is 100 ℃.
(11) And (6) checking and packaging.
Comparative example 1
The production method of the shirt fabric is the same as the example 1, and is different from the following steps: pure polyester fabric is adopted, and only bulk materials are dyed.
Comparative example 2
The production method of the shirt fabric is the same as the example 1, and is different from the following steps: pure cotton fabric is adopted, and only active materials are dyed.
The fabrics prepared in the examples and the comparative examples are subjected to performance detection, and the detection results are shown in table 1.
TABLE 1 test results
Crease recovery angle | Drip spreading time | Breaking strength | |
Example 1 | 260 | 1.7s | 670N |
Example 2 | 240 | 1.5 | 658N |
Comparative example 1 | 248 | 3s | 702N |
Comparative example 2 | 212 | 1s | 589N |
It can be seen from table 1 that the cotton-covered polyester fiber fabric is processed by the dyeing and finishing process, so that the characteristics of high strength and stiffness of the polyester fiber are maintained, the skin-friendly property of the pure polyester fiber is improved, the low strength of the cotton fiber is covered, the crease-resistant resilience is improved, and the fabric is comfortable and skin-friendly and is stiff and tangible in wearing.
Claims (8)
1. A production method of cotton-covered polyester shirt fabric is characterized by comprising the following steps: the method comprises the following specific steps:
(1) preparing a grey fabric: the polyester-cotton core-spun yarn plain cloth consists of 50% of terylene and 50% of cotton fiber, wherein the cotton fiber is wound outside the terylene filament, the gram weight is 210g/m, and each cylinder is 800-1200 meters;
(2) boiling and bleaching: treating the fabric by using a high-temperature high-pressure overflow dyeing machine and adopting mixed liquor of caustic soda, hydrogen peroxide, a refined deoiling agent, a high-efficiency penetrating agent and a chelating dispersant;
(3) shaping and drying;
(4) singeing: a natural gas singeing machine is adopted, singeing is carried out on a fire hole in a forward direction and a reverse direction, and the speed is 80-100 m/min;
(5) mercerizing:
(6) dyeing:
the formula of the disperse dye dyed terylene comprises: 0.3 percent of disperse blue, 0.02 percent of disperse orange, 0.04 percent of disperse red jade, 1g/l of acetic acid, 2g/l of level dyeing dispersant and 1g/l of water softener;
the temperature is 130 ℃, and the time is 30-50 min;
the formula of the cotton dyed by the reactive dye comprises the following steps: 0.01 percent of reactive red, 0.02 percent of reactive yellow, 0.21 percent of reactive brilliant blue, 20g/l of anhydrous sodium sulphate, 10g/l of soda ash and 1g/l of water softener;
the temperature is 60 ℃, and the time is 30-50 min;
the soaping formula comprises: soaping agent 1g/l, acetic acid 1g/l, temperature 80 deg.C, time 20 min;
(7) dehydrating and scutching;
(8) shaping and drying;
(9) softening and finishing: the temperature is 160 ℃, the speed is 40m/min, the overfeed is 1%, the hydrophilic softening agent is 20-40g/l, and the moisture absorption and sweat releasing finishing agent is 10-50 g/l;
(10) decating;
(11) and (6) checking and packaging.
2. The method for producing a cotton-covered polyester shirt fabric according to claim 1, which is characterized in that: in the step (2), the boiling and bleaching specifically comprises the following steps: the high-temperature high-pressure overflow dyeing machine is used, and the mixed solution of 2g/l of caustic soda, 4g/l of hydrogen peroxide, 1.5g/l of refined degreaser, 1g/l of high-efficiency penetrant and 3g/l of chelating dispersant is adopted for processing at the temperature of 100 ℃ for 40 min.
3. The method for producing a cotton-covered polyester shirt fabric according to claim 2, characterized in that: the refined deoiling agent is DR-N6, the high-efficiency penetrating agent is TX, and the chelating dispersant is DR-99.
4. The method for producing a cotton-covered polyester shirt fabric according to claim 1, which is characterized in that: in the step (3), the shaping and drying are carried out at the temperature of 180 ℃ for 30-50s, the speed of 40m/min and the overfeeding is 2%.
5. The method for producing a cotton-covered polyester shirt fabric according to claim 1, which is characterized in that: in the step (5), the mercerizing is as follows: the treatment is carried out by adopting 220g/l caustic soda solution, and the vehicle speed is 50 m/min.
6. The method for producing a cotton-covered polyester shirt fabric according to claim 1, which is characterized in that: in the step (6), the soaping agent is a soaping agent 535.
7. The method for producing a cotton-covered polyester shirt fabric according to claim 1, which is characterized in that: in the step (8), the shaping and drying are carried out at the temperature of 160 ℃, the vehicle speed of 50m/min and the overfeeding is 0.5 percent.
8. The method for producing a cotton-covered polyester shirt fabric according to claim 1, which is characterized in that: in the step (10), the decating is as follows: a KD series of pot steamers are adopted, the steam temperature is 160 ℃, the pressure is 0.6bar, the steam temperature is 120s from inside to outside, the steam temperature is 150s from outside to inside, and the decating temperature is 100 ℃.